An Approach for Measuring the Dielectric Strength of OLED Materials.

ABSTRACT: Surface roughness of electrodes plays a key role in the dielectric breakdown of thin-film organic devices. The rate of breakdown will increase when there are stochastic sharp spikes on the surface of electrodes. Additionally, surface having spiking morphology makes the determination of dielectric strength very challenging, specifically when the layer is relatively thin. We demonstrate here a new approach to investigate the dielectric strength of organic thin films for organic light-emitting diodes (OLEDs). The thin films were deposited on a substrate using physical vapor deposition (PVD) under high vacuum. The device architectures used were glass substrate/indium tin oxide (ITO)/organic material/aluminum (Al) and glass substrate/Al/organic material/Al. The dielectric strength of the OLED materials was evaluated from the measured breakdown voltage and layer thickness.

SUBMITTER: Sudheendran Swayamprabha S

PROVIDER: S-EPMC6025577 | biostudies-literature | 2018 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

An Approach for Measuring the Dielectric Strength of OLED Materials.

Sudheendran Swayamprabha Sujith S Kumar Dubey Deepak D Song Wei-Chi WC Lin You-Ting YT Ashok Kumar Yadav Rohit R Singh Meenu M Jou Jwo-Huei JH

Materials (Basel, Switzerland) 20180609 6

Surface roughness of electrodes plays a key role in the dielectric breakdown of thin-film organic devices. The rate of breakdown will increase when there are stochastic sharp spikes on the surface of electrodes. Additionally, surface having spiking morphology makes the determination of dielectric strength very challenging, specifically when the layer is relatively thin. We demonstrate here a new approach to investigate the dielectric strength of organic thin films for organic light-emitting diod ...[more]

PMID: 29890755

Similar Datasets

Synthesis of polar polynorbornenes with high dielectric relaxation strength as candidate materials for dielectric applications.

Project description:Materials with high dielectric permittivity and dielectric relaxation strength are sought for thermal and pressure sensors and electrical energy generators. However, most polymers have either too low dielectric permittivity or are so polar that their glass transition temperature (T g) is too high and thus decomposition and side reactions occur before an electric field can polarize the polar groups. Here, we use the power and versatility of ring-opening metathesis polymerization (ROMP) to synthesize polar polymers with high dielectric relaxation strength and T g significantly below the decomposition temperature. We first synthesized six polar norbornene monomers by conventional esterification, which were then polymerized by ROMP using Grubbs first- and third-generation catalysts. The structure of the polynorbornenes obtained were verified by multinuclear NMR spectroscopy, molecular weights determined by gel permeation chromatography (GPC), and thermal properties evaluated by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Additionally, their dielectric permittivity, conductivity, and dielectric losses were measured at different temperatures and frequencies ranging between 0.1 and 106 Hz.

| S-EPMC8784959 | biostudies-literature

Data on dielectric strength heterogeneity associated with printing orientation in additively manufactured polymer materials.

Project description:The following data describe the dielectric performance of additively manufactured polymer materials printed in various orientations for four common additive manufacturing techniques. Data are presented for selected commercial 3D printing materials fabricated using four common 3D printing techniques: Stereolithography (SLA), Fused Deposition Modeling (FDM), Selective Laser Sintering (SLS), and Polymer Jetting (PolyJet). Dielectric strengths are compiled for the listed materials, based on the ASTM D139 standard. This article provides data related to "Dielectric Strength Heterogeneity Associated with Printing Orientation in Additively Manufactured Polymer Materials" [1].

| S-EPMC6122370 | biostudies-literature

Super Dielectric Materials.

Project description:Evidence is provided here that a class of materials with dielectric constants greater than 10⁵ at low frequency (<10-2 Hz), herein called super dielectric materials (SDM), can be generated readily from common, inexpensive materials. Specifically it is demonstrated that high surface area alumina powders, loaded to the incipient wetness point with a solution of boric acid dissolved in water, have dielectric constants, near 0 Hz, greater than 4 × 10⁸ in all cases, a remarkable increase over the best dielectric constants previously measured for energy storage capabilities, ca. 1 × 10⁴. It is postulated that any porous, electrically insulating material (e.g., high surface area powders of silica, titania, etc.), filled with a liquid containing a high concentration of ionic species will potentially be an SDM. Capacitors created with the first generated SDM dielectrics (alumina with boric acid solution), herein called New Paradigm Super (NPS) capacitors display typical electrostatic capacitive behavior, such as increasing capacitance with decreasing thickness, and can be cycled, but are limited to a maximum effective operating voltage of about 0.8 V. A simple theory is presented: Water containing relatively high concentrations of dissolved ions saturates all, or virtually all, the pores (average diameter 500 Å) of the alumina. In an applied field the positive ionic species migrate to the cathode end, and the negative ions to the anode end of each drop. This creates giant dipoles with high charge, hence leading to high dielectric constant behavior. At about 0.8 V, water begins to break down, creating enough ionic species to "short" the individual water droplets. Potentially NPS capacitor stacks can surpass "supercapacitors" in volumetric energy density.

| S-EPMC5456448 | biostudies-other

Acridine Based Small Molecular Hole Transport Type Materials for Phosphorescent OLED Application.

Project description:Two small molecular hole-transporting type materials, namely 4-(9,9-dimethylacridin-10(9H)-yl)-N-(4-(9,9-dimethylacridin-10(9H)-yl)phenyl)-N-phenylaniline (TPA-2ACR) and 10,10'-(9-phenyl-9H-carbazole-3,6-diyl)bis(9,9-dimethyl-9,10-dihydroacridine) (PhCAR-2ACR), were designed and synthesized using a single-step Buchwald-Hartwig amination between the dimethyl acridine and triphenylamine or carbazole moieties. Both materials showed high thermal decomposition temperatures of 402 and 422 °C at 5% weight reduction for PhCAR-2ACR and TPA-2ACR, respectively. TPA-2ACR as hole-transporting material exhibited excellent current, power, and external quantum efficiencies of 55.74 cd/A, 29.28 lm/W and 21.59%, respectively. The achieved device efficiencies are much better than that of the referenced similar, 1,1-Bis[(di-4-tolylamino)phenyl]cyclohexane (TAPC)-based device (32.53 cd/A, 18.58 lm/W and 10.6%). Moreover, phenyl carbazole-based PhCAR-2ACR showed good device characteristics when applied for host material in phosphorescent OLEDs.

| S-EPMC8703516 | biostudies-literature

Strength through defects: A novel Bayesian approach for the optimization of architected materials.

Project description:We use a previously unexplored Bayesian optimization framework, “evolutionary Monte Carlo sampling,” to systematically design the arrangement of defects in an architected microlattice to maximize its strain energy density before undergoing catastrophic failure. Our algorithm searches a design space with billions of 4 × 4 × 5 3D lattices, yet it finds the global optimum with only 250 cost function evaluations. Our optimum has a normalized strain energy density 12,464 times greater than its commonly studied defect-free counterpart. Traditional optimization is inefficient for this microlattice because (i) the design space has discrete, qualitative parameter states as input variables, (ii) the cost function is computationally expensive, and (iii) the design space is large. Our proposed framework is useful for architected materials and for many optimization problems in science and elucidates how defects can enhance the mechanical performance of architected materials.

| S-EPMC8500519 | biostudies-literature

An approach for predicting the compressive strength of cement-based materials exposed to sulfate attack.

Project description:In this paper, a support vector machine (SVM) model which can be used to predict the compressive strength of mortars exposed to sulfate attack was established. An accelerated corrosion test was applied to collect compressive strength data. For predicting the compressive strength of mortars, a total of 638 data samples obtained from experiment was chosen as a dataset to establish a SVM model. The values of the coefficient of determination, the mean absolute error, the mean absolute percentage error and the root mean square error were used for evaluating the predictive accuracy. The main factors affecting the predicted compressive strength were obtained by sensitivity analysis. A SVM model was calibrated, validated, and finally established. Moreover, the performance of the SVM model was compared to an artificial neural network (ANN) model. Results show that the prediction values from the SVM model were close to the experimental values; the main factors sensitive to concrete compressive strength were exposure time, water-cement ratio and sulfate ions; the performance of the SVM model was better than the ANN model. The SVM model developed in this study can be potentially used for predicting the compressive strength of cement-based materials servicing in harsh environments.

| S-EPMC5773203 | biostudies-literature

High-performance blue OLED using multiresonance thermally activated delayed fluorescence host materials containing silicon atoms.

Project description:We report three highly efficient multiresonance thermally activated delayed fluorescence blue-emitter host materials that include 5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracene (DOBNA) and tetraphenylsilyl groups. The host materials doped with the conventional N7,N7,N13,N13,5,9,11,15-octaphenyl-5,9,11,15-tetrahydro-5,9,11,15-tetraaza-19b,20b-diboradinaphtho[3,2,1-de:1',2',3'-jk]pentacene-7,13-diamine (ν-DABNA) blue emitter exhibit a high photoluminescence quantum yield greater than 0.82, a high horizontal orientation greater than 88%, and a short photoluminescence decay time of 0.96-1.93 μs. Among devices fabricated using six synthesized compounds, the device with (4-(2,12-di-tert-butyl-5,9-dioxa-13b-boranaphtho[3,2,1-de]anthracen-7-yl)phenyl)triphenylsilane (TDBA-Si) shows high external quantum efficiency values of 36.2/35.0/31.3% at maximum luminance/500 cd m-2/1,000 cd m-2. This high performance is attributed to fast energy transfer from the host to the dopant. Other factors possibly contributing to the high performance are a T1 excited-state contribution, inhibition of aggregation by the bulky tetraphenylsilyl groups, high horizontal orientation, and high thermal stability. We achieve a high efficiency greater than 30% and a small roll-off value of 4.9% at 1,000 cd m-2 using the TDBA-Si host material.

| S-EPMC10495399 | biostudies-literature

Recycling of dielectric electroactive materials enabled through thermoplastic PDMS.

Project description:In the green transition, actuators and generators play an essential role in the development of sustainable solutions across a broad range of applications. In this context, dielectric transducers are advocated as one of the most promising solutions in terms of effectiveness, lifetime and running costs. However, they are classically produced as sandwich structures, whereby a cross-linked dielectric material is placed between two compliant electrodes. From a materials consumption viewpoint, this is problematic, since it will inherently result in a loss of material during production as well as inhibit the recycling of expended systems when their life comes to an end. Herein, we present a cleaning method employing surfactants and sonication to remove electrodes from the surface of the dielectric material. By applying a thermoplastic silicone elastomer as the dielectric material, it is possible to reprocess the material by hot-pressing, and to prepare new actuators after the rinsing process. This effectively shows that recycling production scrap, for example, is possible. By comparing the cleaned material with a directly recycled material, it is clear that cleaning removes a critical amount of metals from the material and enables recycling for at least five cycles. Comparatively, a directly recycled material is prone to a high leakage current and premature electronic breakdown after only two cycles. This simple cleaning process, in combination with use of a thermoplastic dielectric material, enables less waste from production as well as the possibility of reclaiming and recycling materials in general.

| S-EPMC8984943 | biostudies-literature

Rational design of inorganic dielectric materials with expected permittivity.

Project description:Techniques for rapid design of dielectric materials with appropriate permittivity for many important technological applications are urgently needed. It is found that functional structure blocks (FSBs) are helpful in rational design of inorganic dielectrics with expected permittivity. To achieve this, coordination polyhedra are parameterized as FSBs and a simple empirical model to evaluate permittivity based on these FSB parameters is proposed. Using this model, a wide range of examples including ferroelectric, high/low permittivity materials are discussed, resulting in several candidate materials for experimental follow-up.

| S-EPMC4663754 | biostudies-literature

Allotropy in ultra high strength materials.

Project description:Allotropic phase transformations may be driven by the application of stresses in many materials; this has been especially well-documented for pressure driven transformations. Recent advances in strengthening materials allow for the application of very large shear stresses as well - opening up vast new regions of stress space. This means that the stress space is six-dimensional (rather than one for pressure) and that phase transformations depend upon crystal/grain orientation. We propose a novel approach for predicting the role of the entire stress tensor on phase transformations in grains of all orientations in any material. This multiscale approach is density functional theory based and guided by nonlinear elasticity. We focus on stress tensor dependent allotropic phase transformations in iron at high pressure and ultra-fine grained nickel and titanium. The results are quantitatively consistent with a range of experimental observations in these disparate systems. This approach enables the balanced design of high strength-high ductility materials.

| S-EPMC9184473 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data