Trifunctional Epoxy Resin Composites Modified by Soluble Electrospun Veils: Effect on the Viscoelastic and Morphological Properties.

ABSTRACT: Electrospun veils from copolyethersulfones (coPES) were prepared as soluble interlaminar veils for carbon fiber/epoxy composites. Neat, resin samples were impregnated into coPES veils with unmodified resin, while dry carbon fabrics were covered with electrospun veils and then infused with the unmodified epoxy resin to prepare reinforced laminates. The thermoplastic content varied from 10 wt% to 20 wt%. TGAP epoxy monomer showed improved and fast dissolution for all the temperatures tested. The unreinforced samples were cured first at 180 °C for 2 h and then were post-cured at 220 °C for 3 h. These sample showed a high dependence on the curing cycle. Carbon reinforced samples showed significant differences compared to the neat resin samples in terms of both viscoelastic and morphological properties.

SUBMITTER: Ognibene G

PROVIDER: S-EPMC5872984 | biostudies-literature | 2018 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Trifunctional Epoxy Resin Composites Modified by Soluble Electrospun Veils: Effect on the Viscoelastic and Morphological Properties.

Ognibene Giulia G Mannino Salvatore S Fragalà Maria Elena ME Cicala Gianluca G

Materials (Basel, Switzerland) 20180309 3

Electrospun veils from copolyethersulfones (coPES) were prepared as soluble interlaminar veils for carbon fiber/epoxy composites. Neat, resin samples were impregnated into coPES veils with unmodified resin, while dry carbon fabrics were covered with electrospun veils and then infused with the unmodified epoxy resin to prepare reinforced laminates. The thermoplastic content varied from 10 wt% to 20 wt%. TGAP epoxy monomer showed improved and fast dissolution for all the temperatures tested. The u ...[more]

PMID: 29522444

Similar Datasets

Novel Antibacterial and Toughened Carbon-Fibre/Epoxy Composites by the Incorporation of TiO2 Nanoparticles Modified Electrospun Nanofibre Veils.

Project description:The inclusion of electrospun nanofiber veils was revealed as an effective method for enhancing the mechanical properties of fiber-reinforced epoxy resin composites. These veils will eventually allow the incorporation of nanomaterials not only for mechanical reinforcement but also in multifunctional applications. Therefore, this paper investigates the effect of electrospun nanofibrous veils made of polyamide 6 modified with TiO2 nanoparticles on the mechanical properties of a carbon-fiber/epoxy composite. The nanofibers were included in the carbon-fiber/epoxy composite as a single structure. The effect of positioning these veils in different composite positions was investigated. Compared to the reference, the use of unmodified and TiO2 modified veils increased the flexural stress at failure and the fracture toughness of composites. When TiO2 modified veils were incorporated, new antibacterial properties were achieved due to the photocatalytic properties of the veils, widening the application area of these composites.

| S-EPMC6780269 | biostudies-literature

Toward Sustainable Composites: Graphene-Modified Jute Fiber Composites with Bio-Based Epoxy Resin.

Project description:Sustainable natural fiber reinforced composites have attracted significant interest due to the growing environmental concerns with conventional synthetic fiber as well as petroleum-based resins. One promising approach to reducing the large carbon footprint of petroleum-based resins is the use of bio-based thermoset resins. However, current fiber-reinforced bio-based epoxy composites exhibit relatively lower mechanical properties such as tensile, flexural strength, and modulus, which limits their wider application. Here the fabrication of high-performance composites using jute fibers is reported, modified with graphene nanoplates (GNP) and graphene oxide (GO), and reinforced with bio-based epoxy resin. It is demonstrated that physical and chemical treatments of jute fibers significantly improve their fiber volume fraction (Vf) and matrix adhesion, leading to enhanced mechanical properties of the resulting Jute/Bio-epoxy (J/BE) composites. Furthermore, the incorporation of GNP and GO further increases the tensile and flexural strength of the J/BE composites. The study reveals the potential of graphene-based jute fiber-reinforced composites with bio-based epoxy resin as a sustainable and high-performance material for a wide range of applications. This work contributes to the development of sustainable composites that have the potential to reduce the negative environmental impact of conventional materials while also offering improved mechanical properties.

| S-EPMC10517308 | biostudies-literature

Self-Extinguishing Resin Transfer Molding Composites Using Non-Fire-Retardant Epoxy Resin.

Project description:Introducing fire-retardant additives or building blocks into resins is a widely adopted method used for improving the fire retardancy of epoxy composites. However, the increase in viscosity and the presence of insoluble additives accompanied by resin modification remain challenges for resin transfer molding (RTM) processing. We developed a robust approach for fabricating self-extinguishing RTM composites using unmodified and flammable resins. To avoid the effects on resin fluidity and processing, we loaded the flame retardant into tackifiers instead of resins. We found that the halogen-free flame retardant, a microencapsulated red phosphorus (MRP) additive, was enriched on fabric surfaces, which endowed the composites with excellent fire retardancy. The composites showed a 79.2% increase in the limiting oxygen index, a 29.2% reduction in heat release during combustion, and could self-extinguish within two seconds after ignition. Almost no effect on the mechanical properties was observed. This approach is simple, inexpensive, and basically applicable to all resins for fabricating RTM composites. This approach adapts insoluble flame retardants to RTM processing. We envision that this approach could be extended to load other functions (radar absorbing, conductivity, etc.) into RTM composites, broadening the application of RTM processing in the field of advanced functional materials.

| S-EPMC6315867 | biostudies-other

Eco-Friendly Epoxy-Terminated Polyurethane-Modified Epoxy Resin with Efficient Enhancement in Toughness.

Project description:Polyurethane is widely used to toughen epoxy resins due to its excellent comprehensive properties and compatibility. However, some demerits of polyurethanes limit their applications, such as the harsh storage condition of isocyanate-terminated polyurethane (ITPU), the limited amount of ITPU in epoxy resin, and using solvents during the preparation of polyurethane-modified epoxy resins. To address these issues, in this study, we reported a facile and green approach for preparing epoxy-terminated polyurethane (EPU)-modified epoxy resins with different EPU contents. It was found that the toughness of the epoxy resin was significantly improved after the addition of EPU. When the EPU content was 30 wt%, the elongation at break and toughness were improved by 358.36% and 73.56%, respectively. In comparison, the toughening effect of EPU outperformed that of ITPU. Moreover, the high content of EPU did not significantly decrease the glass transition temperature and had little effect on the thermal stability of the epoxy resin.

| S-EPMC10346895 | biostudies-literature

Enhancing the Mechanical Toughness of Epoxy-Resin Composites Using Natural Silk Reinforcements.

Project description:Strong and tough epoxy composites are developed using a less-studied fibre reinforcement, that of natural silk. Two common but structurally distinct silks from the domestic B. mori/Bm and the wild A. pernyi/Ap silkworms are selected in fabric forms. We show that the toughening effects on silk-epoxy composites or SFRPs are dependent on the silk species and the volume fraction of silk. Both silks enhance the room-temperature tensile and flexural mechanical properties of the composite, whereas the more resilient Ap silk shows a more pronounced toughening effect and a lower critical reinforcement volume for the brittle-ductile transition. Specifically, our 60 vol.% Ap-SFRP displays a three-fold elevation in tensile and flexural strength, as compared to pure epoxy resin, with an order of magnitude higher breaking energy via a distinct, ductile failure mode. Importantly, the 60 vol.% Ap-SFRP remains ductile with 7% flexural elongation at lower temperatures (-50?°C). Under impact, these SFRPs show significantly improved energy absorption, and the 60 vol.% Ap-SFRP has an impact strength some eight times that of pure epoxy resin. The findings demonstrate both marked toughening and strengthening effects for epoxy composites from natural silk reinforcements, which presents opportunities for mechanically superior and "green" structural composites.

| S-EPMC5607334 | biostudies-literature

Block Copolymer Modified Nanonetwork Epoxy Resin for Superior Energy Dissipation.

Project description:Herein, this work aims to fabricate well-ordered nanonetwork epoxy resin modified with poly(butyl acrylate)-b-poly(methyl methacrylate) (PBA-b-PMMA) block copolymer (BCP) for enhanced energy dissipation using a self-assembled diblock copolymer of polystyrene-b-poly(dimethylsiloxane) (PS-b-PDMS) with gyroid and diamond structures as templates. A systematic study of mechanical properties using nanoindentation of epoxy resin with gyroid- and diamond-structures after modification revealed significant enhancement in energy dissipation, with the values of 0.36 ± 0.02 nJ (gyroid) and 0.43 ± 0.03 nJ (diamond), respectively, when compared to intrinsic epoxy resin (approximately 0.02 ± 0.002 nJ) with brittle characteristics. This enhanced property is attributed to the synergic effect of the deliberate structure with well-ordered nanonetwork texture and the toughening of BCP-based modifiers at the molecular level. In addition to the deliberate structural effect from the nanonetwork texture, the BCP modifier composed of epoxy-philic hard segment and epoxy-phobic soft segment led to dispersed soft-segment domains in the nanonetwork-structured epoxy matrix with superior interfacial strength for the enhancement of applied energy dissipation.

| S-EPMC9105528 | biostudies-literature

Thermal Conductivity of Epoxy Resin Composites Filled with Combustion Synthesized h-BN Particles.

Project description:The thermal conductivity of epoxy resin composites filled with combustion-synthesized hexagonal boron nitride (h-BN) particles was investigated. The mixing of the composite constituents was carried out by either a dry method (involving no use of solvent) for low filler loadings or a solvent method (using acetone as solvent) for higher filler loadings. It was found that surface treatment of the h-BN particles using the silane 3-glycidoxypropyltrimethoxysilane (GPTMS) increases the thermal conductivity of the resultant composites in a lesser amount compared to the values reported by other studies. This was explained by the fact that the combustion synthesized h-BN particles contain less -OH or active sites on the surface, thus adsorbing less amounts of GPTMS. However, the thermal conductivity of the composites filled with the combustion synthesized h-BN was found to be comparable to that with commercially available h-BN reported in other studies. The thermal conductivity of the composites was found to be higher when larger h-BN particles were used. The thermal conductivity was also found to increase with increasing filler content to a maximum and then begin to decrease with further increases in this content. In addition to the effect of higher porosity at higher filler contents, more horizontally oriented h-BN particles formed at higher filler loadings (perhaps due to pressing during formation of the composites) were suggested to be a factor causing this decrease of the thermal conductivity. The measured thermal conductivities were compared to theoretical predictions based on the Nielsen and Lewis theory. The theoretical predictions were found to be lower than the experimental values at low filler contents (< 60 vol %) and became increasing higher than the experimental values at high filler contents (> 60 vol %).

| S-EPMC6273151 | biostudies-literature

Thermal Stability and Flame Retardancy of a Cured Trifunctional Epoxy Resin with the Synergistic Effects of Silicon/Titanium.

Project description:An amino curing agent containing silicon/titanium flame-retardant elements (STCA) based on (3-aminopropyl)triethoxysilane (APTES) and tetrabutyl titanate was successfully prepared. The thermal decomposition and flame-retardant properties of a STCA-cured trifunctional epoxy resin, which was facilely synthesized by 1,1,1-tris(4-hydroxyphenyl)ethane and epichlorohydrin via a two-step method, were compared with those of another amino curing agent containing silicon (SCA) based on APTES and methyltrimethoxysilane. The structures of STCA and SCA were characterized by Fourier transform infrared (FT-IR), 29Si NMR, and Raman spectroscopies. The STCA-cured thermoset not only had good thermal stability with an initial decomposition temperature of 344.8 °C and a char yield of 52.7% at 800 °C but also exhibited the overall improvement of flame-retardant properties. V-0 rating was achieved using the UL-94 test, and the value of limiting oxygen index reached 33.8%. From the thermogravimetry-infrared test, the yield of pyrolysis products of the STCA-cured thermoset was significantly decreased, indicating the lower toxicity in contrast to the SCA-cured thermoset. Flame-retardant performances were also investigated using the cone calorimetry test, and the flame retardancy mechanism was studied using scanning electron microscopy, FT-IR, and energy-dispersive spectrometry. The results indicate that the introduction of silicon/titanium to the system reveals the synergistic effects to promote the formation of an intumescent, sufficient, and compact char layer during combustion, which could effectively prevent heat, oxygen, and flame from penetrating into the interior structure, and lead to the retardance of further combustion.

| S-EPMC7057714 | biostudies-literature

Functionalization of Commercial Electrospun Veils with Zinc Oxide Nanostructures.

Project description:The present research is focused on the synthesis of hexagonal ZnO wurtzite nanorods for the decoration of commercially available electrospun nylon nanofibers. The growth of ZnO was performed by a hydrothermal technique and for the first time on commercial electrospun veils. The growth step was optimized by adopting a procedure with the refresh of growing solution each hour of treatment (Method 1) and with the maintenance of a specific growth solution volume for the entire duration of the treatment (Method 2). The overall treatment time and volume of solution were also optimized by analyzing the morphology of ZnO nanostructures, the coverage degree, the thermal and mechanical stability of the obtained decorated electrospun nanofibers. In the optimal synthesis conditions (Method 2), hexagonal ZnO nanorods with a diameter and length of 53.5 nm ± 5.7 nm and 375.4 nm ± 37.8 nm, respectively, were obtained with a homogeneous and complete coverage of the veils. This easily scalable procedure did not damage the veils that could be potentially used as toughening elements in composites to prevent delamination onset and propagation. The presence of photoreactive species makes these materials ideal also as environmentally friendly photocatalysts for wastewater treatment. In this regard, photocatalytic tests were performed using methylene blue (MB) as model compound. Under UV light irradiation, the degradation of MB followed a first kinetic order data fitting and after 3 h of treatment a MB degradation of 91.0% ± 5.1% was achieved. The reusability of decorated veils was evaluated and a decrease in photocatalysis efficiency was detected after the third cycle of use.

| S-EPMC7916010 | biostudies-literature

Preparation and Application of a Multifunctional Interfacial Modifier for Ramie Fiber/Epoxy Resin Composites.

Project description:A multi-functional modifier, which could improve the mechanical and thermal performance simultaneously, is significant in composites production. Herein, inspired by the chemistry of mussel, an interfacial modifier named FPD was designed and synthesized through one simple step, which was attached by three functional groups (including catechol, N-H bond, and DOPO). Due to the innate properties of each functional group, FPD played multiple roles: adhere to the ramie fibers from catechol and cure with the epoxy resin from -NH-, an antiflaming property from DOPO, and the compatibilizer between ramie fibers and epoxy resin was also improved by changing the polarity of ramie fiber. All of the above functions can be proved by means of water contact angle (WCA), atomic force microscope (AFM), and scanning electron microscopy (SEM), etc. After solidification, the ramie fiber/epoxy composites demonstrated superior performances in terms of good mechanical properties and excellent flame retardant property. With the addition of 30 wt.% FPD, the tensile strength and modulus of the ramie/epoxy composite showed an improvement of 37.1% and 60.9%, and flexural strength and modulus of the composite were improved by 8.9% and 19.3% comparing with no addition composite. Moreover, the composite could achieve the goal for V-0 rating in the UL-94 test and LOI value was 34.6% when the addition of FPD reached 30 wt.%. This work provided us with an efficient method for fabricating nature fiber/epoxy composites with good properties.

| S-EPMC10537050 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data