Study on the Photocatalytic and Antibacterial Properties of TiO₂ Nanoparticles-Coated Cotton Fabrics.

ABSTRACT: Herein, the amino-capped TiO₂ nanoparticles were synthesized using tetrabutyl titanate and amino polymers by a two-step sol-gel and hydrothermal method technique for the fabrication of functional cotton fabric. The prepared TiO₂ nanoparticles and the treated cotton fabric were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD), field emission scanning electron microcopy (FE-SEM) photocatalytic and antibacterial measurement. The results indicate the typical characteristic anatase form of the amino-capped TiO₂ NPs with an average crystallite size of 14.9 nm. The treated cotton fabrics exhibit excellent antibacterial property and good photocatalytic degradation of methylene blue.

SUBMITTER: Zhang G

PROVIDER: S-EPMC6630916 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Cotton Fabrics Decorated with Antimicrobial Ag-Coated TiO2 Nanoparticles Are Unable to Fully and Rapidly Eradicate SARS-CoV-2

Project description:The successful development of multifunctional cotton fabrics with antimicrobial and

| S-EPMC8673468 | biostudies-literature

Photocatalytic Self-Cleaning Cotton Fabrics Coated by Cu?(OH)PO? under VIS/NIR Irradiation.

Project description:In the present work, a mild strategy was employed to obtain cotton fabrics (CFs) coated with Cu?(OH)PO? (CHP) nanoparticles to achieve self-cleaning property. The phytic acid (IP6) assisted method was employed to synthesize nanoparticles (CHP-IP6). The as-prepared coated cotton fabrics were characterized using the following techniques: Fourier-transform infrared spectroscopy (FTIR), X-ray diffractometry (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX) analysis, transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis (TGA). The CHP-IP6 coated cotton fabrics showed significant photocatalytic activity, excellent photocatalytic stability, and good discoloration of methylene blue (MB) stains when exposed to sunlight, which could have important applications as tablecloths, household apparels, and industrial workwear.

| S-EPMC6356686 | biostudies-literature

Gamma Ray Irradiation Enhances the Linkage of Cotton Fabrics Coated with ZnO Nanoparticles.

Project description:In this work, we aim to study zinc oxide (ZnO)-based functional materials over cotton fabrics and their effects after gamma ray exposure of 9 kGy. We found that the binding of the nanoparticles with cotton fabrics can be enhanced after irradiation. This could be due to the oxygen deficiency or defects created in the interface between ZnO and cotton fabrics after irradiation. Near-edge X-ray absorption fine structure and X-ray photoelectron spectroscopy (XPS) were used to detect the oxygen inadequacies generated in the interior and at the surface of the ZnO nanoparticles after gamma ray exposure. XPS results showed that the binding energy of Zn shifts by 2 eV at 1.5 kGy and by 4 eV at 9 kGy. This huge shift of about 4 eV is completely different from other works due to the reaction that takes place on the interface between ZnO nanostructures and cotton fabrics after gamma ray irradiation. Overall, this work suggests that after gamma ray irradiation, there is an enhanced level of binding between the coated functional nanoparticles and cotton fabrics, which can be advantageous for the textile industries.

| S-EPMC7331028 | biostudies-literature

Contact/Release Coordinated Antibacterial Cotton Fabrics Coated with N-Halamine and Cationic Antibacterial Agent for Durable Bacteria-Killing Application.

Project description:Coating a cationic antibacterial layer on the surface of cotton fabric is an effective strategy to provide it with excellent antibacterial properties and to protect humans from bacterial cross-infection. However, washing with anionic detergent will inactivate the cationic antibacterial coating. Although this problem can be solved by increasing the amount of cationic antibacterial coating, excessive cationic antibacterial coating reduces the drapability of cotton fabric and affects the comfort of wearing it. In this study, a coordinated antibacterial coating strategy based on quaternary ammonium salt and a halogenated amine compound was designed. The results show that the antibacterial effect of the modified cotton fabric was significantly improved. In addition, after mechanically washing the fabric 50 times in the presence of anionic detergent, the antibacterial effect against Staphylococcus aureus and Escherichia coli was still more than 95%. Furthermore, the softness of the obtained cotton fabric showed little change compared with the untreated cotton fabric. This easy-to-implement and cost-effective approach, combined with the cationic contact and the release effect of antibacterial agents, can endow cotton textiles with durable antibacterial properties and excellent wearability.

| S-EPMC7555230 | biostudies-literature

Surface Modification of Cotton Fabric Using TiO2 Nanoparticles for Self-Cleaning, Oil-Water Separation, Antistain, Anti-Water Absorption, and Antibacterial Properties.

Project description:Superhydrophobicity is of interest for practical applications such as water repellency, self-cleaning, stain resistance, antibacterial properties, and oil-water separation. In this work, a superhydrophobic coating on cotton fabric is prepared by simple immersion in TiO2 nanoparticles and perfluorodecyltriethoxysilane solution. Its antiwetting properties, surface morphology, and functionality are characterized. The cotton fabric shows superhydrophobicity with a water static contact angle of 169.3 ± 2.1° and tilt angle of 6.3 ± 2.0°. The coating is also characterized by performing stability tests, and it shows excellent mechanical durability, chemical stability, and thermal stability. Additionally, the water droplet dynamic on the coated surface is also studied. The coated cotton fabric exhibits excellent self-cleaning, stain resistance, rust stain resistance, anti-water absorption, and antibacterial properties. It can also be used in oil-water separation with a high separation efficiency and excellent reusability.

| S-EPMC7160840 | biostudies-literature

Hydrophobic cellulose-based and non-woven fabrics coated with mesoporous TiO2 and their virucidal properties under indoor light

Project description:Antiviral hydrophobic cellulose-based cotton or non-woven fabrics containing mesoporous TiO2 particles were developed for potential use in healthcare and in other contaminated environments. Hydrosols made with the sol-gel method using two different amounts of the Ti precursor were applied to cotton and non-woven fabrics and their virucidal effect on Murine Coronavirus (MHV-3) and Human Adenovirus (HAdV-5) was evaluated under indoor light irradiation. The results show 90% reduction of HAdV-5 and up to 99% of MHV-3 in non-woven fabric, and 90% reduction of MHV-3 and no reduction of HAdV-5 in cotton fabric. The antiviral activity was related to the properties of the TiO2 powders and coatings characterized by BET surface area, DRX, DLS, FTIR, DRS, SEM, TEM and water contact angle. The hydrophobic characteristic of the treated fabrics and the high surface area of the TiO2 particles favor interaction with the virus, especially MHV-3. These results demonstrate that non-woven fabric and cotton, coated with TiO2, can be highly effective in preventing contamination with MHV-3 and HAdV-5 viruses, particularly for applications in healthcare indoor environments. Graphical abstract Image, graphical abstract

| S-EPMC8717712 | biostudies-literature

Photocatalytic, Antimicrobial and Biocompatibility Features of Cotton Knit Coated with Fe-N-Doped Titanium Dioxide Nanoparticles.

Project description:Our research was focused on the evaluation of the photocatalytic and antimicrobial properties, as well as biocompatibility of cotton fabrics coated with fresh and reused dispersions of nanoscaled TiO₂-1% Fe-N particles prepared by the hydrothermal method and post-annealed at 400 °C. The powders were characterized by X-ray diffraction (XRD), Mössbauer spectroscopy and X-ray photoelectron spectroscopy. The textiles coated with doped TiO₂ were characterized by scanning electron microscopy and energy dispersive X-ray analyses, and their photocatalytic effect by trichromatic coordinates of the materials stained with methylene blue and coffee and exposed to UV, visible and solar light. The resulting doped TiO₂ consists of a mixture of prevailing anatase phase and a small amount (~15%-20%) of brookite, containing Fe3+ and nitrogen. By reusing dispersions of TiO₂-1% Fe-N, high amounts of photocatalysts were deposited on the fabrics, and the photocatalytic activity was improved, especially under visible light. The treated fabrics exhibited specific antimicrobial features, which were dependent on their composition, microbial strain and incubation time. The in vitro biocompatibility evaluation on CCD-1070Sk dermal fibroblasts confirmed the absence of cytotoxicity after short-term exposure. These results highlight the potential of TiO₂-1% Fe-N nanoparticles for further use in the development of innovative self-cleaning and antimicrobial photocatalytic cotton textiles. However, further studies are required in order to assess the long-term skin exposure effects and the possible particle release due to wearing.

| S-EPMC5457061 | biostudies-other

Production and Characterization of Superhydrophobic and Antibacterial Coated Fabrics Utilizing ZnO Nanocatalyst.

