Poly(3-hydroxybutyrate)/poly(ethylene glycol) scaffolds with different microstructure: the effect on growth of mesenchymal stem cells.

ABSTRACT: Development of biocompatible 3D scaffolds is one of the most important challenges in tissue engineering. In this study, we developed polymer scaffolds of different design and microstructure to study cell growth in them. To obtain scaffolds of various microstructure, e.g., size of pores, we used double- and one-stage leaching methods using porogens with selected size of crystals. A composite of poly(3-hydroxybutyrate) (PHB) with poly(ethylene glycol) (PEG) (PHB/PEG) was used as polymer biomaterial for scaffolds. The morphology of scaffolds was analyzed by scanning electron microscopy; the Young modulus of scaffolds was measured by rheometry. The ability to support growth of mesenchymal stem cells (MSCs) in scaffolds was studied using the XTT assay; the phenotype of MSC was preliminarily confirmed by flow cytometry and the activity of alkaline phosphatase and expression level of CD45 marker was studied to test possible MSC osteogenic differentiation. The obtained scaffolds had different microstructure: the scaffolds with uniform pore size of about 125 µm (normal pores) and 45 µm (small pores) and scaffolds with broadly distributed pores size from about 50-100 µm. It was shown that PHB/PEG scaffolds with uniform pores of normal size did not support MSCs growth probably due to their marked spontaneous osteogenic differentiation in these scaffolds, whereas PHB/PEG scaffolds with diverse pore size promoted stem cells growth that was not accompanied by pronounced differentiation. In scaffolds with small pores (about 45 µm), the growth of MSC was the lowest and cell growth suppression was only partially related to stem cells differentiation. Thus, apparently, the broadly distributed pore size of PHB/PEG scaffolds promoted MSC growth in them, whereas uniform size of scaffold pores stimulated MSC osteogenic differentiation.

SUBMITTER: Bonartsev AP

PROVIDER: S-EPMC6051946 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Polylactide (PLA) electrospun fibers have been reported as a scaffold for bone tissue engineering application, however, the great hydrophobicity limits its broad application. In this study, the hybrid amphiphilic poly(ethylene glycol) (PEG)/hydrophobic PLA fibrous scaffolds exhibited improved morphology with regular and continuous fibers compared to corresponding blank PLA fiber mats. The prepared PEG/PLA fibrous scaffolds favored mesenchymal stem cell (MSC) attachment and proliferation by providing an interconnected porous extracellular environment. Meanwhile, MSCs can penetrate into the fibrous scaffold through the interstitial pores and integrate well with the surrounding fibers, which is very important for favorable application in tissue engineering. More importantly, the electrospun hybrid PEG/PLA fibrous scaffolds can enhance MSCs to differentiate into bone-associated cells by comprehensively evaluating the representative markers of the osteogenic procedure with messenger ribonucleic acid quantitation and protein analysis. MSCs on the PEG/PLA fibrous scaffolds presented better differentiation potential with higher messenger ribonucleic acid expression of the earliest osteogenic marker Cbfa-1 and mid-stage osteogenic marker Col I. The significantly higher alkaline phosphatase activity of the PEG/PLA fibrous scaffolds indicated that these can enhance the differentiation of MSCs into osteoblast-like cells. Furthermore, the higher messenger ribonucleic acid level of the late osteogenic differentiation markers OCN (osteocalcin) and OPN (osteopontin), accompanied by the positive Alizarin red S staining, showed better maturation of osteogenic induction on the PEG/PLA fibrous scaffolds at the mineralization stage of differentiation. After transplantation into the thigh muscle pouches of rats, and evaluating the inflammatory cells surrounding the scaffolds and the physiological characteristics of the surrounding tissues, the PEG/PLA scaffolds presented good biocompatibility. Based on the good cellular response and excellent osteogenic potential in vitro, as well as the biocompatibility with the surrounding tissues in vivo, the electrospun PEG/PLA fibrous scaffolds could be one of the most promising candidates in bone tissue engineering.

Project description:Human mesenchymal stem cells (hMSCs) are motile cells that migrate from their native niche to wounded sites where they regulate inflammation during healing. New materials are being developed as hMSC delivery platforms to enhance wound healing. To act as an effective wound healing material, the hydrogel must degrade at the same rate as tissue regeneration, while maintaining a high cell viability. This work determines the kinetics and mechanism of cell-mediated degradation in hMSC-laden poly(ethylene glycol) (PEG) hydrogels. We use a well-established hydrogel scaffold that is composed of a backbone of four-arm star PEG functionalized with norbornene that is cross-linked with a matrix metalloproteinase (MMP) degradable peptide. This peptide sequence is cleaved by cell-secreted MMPs, which allow hMSCs to actively degrade the hydrogel during motility. Three mechanisms of degradation are characterized: hydrolytic, noncellular enzymatic and cell-mediated degradation. We use bulk rheology to characterize hydrogel material properties and quantify degradation throughout the entire reaction. Hydrolysis and noncellular enzymatic degradation are first characterized in hydrogels without hMSCs, and follow first-order and Michaelis-Menten kinetics, respectively. A high cell viability is measured in hMSC-laden hydrogels, even after shearing on the rheometer. After confirming hMSC viability, bulk rheology characterizes cell-mediated degradation. When comparing cell-mediated degradation to noncellular degradation mechanisms, cell-mediated degradation is dominated by enzymatic degradation. This indicates hydrogels with hMSCs are degraded primarily due to cell-secreted MMPs and very little network structure is lost due to hydrolysis. Modeling cell-mediated degradation provides an estimate of the initial concentration of MMPs secreted by hMSCs. By changing the concentration of hMSCs, we determine the initial MMP concentration increases with increasing hMSC concentration. This work characterizes the rate and mechanism of scaffold degradation, giving new insight into the design of these materials as implantable scaffolds.

Dataset Information

Poly(3-hydroxybutyrate)/poly(ethylene glycol) scaffolds with different microstructure: the effect on growth of mesenchymal stem cells.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets