High-Quality GaSe Single Crystal Grown by the Bridgman Method.

ABSTRACT: A high-quality GaSe single crystal was grown by the Bridgman method. The X-ray rocking curve for the studied GaSe sample is symmetric and the Full Width at Half Maximum (FWHM) is only 46 arcs, which is the smallest value ever reported for GaSe crystals. The IR-transmittance is about 66% in the range from 500 to 4000 cm-1. The photoluminescence spectrum at 9.2 K shows a symmetric and sharp excition peak in 2.1046 eV. The results indicate that the as-grown GaSe crystal is of high crystalline quality. The as-grown ε -GaSe crystal has a p-type conductance with the resistivity of 10³ Ω/cm, and the Hall mobility is ~25 cm² V-1 s-1. Few-layer GaSe crystals were prepared through mechanical exfoliation from this high-quality crystal sample. Few-layer GaSe-based photodetectors were fabricated, which exhibit an on/off ratio of 10⁴, a field-effect differential mobility of 0.4 cm² V-1 s-1, and have a fast response time less than 60 ms under light illumination.

SUBMITTER: Wang T

PROVIDER: S-EPMC5848883 | biostudies-literature | 2018 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

High-Quality GaSe Single Crystal Grown by the Bridgman Method.

Wang Tao T Li Jie J Zhao Qinghua Q Yin Ziang Z Zhang Yinghan Y Chen Bingqi B Xie Yong Y Jie Wanqi W

Materials (Basel, Switzerland) 20180124 2

A high-quality GaSe single crystal was grown by the Bridgman method. The X-ray rocking curve for the studied GaSe sample is symmetric and the Full Width at Half Maximum (FWHM) is only 46 arcs, which is the smallest value ever reported for GaSe crystals. The IR-transmittance is about 66% in the range from 500 to 4000 cm-1. The photoluminescence spectrum at 9.2 K shows a symmetric and sharp excition peak in 2.1046 eV. The results indicate that the as-grown GaSe crystal is of high crysta ...[more]

PMID: 29364845

Similar Datasets

A Single-Entity Method for Actively Controlled Nucleation and High-Quality Protein Crystal Synthesis.

Project description:Lack of controls and understanding in nucleation, which proceeds crystal growth and other phase transitions, has been a bottleneck challenge in chemistry, materials, biology, and other fields. The exemplary needs for better methods for biomacromolecule crystallization include (1) synthesizing crystals for high-resolution structure determinations in fundamental research and (2) tuning the crystal habit and thus the corresponding properties in materials and pharmaceutical applications. Herein, a deterministic method is established capable of sustaining the nucleation and growth of a single crystal using the protein lysozyme as a prototype. The supersaturation is localized at the interface between a sample and a precipitant solution, spatially confined by the tip of a single nanopipette. The exchange of matter between the two solutions determines the supersaturation, which is controlled by electrokinetic ion transport driven by an external potential waveform. Nucleation and subsequent crystal growth disrupt the ionic current limited by the nanotip and are detected. The nucleation and growth of individual single crystals are measured in real time. Electroanalytical and optical signatures are elucidated as feedbacks with which active controls in crystal quality and method consistency are achieved: five out of five crystals diffract at a true atomic resolution of up to 1.2 Å. As controls, those synthesized under less optimized conditions diffract poorly. The crystal habits during the growth process are tuned successfully by adjusting the flux. The universal mechanism of nano-transport kinetics, together with the correlations of the diffraction quality and crystal habit with the crystallization control parameters, lay the foundation for the generalization to other materials systems.

| S-EPMC10308327 | biostudies-literature

High-quality AlN grown with a single substrate temperature below 1200 °C.

Project description:1.5-μm AlN grown by metal-organic chemical vapor deposition (MOCVD), with a single substrate temperature of 1180 °C, exhibits atomically flat surface and the XRD (102) peak width of 427 arcsec. The results are achieved with a pulsed NH3-flow condition, serving as an alternative for the commonly used temperature-varied buffer structure, which is often complicated and time-consuming. Inserting two pulsed-NH3-flow AlN layers in the epitaxial structure not only releases the lattice strain via the formation of three-dimensional nano-islands, but also smoothens the surface with prolonged lateral migration of Al adatoms. This effective growth technique substantially simplifies the manufacture of device-quality AlN.

| S-EPMC5541044 | biostudies-literature

Substrate-induced strain in 2D layered GaSe materials grown by molecular beam epitaxy.

Project description:Two-dimensional (2D) layered GaSe films were grown on GaAs (001), GaN/Sapphire, and Mica substrates by molecular beam epitaxy (MBE). The in situ reflective high-energy electron diffraction monitoring reveals randomly in-plane orientations of nucleated GaSe layers grown on hexagonal GaN/Sapphire and Mica substrates, whereas single-orientation GaSe domain is predominant in the GaSe/GaAs (001) sample. Strong red-shifts in the frequency of in-plane [Formula: see text] vibration modes and bound exciton emissions observed from Raman scattering and photoluminescence spectra in all samples are attributed to the unintentionally biaxial in-plane tensile strains, induced by the dissimilarity of symmetrical surface structure between the 2D-GaSe layers and the substrates during the epitaxial growth. The results in this study provide an important understanding of the MBE-growth process of 2D-GaSe on 2D/3D hybrid-heterostructures and pave the way in strain engineering and optical manipulation of 2D layered GaSe materials for novel optoelectronic integrated technologies.

| S-EPMC7395717 | biostudies-literature

Controlled vapor phase growth of single crystalline, two-dimensional GaSe crystals with high photoresponse.

Project description:Compared with their bulk counterparts, atomically thin two-dimensional (2D) crystals exhibit new physical properties, and have the potential to enable next-generation electronic and optoelectronic devices. However, controlled synthesis of large uniform monolayer and multi-layer 2D crystals is still challenging. Here, we report the controlled synthesis of 2D GaSe crystals on SiO2/Si substrates using a vapor phase deposition method. For the first time, uniform, large (up to ~60 μm in lateral size), single-crystalline, triangular monolayer GaSe crystals were obtained and their structure and orientation were characterized from atomic scale to micrometer scale. The size, density, shape, thickness, and uniformity of the 2D GaSe crystals were shown to be controllable by growth duration, growth region, growth temperature, and argon carrier gas flow rate. The theoretical modeling of the electronic structure and Raman spectroscopy demonstrate a direct-to-indirect bandgap transition and progressive confinement-induced bandgap shifts for 2D GaSe crystals. The 2D GaSe crystals show p-type semiconductor characteristics and high photoresponsivity (~1.7 A/W under white light illumination) comparable to exfoliated GaSe nanosheets. These 2D GaSe crystals are potentially useful for next-generation electronic and optoelectronic devices such as photodetectors and field-effect transistors.

| S-EPMC4074793 | biostudies-literature

Patterning GaSe by High-Powered Laser Beams.

Project description:We report the high-powered laser modification of the chemical, physical, and structural properties of the two-dimensional (2D) van der Waals material GaSe. Our results show that contrary to expectations and previous reports, GaSe at the periphery of a high-power laser beam does not entirely decompose into Se and Ga2O3. In contrast, we find unexpectedly that the Raman signal from GaSe gets amplified around regions where it was not expected to exist. Atomic force microscopy (AFM), dielectric force microscopy (DFM), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDX) results show that laser irradiation induces the formation of nanoparticles. Our analyses demonstrate that, except for a fraction of Ga2Se3, these nanoparticles still belong to the GaSe phase but possess different electrical and optical properties. These changes are evidenced in the increased Raman intensity attributed to the near-resonance conditions with the Raman excitation laser. The elemental analysis of nanoparticles shows that the relative selenium content increased to as much as 70% from a 50:50 value in stoichiometric GaSe. This elemental change is related to the formation of the Ga2Se3 phase identified by Raman spectroscopy at some locations near the edge. Further, we exploit the localized high-power laser processing of GaSe to induce the formation of Ag-GaSe nanostructures by exposure to a solution of AgNO3. The selective reaction of AgNO3 with laser-irradiated GaSe gives rise to composite nanostructures that display photocatalytic activity originally absent in the pristine 2D material. The photocatalytic activity was investigated by the transformation of 4-nitrobenzenethiol to its amino and dimer forms detected in situ by Raman spectroscopy. This work improves the understanding of light-matter interaction in layered systems, offering an approach to the formation of laser-induced composites with added functionality.

| S-EPMC7203990 | biostudies-literature

Fabrication of high-quality single-crystal Cu thin films using radio-frequency sputtering.

Project description:Copper (Cu) thin films have been widely used as electrodes and interconnection wires in integrated electronic circuits, and more recently as substrates for the synthesis of graphene. However, the ultra-high vacuum processes required for high-quality Cu film fabrication, such as molecular beam epitaxy (MBE), restricts mass production with low cost. In this work, we demonstrated high-quality Cu thin films using a single-crystal Cu target and radio-frequency (RF) sputtering technique; the resulting film quality was comparable to that produced using MBE, even under unfavorable conditions for pure Cu film growth. The Cu thin film was epitaxially grown on an Al2O3 (sapphire) (0001) substrate, and had high crystalline orientation along the (111) direction. Despite the 10(-3) Pa vacuum conditions, the resulting thin film was oxygen free due to the high chemical stability of the sputtered specimen from a single-crystal target; moreover, the deposited film had >5× higher adhesion force than that produced using a polycrystalline target. This fabrication method enabled Cu films to be obtained using a simple, manufacturing-friendly process on a large-area substrate, making our findings relevant for industrial applications.

| S-EPMC4148649 | biostudies-other

Low surface recombination velocity in solution-grown CH3NH3PbBr3 perovskite single crystal.

Project description:Organic-inorganic hybrid perovskites are attracting intense research effort due to their impressive performance in solar cells. While the carrier transport parameters such as mobility and bulk carrier lifetime shows sufficient characteristics, the surface recombination, which can have major impact on the solar cell performance, has not been studied. Here we measure surface recombination dynamics in CH3NH3PbBr3 perovskite single crystals using broadband transient reflectance spectroscopy. The surface recombination velocity is found to be 3.4±0.1 × 10(3) cm s(-1), ∼2-3 orders of magnitude lower than that in many important unpassivated semiconductors employed in solar cells. Our result suggests that the planar grain size for the perovskite thin films should be larger than ∼30 μm to avoid the influence of surface recombination on the effective carrier lifetime.

| S-EPMC4918347 | biostudies-literature

Dramatic improvement of crystal quality for low-temperature-grown rabbit muscle aldolase.

Project description:Rabbit muscle aldolase (RMA) was crystallized in complex with the low-complexity domain (LC4) of sorting nexin 9. Monoclinic crystals were obtained at room temperature that displayed large mosaicity and poor X-ray diffraction. However, orthorhombic RMA-LC4 crystals grown at 277 K under similar conditions exhibited low mosaicity, allowing data collection to 2.2 A Bragg spacing and structure determination. It was concluded that the improvement of crystal quality as indicated by the higher resolution of the new RMA-LC4 complex crystals was a consequence of the introduction of new lattice contacts at lower temperature. The lattice contacts corresponded to an increased number of interactions between high-entropy side chains that mitigate the lattice strain incurred upon cryocooling and accompanying mosaic spread increases. The thermodynamically unfavorable immobilization of high-entropy side chains used in lattice formation was compensated by an entropic increase in the bulk-solvent content owing to the greater solvent content of the crystal lattice.

| S-EPMC2864701 | biostudies-literature

Precursor Phenomena of Barium Titanate Single Crystals Grown Using a Solid-State Single Crystal Growth Method Studied with Inelastic Brillouin Light Scattering and Birefringence Measurements.

Project description:The nature of precursor phenomena in the paraelectric phase of ferroelectrics is one of the main questions to be resolved from a fundamental point of view. Barium titanate (BaTiO₃) is one of the most representative perovskite-structured ferroelectrics intensively studied until now. The pretransitional behavior of BaTiO₃ single crystal grown using a solid-state crystal growth (SSCG) method was investigated for the first time and compared to previous results. There is no melting process in the SSCG method, thus the crystal grown using a SSCG method have inherent higher levels of impurity and defect concentrations, which is a good candidate for investigating the effect of crystal quality on the precursor phenomena. The acoustic, dielectric, and piezoelectric properties, as well as birefringence, of the SSCG-grown BaTiO₃ were examined over a wide temperature range. Especially, the acoustic phonon behavior was investigated in terms of Brillouin spectroscopy, which is a complementary technique to Raman spectroscopy. The obtained precursor anomalies of the SSCG-grown BaTiO₃ in the cubic phase were similar to those of other single crystals, in particular, of high-quality single crystal grown by top-seeded solution growth method. These results clearly indicate that the observed precursor phenomena are common and intrinsic effect irrespective of the crystal quality.

| S-EPMC6321232 | biostudies-literature

Centimeter-scale 2D perovskite (PEA)2PbBr4 single crystal plates grown by a seeded solution method for photodetectors.

Project description:Large-sized single-crystal two-dimensional (2D) perovskites are highly desirable owing to their fundamental properties and intriguing ability to boost devices. Herein, 2-phenylethylammonium lead bromide [(PEA)2PbBr4] single crystals, which are a violet-light-emitting 2D perovskite material, with typical lateral sizes of about one centimeter were successfully grown using a seeded solution method. The single-crystal plates showed a well-defined shape (rectangle or hexagon), a natural thickness (300-500 μm) similar to that of conventional silicon and InP wafers, a large aspect ratio of ∼20, and a smooth surface (root mean square, ∼0.7 nm). We integrated these single crystal plates into an ultraviolet photodetector, achieving a low dark current of ∼10-13 A and an efficient photoresponse (on/off ratio, ∼103). This experiment could easily be extended to grow freestanding 2D perovskite single crystals on a wafer scale for practical integrated optoelectronics.

| S-EPMC9064435 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data