Nanometre-scale 3D defects in Cr₂AlC thin films.

ABSTRACT: MAX-phase Cr₂AlC containing thin films were synthesized by magnetron sputtering in an industrial system. Nanometre-scale 3D defects are observed near the boundary between regions of Cr₂AlC and of the disordered solid solution (CrAl)_xC_y. Shrinkage of the Cr-Cr interplanar distance and elongation of the Cr-Al distance in the vicinity of the defects are detected using transmission electron microscopy. The here observed deformation surrounding the defects was described using density functional theory by comparing the DOS of bulk Cr₂AlC with the DOS of a strained and unstrained Cr₂AlC(0001) surface. From the partial density of states analysis, it can be learned that Cr-C bonds are stronger than Cr-Al bonds in bulk Cr₂AlC. Upon Cr₂AlC(0001) surface formation, both bonds are weakened. While the Cr-C bonds recover their bulk strength as Cr₂AlC(0001) is strained, the Cr-Al bonds experience only a partial recovery, still being weaker than their bulk counterparts. Hence, the strain induced bond strengthening in Cr₂AlC(0001) is larger for Cr d - C p bonds than for Cr d - Al p bonds. The here observed changes in bonding due to the formation of a strained surface are consistent with the experimentally observed elongation of the Cr-Al distance in the vicinity of nm-scale 3D defects in Cr₂AlC thin films.

SUBMITTER: Chen YT 

PROVIDER: S-EPMC5430507 | biostudies-literature | 2017 Apr

REPOSITORIES: biostudies-literature