Size effect of gold nanoparticles in catalytic reduction of p-nitrophenol with NaBH4.

ABSTRACT: Gold nanoparticles (Au NPs) were prepared by reducing HAuCl4 with NaBH4. Their average particle sizes could be tuned in the range of 1.7 and 8.2 nm, by adjusting the amount of NaBH4 used during synthesis. The obtained Au NPs (colloids) were then loaded onto a commercial Al2O3 support to prepare Au/Al2O3 catalysts with tunable Au particle sizes. An optimal pH value (5.9) of the Au colloid solution was found to be essential for loading Au NPs onto Al2O3 while avoiding the growth of Au NPs. Au NPs and Au/Al2O3 catalysts were tested in the reduction of p-nitrophenol with NaBH4. Interestingly, the catalytic activity depended on the size of Au NPs, being the highest when the average size was 3.4 nm. Relevant characterization by UV-Vis, TEM, and XRD was conducted.

SUBMITTER: Lin C

PROVIDER: S-EPMC6269978 | biostudies-literature | 2013 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Size effect of gold nanoparticles in catalytic reduction of p-nitrophenol with NaBH4.

Lin Chao C Tao Kai K Hua Dayin D Ma Zhen Z Zhou Shenghu S

Molecules (Basel, Switzerland) 20131011 10

Gold nanoparticles (Au NPs) were prepared by reducing HAuCl4 with NaBH4. Their average particle sizes could be tuned in the range of 1.7 and 8.2 nm, by adjusting the amount of NaBH4 used during synthesis. The obtained Au NPs (colloids) were then loaded onto a commercial Al2O3 support to prepare Au/Al2O3 catalysts with tunable Au particle sizes. An optimal pH value (5.9) of the Au colloid solution was found to be essential for loading Au NPs onto Al2O3 while avoiding the growth of Au NPs. Au NPs ...[more]

PMID: 24126378

Similar Datasets

Size controlled green synthesis of gold nanoparticles using <i>Coffea arabica</i> seed extract and their catalytic performance in 4-nitrophenol reduction.

Project description:Well crystalline gold nanoparticles (AuNPs) of different sizes were fabricated using sundried Coffea arabica seed (CAS) extract at room temperature by controlling the pH of the green extract. The size, shape and crystallinity of the nanoparticles have been studied using electron microscopy and X-ray diffraction. The presence of phenolic groups (revealed through FT-IR studies) from the CAS extract are responsible both for the reduction of Au ions and stabilization of the formed AuNPs. The efficiency of the CAS extract mediated green synthesis technique for the production of AuNPs has been compared to the conventional chemical Turkevich technique, which not only uses a toxic reductant such as NaBH4, but also operates around the boiling point of water. It has been observed that the CAS extract mediated synthesis process produces relatively bigger AuNPs at similar pH values of the reaction mixture in comparison to the AuNPs produced in the Turkevich process. Although the AuNPs synthesized using CAS extract are relatively larger and polydisperse in nature, their catalytic efficiencies for the degradation of an aromatic nitro compound (4-nitrophenol) are found to be comparable to the chemically fabricated AuNPs. Probable mechanisms associated with the formation of AuNPs and their size control in the CAS extract mediated green synthesis process have been discussed.

| S-EPMC9082294 | biostudies-literature

Highly ordered mesoporous silica film nanocomposites containing gold nanoparticles for the catalytic reduction of 4-nitrophenol.

Project description:We report that transparent mesostructured silica/gold nanocomposite materials with an interpore distance of 4.1 nm, as-synthesized from a templated sol-gel synthesis method using discotic trinuclear gold(I) pyrazolate complex, were successfully utilized for the fabrication of thin film mesoporous silica nanocomposites containing gold nanoparticles. The material exhibited a highly ordered hexagonal structure when subjected to a thermal hydrogen reduction treatment at 210 °C. In contrast, when the material was subjected to calcination as a heat treatment from 190 to 450 °C, the thin film nanocomposites showed an intense d 100 X-ray diffraction peak. Moreover, gold nanoparticles inside the thin film nanocomposites were confirmed by the presence of the d 111 diffraction peak at 2θ = 38.2°, a surface plasmon resonance peak between 500-580 nm, and the spherical shape observed in the transmission electron microscope images, as well as the visual change in color from pink to purple. Interestingly, by simply dipping the material into a reaction solution of 4-nitrophenol at room temperature, the highly ordered structure of the as-fabricated silica/gold nanoparticle thin film composite after thermal hydrogen reduction at 210 °C resulted in an improved catalytic activity for the reduction of 4-nitrophenol to 4-aminophenol compared to the material calcined at 250 °C. Such catalytic activity is due to the presence of gold nanoparticles of smaller size in the silicate channels of the highly ordered mesoporous film nanocomposites.

| S-EPMC6633902 | biostudies-literature

Size-Dependent Catalytic Activity of PVA-Stabilized Palladium Nanoparticles in <i>p</i>-Nitrophenol Reduction: Using a Thermoresponsive Nanoreactor.

Project description:Palladium nanoparticles (Pd NPs) of various average global diameters (2.1-7.1 nm) encapsulated with hydrophilic polymer polyvinyl alcohol (PVA) have been synthesized and used as catalysts for sodium borohydride assisted reduction of p-nitrophenol to p-aminophenol. The synthesized catalysts exhibit excellent and typical size-dependent catalytic activity in the green protocol. UV-visible absorption spectroscopy, X-ray diffraction, scanning electron microscopy, and transmission electron microscopy were employed to characterize the prepared Pd NPs. The kinetics of this reaction was easily monitored by a UV-visible absorption spectrophotometer. The mechanism of the reaction is explained by the Langmuir-Hinshelwood model. The catalytic performance increases with decreasing size of the synthesized nanoparticles. The apparent rate constants (k app × 103/s-1) of the catalytic reduction in the presence of Pd NPs of average diameters of 2.1, 3.35, 6.2, and 7.1 nm are determined as 8.57, 7.67, 6.16, and 5.04, respectively, at 298 K by using 2.91 mol % palladium nanocatalyst in each case. Moreover, the estimated activation energy of 22.2 kJ mol-1 obtained for Pd NPs with the smallest average diameter of 2.1 nm is very low as reported in the literature for the reduction. The influences of catalyst dose and concentration of p-nitrophenol on catalytic reduction are fully investigated. The catalyst with the largest diameter shows a temperature-sensitive property that might be due to the presence of a very low amount of rapped PVA used as stabilizer during the fabrication process. Thus, the synthetic protocol provides a unique fabrication process of a catalytically active thermoresponsive nanoreactor consisting of Pd NPs encapsulated into a PVA stabilizing agent.

| S-EPMC8374901 | biostudies-literature

Facile Synthesis of Gold Nanoparticles with Alginate and Its Catalytic Activity for Reduction of 4-Nitrophenol and H₂O₂ Detection.

Project description:Gold nanoparticles (AuNPs) were synthesized using a facile solvothermal method with alginate sodium as both reductant and stabilizer. Formation of AuNPs was confirmed by UV-vis spectroscopic analysis. The synthesized AuNPs showed a localized surface plasmon resonance at approximately 520-560 nm. The AuNPs were characterized using transmission electron microscopy, X-ray diffraction and dynamic light scattering. Transmission electron microscopy revealed that the AuNPs were mostly nanometer-sized spherical particles. Powder X-ray diffraction analysis proved the formation of face-centered cubic structure of Au. Catalytic reduction of 4-nitrophenol was monitored via spectrophotometry using AuNPs as catalyst, and further a non-enzymatic sensor was fabricated. The results demonstrated that AuNPs presented excellent catalytic activity and provided a sensitive response to H₂O₂ detection.

| S-EPMC5459079 | biostudies-literature

Copper-Based Integral Catalytic Impeller for the Rapid Catalytic Reduction of 4-Nitrophenol.

Project description:The integral catalytic impeller can simultaneously improve reaction efficiency and avoid the problem of catalyst separation, which has great potential in applying heterogeneous catalysis. This paper introduced a strategy of combining electroless copper plating with 3D printing technology to construct a pluggable copper-based integral catalytic agitating impeller (Cu-ICAI) and applied it to the catalytic reduction of 4-nitrophenol (4-NP). The obtained Cu-ICAI exhibits very excellent catalytic activity. The 4-NP conversion rate reaches almost 100% within 90 s. Furthermore, the Cu-ICAI can be easily pulled out from the reactor to be repeatedly used more than 15 times with high performance. Energy-dispersive spectrometry, X-ray diffraction, and X-ray photoelectron spectroscopy characterizations show that the catalyst obtained by electroless copper plating is a ternary Cu-Cu2O-CuO composite catalyst, which is conducive to the electron transfer process. This low-cost, facile, and versatile strategy, combining electroless plating and 3D printing, may provide a new idea for the preparation of the integral impeller with other metal catalytic activities.

| S-EPMC8388078 | biostudies-literature

Synthesis of Prolate-Shaped Au Nanoparticles and Au Nanoprisms and Study of Catalytic Reduction Reactions of 4-Nitrophenol.

Project description:The growth into anisotropic one or two dimensions is important in plasmonic gold nanomaterials because extinction occurs along multiple axes and sometimes the resonance extends to the near-infrared region. The surfactant mixture of cetyltrimethylammonium bromide (CTAB) and Pluronic triblock copolymers has been recently demonstrated to be efficient anisotropic soft templates for the growth of noble metal nanomaterials. Seed-mediated growth of two types of anisotropic Au nanoparticles is achieved in this study. One is one-dimensional prolate-shaped Au nanoparticles with the average aspect ratios of 2.29 and 2.59, and the other is two-dimensional gold nanoprisms with the average edge length of 50.4 nm. These anisotropic structures are believed to be produced by the tendency of Pluronic copolymers to be micellized anisotropically at the elevated temperatures and by the preference for being lamellar mesophases in the phase diagrams when the concentration is highest. When prepared in the surfactant mixture of CTAB and L-64 (17.9%), Au nanoparticles containing spherical particles (27.9 nm) as the major products show the best catalytic performances in the reduction reactions of 4-nitrophenol.

| S-EPMC6647965 | biostudies-literature

Size-controlled synthesis of monodispersed gold nanoparticles via carbon monoxide gas reduction.

Project description:An in depth analysis of gold nanoparticle (AuNP) synthesis and size tuning, utilizing carbon monoxide (CO) gas as a reducing agent, is presented for the first time. The sizes of the AuNPs are tunable from ~4 to 100 nm by altering the concentration of HAuCl4 and inlet CO gas-injection flow rate. It is also found that speciation of aqueous HAuCl4, prior to reduction, influences the size, morphology, and properties of AuNPs when reduced with CO gas. Ensemble extinction spectra and TEM images provide clear evidence that CO reduction offers a high level of monodispersity with standard deviations as low as 3%. Upon synthesis, no excess reducing agent remains in solution eliminating the need for purification. The time necessary to synthesize AuNPs, using CO, is less than 2 min.

| S-EPMC3211845 | biostudies-other

Effect of the Preparation Conditions on the Catalytic Properties of CoPt for Highly Efficient 4-Nitrophenol Reduction.

Project description:CoPt alloys with Pt contents from 15 to 90% were prepared using low-cost electrochemical deposition. Different samples were synthesized from electrochemical baths at pH = 2.5 and 5.5 in a solution with and without saccharin as an additive. The morphology, composition and crystalline structure of the as-prepared samples were investigated by High Resolution-Scanning Electron Microscopy (HR-SEM), Atomic Force Microscopy (AFM), Ultra-high Resolution-Transmission Electron Microscopy (UHR-TEM), Energy-Dispersive X-ray Spectroscopy (EDX), and X-ray Diffraction (XRD). XRD investigations revealed that fcc crystalline structure transforms into hcp crystalline structure when the pH of the electrochemical bath is increased from 2.5 to 5.5 as well as when saccharin is added to the electrochemical bath. The catalytic performance of the CoPt alloys for the nitro to amino phenol compounds conversion was investigated for all the prepared samples, and the results show that the conversion degree increases (from 11.4 to 96.5%) even though the Pt content in the samples decreases. From the samples prepared from the electrochemical bath with saccharin, a study regarding the effect of contact time was performed. The results indicated that after only 5 min, the CoPt sample prepared at pH = 5.5 in the presence of saccharin completely converted the nitro compound to an amino compound.

| S-EPMC9501049 | biostudies-literature

One-Pot Facile Synthesis of Noble Metal Nanoparticles Supported on rGO with Enhanced Catalytic Performance for 4-Nitrophenol Reduction.

Project description:In this study, reduced graphene oxide (rGO)-supported noble metal (gold, silver, and platinum) nanoparticle catalysts were prepared via the one-pot facile co-reduction technique. Various measurement techniques were used to investigate the structures and properties of the catalysts. The relative intensity ratios of ID/IG in rGO/Au, rGO/Ag, rGO/Pt, and GO were 1.106, 1.078, 1.047, and 0.863, respectively. The results showed the formation of rGO and that noble metal nanoparticles were decorated on rGO. Furthermore, the catalytic activities of the designed nanocomposites were investigated via 4-nitrophenol. The catalysts were used in 4-nitrophenol reduction. The catalytic performance of the catalysts was evaluated using the apparent rate constant k values. The k value of rGO/Au was 0.618 min-1, which was higher than those of rGO/Ag (0.55 min-1) and rGO/Pt (0.038 min-1). The result proved that the rGO/Au catalyst exhibited a higher catalytic performance than the rGO/Ag catalyst and the rGO/Pt catalyst. The results provide a facile method for the synthesis of rGO-supported nanomaterials in catalysis.

| S-EPMC8659260 | biostudies-literature

Catalytic Hydrogen Evolution of NaBH4 Hydrolysis by Cobalt Nanoparticles Supported on Bagasse-Derived Porous Carbon.

Project description:As a promising hydrogen storage material, sodium borohydride (NaBH4) exhibits superior stability in alkaline solutions and delivers 10.8 wt.% theoretical hydrogen storage capacity. Nevertheless, its hydrolysis reaction at room temperature must be activated and accelerated by adding an effective catalyst. In this study, we synthesize Co nanoparticles supported on bagasse-derived porous carbon (Co@xPC) for catalytic hydrolytic dehydrogenation of NaBH4. According to the experimental results, Co nanoparticles with uniform particle size and high dispersion are successfully supported on porous carbon to achieve a Co@150PC catalyst. It exhibits particularly high activity of hydrogen generation with the optimal hydrogen production rate of 11086.4 mLH2∙min-1∙gCo-1 and low activation energy (Ea) of 31.25 kJ mol-1. The calculation results based on density functional theory (DFT) indicate that the Co@xPC structure is conducive to the dissociation of [BH4]-, which effectively enhances the hydrolysis efficiency of NaBH4. Moreover, Co@150PC presents an excellent durability, retaining 72.0% of the initial catalyst activity after 15 cycling tests. Moreover, we also explored the degradation mechanism of catalyst performance.

| S-EPMC8708045 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data