Dataset showing steel cold rolling process parameters for a 6-high cold rolling mill in Nigeria.

ABSTRACT: The data contained in this article was acquired from the automatic gauge control system for a steel cold rolling mill production line in Nigeria. Accuracy is the one of the most important indices of productivity during a milling process. A total of 486 data points were obtained from selected feedback sensors located on the rolling mill machine via the control panel Human Machine Interface (HMI). The selected rolling parameters were gathered at different time intervals for different sample coils strips during the different milling stages. The data shows parameters such as actual thickness measured, x-ray gauge temperature, mill speed at both entry and exit and the mill power. This dataset could be used to analyze and improve the accuracy of the Automatic gauge control system and reduction in error in thickness variation.

SUBMITTER: Ayuba EO

PROVIDER: S-EPMC5996350 | biostudies-literature | 2018 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Dataset showing steel cold rolling process parameters for a 6-high cold rolling mill in Nigeria.

Ayuba Emmanuel O EO Bolu Christian A CA John Temitope M TM Abioye Abiodun A AA

Data in brief 20180322

The data contained in this article was acquired from the automatic gauge control system for a steel cold rolling mill production line in Nigeria. Accuracy is the one of the most important indices of productivity during a milling process. A total of 486 data points were obtained from selected feedback sensors located on the rolling mill machine via the control panel Human Machine Interface (HMI). The selected rolling parameters were gathered at different time intervals for different sample coils ...[more]

PMID: 29900256

Similar Datasets

Online Prediction Under Model Uncertainty via Dynamic Model Averaging: Application to a Cold Rolling Mill.

Project description:We consider the problem of online prediction when it is uncertain what the best prediction model to use is. We develop a method called Dynamic Model Averaging (DMA) in which a state space model for the parameters of each model is combined with a Markov chain model for the correct model. This allows the "correct" model to vary over time. The state space and Markov chain models are both specified in terms of forgetting, leading to a highly parsimonious representation. As a special case, when the model and parameters do not change, DMA is a recursive implementation of standard Bayesian model averaging, which we call recursive model averaging. The method is applied to the problem of predicting the output strip thickness for a cold rolling mill, where the output is measured with a time delay. We found that when only a small number of physically motivated models were considered and one was clearly best, the method quickly converged to the best model, and the cost of model uncertainty was small; indeed DMA performed slightly better than the best physical model. When model uncertainty and the number of models considered were large, our method ensured that the penalty for model uncertainty was small. At the beginning of the process, when control is most difficult, we found that DMA over a large model space led to better predictions than the single best performing physically motivated model. We also applied the method to several simulated examples, and found that it recovered both constant and time-varying regression parameters and model specifications quite well.

| S-EPMC2895940 | biostudies-literature

On the Strength of a 316L-Type Stainless Steel Subjected to Cold or Warm Rolling Followed by Annealing.

Project description:The ultrafine-grained microstructures and their effect on the yield strength of a 316L-type austenitic stainless steel processed by large strain cold/warm rolling and subsequent annealing were studied. A kind of continuous recrystallization developed during annealing, resulting in the evolution of uniform ultrafine-grained microstructures with relatively high residual dislocation densities. The development of such microstructure at 973 K led to excellent combination of tensile properties including high yield strength (?0.2 > 900 MPa) and satisfactory plasticity (? > 15%). A unique power law function between the annealed grain size and the dislocation density with a dislocation density exponent of -0.5 was obtained for these continuously recrystallized microstructures. A physically justified explanation of the observed structural/substructural strengthening is introduced.

| S-EPMC7254252 | biostudies-literature

Two gas metal arc welding process dataset of arc parameters and input parameters.

Project description:The dataset was collected from experiments using the gas metal arc welding (GMAW) process. The experiments were planned with Central Composite Design to obtain a greater variety of data. This variability helps to develop a predictive model more generalistic with machine learning techniques. It was collected welding arc images and weld bead geometry images. Welding arc images were processed with a deep learning technique to detect drop detachment and short circuit transfer mode. These detections were useful to calc drop detachment frequency, short circuit frequency, and molten volume in every moment of GMAW process time. It was obtained the weld bead geometry parameters by process time too. All these data, joining input parameters were correlated, resulting in the datasets shown in this article.

| S-EPMC7881253 | biostudies-literature

Bending Fatigue Behaviour and Fatigue Endurance Limit Prediction of 20Cr2Ni4A Gear Steel after the Ultrasonic Surface Rolling Process.

Project description:To study the effect of the surface properties on the bending fatigue performance of heavy-duty gear steel, the authors of this paper used the ultrasonic surface rolling process (USRP) to strengthen 20Cr2Ni4A carburized gear steel. USRP is a novel technique in which the ultrasonic technology is incorporated into the concept of conventional deep rolling. In this study, we illustrated how the surface properties and cross-section mechanical property influence the three-point bending fatigue life of the samples before and after USRP treatment. At the same time, the predicted failure probability-stress-number of cycles (P-S-N) curve was drawn, and the fatigue fracture was analysed. The results show that the fatigue limit increased from 651.36 MPa to 918.88 MPa after USRP treatment. The fatigue source is mainly from the sample interior or surface scratches, and the fatigue performance is positively correlated with the results of the material surface roughness, surface residual stress and surface hardness. At the same time, combined with the change in the phase structure, dislocation structure, residual stress and hardness of the cross section of the material, it is found that the USRP process turns the steel into a gradient material with five layers. Finally, the coupling mechanism between the ultrasonic surface strengthening deformation layer and the carburized layer of 20Cr2Ni4A carburized gear steel is presented, and the grain structure distribution diagram of the section of the 20Cr2Ni4A model after surface strengthening treatment was simulated. The mechanism that influenced the fatigue performance after USRP treatment is explained from the perspectives of the surface and cross section of the samples.

| S-EPMC8152014 | biostudies-literature

Defining the process parameters affecting the fabrication of rosuvastatin calcium nanoparticles by planetary ball mill.

Project description:Purpose:Rosuvastatin calcium (ROSCa) nanoparticles were fabricated by planetary ball mill to enhance ROSCa dissolution rate and bioavailability. Methods:Milling time factors (milling cycle time and number as well as pause time) were explored. The effect of different milling ball size, speed, and solid-to-solvent ratio were also studied using Box-Behnken factorial design. The fabricated nanoparticles were evaluated in term of physicochemical properties and long-term stability. Results:The obtained data revealed that the integrated formulation and process factors should be monitored to obtain desirable nanoparticle attributes in terms of particle size, zeta potential, dissolution rate, and bioavailability. The optimized ROSCa nanoparticles prepared by milling technique showed a significant enhancement in the dissolution rate by 1.3-fold and the plasma concentration increased by 2-fold (P<0.05). Moreover, stability study showed that the optimized formula of ROSCa nanoparticles exhibits higher stability in long-term stability conditions at 30°C with humidity of 60%. Conclusion:Formulation of ROSCa as nanoparticles using milling technique showed a significant enhancement in both dissolution rate and plasma concentration as well as stability compared with untreated drug.

| S-EPMC6603996 | biostudies-literature

Dataset of the synthesis parameters to deposit YSZ on stainless steel AISI 316L by sputtering technique.

Project description:The data presented in this article are related to the research previously published "improvement of adhesion and barrier properties of biomedical stainless steel by deposition of YSZ coatings using RF magnetron sputtering". It contains the structural, morphological, compositional and electrochemical characterization of bare AISI 316L substrate which was used as a substrate to coat with yttria-stabilized zirconia (YSZ). The chemical composition and topography analyses from X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES) and micrographs from atomic force microscopy (AFM) as well as the roughness value of the YSZ-sputtered coating on AISI 316L substrates are presented as complementary data of the article.

| S-EPMC6811928 | biostudies-literature

Optimization design of a novel X-type six-high rolling mill based on maximum roll system stiffness.

Project description:The present investigation devices a novel X-type six-high (X-6h) mill. In addition, parametric models of different roll layouts such as the four-high (4-h), I-type six-high (I-6h), and X-6h mills are established. Three-dimensional (3D) finite element (FE) contact analysis for a strip rolling process is conducted when the mills are subjected to a constant vertical load of 65 kN. Through comparative analysis of von Mises stress, contact stress and elastic deformation displacement in three roll layouts, the rigidity characteristic of each is obtained, and it is found that the proposed X-6h mill has the largest roll gap stiffness. The influence of different roll diameter ratios on the roll gap stiffness of the roll system is investigated, based on which an optimization design model is built. Further, by taking into account the roll gap stiffness of the roll system as the optimization objective, the optimum diameter ratios of backup roll (BUR) to work roll (WR) of the X-6h rolling mill is achieved via the genetic algorithm (GA) optimization method, obtaining the optimum structural parameters of BUR and WR as well. The reliability of the proposed design is verified by manufacturing a prototype mill which produced magnesium alloy and aluminum alloy strips of high quality.

| S-EPMC7029872 | biostudies-literature

Designing Inorganic Semiconductors with Cold-Rolling Processability.

Project description:While metals can be readily processed and reshaped by cold rolling, most bulk inorganic semiconductors are brittle materials that tend to fracture when plastically deformed. Manufacturing thin sheets and foils of inorganic semiconductors is therefore a bottleneck problem, severely restricting their use in flexible electronic applications. It is recently reported that a few single-crystalline 2D van der Waals (vdW) semiconductors, such as InSe, are deformable under compressive stress. Here it is demonstrated that intralayer fracture toughness can be tailored via compositional design to make inorganic semiconductors processable by cold rolling. Systematic ab initio calculations covering a range of van der Waals semiconductors homologous to InSe are reported, leading to material-property maps that forecast trends in both the susceptibility to interlayer slip and the intralayer fracture toughness against cracking. GaSe is predicted, and experimentally confirmed, to be practically amenable to being rolled to large (three quarters) thickness reduction and length extension by a factor of three. The fracture toughness and cleavage energy are predicted to be 0.25 MPa m0.5 and 15 meV Å-2 , respectively. The findings open a new realm of possibility for alloy selection and design toward processing-friendly group-III chalcogenides for practical applications.

| S-EPMC9596854 | biostudies-literature

High Temperature Epoxy Foam: Optimization of Process Parameters.

Project description:For many years, reduction of fuel consumption has been a major aim in terms of both costs and environmental concerns. One option is to reduce the weight of fuel consumers. For this purpose, the use of a lightweight material based on rigid foams is a relevant choice. This paper deals with a new high temperature epoxy expanded material as substitution of phenolic resin, classified as potentially mutagenic by European directive Reach. The optimization of thermoset foam depends on two major parameters, the reticulation process and the expansion of the foaming agent. Controlling these two phenomena can lead to a fully expanded and cured material. The rheological behavior of epoxy resin is studied and gel time is determined at various temperatures. The expansion of foaming agent is investigated by thermomechanical analysis. Results are correlated and compared with samples foamed in the same temperature conditions. The ideal foaming/gelation temperature is then determined. The second part of this research concerns the optimization of curing cycle of a high temperature trifunctional epoxy resin. A two-step curing cycle was defined by considering the influence of different curing schedules on the glass transition temperature of the material. The final foamed material has a glass transition temperature of 270 °C.

| S-EPMC6432331 | biostudies-literature

Dataset showing the abundance and distribution of benthic foraminifera in relation to marine sediment parameters from western Arabian Gulf.

Project description:This dataset supports the paper entitled "A baseline investigation of benthic foraminifera in relation to marine sediments parameters in western parts of the Arabian Gulf". Duplicate sediment samples (sets A and B) were collected from 30 stations in an area covering approximately 25000 km2 in the offshore northern Arabian Gulf, using a van Veen grab (0.1 m2 area) and the top 1 cm was analysed for living benthic foraminifera. A set of samples was devoted to foraminiferal analysis while the other, set B, for sediment analyses. In situ hydrographical parameters such as temperature, salinity, pH, turbidity and DO were measured at surface waters. The top 1 cm was subsampled for foraminiferal analyses from the grab and preserved using 70% ethanol with Rose-Bengal stain. Potentially Toxic Elements (PTE) levels in sediment and grain size distributions were analysed. The dataset is expected to provide a baseline for PTE levels in sediment, benthic foraminiferal communities, and identify endemic species adapted to extremes of temperature and saline conditions typical of the Gulf. It can also be used by environmental managers, micropaleotologists, students in environmental/geology/marine science as reference background conditions based on sediment toxicity and benthic community information in revising environmental guidelines in the region. Data from this study suggest that PTEs are within the range of background values, and the sediments support highly diversified and stable benthic foraminiferal communities adapted to the unique environmental conditions in the Gulf. To date, this dataset documents the highest number of living benthic foraminifera species reported from the Gulf, and the most diverse living community compared to all previous studies. It also provides evidence for the full recovery of areas impacted during the 1991 Gulf oil spill which is evident by the diverse and flourishing assemblages of living benthic foraminifera documented.

| S-EPMC6948127 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data