Production and Characterization of Superhydrophobic and Antibacterial Coated Fabrics Utilizing ZnO Nanocatalyst.

ABSTRACT: Dirt and microorganisms are the major problems in textiles which can generate unpleasant odor during their growth. Here, zinc oxide (ZnO) nanoparticles prepared by sol-gel method were loaded on the cotton fabrics using spin coating technique to enhance their antimicrobial properties and water repellency. The effects of ZnO precursor concentration, precursor solution pH, number of coating runs, and Mg doping percent on the structures, morphologies, and water contact angles (WCA) of the ZnO-coated fabrics were addressed. At 0.5?M concentration and pH7, more homogeneous and smaller ZnO nanoparticles were grown along the preferred (0 0 2) direction and uniformly distributed on the fabric with a crystallite size 17.98?nm and dislocation density 3.09?×?10-3 dislocation/nm2. The substitution of Zn 2+ with Mg 2+ ions slightly shifted the (002) peak position to a higher angle. Also, the zeta potential and particle size distribution were measured for ZnO nanoparticle suspension. A superhydrophobic WCA?=?154° was measured for the fabric that coated at 0.5?M precursor solution, pH 7, 20 runs and 0% Mg doping. Moreover, the antibacterial activities of the ZnO-coated fabric were investigated against some gram-positive and gram-negative bacteria such as Salmonella typhimurium, Klebsiella pneumonia, Escherichia coli, and Bacillus subtilis.

SUBMITTER: Shaban M

PROVIDER: S-EPMC5834644 | biostudies-literature | 2018 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Production and Characterization of Superhydrophobic and Antibacterial Coated Fabrics Utilizing ZnO Nanocatalyst.

Shaban Mohamed M Mohamed Fatma F Abdallah Semsem S

Scientific reports 20180302 1

Dirt and microorganisms are the major problems in textiles which can generate unpleasant odor during their growth. Here, zinc oxide (ZnO) nanoparticles prepared by sol-gel method were loaded on the cotton fabrics using spin coating technique to enhance their antimicrobial properties and water repellency. The effects of ZnO precursor concentration, precursor solution pH, number of coating runs, and Mg doping percent on the structures, morphologies, and water contact angles (WCA) of the ZnO-coated ...[more]

PMID: 29500470

Similar Datasets

Project description:One of the emerging and environmentally friendly technologies is the photoelectrochemical generation of green hydrogen; however, the cheap cost of production and the need for customizing photoelectrode properties are thought to be the main obstacles to the widespread adoption of this technology. The primary players in hydrogen production by photoelectrochemical (PEC) water splitting, which is becoming more common on a worldwide basis, are solar renewable energy and widely available metal oxide based PEC electrodes. This study attempts to prepare nanoparticulate and nanorod-arrayed films to better understand how nanomorphology can impact structural, optical, and PEC hydrogen production efficiency, as well as electrode stability. Chemical bath deposition (CBD) and spray pyrolysis are used to create ZnO nanostructured photoelectrodes. Various characterization methods are used to investigate morphologies, structures, elemental analysis, and optical characteristics. The crystallite size of the wurtzite hexagonal nanorod arrayed film was 100.8 nm for the (002) orientation, while the crystallite size of nanoparticulate ZnO was 42.1 nm for the favored (101) orientation. The lowest dislocation values for (101) nanoparticulate orientation and (002) nanorod orientation are 5.6 × 10-4 and 1.0 × 10-4 dislocation/nm2, respectively. By changing the surface morphology from nanoparticulate to hexagonal nanorod arrangement, the band gap is decreased to 2.99 eV. Under white and monochromatic light irradiation, the PEC generation of H2 is investigated using the proposed photoelectrodes. The solar-to-hydrogen conversion rate of ZnO nanorod-arrayed electrodes was 3.72% and 3.12%, respectively, under 390 and 405 nm monochromatic light, which is higher than previously reported values for other ZnO nanostructures. The output H2 generation rates for white light and 390 nm monochromatic illuminations were 28.43 and 26.11 mmol.h-1cm-2, respectively. The nanorod-arrayed photoelectrode retains 96.6% of its original photocurrent after 10 reusability cycles, compared to 87.4% for the nanoparticulate ZnO photoelectrode. The computation of conversion efficiencies, H2 output rates, Tafel slope, and corrosion current, as well as the application of low-cost design methods for the photoelectrodes, show how the nanorod-arrayed morphology offers low-cost, high-quality PEC performance and durability.

Dataset Information

Production and Characterization of Superhydrophobic and Antibacterial Coated Fabrics Utilizing ZnO Nanocatalyst.

Publications

Production and Characterization of Superhydrophobic and Antibacterial Coated Fabrics Utilizing ZnO Nanocatalyst.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets