Impact of Pore Size and Surface Chemistry of Porous Silicon Particles and Structure of Phospholipids on Their Interactions.

ABSTRACT: By exploiting its porous structure and high loading capacity, porous silicon (PSi) is a promising biomaterial to fabricate protocells and biomimetic reactors. Here, we have evaluated the impact of physicochemical properties of PSi particles [thermally oxidized PSi, TOPSi; annealed TOPSi, AnnTOPSi; (3-aminopropyl) triethoxysilane functionalized thermally carbonized PSi, APTES-TCPSi; and thermally hydrocarbonized PSi, THCPSi] on their surface interactions with different phospholipids. All of the four phospholipids were similarly adsorbed by the surface of PSi particles, except for TOPSi. Among four PSi particles, TOPSi with hydrophilic surface and smaller pore size showed the weakest adsorption toward phosphatidylcholines. By increasing the pore size from roughly 12.5 to 18.0 nm (TOPSi vs AnnTOPSi), the quantity of phosphatidylcholines adsorbed by TOPSi was enhanced to the same level of hydrophilic APTES-TCPSi and hydrophobic THCPSi. The 1,2-dioleoyl-sn-glycero-3-phosphocholine (DOPC) exhibited the highest release ratio of phospholipids from all four PSi particles, and phosphatidylserine (DPPS) showed the lowest release ratio of phospholipids from PSi particles, except for TOPSi, which adsorbed less phospholipids due to the small pore size. There is consistency in the release extent of phospholipids from PSi particles and the isosteric heat of adsorption. Overall, our study demonstrates the importance of pore size and surface chemistry of PSi particles as well as the structure of phospholipids on their interactions. The obtained information can be employed to guide the selection of PSi particles and phospholipids to fabricate highly ordered structures, for example, protocells, or biomimetic reactors.

SUBMITTER: Liu D

PROVIDER: S-EPMC6108535 | biostudies-literature | 2018 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Impact of Pore Size and Surface Chemistry of Porous Silicon Particles and Structure of Phospholipids on Their Interactions.

Liu Dongfei D Lipponen Katriina K Quan Peng P Wan Xiaocao X Zhang Hongbo H Mäkilä Ermei E Salonen Jarno J Kostiainen Risto R Hirvonen Jouni J Kotiaho Tapio T Santos Hélder A HA

ACS biomaterials science & engineering 20180614 7

By exploiting its porous structure and high loading capacity, porous silicon (PSi) is a promising biomaterial to fabricate protocells and biomimetic reactors. Here, we have evaluated the impact of physicochemical properties of PSi particles [thermally oxidized PSi, TOPSi; annealed TOPSi, AnnTOPSi; (3-aminopropyl) triethoxysilane functionalized thermally carbonized PSi, APTES-TCPSi; and thermally hydrocarbonized PSi, THCPSi] on their surface interactions with different phospholipids. All of the f ...[more]

PMID: 30159385

Similar Datasets

Project description:3D printed scaffolds can be used, for example, in medical applications for simulating body tissues or for manufacturing prostheses. However, it is difficult to print porous structures of specific porosity and pore size values with fused deposition modelling (FDM) technology. The present paper provides a methodology to design porous structures to be printed. First, a model is defined with some theoretical parallel planes, which are bounded within a geometrical figure, for example a disk. Each plane has randomly distributed points on it. Then, the points are joined with lines. Finally, the lines are given a certain volume and the structure is obtained. The porosity of the structure depends on three geometrical variables: the distance between parallel layers, the number of columns on each layer and the radius of the columns. In order to obtain mathematical models to relate the variables with three responses, the porosity, the mean of pore diameter and the variance of pore diameter of the structures, design of experiments with three-level factorial analysis was used. Finally, multiobjective optimization was carried out by means of the desirability function method. In order to favour fixation of the structures by osseointegration, porosity range between 0.5 and 0.75, mean of pore size between 0.1 and 0.3 mm, and variance of pore size between 0.000 and 0.010 mm² were selected. Results showed that the optimal solution consists of a structure with a height between layers of 0.72 mm, 3.65 points per mm² and a radius of 0.15 mm. It was observed that, given fixed height and radius values, the three responses decrease with the number of points per surface unit. The increase of the radius of the columns implies the decrease of the porosity and of the mean of pore size. The decrease of the height between layers leads to a sharper decrease of both the porosity and the mean of pore size. In order to compare calculated and experimental values, scaffolds were printed in polylactic acid (PLA) with FDM technology. Porosity and pore size were measured with X-ray tomography. Average value of measured porosity was 0.594, while calculated porosity was 0.537. Average value of measured mean of pore size was 0.372 mm, while calculated value was 0.434 mm. Average value of variance of pore size was 0.048 mm², higher than the calculated one of 0.008 mm². In addition, both round and elongated pores were observed in the printed structures. The current methodology allows designing structures with different requirements for porosity and pore size. In addition, it can be applied to other responses. It will be very useful in medical applications such as the simulation of body tissues or the manufacture of prostheses.

Dataset Information

Impact of Pore Size and Surface Chemistry of Porous Silicon Particles and Structure of Phospholipids on Their Interactions.

Publications

Impact of Pore Size and Surface Chemistry of Porous Silicon Particles and Structure of Phospholipids on Their Interactions.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets