29Si NMR and SAXS investigation of the hybrid organic-inorganic glasses obtained by consolidation of the melting gels.

ABSTRACT: This study is focused on structural characterization of hybrid glasses obtained by consolidation of melting gels. The melting gels were prepared in molar ratios of methyltriethoxysilane (MTES) and dimethyldiethoxysilane (DMDES) of 75%MTES-25%DMDES and 65%MTES-35%DMDES. Following consolidation, the hybrid glasses were characterized using Raman, 29Si and 13C Nuclear Magnetic Resonance (NMR) spectroscopies, synchrotron Small Angle X-Ray Scattering (SAXS) and scanning electron microscopy (SEM). Raman spectroscopy revealed the presence of Si-C bonds in the hybrid glasses and 8-membered ring structures in the Si-O-Si network. Qualitative NMR spectroscopy identified the main molecular species, while quantitative NMR data showed that the ratio of trimers (T) to dimers (D) varied between 4.6 and 3.8. Two-dimensional 29Si NMR data were used to identify two distinct types of T3 environments. SAXS data showed that the glasses are homogeneous across the nm to micrometer length scales. The scattering cross section was one thousand times lower than what is expected when phase separation occurs. The SEM images show a uniform surface without defects, in agreement with the SAXS results, which further supports that the hybrid glasses are nonporous.

SUBMITTER: Jitianu A

PROVIDER: S-EPMC5542885 | biostudies-literature | 2017 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

29Si NMR and SAXS investigation of the hybrid organic-inorganic glasses obtained by consolidation of the melting gels.

Jitianu Andrei A Cadars Sylvian S Zhang Fan F Rodriguez Gabriela G Picard Quentin Q Aparicio Mario M Mosa Jadra J Klein Lisa C LC

Dalton transactions (Cambridge, England : 2003) 20170301 11

This study is focused on structural characterization of hybrid glasses obtained by consolidation of melting gels. The melting gels were prepared in molar ratios of methyltriethoxysilane (MTES) and dimethyldiethoxysilane (DMDES) of 75%MTES-25%DMDES and 65%MTES-35%DMDES. Following consolidation, the hybrid glasses were characterized using Raman, 29Si and 13C Nuclear Magnetic Resonance (NMR) spectroscopies, synchrotron Small Angle X-Ray Scattering (SAXS) and scanning electron ...[more]

PMID: 28262904

Similar Datasets

Project description:Three poly(organosiloxanes) (hydromethyl-, dimethyl-, and epoxymethylsiloxane) of different chain lengths and pendant groups and their mixtures of dimethyl (DMC) or diethyl carbonates (DEC) were applied in the modification of fumed silica nanoparticles (FSNs). The resulting modified silicas were studied in depth using 29Si, 1H, and 13C solid-state NMR spectroscopy, elemental analysis, and nitrogen adsorption-desorption (BET) analysis. The obtained results reveal that the type of grafting, grafting density, and structure of the grafted species at the silica surface depend strongly on the length of organosiloxane polymer and on the nature of the "green" additive, DMC or DEC. The spectral changes observed by solid-state NMR spectroscopy suggest that the major products of the reaction of various organosiloxanes and their DMC or DEC mixtures with the surface are D (RR'Si(O0.5)2) and T (RSi(O0.5)3) organosiloxane units. It was found that shorter methylhydro (PMHS) and dimethylsiloxane (PDMS) and their mixtures with DMC or DEC form a denser coverage at the silica surface since SBET diminution is larger and grafting density is higher than the longest epoxymethylsiloxane (CPDMS) used for FSNs modification. Additionally, for FSNs modified with short organosiloxane PMHS/DEC and also medium organosiloxane PDMS/DMC, the dense coverage formation is accompanied by a greater reduction of isolated silanols, as shown by solid-state 29Si NMR spectroscopy, in contrast to reactions with neat organosiloxanes. The surface coverage at FSNs with the longest siloxane (CPDMS) greatly improves with the addition of DMC or DEC. The data on grafting density suggest that molecules in the attached layers of FSNs modified with short PMHS and its mixture of DMC or DEC and medium PDMS and its mixture of DMC form a "vertical" orientation of the grafted methylhydrosiloxane and dimethylsiloxane chains, in contrast to the reaction with PDMS/DEC and epoxide methylsiloxane in the presence of DMC or DEC, which indicates a "horizontal" chain orientation of the grafted methyl and epoxysiloxane molecules. This study highlights the major role of solid-state NMR spectroscopy for comprehensive characterization of solid surfaces.

Dataset Information

29Si NMR and SAXS investigation of the hybrid organic-inorganic glasses obtained by consolidation of the melting gels.

Publications

<sup>29</sup>Si NMR and SAXS investigation of the hybrid organic-inorganic glasses obtained by consolidation of the melting gels.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets