Ex-situ X-ray computed tomography data for a non-crimp fabric based glass fibre composite under fatigue loading.

ABSTRACT: The data published with this article are high resolution X-ray computed tomography (CT) data obtained during an ex-situ fatigue test of a coupon test specimen made from a non-crimp fabric based glass fibre composite similar to those used for wind turbine blades. The fatigue test was interrupted four times for X-ray CT examination during the fatigue life of the considered specimen. All the X-ray CT experiments were performed in the region where unidirectional fibre fractures first became visible, and thereby include the damage progression in 3D in this specific region during fatigue loading of the specimen.

SUBMITTER: Jespersen KM

PROVIDER: S-EPMC5684534 | biostudies-literature | 2017 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Ex-situ X-ray computed tomography data for a non-crimp fabric based glass fibre composite under fatigue loading.

Jespersen Kristine M KM Mikkelsen Lars P LP

Data in brief 20171103

The data published with this article are high resolution X-ray computed tomography (CT) data obtained during an ex-situ fatigue test of a coupon test specimen made from a non-crimp fabric based glass fibre composite similar to those used for wind turbine blades. The fatigue test was interrupted four times for X-ray CT examination during the fatigue life of the considered specimen. All the X-ray CT experiments were performed in the region where unidirectional fibre fractures first became visible, ...[more]

PMID: 29159241

Similar Datasets

Ex-situ X-ray computed tomography, tension clamp and in-situ transilluminated white light imaging data of non-crimp fabric based fibre composite under fatigue loading.

Project description:The data published with this paper is obtained during fatigue testing of a unidirectional non-crimp fabric based glass fibre composite by means of ex-situ X-ray CT and in-situ transilluminated white light imaging experiments. The data experimentally shows the damage initiation and progression under fatigue loading both in terms of off-axis cracks in the thin supporting backing fibre bundles and fibre fractures in the load carrying fibre bundles. X-ray CT data comparing the loaded and unloaded state of damage regions by means of a tension clamp solution are also published with this paper.

| S-EPMC6197955 | biostudies-literature

Complementary time-lapse datasets of x-ray computed tomography and real-time strain mapping for an <i>ex-situ</i> study of non-crimp glass fibre composites under fatigue loading.

Project description:Data published in this paper corresponds to a time-lapse ex-situ experiment aimed at analyzing the tension-tension fatigue damage in non-crimp glass-epoxy composites by multi-scale x-ray computed tomography (XCT) of the damage features and their timeline. This is then correlated with the strain fields obtained through digital image correlation (DIC). The XCT - DIC datasets by is acquired by interrupting mechanical fatigue tests at three time-steps, after the material has undergone 0 cycles, 70,000 cycles, 80,000 cycles, and 120,000 cycles. This is one of the first multi-modally correlated datasets available for these types of non-crimp glass fibre composites, which explore the structure-property relationship in a time-dependent behavior. This dataset can be used to explore glass-fibre composites microstructure under a progressive damage scheme and can be used to test and train a plethora of image processing and analysis techniques. This dataset can also be used as an attempt to model the fatigue behavior of quasi-unidirectional non-crimp fibre composites by image-based simulations.

| S-EPMC8167186 | biostudies-literature

Characterisation of the mechanical and fracture properties of a uni-weave carbon fibre/epoxy non-crimp fabric composite.

Project description:A complete database of the mechanical properties of an epoxy polymer reinforced with uni-weave carbon fibre non-crimp fabric (NCF) is established. In-plane and through-the-thickness tests were performed on unidirectional laminates under normal loading and shear loading. The response under cyclic shear loading was also measured. The material has been characterised in terms of stiffness, strength, and failure features for the different loading cases. The critical energy release rates associated with different failure modes in the material were measured from interlaminar and translaminar fracture toughness tests. The stress-strain data of the tensile, compressive, and shear test specimens are included. The load-deflection data for all fracture toughness tests are also included. The database can be used in the development and validation of analytical and numerical models of fibre reinforced plastics (FRPs), in particular FRPs with NCF reinforcements.

| S-EPMC4773377 | biostudies-literature

Scanning electron microscopy datasets for local fibre volume fraction determination in non-crimp glass-fibre reinforced composites.

Project description:The fatigue damage evolution depends on the local fibre volume fraction as observed in the co-submitted publication [1]. Conventionally, fibre volume fractions are determined as an averaged overall fibre volume fraction determined from small cuts of the laminate. Alternatively, automatically stitching of scanning electron microscopy (SEM) images can make high-resolution scans of large cross-section area with large contrast between the polymer and glass-fibre phase. Therefore, local distribution of the fibre volume fraction can be characterised automatically using such scan-data. The two datasets presented here cover two large Field of Views scanning electron microscopy (SEM) images. The two images is generated from between 1200 and 1800 high-resolution scan pictures which have been stitched into two high-resolution tif-files. The resolution corresponds to between 700 and 5000 pixels covering each fibre. The datasets are coming from two different non-crimp fabric glass fibre reinforced epoxy composites typically used in the wind turbine industry. Depending on the regions analysed, fibre volume fraction in the range of 50-85% is found. The maximum local fibre volume fraction is found averaging the local fibre volume fraction over 5 × 5 fibre diameter (80 × 80 µm2) areas. The local fibre volume fraction has been used in the analysis performed in [1].

| S-EPMC7905358 | biostudies-literature

Dataset for scanning electron microscopy based local fiber volume fraction analysis of non-crimp fabric glass fiber reinforced composites

Project description:This dataset includes four large field-of-view scanning electron microscopy (SEM) images together with associated Matlab scripts aimed for the analysis used in the joint publication. Each of the four stitched images is generated from a large number (between 15500 and 24500) high-resolution (195nm/pixel) scans, which have been stitched into four images stored as tiff-files. The images show the cross-section of fiber bundles in composite laminate and are well-suited for local fiber volume determination. The image resolution corresponds to between 600 and 2000 pixels covering each fiber. The imaged samples are from composite laminates with an overall fiber volume fraction in the range of 55% to 60%. The local fiber volume fraction is found both for the full cross-section, as an average fiber volume fraction over the individual bundles, and as a local fiber volume fraction found in a moving averaging box with a size corresponding to 5×5 fiber diameter (80×80 µm2) areas.

| S-EPMC10113767 | biostudies-literature

MWCNT-Coated Glass Fabric/Phenol Composite Heating Panel Fabricated by Resin Infusion Process.

Project description:MWCNTs (multiwalled carbon nanotubes) were applied to fiber-reinforced composite materials with phenolic resin having flame retardance for the composite heating panels of railroad vehicles. Instead of dispersing MWCNTs in the matrix, the surface of a pristine plain-weave glass fiber fabric was coated with MWCNTs through a series of dip-coating and drying processes, followed by the resin infusion of the phenolic resin to make the composite heating panel. Before and after the resin infusion process, low percolation thresholds of 0.00216 wt%MWCNT (weight percent of MWCNTs) and 0.001 wt%MWCNT, respectively, were achieved, as were very high electrical conductivities of 47.5 S/m at 0.210 wt%MWCNT and 26.7 S/m at 0.116 wt%, respectively. The low threshold and high conductivity can be attributed to the formation of electrical pathways directly onto the glass fabrics. It was confirmed that mechanical properties such as modulus, strength, and maximum strain were at the same level as those of the pristine glass fabric composite. The heating performance with temperature uniformity, as well as the electrical and mechanical properties, indicates that the resin-infused glass fabric composite having MWCNTs directly coated onto the fabric surface can be a solution for lightweight structural composite heating panels for railway vehicles.

| S-EPMC10459559 | biostudies-literature

A multimodal data-set of a unidirectional glass fibre reinforced polymer composite.

Project description:A unidirectional (UD) glass fibre reinforced polymer (GFRP) composite was scanned at varying resolutions in the micro-scale with several imaging modalities. All six scans capture the same region of the sample, containing well-aligned fibres inside a UD load-carrying bundle. Two scans of the cross-sectional surface of the bundle were acquired at a high resolution, by means of scanning electron microscopy (SEM) and optical microscopy (OM), and four volumetric scans were acquired through X-ray computed tomography (CT) at different resolutions. Individual fibres can be resolved from these scans to investigate the micro-structure of the UD bundle. The data is hosted at https://doi.org/10.5281/zenodo.1195879 and it was used in Emerson et al. (2018) [1] to demonstrate that precise and representative characterisations of fibre geometry are possible with relatively low X-ray CT resolutions if the analysis method is robust to image quality.

| S-EPMC6060273 | biostudies-literature

In situ and tunable structuring of semiconductor-in-glass transparent composite.

Project description:Semiconductor-in-glass composites are an exciting class of photonic materials for various fundamental applications. The significant challenge is the scalable elaboration of composite with the desirable combination of tunable structure, high semiconductor loading ratio, and excellent transparency. Here we report that the topological engineering strategy via hybridization of the glass network former enables to surmount the aforementioned challenge. It not only facilitates the in situ precipitation of (Ga2-xAlx)O3 domains with continuously tunable composition but also allows to simultaneously refine the grain size and enhance the crystallinity. In addition, the composites exhibit excellent transparency and can host various active dopants. We demonstrate the attractive broadband optical response of the composite and achieve the pulse laser operation in mid-infrared waveband. The findings are expected to provide a fundamental principle of in situ modification in hybrid system for generation of high-performance semiconductor-in-glass composites.

| S-EPMC7803658 | biostudies-literature

Electrically and Thermally Conductive Carbon Fibre Fabric Reinforced Polymer Composites Based on Nanocarbons and an In-situ Polymerizable Cyclic Oligoester.

Project description:There is growing interest in carbon fibre fabric reinforced polymer (CFRP) composites based on a thermoplastic matrix, which is easy to rapidly produce, repair or recycle. To expand the applications of thermoplastic CFRP composites, we propose a process for fabricating conductive CFRP composites with improved electrical and thermal conductivities using an in-situ polymerizable and thermoplastic cyclic butylene terephthalate oligomer matrix, which can induce good impregnation of carbon fibres and a high dispersion of nanocarbon fillers. Under optimal processing conditions, the surface resistivity below the order of 10+10 Ω/sq, which can enable electrostatic powder painting application for automotive outer panels, can be induced with a low nanofiller content of 1 wt%. Furthermore, CFRP composites containing 20 wt% graphene nanoplatelets (GNPs) were found to exhibit an excellent thermal conductivity of 13.7 W/m·K. Incorporating multi-walled carbon nanotubes into CFRP composites is more advantageous for improving electrical conductivity, whereas incorporating GNPs is more beneficial for enhancing thermal conductivity. It is possible to fabricate the developed thermoplastic CFRP composites within 2 min. The proposed composites have sufficient potential for use in automotive outer panels, engine blocks and other mechanical components that require conductive characteristics.

| S-EPMC5955969 | biostudies-literature

Numerical Modelling of Geopolymer Concrete In-Filled Fibre-Reinforced Polymer Composite Columns Subjected to Axial Compression Loading

Project description:In this research study, the performance of geopolymer concrete (GPC) in-filled fibre-reinforced polymer (FRP) composite (GPC-FRP) columns exposed to compressive loading is examined using the finite element (FE) analysis. The load–deflection behaviour is investigated by considering the impact of the strength of concrete, different fibre orientations and thicknesses of FRP tubes in terms of the diameter/thickness (D/t) ratio, surface friction in between the concrete and enclosing FRP tube, the lateral confinement and the axial stress distribution characteristics. The load-carrying capacity (LCC) of the GPC-FRP composite columns and cement concrete (CC) in-filled FRP composite (CC-FRP) columns is compared and the results imply that the LCC of the GPC-FRP composite columns is (0.9 to 2.04%) greater than the CC-FRP composite columns. The improvement in the LCC and lateral confining pressure of the GPC-FRP composite columns is observed as the thickness of the FRP tube increases. The LCC of the GPC-FRP composite columns with a D/t ratio of 30 was almost (12.70 to 14.23%) greater than the GPC-FRP composite columns with a D/t ratio of 50. The GPC-FRP composite columns with a fibre orientation in the axial and hoop directions (0°) exhibit (8.4 to 11.39%) better performance than the columns with any other orientations (30° and 53°). The LCC of the GPC-FRP composite columns with a coefficient of friction of 0.25 and 0.5 are quite comparable. The axial stress distribution in the GPC-FRP composite columns with different tube thicknesses is explored in this research. This FE model is validated with the experimental results obtained by Kim et al., (2015) and the load and deflection are predicted with the validation error of 6.5 and 6.1%, respectively.

| S-EPMC9102813 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data