Delayed diagnosis of catastrophic ceramic liner failure with resultant pelvic discontinuity and massive metallosis.

ABSTRACT: With newer-generation ceramic components used in total hip arthroplasty, component fracture is a rare complication. However rare, when ceramic component fracture does occur, prompt identification and revision is necessary as delay can lead to dramatic failure with resultant metallosis as the extremely hard ceramic debris abrades remaining components. We present a case of a 70-year-old woman with ceramic liner fracture and an estimated 10-year delay in intervention with failure resulting in pelvic discontinuity and massive metallosis with associated cutaneous manifestation. She was treated with a complex revision and reconstruction and is 2 years postrevision without major complication.

SUBMITTER: Winston BA

PROVIDER: S-EPMC5485230 | biostudies-literature | 2017 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Delayed diagnosis of catastrophic ceramic liner failure with resultant pelvic discontinuity and massive metallosis.

Winston Benjamin A BA Kagan Ryland P RP Huff Thomas W TW

Arthroplasty today 20161201 2

With newer-generation ceramic components used in total hip arthroplasty, component fracture is a rare complication. However rare, when ceramic component fracture does occur, prompt identification and revision is necessary as delay can lead to dramatic failure with resultant metallosis as the extremely hard ceramic debris abrades remaining components. We present a case of a 70-year-old woman with ceramic liner fracture and an estimated 10-year delay in intervention with failure resulting in pelvi ...[more]

PMID: 28695178

Similar Datasets

Liner dissociation leading to catastrophic failure of an Oxinium femoral head.

Project description:Oxinium is an alternative bearing surface designed to emulate the superior wear and scratch properties of ceramic femoral heads in total hip arthroplasty while minimizing the risk for brittle fracturing. However, recent studies have indicated that hip dislocation following total hip arthroplasty may be a risk factor for catastrophic failure of the femoral head. Here, we report on a novel case of a catastrophic Oxinium head and polyethylene liner failure in the absence of previous hip dislocation or trauma and review the probable failure mechanism. This report underscores the need to be vigilant about proper acetabular cup and liner seating, particularly in the setting of Oxinium femoral head use. In the event of Oxinium head failure, metallosis may compromise stabilizing soft tissues including the abductors. Dual-mobility articulation, which was successful in this case, is one option to consider when the risk for chronic redislocation is elevated.

| S-EPMC6470327 | biostudies-literature

Ceramic liner fracture and impingement in total hip arthroplasty.

Project description:BackgroundCeramic-on-ceramic bearing surfaces were developed to provide an alternate to metal-on-polyethylene to decrease wear-induced osteolysis in total hip arthroplasty patients. In an effort to decrease the risk of ceramic acetabular component fracture or damage during implantation, a raised metal rim was added.Questions/purposesHow many fractures or impingements have occurred in our population of patients with ceramic liners with raised rims?MethodsWith IRB-approved consent, a case series was reviewed from a single center registry and 4 of 169 patients were identified who had revision hip surgery with the ceramic liner with a raised metal rim: one for ceramic liner fracture and three for metallosis, pain, and squeaking. Implant alignment and operative findings were reviewed.ResultsOne ceramic liner fracture and three cases of metallosis from impingement of the femoral neck on the posterior elevated metal rim of the acetabular liner were observed at revision. The femoral neck in each patient had a divot that corresponded to a divot in the posterosuperior liner rim. Three of the four patients had audible squeaking or clicking prior to revision. A total of 3% of patients in this series had clinically significant impingement with this implant type.ConclusionAcoustic phenomenon in a ceramic on ceramic bearing surface should be investigated with a cross-table lateral radiograph to evaluate component position. If symptomatic impingement is demonstrated, revision should be considered to avoid failure from metallosis or fracture.

| S-EPMC4342397 | biostudies-literature

Bilateral pelvic discontinuity: a unique condition characterized by high failure rates of current treatment.

Project description:BackgroundBilateral pelvic discontinuity is characterized by complete dissociation of the superior and inferior pelvis secondary to bone loss or fracture. The end result is a freely mobile inferior pelvis at the level of each discontinuity which presents a significant reconstruction challenge. This clinical entity has not been described previously, and the results of surgical treatment are not known.MethodsWe retrospectively reviewed all identified cases of pelvic discontinuity (PD) treated with revision THA at one institution. We identified 133 pelvic discontinuities. Within this group, 6 patients had bilateral simultaneous PDs. Preoperative, intraoperative, and postoperative data and radiographic imaging were reviewed preoperatively and postoperatively for the characteristics of the dissociation and assessing PD healing and fixation of components after surgery.ResultsThere were no preoperative factors that could distinguish these patients from the rest of the group of discontinuities (3 rheumatoid arthritis, 2 osteonecrosis of the femoral head, 1 developmental dysplasia). The reconstructions performed included 2 cup/cage, 5 posterior plating and uncemented cup, 3 cage alone, and 2 cups only. Ten of 12 hips had at least 1 complication postoperatively. At final follow-up, only 1 patient (17%) had radiographic evidence that both discontinuities had healed (posterior plate with uncemented cup).ConclusionsBilateral pelvic discontinuity is rare but presents the surgeon with a major reconstructive challenge. Only 1 patient went on to radiographic healing with current treatment strategies. Continued motion of the contralateral pelvic dissociation may account for the high failure rates. Surgeons should be aware of the challenges presented by this diagnosis and develop strategies to improve outcomes.

| S-EPMC5247510 | biostudies-literature

Early failure with massive metallosis and posteromedial wear following atraumatic anterior cruciate ligament rupture after medial unicompartmental knee arthroplasty.

Project description:Severe metallosis following medial unicompartmental knee arthroplasty (UKA) is relatively rare. It is usually due to long-standing wear of the polyethylene component, resulting in frictional wear between the femoral and tibial metallic components. Biomechanical and cadaveric studies have shown the effects of anterior cruciate ligament (ACL) transection following medial UKA. We describe a case of a 58-year-old male who developed attritional rupture of the ACL 16 months following medial UKA leading on to early accelerated failure over the next 8 months. The patient underwent revision to total knee arthroplasty with good outcome. The clinical effect of spontaneous ACL transection on medial UKA causing abnormal posteromedial wear of polyethylene component and tibial tray, massive metallosis, and worsening of mechanical axis can be demonstrated in this case report.

| S-EPMC5859552 | biostudies-literature

A review of the treatment of pelvic discontinuity.

Project description:Pelvic discontinuity is a complex entity with a high surgical complication rate and no standardized treatment to date. Revision hip arthroplasty in cases of massive bone loss remains a difficult and unsolved problem. The goal of the surgeon is to preserve limb function by restoring bone stock and the biomechanics of the hip. In cases of severe acetabular bone loss, biologic fixation is often inadequate, requiring extensive bone grafting and reconstructive cages. Reconstructive cages are the most commonly used devices and are designed to bridge bone defects, protect the bone graft, and reestablish the rotation center of the hip. A major limitation of current cages is that they do not allow for biologic fixation. We review the options for treating patients with massive bone loss and pelvic discontinuity and discuss therapeutic options and the clinical and radiological criteria for success.

| S-EPMC2553162 | biostudies-other

High Risk of Neck-liner Impingement and Notching Observed with Thick Femoral Neck Implants in Ceramic-on-ceramic THA.

Project description: Not available

| S-EPMC8923570 | biostudies-literature

A Simple Technique to Remove an Incarcerated Ceramic Liner in Revision Hip Arthroplasty.

Project description:Extraction of a well-fixed ceramic liner during revision total hip arthroplasty can be technically challenging, particularly when acetabular fixation screws prevent en bloc removal of the shell and insert without causing collateral damage to the adjacent pelvic bone. It is also important to remove the ceramic liner intact, as ceramic debris left in the joint may cause third body wear with premature articular wear of the revised implants. We describe a novel technique to extract an incarcerated ceramic liner when previously described strategies prove ineffective. Knowledge of this technique will help surgeons avoid unnecessary damage to the acetabular bone and optimize prospects for stable implantation of revision components.

| S-EPMC10185739 | biostudies-literature

Surgeons' Awareness and Impaction Technique of a Ceramic Liner into a Metal Shell.

Project description:BackgroundIn ceramic-on-ceramic total hip arthroplasty, firm locking is necessary between a ceramic liner and an acetabular metal shell to prevent dissociation of the liner from the metal shell. We evaluated surgeons' awareness of the technique for inserting the ceramic liner and measured the impaction force applied by surgeons during the insertion of the ceramic liner.MethodsTo evaluate the awareness, we conducted a survey using a questionnaire including techniques for ceramic liner insertion. The impaction force was measured using an impaction simulator in 224 surgeons.ResultsMost surgeons answered that they cleaned and dried up the inner surface of the metal shell before inserting a ceramic liner (96.4% and 86.2%, respectively), and 74.6% checked the correct seating of the ceramic liner. However, only 23.2% correctly answered that a minimum of 2kN (a light strike) was necessary to obtain a sufficient fit between the metal shell and the ceramic liner. The impaction force was weaker than 2 kN in 9.4% of the surgeons.ConclusionsEducation about the adequate impaction force to obtain a firm fit of the ceramic liner is necessary for surgeons who perform total hip arthroplasty using ceramic-on-ceramic bearings.

| S-EPMC9152890 | biostudies-literature

Triflange acetabular reconstruction for pelvic discontinuity through a direct anterior approach.

Project description:A 74-year-old female patient presented to our clinic with pelvic discontinuity after multiple revision total hip surgeries requiring custom triflange acetabular reconstruction, which we accomplished through a direct anterior approach to the hip. The direct anterior approach to the hip has grown in popularity but still has the reputation of being a minimally invasive approach without the capacity for extensile exposure in the revision setting. We describe the extensile technique and demonstrate through our case the ability to perform the most challenging cases through this approach and discuss the potential benefits of its utilization.

| S-EPMC6920714 | biostudies-literature

Massive genomic rearrangement acquired in a single catastrophic event during cancer development.

Project description:Cancer is driven by somatically acquired point mutations and chromosomal rearrangements, conventionally thought to accumulate gradually over time. Using next-generation sequencing, we characterize a phenomenon, which we term chromothripsis, whereby tens to hundreds of genomic rearrangements occur in a one-off cellular crisis. Rearrangements involving one or a few chromosomes crisscross back and forth across involved regions, generating frequent oscillations between two copy number states. These genomic hallmarks are highly improbable if rearrangements accumulate over time and instead imply that nearly all occur during a single cellular catastrophe. The stamp of chromothripsis can be seen in at least 2%-3% of all cancers, across many subtypes, and is present in ?25% of bone cancers. We find that one, or indeed more than one, cancer-causing lesion can emerge out of the genomic crisis. This phenomenon has important implications for the origins of genomic remodeling and temporal emergence of cancer.

| S-EPMC3065307 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data