Project description:Dirt and microorganisms are the major problems in textiles which can generate unpleasant odor during their growth. Here, zinc oxide (ZnO) nanoparticles prepared by sol-gel method were loaded on the cotton fabrics using spin coating technique to enhance their antimicrobial properties and water repellency. The effects of ZnO precursor concentration, precursor solution pH, number of coating runs, and Mg doping percent on the structures, morphologies, and water contact angles (WCA) of the ZnO-coated fabrics were addressed. At 0.5?M concentration and pH7, more homogeneous and smaller ZnO nanoparticles were grown along the preferred (0 0 2) direction and uniformly distributed on the fabric with a crystallite size 17.98?nm and dislocation density 3.09?×?10-3 dislocation/nm2. The substitution of Zn 2+ with Mg 2+ ions slightly shifted the (002) peak position to a higher angle. Also, the zeta potential and particle size distribution were measured for ZnO nanoparticle suspension. A superhydrophobic WCA?=?154° was measured for the fabric that coated at 0.5?M precursor solution, pH 7, 20 runs and 0% Mg doping. Moreover, the antibacterial activities of the ZnO-coated fabric were investigated against some gram-positive and gram-negative bacteria such as Salmonella typhimurium, Klebsiella pneumonia, Escherichia coli, and Bacillus subtilis.

| S-EPMC5834644 | biostudies-literature

Chitosan Nanoparticles Functionalized Viscose Fabrics as Potentially Durable Antibacterial Medical Textiles.

Project description:This research proposed two pretreatments of viscose fabrics: oxidation with 2,2,6,6-tetramethylpiperidine-1-oxy radical (TEMPO) and coating with TEMPO-oxidized cellulose nanofibrils (TOCN), to introduce functional groups (COOH and CHO) suitable for irreversible binding of chitosan nanoparticles without and with embedded zinc (NCS and NCS + Zn, respectively) and consequently achieving washing durable antibacterial properties of the chitosan nanoparticles functionalized fabrics. The characterizations of pretreated and chitosan nanoparticles functionalized fabrics were performed by FTIR and XPS spectroscopy, elemental analysis, inductively coupled plasma optical emission spectrometry, zeta potential measurements, scanning electron microscopy, determination of COOH and CHO groups content, and antimicrobial activity under dynamic contact conditions. Influence of pretreatments on NCS and NCS + Zn adsorption, chemical, electrokinetic, and antibacterial properties as well as morphology, and washing durability of NCS and NCS + Zn functionalized fabrics were studied and compared. Washing durability was evaluated through changes in the chitosan and zinc content, zeta potential, and antibacterial activity after 1, 3, and 5 washing cycles. Pretreatments improved washing durability of antibacterial properties of chitosan nanoparticles functionalized fabrics. The NCS and NCS + Zn functionalized pretreated fabrics preserved antibacterial activity against S. aureus after five washing cycles, while antibacterial activity against E. coli was preserved only after one washing cycle in the case NCS + Zn functionalized pretreated viscose fabrics.

| S-EPMC8269808 | biostudies-literature

Novel TiO2 Nanoparticles/Polysulfone Composite Hollow Microspheres for Photocatalytic Degradation.

Project description:Nanosized titanium oxide (TiO2) material is a promising photocatalyst for the degradation of organic pollutants, whereas the difficulty of its recycling hinders its practical application. Herein, we reported the preparation of a novel titanium oxide/polysulfone (TiNPs/PSF) composite hollow microspheres by the combination of Pickering emulsification and the solvent evaporation technique and their application for the photodegradation of methyl blue (MB). P25 TiO2 nanoparticles dispersed on the surface of PSF microspheres. The porosity, density and photoactivity of the TiNPs/PSF composite microsphere are influenced by the TiO2 loading amount. The composite microsphere showed good methyl blue (MB) removal ability. Compared with TiO2 P25, and PSF, a much higher MB adsorption speed was observed for TiNPs/PSF microspheres benefited from their porous structure and the electrostatic attractions between the MB+ and the negatively charged PSF materials, and showed good degradation efficiency. For TiNPs/PSF composite microsphere with density close to 1, a 100% MB removal (10 mg L-1) within 120 min at a catalyst loading of 2.5 g L-1 can be obtained under both stirring and static condition, due to well dispersing of TiO2 particles on the microsphere surface and its stable suspending in water. For the non-suspended TiNPs/PSF composite microsphere with density bigger than 1, the 100% MB removal can be only obtained under stirring condition. The removal efficiency of MB for the composite microspheres retained 96.5%, even after 20 cycles. Moreover, this composite microsphere also showed high MB removal ability at acidic condition. The high catalysis efficiency, excellent reusability and good stability make this kind of TiNPs/PSF composite microsphere a promising photocatalyst for the water organic pollution treatment.

| S-EPMC7865213 | biostudies-literature