Effect of bioactive glass nanoparticles on biological properties of PLGA/collagen scaffold.

ABSTRACT: Bioactive glasses have shown some interesting biological properties such as biocompatibility, biodegradation, and angiogenesis in skin tissue engineering. In the current research, the effects of MgO- or CoO-doped 64S bioactive glass with a composition of 64 SiO2-26 CaO-5 P2O5-5 MgO or CoO (mol%) were studied in relation with biological properties of electrospun [poly(lactic-co-glycolic acid) (PLGA)/collagen]. PLGA/collagen samples were rinsed in suspension of bioactive glass nanoparticles in distilled water with a concentration of 0.1 w/v and then freeze dried. Cell adhesion, viability, angiogenesis, and ionic release were performed and tested in culture medium containing fibroblast cells. Attachment and viability of fibroblast cells were increased significantly in bioglass-coated samples, while shrinkage in PLGA/collagen scaffold was reduced by the addition of bioactive glass. Vascular endothelial growth factor secretion in coated scaffold was dropped compared to the uncoated samples. This could be attributed to the fast degradation of glass nanoparticles, according to the inductively coupled plasma-atomic emission spectroscopy results.

SUBMITTER: Nokhasteh S

PROVIDER: S-EPMC6068071 | biostudies-literature | 2018 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of bioactive glass nanoparticles on biological properties of PLGA/collagen scaffold.

Nokhasteh Samira S Sadeghi-Avalshahr Alireza A Molavi Amir Mahdi AM Khorsand-Ghayeni Mohammad M Naderi-Meshkin Hojjat H

Progress in biomaterials 20180511 2

Bioactive glasses have shown some interesting biological properties such as biocompatibility, biodegradation, and angiogenesis in skin tissue engineering. In the current research, the effects of MgO- or CoO-doped 64S bioactive glass with a composition of 64 SiO2-26 CaO-5 P2O5-5 MgO or CoO (mol%) were studied in relation with biological properties of electrospun [poly(lactic-co-glycolic acid) (PLGA)/collagen]. PLGA/collagen samples were rinsed in suspension of bio ...[more]

PMID: 29748742

Similar Datasets

Project description:Objective:To compare the elastic modulus, flexural strength, and hardness of an experimental resin based composite (RBC) with and without containing silver nanoparticles (AgNPs) and bioactive glass (BAG) with a commercially available RBC. Methods:This study was conducted, during the period August 2016-May 2018, at the Department of Dental Materials, Peshawar Dental College, Peshawar (Pakistan) and Department of Chemistry, University of Montreal, Canada. Test specimens made in the commercial RBC acted as Group-1 (G1). An experimental RBC containing 70 wt % filler content was synthesized. It was first used as such to prepare test specimens to act as the experimental control group (G2). This RBC was then modified by adding various amounts of BAG (5%, 10% and 15%) and a fixed amount of 0.009% AgNPs to use the so modified RBCs for preparing the test specimens to belong to three groups (G3, G4 & G5). The AgNPs had been synthesized in situ by reduction of salt during photo-polymerization. Flexural strength (FS), elastic modulus (EM) and Vickers hardness were determined using universal testing machine and hardness tester respectively. Data were analyzed using one-way ANOVA and Tukey post-hoc test. Results:Except for G3 restorations showing significantly lower mean FS value, the FS for those in the other groups were not significantly different (p>0.05). Elastic modulus of the experimental RBC restorations was though higher than those of the others but the difference was statistically insignificant (p>0.05). Reduced Vickers hardness values were documented for the restorations in the G4 and G5 compared to those in the G3 but again the difference was insignificant (p>0.05). Flexural strength and hardness values of the test specimens in the experimental RBCs were significantly lower than those made in the commercial hybrid RBC (p<0.05). Conclusion:BAG and AgNPs addition to the experimental RBC in the mentioned concentration adversely affected the tested mechanical properties.

Project description:Mesoporous bioactive nanoparticles (MBNs) have been developed as promising additives to various types of bone or dentin regenerative material. However, biofunctionality of MBNs as dentin regenerative additive to dental materials have rarely been studied. We investigated the uptake efficiency of MBNs-NH2 with their endocytosis pathway and the role of MBNs-NH2 in odontogenic differentiation to clarify inherent biofunctionality. MBNs were fabricated by sol-gel synthesis, and 3% APTES was used to aminate these nanoparticles (MBNs-NH2) to reverse their charge from negative to positive. To characterize the MBNs-NH2, TEM, XRD, FTIR, zeta(ξ)-potential measurements, and Brunauer-Emmett-Teller analysis were performed. After primary cultured rat dental pulp stem cells (rDPSCs) were incubated with various concentrations of MBNs-NH2, stem cell viability (24 hours) with or without differentiated media, internalization of MBNs-NH2 in rDPSCs (~4 hours) via specific endocytosis pathway, intra or extracellular ion concentration and odontoblastic differentiation (~28 days) were investigated. Incubation with up to 50 μg/mL of MBNs-NH2 had no effect on rDPSCs viability with differentiated media (p>0.05). The internalization of MBNs-NH2 in rDPSCs was determined about 92% after 4 hours of incubation. Uptake was significantly decreased with ATP depletion and after 1 hour of pre-treatment with the inhibitor of macropinocytosis (p<0.05). There was significant increase of intracellular Ca and Si ion concentration in MBNs-NH2 treated cells compared to no-treated counterpart (p<0.05). The expression of odontogenic-related genes (BSP, COL1A, DMP-1, DSPP, and OCN) and the capacity for biomineralization (based on alkaline phosphatase activity and alizarin red staining) were significantly upregulated with MBNs-NH2. These results indicate that MBNs-NH2 induce odontogenic differentiation of rDPSCs and may serve as a potential dentin regenerative additive to dental material for promoting odontoblast differentiation.

Dataset Information

Effect of bioactive glass nanoparticles on biological properties of PLGA/collagen scaffold.

Publications

Effect of bioactive glass nanoparticles on biological properties of PLGA/collagen scaffold.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets