Bone-Healing Pattern on the Surface of Titanium Implants at Cortical and Marrow Compartments in Two Topographic Sites: an Experimental Study in Rabbits.

ABSTRACT: This study evaluates the bone-healing patterns on the surface of titanium implants at the cortical and marrow compartments of bicortically-installed implants in the diaphysis and metaphysis of rabbit tibiae. In 27 New Zealand rabbits, two implants, one for each macro-design and with equal resorbable blasted media (RBM) implant surfaces, were randomly implanted in the diaphysis or metaphysis of each tibia. The flaps were sutured to allow submerged healing. The animals were sacrificed after two, four, or eight weeks, with nine weeks used for the period of healing. Ground sections were prepared and analyzed. No statistically significant differences were found between the two groups for newly formed bone in contact with the implant surface after two, four, and eight weeks of healing. Bone apposition in the marrow compartment was slightly higher in the diaphysis compared to metaphysis regions across healing stages. Despite the limitations of the present study, it can be concluded that new bone apposition was better than average in the cortical compartment as compared to the marrow compartments. Bone morphometry and density may affect bone apposition onto the implant surface. The apposition rates were slightly better at both the cortical and marrow compartments in diaphysis as compared to metaphysis sites. The new bone formation at the marrow compartment showed slightly better increasing values at diaphysis compared to metaphysis implantation sites.

SUBMITTER: Soto-Penaloza D

PROVIDER: S-EPMC6337604 | biostudies-literature | 2018 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Bone-Healing Pattern on the Surface of Titanium Implants at Cortical and Marrow Compartments in Two Topographic Sites: an Experimental Study in Rabbits.

Soto-Peñaloza David D Caneva Marco M Viña-Almunia José J Martín-de-Llano José Javier JJ Peñarrocha-Oltra David D Peñarrocha-Diago Miguel M Peñarrocha-Diago Miguel M

Materials (Basel, Switzerland) 20181227 1

This study evaluates the bone-healing patterns on the surface of titanium implants at the cortical and marrow compartments of bicortically-installed implants in the diaphysis and metaphysis of rabbit tibiae. In 27 New Zealand rabbits, two implants, one for each macro-design and with equal resorbable blasted media (RBM) implant surfaces, were randomly implanted in the diaphysis or metaphysis of each tibia. The flaps were sutured to allow submerged healing. The animals were sacrificed after two, f ...[more]

PMID: 30591652

Similar Datasets

Project description:Orthopedic implant failure due to aseptic loosening and mechanical instability remains a major problem in total joint replacement. Improving osseointegration at the bone-implant interface may reduce micromotion and loosening. Bone sialoprotein (BSP) has been shown to enhance bone formation when coated onto titanium femoral implants and in rat calvarial defect models. However, the most appropriate method of BSP coating, the necessary level of BSP coating, and the effect of BSP coating on cell behavior remain largely unknown. In this study, BSP was covalently coupled to titanium surfaces via an aminosilane linker (APTES), and its properties were compared to BSP applied to titanium via physisorption and untreated titanium. Cell functions were examined using primary human osteoblasts (hOBs) and L929 mouse fibroblasts. Gene expression of specific bone turnover markers at the RNA level was detected at different intervals. Cell adhesion to titanium surfaces treated with BSP via physisorption was not significantly different from that of untreated titanium at any time point, whereas BSP application via covalent coupling caused reduced cell adhesion during the first few hours in culture. Cell migration was increased on titanium disks that were treated with higher concentrations of BSP solution, independent of the coating method. During the early phases of hOB proliferation, a suppressive effect of BSP was observed independent of its concentration, particularly when BSP was applied to the titanium surface via physisorption. Although alkaline phosphatase activity was reduced in the BSP-coated titanium groups after 4 days in culture, increased calcium deposition was observed after 21 days. In particular, the gene expression level of RUNX2 was upregulated by BSP. The increase in calcium deposition and the stimulation of cell differentiation induced by BSP highlight its potential as a surface modifier that could enhance the osseointegration of orthopedic implants. Both physisorption and covalent coupling of BSP are similarly effective, feasible methods, although a higher BSP concentration is recommended.

Dataset Information

Bone-Healing Pattern on the Surface of Titanium Implants at Cortical and Marrow Compartments in Two Topographic Sites: an Experimental Study in Rabbits.

Publications

Bone-Healing Pattern on the Surface of Titanium Implants at Cortical and Marrow Compartments in Two Topographic Sites: an Experimental Study in Rabbits.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure