Biocompatibility and Corrosion Protection Behaviour of Hydroxyapatite Sol-Gel-Derived Coatings on Ti6Al4V Alloy.

ABSTRACT: The aim of this work was to prepare hydroxyapatite coatings (HAp) by a sol-gel method on Ti6Al4V alloy and to study the bioactivity, biocompatibility and corrosion protection behaviour of these coatings in presence of simulated body fluids (SBFs). Thermogravimetric/Differential Thermal Analyses (TG/DTA) and X-ray Diffraction (XRD) have been applied to obtain information about the phase transformations, mass loss, identification of the phases developed, crystallite size and degree of crystallinity of the obtained HAp powders. Fourier Transformer Infrared Spectroscopy (FTIR) has been utilized for studying the functional groups of the prepared structures. The surface morphology of the resulting HAp coatings was studied by Scanning Electron Microscopy (SEM). The bioactivity was evaluated by soaking the HAp-coatings/Ti6Al4V system in Kokubo's Simulated Body Fluid (SBF) applying Inductively Coupled Plasma (ICP) spectrometry. 3-[4,5-dimethylthiazol-2-yl]-2,5-diphenyl tetrazolium bromide (MTT) and Alamar blue cell viability assays were used to study the biocompatibility. Finally, the corrosion behaviour of HAp-coatings/Ti6Al4V system was researched by means of Electrochemical Impedance Spectroscopy (EIS). The obtained results showed that the prepared powders were nanocrystalline HAp with little deviations from that present in the human bone. All the prepared HAp coatings deposited on Ti6Al4V showed well-behaved biocompatibility, good bioactivity and corrosion protection properties.

SUBMITTER: El Hadad AA

PROVIDER: S-EPMC5459123 | biostudies-other | 2017 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Electrochemical data of single and hybrid sol-gel coating precursors for aluminum alloy corrosion protection in 3.5% NaCl.

Project description:The anti-corrosion performances of single(TEOS) and hybrid (APTES-TEOS) sol-gel coatings on Al alloy samples exposed to 3.5 wt% NaCl were evaluated employing electrochemical techniques such as electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The data acquired using the three corrosion analysis techniques were in accordance with each other where hybrid sol-gel coating offered the lowest corrosion rate and current density in comparison to the single precursor silanol coating. Tafel curves suggested that the hybrid silane coatings mitigate both the anodic and cathodic reactions simultaneously (mixed type inhibitor). These techniques justified that incorporation of hybrid sol-gel improved the Al corrosion protection performance considerably.

| S-EPMC6355958 | biostudies-literature

Clinoenstatite/Tantalum Coating for Enhancement of Biocompatibility and Corrosion Protection of Mg Alloy.

Project description:Biodegradable Mg alloys have appeared as the most appealing metals for biomedical applications, particularly as temporary bone implants. However, issues regarding high corrosion rate and biocompatibility restrict their application. Hence, in the present work, nanostructured clinoenstatite (CLT, MgSiO3)/tantalum nitride (TaN) was deposited on the Mg-Ca-Zn alloy via electrophoretic deposition (EPD) along with physical vapor deposition (PVD) to improve the corrosion and biological characteristics of the Mg-Ca-Zn alloy. The TaN intermediate layer with bubble like morphology possessed a compact and homogenous structure with a thickness of about 950 nm while the thick CLT over-layer (~15 ?m) displayed a less compact structure containing nano-porosities as well as nanoparticles with spherical morphology. The electrochemical tests demonstrated that the as prepared CLT/TaN film is able to substantially increase the anticorrosion property of Mg-Ca-Zn bare alloy. Cytocompatibility outcomes indicated that formation of CLT and TaN on the Mg bare alloy surface enhanced cell viability, proliferation and growth, implying excellent biocompatibility. Taken together, the CLT/TaN coating exhibits appropriate characteristic including anticorrosion property and biocompatibility in order to employ in biomedical files.

| S-EPMC7353525 | biostudies-literature

Marine Polysaccharide-Collagen Coatings on Ti6Al4V Alloy Formed by Self-Assembly.

Project description:Polysaccharides of marine origin are gaining interest as biomaterial components. Bacteria derived from deep-sea hydrothermal vents can produce sulfated exopolysaccharides (EPS), which can influence cell behavior. The use of such polysaccharides as components of organic, collagen fibril-based coatings on biomaterial surfaces remains unexplored. In this study, collagen fibril coatings enriched with HE800 and GY785 EPS derivatives were deposited on titanium alloy (Ti6Al4V) scaffolds produced by rapid prototyping and subjected to physicochemical and cell biological characterization. Coatings were formed by a self-assembly process whereby polysaccharides were added to acidic collagen molecule solution, followed by neutralization to induced self-assembly of collagen fibrils. Fibril formation resulted in collagen hydrogel formation. Hydrogels formed directly on Ti6Al4V surfaces, and fibrils adsorbed onto the surface. Scanning electron microscopy (SEM) analysis of collagen fibril coatings revealed association of polysaccharides with fibrils. Cell biological characterization revealed good cell adhesion and growth on bare Ti6Al4V surfaces, as well as coatings of collagen fibrils only and collagen fibrils enhanced with HE800 and GY785 EPS derivatives. Hence, the use of both EPS derivatives as coating components is feasible. Further work should focus on cell differentiation.

| S-EPMC6356479 | biostudies-literature

Corrosion Resistance of Heat-Treated Ni-W Alloy Coatings.

Project description:The paper presents research on evaluation of corrosion resistance of Ni-W alloy coatings subjected to heat treatment. The corrosion resistance was tested in 5% NaCl solution by the use of potentiodynamic polarization technique and electrochemical impedance spectroscopy. Characteristics of the Ni-W coatings after heat treatment were carried out using scanning electron microscopy, scanning Kelvin probe technique and X-ray diffraction. Suggested reasons for the improvement of properties of the heat treated Ni-W coating, obtained at the lowest current density value (125 mA?cm-2), are the highest tungsten content (c.a. 25 at.%) as well as the smallest and the most homogeneous electrochemically active surface area.

| S-EPMC7085042 | biostudies-literature

Ultrasound-Assisted Hydroxyapatite-Decorated Breath-Figure Polymer-Derived Ceramic Coatings for Ti6Al4V Substrates.

Project description:The introduction of nanoparticles (NPs) into the breath-figure-templated self-assembly (BFTSA) process is an increasingly common method to selectively decorate a surface porous structure. In the field of prosthetic devices, besides controlling the morphology and roughness of the structure, NPs can enhance the osteointegration mechanism because of their specific ion release. Among the most widely used NPs, there are silica and hydroxyapatite (HAp). In this work, we propose a novel one-stage method to fabricate NP-decorated surface porous structures that are suitable for prosthetic coating applications. This technique combines the classical direct BFTSA process with the cavitation effect induced by an ultrasonic atomizer that generates a mist of water droplets with embedded NPs. Coatings were successfully obtained by combining a UV cross-linkable polymer precursor, alkoxy silicone, with synthesized HAp NPs, on Ti6Al4V alloy discs. The cross-linked polymeric surface porous structures at selected concentrations were then pyrolyzed in an ammonia atmosphere to obtain a silicon oxynitride (SiON) ceramic coating. Herein, we report the chemical and morphological analyses of both the polymeric and ceramic coatings as well as the effect of NPs at the interface.

| S-EPMC8016169 | biostudies-literature

Study of Different Sol-Gel Coatings to Enhance the Lifetime of PDMS Devices: Evaluation of Their Biocompatibility.

Project description:A study of PDMS (polydimethylsiloxane) sol-gel-coated channels fabricated using soft lithography and a laser direct writing technique is presented. PDMS is a biocompatible material that presents a high versatility to reproduce several structures. It is widely employed in the fabrication of preclinical devices due to its advantages but it presents a rapid chemical deterioration to organic solvents. The use of sol-gel layers to cover the PDMS overcomes this problem since it provides the robustness of glass for the structures made with PDMS, decreasing its deterioration and changing the biocompatibility of the surface. In this work, PDMS channels are coated with three different kinds of sol-gel compositions (60MTES/40TEOS, 70MTES/30TISP and 80MTES/20TISP). The endothelial cell adhesion to the different coated devices is evaluated in order to determine the most suitable sol-gel preparation conditions to enhance cellular adhesion.

| S-EPMC5457110 | biostudies-other

Fretting and Fretting Corrosion Processes of Ti6Al4V Implant Alloy in Simulated Oral Cavity Environment.

Project description:The paper presents the results of in vitro studies of fretting and fretting corrosion processes of Ti6Al4V implant alloy in the environment of natural saliva and self-made mucin-based artificial saliva solutions. The study was performed on a specially designed fretting pin-on-disc tester, which was combined with a set used for electrochemical research. The open circuit potential measurements and potentiodynamic method were used for corrosion tests. The worn surfaces were subjected to microscopic observations and an evaluation of wear. Results were interpreted using the dissipated energy and third-body approaches. The X-ray diffraction analysis showed that titanium oxides constitute over 80% of the friction products. Special attention was paid to the role of saliva and its substitutes, which in certain cases can lead to the intensification of fretting wear. On the basis of the received results, a new phenomenological model of fretting corrosion processes was proposed. This model involves the formation of an abrasive paste that is a combination of metal oxides and the organic components of saliva.

| S-EPMC7177599 | biostudies-literature

Effect of reaction solvent on hydroxyapatite synthesis in sol-gel process.

Project description:Synthesis of hydroxyapatite (HA) through sol-gel process in different solvent systems is reported. Calcium nitrate tetrahydrate (CNTH) and diammonium hydrogen phosphate (DAHP) were used as calcium and phosphorus precursors, respectively. Three different synthesis reactions were carried out by changing the solvent media, while keeping all other process parameters constant. A measure of 0.5?M aqueous DAHP solution was used in all reactions while CNTH was dissolved in distilled water, tetrahydrofuran (THF) and N,N-dimethylformamide (DMF) at a concentration of 0.5?M. Ammonia solution (28-30%) was used to maintain the pH of the reaction mixtures in the 10-12 range. All reactions were carried out at 40?±?2°C for 4?h. Upon completion of the reactions, products were filtered, washed and calcined at 500°C for 2?h. It was clearly demonstrated through various techniques that the dielectric constant and polarity of the solvent mixture strongly influence the chemical structure and morphological properties of calcium phosphate synthesized. Water-based reaction medium, with highest dielectric constant, mainly produced ?-calcium pyrophosphate (?-CPF) with a minor amount of HA. DMF/water system yielded HA as the major phase with a very minor amount of ?-CPF. THF/water solvent system with the lowest dielectric constant resulted in the formation of pure HA.

| S-EPMC5750015 | biostudies-literature

Stable sol-gel hydroxyapatite coating on zirconia dental implant for improved osseointegration.

Project description:Aside from being known for its excellent mechanical properties and aesthetic effect, zirconia has recently attracted attention as a new dental implant material. Many studies have focused on hydroxyapatite (HA) coating for obtaining improved biocompatibility, however the coating stability was reduced by a byproduct produced during the high-temperature sintering process. In this study, to overcome this problem, we simply coated the zirconia surface with a sol-gel-derived hydroxyapatite (HA) layer and then sintered it at a varied temperature (<1000 °C). The surface showed a nanoporous structure, and there was no crystalline phase other than HA and zirconia when the sintering temperature was 800 °C. The adhesion strength of the HA layer (>40 MPa) was also appropriate as a dental implant application. In addition, in vitro cell experiments using a preosteoblast cell line revealed that the HA-coated zirconia surface acts as a preferable surface for cell attachment and proliferation than bare zirconia surface. In vivo animal experiments also demonstrated that the osteoconductivity of zirconia were dramatically enhanced by HA coating, which was comparable to that of Ti implant. These results suggest that the sol-gel-based HA-coated zirconia has a great potential for use as a dental implant material.

| S-EPMC8245356 | biostudies-literature

Sol-Gel Nanocomposite Coatings for Preventing Biofilm Formation on Contact Lens Cases.

Project description:PurposeTo evaluate the efficacy of a nanosilver-based sol-gel coating in preventing biofilm formation on contact lens cases.MethodsAn organic-inorganic hybrid silica-zirconia sol formulation with immobilized silver nanoparticles was deposited on contact lens case coupons. The coated and uncoated coupons were subjected to biofilm formation to Gram-negative and Gram-positive keratitis isolates and ATCC strains using a standard protocol. The biofilms were evaluated using crystal violet, MTT assay, and scanning electron microscope (SEM) examination. The duration of efficacy of the coating was evaluated by exposing the coated and uncoated coupons to a multipurpose lens cleaning solution for various durations up to 30 days and comparing their biofilm characteristics. The cytotoxicity of the coated surface was assessed using cell culture studies.ResultsCross-hatch tests and SEM confirmed the presence of a uniform, well-adhered coating on the surface. The coating resulted in a nearly 95% reduction in biofilm formation of the tested bacteria and was effective despite exposures of up to 30 days to a multipurpose lens cleaning solution. The coating did not exhibit cytotoxicity to human corneal epithelial cells.ConclusionsThe silver nanoparticle-based coating exhibits a good antibiofilm property for both Gram-negative bacilli and Gram-positive cocci and is promising for commercial use in preventing contact lens-related infections.Translational relevanceBiofilm formation on lens cases continues to be an important concern. The proposed coating will help reduce such formations, thus reducing the risk of lens-associated microbial keratitis.

| S-EPMC7794269 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data