Nanoscale Structural Modulation and Low-temperature Magnetic Response in Mixed-layer Aurivillius-type Oxides.

ABSTRACT: Nanoscale structural modulation with different layer numbers in layer-structured complex oxides of the binary Bi4Ti3O12-BiFeO3 system can give rise to intriguing phenomena and extraordinary properties, originating from the correlated interfaces of two different phases with different strain states. In this work, we studied the nanoscale structural modulation induced by Co-substitution in the Aurivillius-type oxide of Bi11Fe3Ti6O33 with a unique and naturally occurred mixed-layer structure. Nanoscale structural evolution via doping occurred from the phase-modulated structure composed of 4- and 5-layer phases to a homogeneous 4-layer structure was clearly observed utilizing x-ray diffraction and electron micro-techniques. Significantly, magnetic response for the samples under various temperatures was recorded and larger magnetic coercive fields (e.g. H c ???10?kOe at 50?K) were found in the phase-modulated samples. Analyses of the x-ray absorption spectra and magnetic response confirmed that the low-temperature magnetic behaviour should be intrinsic to the phase-modulated structure inside the structural transformation region, mainly arising from structural distortions at the correlated interfaces.

SUBMITTER: Sun S

PROVIDER: S-EPMC5772624 | biostudies-literature | 2018 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nanoscale Structural Modulation and Low-temperature Magnetic Response in Mixed-layer Aurivillius-type Oxides.

Sun Shujie S Chen Zezhi Z Wang Guopeng G Geng Xiaoju X Xiao Zhenyu Z Sun Zhuzhu Z Sun Zhihu Z Peng Ranran R Lu Yalin Y

Scientific reports 20180117 1

Nanoscale structural modulation with different layer numbers in layer-structured complex oxides of the binary Bi4Ti3O12-BiFeO3 system can give rise to intriguing phenomena and extraordinary properties, originating from the correlated interfaces of two different phases with different strain states. In this work, we studied the nanoscale structural modulation induced by Co-substitution in the Aurivillius-type oxide of Bi11Fe3Ti ...[more]

PMID: 29343705

Similar Datasets

Project description:Aurivillius oxides ferroelectric layered materials are formed by bismuth oxide and pseu-do-perovskite layers. They have a good ionic conductivity, which is beneficial for various photo-catalyzed reactions. Here, we synthesized ultra-thin nanosheets of two different Aurivillius oxides, Bi2WO6 (BWO) and Bi2MoO6 (BMO), by using a hard-template process. All materials were characterized through XRD, TEM, FTIR, TGA/DSC, DLS/ELS, DRS, UV-Vis. Band gap material (Eg) and potential of the valence band (EVB) were calculated for BWO and BMO. In contrast to previous reports on the use of multi composite materials, a new procedure for photocatalytic efficient BMO nanosheets was developed. The procedure, with an additional step only, avoids the use of composite materials, improves crystal structure, and strongly reduces impurities. BWO and BMO were used as photocatalysts for the degradation of the water pollutant dye malachite green (MG). MG removal kinetics was fitted with Langmuir-Hinshelwood model obtaining a kinetic constant k = 7.81 × 10-2 min-1 for BWO and k = 9.27 × 10-2 min-1 for BMO. Photocatalytic dye degradation was highly effective, reaching 89% and 91% MG removal for BWO and BMO, respectively. A control experiment, carried out in the absence of light, allowed to quantify the contribution of adsorption to MG removal process. Adsorption contributed to MG removal by a 51% for BWO and only by a 19% for BMO, suggesting a different degradation mechanism for the two photocatalysts. The advanced MG degradation process due to BMO is likely caused by the high crystallinity of the material synthetized with the new procedure. Reuse tests demonstrated that both photocatalysts are highly active and stable reaching a MG removal up to 95% at the 10th reaction cycle. These results demonstrate that BMO nanosheets, synthesized with an easy additional step, achieved the best degradation performance, and can be successfully used for environmental remediation applications.

Project description:Due to the fact that the application of AW and EP additives in low-temperature greases may lead to worse high-temperature and anti-corrosion characteristics as well as additional burden on the environment due to the content of aggressive components, in this paper, the possibility of replacing these additives with NFA, which do not have these disadvantages, was investigated. The analysis of nanosized particles being used as functional additives in greases was carried out. The morphology of the following nanoparticles was studied: montmorillonite K 10, silica, calcium car-bonate and borate, halloysite, and molybdenum disulfide incorporated in halloysite tubes. The effect of nanostructured components on the physicochemical characteristics and anti-wear and anti-scuffing properties of complex lithium, polyurea, and polymer greases were studied. Maximal improvement of anti-wear and anti-scuffing characteristics of cLi-greases was reached when using silica and calcium borate. Maximal improvement of anti-scuffing properties of PU-lubricant was reached when using calcium carbonate and the two-component NFA based on halloysite, for anti-wear properties when adding silicon dioxide and halloysite. When the concentrations of silicon dioxide and calcium carbonate was increased from 1 to 3 wt.%, there was a decrease in yield stress of the structural frame of the PU-lubricant and its colloidal stability was worse. The increase of the concentration of calcium carbonate and borate nanoparticles in the studied range led to a significant improvement of the anti-wear and anti-scuffing characteristics of the PU grease, respectively. The greases properties' dependence from the nanostructured functional additives' introduction method and their concentration were investigated. Nanoparticles were added into the test lubricants before and after the thermo-mechanical dispersion stage. The addition of silicon dioxide and calcium carbonate NFA after the heat treatment stage led to worsening of the characteristics of the plastic material, and the increase of their concentration from 1 to 3 wt.% formed a harder structure of Li-grease. On the contrary, the addition of calcium borate NFA is recommended after the thermomechanical dispersion. The choice of nanoparticles and the method of their addition to the lubricants of various types was carried out according to the results of the previous stage of the research. Along with the analysis of the physicochemical characteristics and anti-wear and anti-scuffing properties of the lubricants, the structure of the dispersion phase of nanomodified lubricants were studied.

Dataset Information

Nanoscale Structural Modulation and Low-temperature Magnetic Response in Mixed-layer Aurivillius-type Oxides.

Publications

Nanoscale Structural Modulation and Low-temperature Magnetic Response in Mixed-layer Aurivillius-type Oxides.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets