Effect of Crystallization Modes in TIPS-pentacene/Insulating Polymer Blends on the Gas Sensing Properties of Organic Field-Effect Transistors.

ABSTRACT: Blending organic semiconductors with insulating polymers has been known to be an effective way to overcome the disadvantages of single-component organic semiconductors for high-performance organic field-effect transistors (OFETs). We show that when a solution processable organic semiconductor (6,13-bis(triisopropylsilylethynyl)pentacene, TIPS-pentacene) is blended with an insulating polymer (PS), morphological and structural characteristics of the blend films could be significantly influenced by the processing conditions like the spin coating time. Although vertical phase-separated structures (TIPS-pentacene-top/PS-bottom) were formed on the substrate regardless of the spin coating time, the spin time governed the growth mode of the TIPS-pentacene molecules that phase-separated and crystallized on the insulating polymer. Excess residual solvent in samples spun for a short duration induces a convective flow in the drying droplet, thereby leading to one-dimensional (1D) growth mode of TIPS-pentacene crystals. In contrast, after an appropriate spin-coating time, an optimum amount of the residual solvent in the film led to two-dimensional (2D) growth mode of TIPS-pentacene crystals. The 2D spherulites of TIPS-pentacene are extremely advantageous for improving the field-effect mobility of FETs compared to needle-like 1D structures, because of the high surface coverage of crystals with a unique continuous film structure. In addition, the porous structure observed in the 2D crystalline film allows gas molecules to easily penetrate into the channel region, thereby improving the gas sensing properties.

SUBMITTER: Lee JH

PROVIDER: S-EPMC6328639 | biostudies-literature | 2019 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Inkjet-Printed Organic Transistors Based on Organic Semiconductor/Insulating Polymer Blends.

Project description:Recent advances in inkjet-printed organic field-effect transistors (OFETs) based on organic semiconductor/insulating polymer blends are reviewed in this article. Organic semiconductor/insulating polymer blends are attractive ink candidates for enhancing the jetting properties, inducing uniform film morphologies, and/or controlling crystallization behaviors of organic semiconductors. Representative studies using soluble acene/insulating polymer blends as an inkjet-printed active layer in OFETs are introduced with special attention paid to the phase separation characteristics of such blended films. In addition, inkjet-printed semiconducting/insulating polymer blends for fabricating high performance printed OFETs are reviewed.

| S-EPMC5509261 | biostudies-other

Compatibilized Immiscible Polymer Blends for Gas Separations.

Project description:Membrane-based gas separation has attracted a great deal of attention recently due to the requirement for high purity gasses in industrial applications like fuel cells, and because of environment concerns, such as global warming. The current methods of cryogenic distillation and pressure swing adsorption are energy intensive and costly. Therefore, polymer membranes have emerged as a less energy intensive and cost effective candidate to separate gas mixtures. However, the use of polymeric membranes has a drawback known as the permeability-selectivity tradeoff. Many approaches have been used to overcome this limitation including the use of polymer blends. Polymer blending technology synergistically combines the favorable properties of different polymers like high gas permeability and high selectivity, which are difficult to attain with a single polymer. During polymer mixing, polymers tend to uncontrollably phase separate due to unfavorable thermodynamics, which limits the number of completely miscible polymer combinations for gas separations. Therefore, compatibilizers are used to control the phase separation and to obtain stable membrane morphologies, while improving the mechanical properties. In this review, we focus on immiscible polymer blends and the use of compatibilizers for gas separation applications.

| S-EPMC5509093 | biostudies-literature

Engineered molecular stacking crystallinity of bar-coated TIPS-pentacene/polystyrene films for organic thin-film transistors.

Project description:Solution-based blended polymer materials are promising for electronic applications in many fields. However, determining a controllable method to achieve electronically active organic films through the practical liquid deposition process is very challenging. In this study, we suggest employing hybrid binary organic mixture inks (an insulating polymer polystyrene (PS)) and an organic semiconductor (6,13-bis(triisopropylsilylethnyl)pentacene (TIPS-pentacene)) to manage and enhance the characteristics of TIPS-pentacene organic layers using a bar-coating method. Binary mixtures with PS molecules can provide various microstructures, crystal orientations, and molecular stacking of the active TIPS-pentacene organic layers under the proper fabrication parameters during bar-coating. Varying the molecular weight of the PS mixture, weight percentage of the TIPS-pentacene, and deposition parameters, such as the bar-coating speed, direction, and contact angles between the crystal orientation of TIPS-pentacene and Au electrodes, is crucial to guarantee high-electronic properties. The electrodes with TIPS-pentacene/PS (MW = 4000) binary films at a 40 wt% TIPS-pentacene ratio demonstrate the outstanding room-temperature field-effect mobility of 1.215 cm2 V-1 s-1, four times higher than that of pure TIPS-pentacene transistors (100 wt%). The performance improvement of the TIPS-pentacene layers is highly attributed to the ideal spherulite structure and thick molecular stacking properties, which can guarantee favorable charge transport paths through organic films. These findings demonstrate a promising strategy for blending organic applications to improve the performance of organic electronic devices using practical fabrication processes.

| S-EPMC9846947 | biostudies-literature

Singlet Heterofission in Tetracene-Pentacene Thin-Film Blends.

Project description:Heterofission is a photophysical process of fundamental and applied interest whereby an excited singlet state is converted into two triplets on chemically distinct chromophores. The potential of this process lies in the tuning of both the optical band gap and the splitting between singlet and triplet energies. Herein, we report the time-domain observation of heterofission in mixed thin films of the prototypical singlet fission chromophores pentacene and tetracene using excitation wavelengths above and below the tetracene band gap. We found a time constant of 26 ps for endothermic heterofission of a singlet exciton on pentacene in blends with low pentacene fractions, which was outcompeted by pentacene homofission for increasing pentacene concentrations. Direct excitation of tetracene lead to fast energy transfer to pentacene and subsequent singlet fission, which prevented homo- or heterofission of a singlet exciton on tetracene.

| S-EPMC7820980 | biostudies-literature

Reversible Plastic Deformation of Polymer Blends as a Means to Achieve Stretchable Organic Transistors.

Project description:Intrinsically stretchable semiconductors will facilitate the realization of seamlessly integrated stretchable electronics. However, to date demonstrations of intrinsically stretchable semiconductors have been limited. In this study, a new approach to achieve intrinsically stretchable semiconductors is introduced by blending a rigid high-performance donor-acceptor polymer semiconductor poly[4(4,4dihexadecyl4Hcyclopenta [1,2b:5,4b' ] dithiopen2yl) alt [1,2,5] thiadiazolo [3,4c] pyridine] (PCDTPT) with a ductile polymer semiconductor poly(3hexylthiophene) (P3HT). Under large tensile strains of up to 75%, the polymers are shown to orient in the direction of strain, and when the strain is reduced, the polymers reversibly deform. During cyclic strain, the local packing order of the polymers is shown to be remarkably stable. The saturated field effect charge mobility is shown to be consistently above 0.04 cm2 V-1s-1 for up to 100 strain cycles with strain ranging from 10% to 75% when the film is printed onto a rigid test bed. At the 75% strain state, the charge mobility is consistently above 0.15 cm2 V-1s-1. Ultimately, the polymer blend process introduced here results in an excellent combination of device performance and stretchability providing an effective approach to achieve intrinsically stretchable semiconductors.

| S-EPMC5497511 | biostudies-literature

Wettability Control of Interfaces for High-Performance Organic Thin-Film Transistors by Soluble Insulating Polymer Films.

Project description:Organic small-molecule semiconductors have higher carrier mobility compared to polymer semiconductors, while the actual performances of these materials are susceptible to morphological defects and misalignment of crystalline grains. Here, a new strategy is explored to control the crystallization and morphologies of a solution-processed organic small-molecule semiconductor 2,7-dioctyl[1]benzothieno[3,2-b][1]benzothiophene (C8-BTBT) using soluble polymer films to control the wettability of substrates. Different from the traditional surface modification method, the polymer layer as a modification layer is soluble in the semiconductor solution during the fabrication of organic thin-film transistors (OTFTs). The dissolved polymer alters the state of the semiconductor solution, which in turn, changes the crystallographic morphologies of the semiconductor films. By controlling the solubility and thickness of the polymer modification layers, it is possible to regulate the grain boundary and domain size of C8-BTBT films, which determine the performances of OTFTs. The bottom-gate transistors modified by a thick PS layer exhibit a mobility of >7 cm2/V·s and an on/off ratio of >107. It is expected that this new modification method will be applicable to high-performance OTFTs based on other small molecular semiconductors and dielectrics.

| S-EPMC7241009 | biostudies-literature

Touching polymer chains by organic field-effect transistors.

Project description:Organic field-effect transistors (OFETs) are used to directly "touch" the movement and dynamics of polymer chains, and then determine Tg. As a molecular-level probe, the conducting channel of OFETs exhibits several unique advantages: 1) it directly detects the motion and dynamics of polymer chain at Tg; 2) it allows the measurement of size effects in ultrathin polymer films (even down to 6 nm), which bridges the gap in understanding effects between surface and interface. This facile and reliable determination of Tg of polymer films and the understanding of polymer chain dynamics guide a new prospect for OFETs besides their applications in organic electronics and casting new light on the fundamental understanding of the nature of polymer chain dynamics.

| S-EPMC4165941 | biostudies-literature

Morphology, Rheology and Crystallization in Relation to the Viscosity Ratio of Polystyrene/Polypropylene Polymer Blends.

Project description:Microfibrillar and droplet morphology of polypropylene (PP) phase dispersed in polypropylene (PS) was fabricated by using melt-extrusion. This morphology was obtained by introducing isotactic PP (20 wt.%) with different viscosity in the PS matrix (80 wt.%). Furthermore, the rheological properties of the blend investigated as a function of the viscosity ratio K. The variations in blend morphology were related to crystallization, melting properties, and viscoelasticity. The blends with K >> 1 develop a fine morphology with PP microfibrils along the flow direction, while diameters of the dispersed PP droplets gradually increase with lower values of K = 1, or K << 1. Crystallinity of the prepared blends significantly decreases compared to neat PP, while the microfibrillar morphology induces homogeneous crystallization with small crystallites. This is reflected in a decrease of the crystallization temperature, small loss in the crystallinity, and lower melting temperature of the PS80/PP20 blend compared to neat PP. The storage moduli, loss moduli, and complex viscosity are highest for the microfibrillar morphology that presents retarded relaxation. The rheological properties are dominated by the dispersed phase (K > 1), or matrix (K < 1). The variation in blend properties with microfibrillar morphology can be clearly distinguished from heterogeneous blends containing PP droplets, providing an efficient tool to create a binary blend with unique properties.

| S-EPMC7078875 | biostudies-literature

Direct-written polymer field-effect transistors operating at 20 MHz.

Project description:Printed polymer electronics has held for long the promise of revolutionizing technology by delivering distributed, flexible, lightweight and cost-effective applications for wearables, healthcare, diagnostic, automation and portable devices. While impressive progresses have been registered in terms of organic semiconductors mobility, field-effect transistors (FETs), the basic building block of any circuit, are still showing limited speed of operation, thus limiting their real applicability. So far, attempts with organic FETs to achieve the tens of MHz regime, a threshold for many applications comprising the driving of high resolution displays, have relied on the adoption of sophisticated lithographic techniques and/or complex architectures, undermining the whole concept. In this work we demonstrate polymer FETs which can operate up to 20 MHz and are fabricated by means only of scalable printing techniques and direct-writing methods with a completely mask-less procedure. This is achieved by combining a fs-laser process for the sintering of high resolution metal electrodes, thus easily achieving micron-scale channels with reduced parasitism down to 0.19 pF mm-1, and a large area coating technique of a high mobility polymer semiconductor, according to a simple and scalable process flow.

| S-EPMC5150525 | biostudies-literature

Interface Energy Alignment between Lead Halide Perovskite Single Crystals and TIPS-Pentacene.

Project description:At present, there is a huge development in optoelectronic applications using lead halide perovskites. Considering that device performance is largely governed by the transport of charges across interfaces and, therefore, the interfacial electronic structure, fundamental investigations of perovskite interfaces are highly necessary. In this study, we use high-resolution soft X-ray photoelectron spectroscopy based on synchrotron radiation to explore the interfacial energetics for the molecular layer of TIPS-pentacene and lead halide perovskite single crystals. We perform ultrahigh vacuum studies on multiple thicknesses of an in situ formed interface of TIPS-pentacene with four different in situ cleaved perovskite single crystals (MAPbI3, MAPbBr3, FAPbBr3, and CsxFA1-xPbBryI3-y). Our findings reveal a substantial shift of the TIPS-pentacene energy levels toward higher binding energies with increasing thickness, while the perovskite energy levels remain largely unaffected regardless of their composition. These shifts can be interpreted as band bending in the TIPS-pentacene, and such effects should be considered when assessing the energy alignment at perovskite/organic transport material interfaces. Furthermore, we were able to follow a reorganization on the MAPbI3 surface with the transformation of the surface C 1s into bulk C 1s.

| S-EPMC10523438 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data