Dataset Information

The Bioactivity and Photocatalytic Properties of Titania Nanotube Coatings Produced with the Use of the Low-Potential Anodization of Ti6Al4V Alloy Surface.

ABSTRACT: Titania nanotube (TNT) coatings were produced using low-potential anodic oxidation of Ti6Al4V substrates in the potential range 3-20 V. They were analysed by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). The wettability was estimated by measuring the contact angle when applying water droplets. The bioactivity of the TNT coatings was established on the basis of the biointegration assay (L929 murine fibroblasts adhesion and proliferation) and antibacterial tests against Staphylococcus aureus (ATCC 29213). The photocatalytic efficiency of the TNT films was studied by the degradation of methylene blue under UV irradiation. Among the studied coatings, the TiO? nanotubes obtained with the use of 5 V potential (TNT5) were found to be the most appropriate for medical applications. The TNT5 sample possessed antibiofilm properties without enriching it by additional antimicrobial agent. Furthermore, it was characterized by optimal biocompatibility, performing better than pure Ti6Al4V alloy. Moreover, the same sample was the most photocatalytically active and exhibited the potential for the sterilization of implants with the use of UV light and for other environmental applications.

SUBMITTER: Radtke A

PROVIDER: S-EPMC5575679 | biostudies-literature | 2017 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The Bioactivity and Photocatalytic Properties of Titania Nanotube Coatings Produced with the Use of the Low-Potential Anodization of Ti6Al4V Alloy Surface.

Radtke Aleksandra A Topolski Adrian A Jędrzejewski Tomasz T Kozak Wiesław W Sadowska Beata B Więckowska-Szakiel Marzena M Szubka Magdalena M Talik Ewa E Pleth Nielsen Lars L Piszczek Piotr P

Nanomaterials (Basel, Switzerland) 20170726 8

Titania nanotube (TNT) coatings were produced using low-potential anodic oxidation of Ti6Al4V substrates in the potential range 3-20 V. They were analysed by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). The wettability was estimated by measuring the contact angle when applying water droplets. The bioactivity of the TNT coatings was established on the basis of the biointegration assay (L929 murine fibroblasts adhesion ...[more]

PMID: 28933732

Similar Datasets

Project description:Titania nanotube (TNT) powder was prepared by rapid breakdown anodization (RBA) in a perchloric acid electrolyte. The photocatalytic efficiency of the as-prepared and powders annealed at temperatures between 250 and 550 °C was tested under UV and natural sunlight irradiation by decolorization of both anionic and cationic organic dyes, i.e., methyl orange (MO) and rhodamine B (RhB), as model pollutants. The tubular structure of the nanotubes was retained up to 250 °C, while at 350 °C and above, the nanotubes transformed into nanorods and nanoparticles. Depending on the annealing temperature, the TNTs consist of anatase, mixed anatase/brookite, or anatase/rutile phases. The bandgap of the as-prepared nanotubes is 3.04 eV, and it shifts towards the visible light region upon annealing. The X-ray photoelectron spectroscopy (XPS) results show the presence of titania and impurities including chlorine on the surface of the TNTs. The atomic ratio of Ti/O remains unchanged for the annealed TNTs, but the concentration of chlorine decreases with temperature. The photoluminescence (PL) indicate high electron-hole recombination for the as-prepared TNTs, probably due to the residual impurities, low crystallinity, and vacancies in the structure, while the highest photocurrent was observed for the TNT sample annealed at 450 °C. The TNTs induce a small degradation of the dyes under UV light; however, contrary to previous reports, complete decolorization of dyes is observed under sunlight. All TNT samples showed higher decolorization rates under sunlight irradiation than under UV light. The highest reaction rate for the TNT samples was obtained for the as-prepared TNT powder sample under sunlight using RhB (?1 = 1.29 h-1). This is attributed to the bandgap, specific surface area and the crystal structure of the nanotubes. The as-prepared TNTs performed most efficiently for decolorization of RhB and outperformed the reference anatase powder under sunlight irradiation. This could be attributed to the abundance of reactive sites, higher specific surface area, and degradation mechanism of RhB. These RBA TNT photocatalyst powders demonstrate a more efficient use of the sunlight spectrum, making them viable for environmental remediation.

Project description:It is well-known that the structure and composition of the material plays an important role in the processes occurring at the surface. In this paper, a surface morphology of nanostructured oxide layers electrochemically grown on Ti15Mo, tuned by applying different anodization parameters, was investigated in detail. The one-step anodization of Ti15Mo alloy was performed at room temperature in an ethylene glycol-based electrolyte containing 0.11 M NH4F and 1.11 M H2O. Different anodization times (ranging from 5 to 60 min) and applied potentials (40-100 V) were tested, and the surface morphology, elemental content, and crystalline structure were monitored by scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDS), and X-ray diffractometry (XRD), respectively. The results showed that contrary to the multistep anodization of titanium foil, the surface morphology of anodic oxide obtained via the one-step process contains the nanoporous outer layer covering the nanotubular structure. What is more, the pore diameter (Dp) and interpore distance (Dint) of such layers exhibit different trends than those observed for anodization of pure titanium. In particular, at a certain potential range, a decrease in both Dp and Dint with increasing potential was observed. However, independently on the used anodization conditions, the elemental content of oxide layers remained similar, showing the amount of molybdenum at c.a. 15 wt.%. Finally, the amorphous nature of as-anodized layers was confirmed, and their optical band-gap was determined from the diffuse reflectance UV-Vis spectra. It was found that Eg is tunable to some extent by changing the anodizing potential. However, further thermal treatment in air at 400 °C resulted in the anatase phase formation that was accompanied by a significant Eg reduction. Therefore, we believe that the presented results will greatly contribute to the understanding of anodic formation of nanostructured functional oxide layers with tunable properties that can be applied in various fields.

Dataset Information

The Bioactivity and Photocatalytic Properties of Titania Nanotube Coatings Produced with the Use of the Low-Potential Anodization of Ti6Al4V Alloy Surface.

Publications

The Bioactivity and Photocatalytic Properties of Titania Nanotube Coatings Produced with the Use of the Low-Potential Anodization of Ti6Al4V Alloy Surface.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets