Growth mechanism of epitaxial YSZ on Si by Pulsed Laser Deposition.

ABSTRACT: The epitaxial growth of yttria-stabilized zirconia (YSZ) on silicon with native oxide was investigated in order to gain more insight in the growth mechanism. Specifically, attention was paid to the possibilities to control the chemical interactions between YSZ, silicon and oxygen during initial growth. The sources of oxygen during growth proved to play an important role in the growth process, as shown by individual manipulation of all sources present during Pulsed Laser Deposition. Partial oxidation of the YSZ plasma and sufficient delivery of oxygen to the growing film were necessary to prevent silicide formation and obtain optimal YSZ crystalline qualities. In these conditions, thickness increase of the silicon native oxide before growth just started to occur, while a much faster regrowth of silicon oxide at the YSZ-Si interface occurred during growth. Control of all these contributions to the growth process is necessary to obtain reproducible growth of high quality YSZ.

SUBMITTER: Dubbink D

PROVIDER: S-EPMC5893595 | biostudies-literature | 2018 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Growth mechanism of epitaxial YSZ on Si by Pulsed Laser Deposition.

Dubbink David D Koster Gertjan G Rijnders Guus G

Scientific reports 20180410 1

The epitaxial growth of yttria-stabilized zirconia (YSZ) on silicon with native oxide was investigated in order to gain more insight in the growth mechanism. Specifically, attention was paid to the possibilities to control the chemical interactions between YSZ, silicon and oxygen during initial growth. The sources of oxygen during growth proved to play an important role in the growth process, as shown by individual manipulation of all sources present during Pulsed Laser Deposition. Partial oxida ...[more]

PMID: 29636484

Similar Datasets

Interfacial reaction control and its mechanism of AlN epitaxial films grown on Si(111) substrates by pulsed laser deposition.

Project description:High-quality AlN epitaxial films have been grown on Si substrates by pulsed laser deposition (PLD) by effective control of the interfacial reactions between AlN films and Si substrates. The surface morphology, crystalline quality and interfacial property of as-grown AlN/Si hetero-interfaces obtained by PLD have been systemically studied. It is found that the amorphous SiAlN interfacial layer is formed during high temperature growth, which is ascribed to the serious interfacial reactions between Si atoms diffused from the substrates and the AlN plasmas produced by the pulsed laser when ablating the AlN target during the high temperature growth. On the contrary, abrupt and sharp AlN/Si hetero-interfaces can be achieved by effectively controlling the interfacial reactions at suitable growth temperature. The mechanisms for the evolution of interfacial layer from the amorphous SiAlN layer to the abrupt and sharp AlN/Si hetero-interfaces by PLD are hence proposed. This work of obtaining the abrupt interfaces and the flat surfaces for AlN films grown by PLD is of paramount importance for the application of high-quality AlN-based devices on Si substrates.

| S-EPMC4473646 | biostudies-other

Electrical and Optical Properties of Nb-doped SrSnO3 Epitaxial Films Deposited by Pulsed Laser Deposition.

Project description:Nb-doped SrSnO3 (SSNO) thin films were epitaxially grown on LaAlO3(001) single-crystal substrates using pulsed laser deposition under various oxygen pressures and substrate temperatures. The crystalline structure, electrical, and optical properties of the films were investigated in detail. X-ray diffraction results show that the cell volume of the films reduces gradually with increasing oxygen pressure while preserving the epitaxial characteristic. X-ray photoelectron spectroscopy analysis confirms the Nb5+ oxidation state in the SSNO films. Hall-effect measurements were performed and the film prepared at 0.2 Pa with the 780 °C substrate temperature exhibits the lowest room-temperature resistivity of 31.3 mΩcm and Hall mobility of 3.31 cm2/Vs with a carrier concentration at 6.03 × 1019/cm3. Temperature-dependent resistivity of this sample displays metal-semiconductor transition and is explained mainly by electron-electron effects. Optical transparency of the films is more than 70% in the wavelength range from 600 to 1800 nm. The band gaps increase from 4.35 to 4.90 eV for the indirect gap and 4.82 to 5.29 eV for the direct by lowering oxygen pressure from 20 to 1 × 10-3 Pa, which can be interpreted by Burstein-Moss effect and oxygen vacancies generated in the high vacuum.

| S-EPMC7431481 | biostudies-literature

Epitaxial Structure of (001)- and (111)-Oriented Perovskite Ferrate Films Grown by Pulsed-Laser Deposition.

Project description:The epitaxial structures of SrFeO(2.5) films grown on SrTiO(3) (001) and (111) substrates by PLD are reported. A layer-by-layer growth mode was achieved in the initial stage on both substrates. The films were stabilized with a monoclinic structure, where we identified the in-plane domain structures and orientation relationship. Our study presents a guide to control the heteroepitaxy of (111)-oriented noncubic perovskites.

| S-EPMC2851191 | biostudies-other

Tandem Si Micropillar Array Photocathodes with Conformal Copper Oxide and a Protection Layer by Pulsed Laser Deposition.

Project description:This work demonstrates the influence of high-quality protection layers on Si-Cu2O micropillar arrays created by pulsed laser deposition (PLD), with the goal to overcome photodegradation and achieve long-term operation during photoelectrochemical (PEC) water splitting. Sequentially, we assessed planar and micropillar device designs with various design parameters and their influence on PEC hydrogen evolution reaction. On the planar device substrates, a Cu2O film thickness of 600 nm and a Cu2O/CuO heterojunction layer with a 5:1 thickness ratio between Cu2O to CuO were found to be optimal. The planar Si/Cu2O/CuO heterostructure showed a higher PV performance (Jsc = 20 mA/cm2) as compared to the planar Si/Cu2O device, but micropillar devices did not show this improvement. Multifunctional overlayers of ZnO (25 nm) and TiO2 (100 nm) were employed by PLD on Si/Cu2O planar and micropillar arrays to provide a hole-selective passivation layer that acts against photocorrosion. A micropillar Si/ITO-Au/Cu2O/ZnO/TiO2/Pt stack was compared to a planar device. Under optimized conditions, the Si/Cu2O photocathode with Pt as a HER catalyst displayed a photocurrent of 7.5 mA cm-2 at 0 V vs RHE and an onset potential of 0.85 V vs RHE, with a stable operation for 75 h.

| S-EPMC6838789 | biostudies-literature

Towards Scalable Large-Area Pulsed Laser Deposition.

Project description:One of the significant limitations of the pulsed laser deposition method in the mass-production-technologies of micro- and nanoelectronic and molecular device electronic fabrication is the issue of ensuring deposition of films with uniform thickness on substrates with large diameter (more than 100 mm) since the area of the laser spot (1-5 mm2) on the surface of the ablated target is incommensurably smaller than the substrate area. This paper reports the methodology that allows to calculate the distribution profile of the film thickness over the surface substrate with a large diameter, taking into account the construction and technological parameters of the pulsed laser deposition equipment. Experimental verification of the proposed methodology showed that the discrepancy with the experiment does not exceed 8%. The modeling of various technological parameters influence on the thickness uniformity has been carried out. Based on the modeling results, recommendations and parameters are proposed for manufacturing uniform thickness films. The results allow for increasing the film thickness uniformity with the thickness distribution < 5% accounts for ~ 31% of 300 mm diameter substrate.

| S-EPMC8432691 | biostudies-literature

Microstructures and growth mechanisms of GaN films epitaxially grown on AlN/Si hetero-structures by pulsed laser deposition at different temperatures.

Project description:2 inch-diameter GaN films with homogeneous thickness distribution have been grown on AlN/Si(111) hetero-structures by pulsed laser deposition (PLD) with laser rastering technique. The surface morphology, crystalline quality, and interfacial property of as-grown GaN films are characterized in detail. By optimizing the laser rastering program, the ~300 nm-thick GaN films grown at 750 °C show a root-mean-square (RMS) thickness inhomogeneity of 3.0%, very smooth surface with a RMS surface roughness of 3.0 nm, full-width at half-maximums (FWHMs) for GaN(0002) and GaN(102) X-ray rocking curves of 0.7° and 0.8°, respectively, and sharp and abrupt AlN/GaN hetero-interfaces. With the increase in the growth temperature from 550 to 850 °C, the surface morphology, crystalline quality, and interfacial property of as-grown ~300 nm-thick GaN films are gradually improved at first and then decreased. Based on the characterizations, the corresponding growth mechanisms of GaN films grown on AlN/Si hetero-structures by PLD with various growth temperatures are hence proposed. This work would be beneficial to understanding the further insight of the GaN films grown on Si(111) substrates by PLD for the application of GaN-based devices.

| S-EPMC4643238 | biostudies-other

Accidental Impurities in Epitaxial Pb(Zr0.2Ti0.8)O3 Thin Films Grown by Pulsed Laser Deposition and Their Impact on the Macroscopic Electric Properties.

Project description:Structural and electrical properties of epitaxial Pb(Zr0.2Ti0.8)O3 films grown by pulsed laser deposition from targets with different purities are investigated in this study. One target was produced in-house by using high purity precursor oxides (at least 99.99%), and the other target was a commercial product (99.9% purity). It was found that the out-of-plane lattice constant is about 0.15% larger and the a domains amount is lower for the film grown from the commercial target. The polarization value is slightly lower, the dielectric constant is larger, and the height of the potential barrier at the electrode interfaces is larger for the film deposited from the pure target. The differences are attributed to the accidental impurities, with a larger amount in the commercial target as revealed by composition analysis using inductive coupling plasma-mass spectrometry. The heterovalent impurities can act as donors or acceptors, modifying the electronic characteristics. Thus, mastering impurities is a prerequisite for obtaining reliable and reproducible properties and advancing towards all ferroelectric devices.

| S-EPMC8146871 | biostudies-literature

Performance and Mechanism of Photoelectrocatalytic Activity of MoSx/WO3 Heterostructures Obtained by Reactive Pulsed Laser Deposition for Water Splitting.

Project description:This work studies the factors that affect the efficiency of the photoelectrochemical hydrogen evolution reaction (HER) using MoSx/WO3 nano-heterostructures obtained by reactive pulsed laser deposition (RPLD) on glass substrates covered with fluorinated tin oxide (FTO). Another focus of the research is the potential of MoSx nanofilms as a precursor for MoOz(S) nanofilms, which enhance the efficiency of the photo-activated oxygen evolution reaction (OER) using the MoOz(S)/WO3/FTO heterostructures. The nanocrystalline WO3 film was created by laser ablation of a W target in dry air at a substrate temperature of 420 °C. Amorphous MoSx nanofilms (2 ? x ? 12) were obtained by laser ablation of an Mo target in H2S gas of varied pressure at room temperature of the substrate. Studies of the energy band structures showed that for all MoSx/WO3/FTO samples, photo-activated HER in an acid solution proceeded through the Z-scheme. The highest photoelectrochemical HER efficiency (a photocurrent density ~1 mA/cm2 at a potential of ~0 V under Xe lamp illumination (~100 mW/cm2)) was found for porous MoS4.5 films containing the highest concentration of catalytically active sites attributed to S ligands. During the anodic posttreatment of porous MoSx nanofilms, MoOz(S) films with a narrow energy band gap were formed. The highest OER efficiency (a photocurrent density ~5.3 mA/cm2 at 1.6 V) was detected for MoOz(S)/WO3/FTO photoanodes that were prepared by posttreatment of the MoSx~3.2 precursor. The MoOz(S) film contributed to the effective photogeneration of electron-hole pairs that was followed by the transport of photoelectrons from MoOz(S) into the WO3 film and the effective participation of holes possessing strong oxidation ability in the OER on the surface of the MoOz(S) film.

| S-EPMC7279322 | biostudies-literature

Pulsed laser deposition of Zn(O,Se) layers in nitrogen background Pressure.

Project description:Zinc oxy-selenide Zn(O,Se) is a novel material, that can replace the toxic CdS buffer layer in thin film solar cells and other optoelectronic devices. In this paper a systematic study of the structural, optical and electrical properties of Zn(O,Se) layers, grown by pulsed laser deposition under 50 mTorr of nitrogen background pressure, over a wide range of the substrate temperature, from RT to 600?°C, is reported. XRD, Raman, HR-SEM, XPS, UV-Vis techniques and Hall effect measurements have been used to investigate the structural, and optoelectronic properties of Zn(O,Se) layers. XRD analysis revealed that the polycrystalline ternary Zn(O,Se) phase formed at 500?°C. Raman analysis confirmed the formation of the polycrystalline Zn(O,Se) phase at 500?°C and an amorphous phase at substrate temperatures below 500?°C. Similarly, XPS analysis accompanied with the modified Auger parameters confirmed formation of ternary Zn(O,Se) layer at 500?°C as well. HR-SEM investigation showed the growth of homogenous, dense and adherent films onto a glass substrate. Furthermore, optical studies revealed that all prepared films are practically transparent in the visible region of the spectrum, with a band gap around 3?eV. Hall effect measurements revealed that conductivity, and electron concentration, increased by four orders of magnitude at 600?°C. It was found, that nitrogen background pressure maintained stable ratios of elemental contents in the whole range of the substrate temperature for Zn(O,Se) layers.

| S-EPMC6877616 | biostudies-literature

Vacancy cluster in ZnO films grown by pulsed laser deposition.

Project description:Undoped and Ga-doped ZnO films were grown on c-sapphire using pulsed laser deposition (PLD) at the substrate temperature of 600 °C. Positron annihilation spectroscopy study (PAS) shows that the dominant VZn-related defect in the as-grown undoped ZnO grown with relative low oxygen pressure P(O2) is a vacancy cluster (most likely a VZn-nVO complex with n = 2, 3) rather than the isolated VZn which has a lower formation energy. Annealing these samples at 900 °C induces out-diffusion of Zn from the ZnO film into the sapphire creating the VZn at the film/sapphire interface, which favors the formation of vacancy cluster containing relatively more VZn. Increasing the P(O2) during growth also lead to the formation of the vacancy cluster with relatively more VZn. For Ga-doped ZnO films, the oxygen pressure during growth has significant influence on the electron concentration and the microstructure of the VZn-related defect. Green luminescence (GL) and yellow luminescence (YL) were identified in the cathodoluminescence study (CL) study, and both emission bands were quenched after hydrogen plasma treatment. The origin of the GL is discussed.

| S-EPMC6401145 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data