Physicochemical, cytotoxicity and in vivo biocompatibility of a high-plasticity calcium-silicate based material.

ABSTRACT: The purpose of this work was to evaluate the physicochemical properties, the cytotoxicity and in vivo biocompatibility of MTA Repair HP (MTA HP) and White MTA (WMTA). The setting time, flow, radiopacity and water solubility were assessed. To the cytotoxicity assay, primary human osteoblast cells were exposed to several dilutions of both materials eluates. MTT assay, apoptosis assay and cell adhesion assay were performed. The in vivo biocompatibility was evaluated through histological analysis using different staining techniques. No differences were observed between MTA HP and WMTA for setting time, radiopacity, solubility and water absorption (P?>?0.05). However, MTA HP showed a significantly higher flow when compared to WMTA (P?

SUBMITTER: Ferreira CMA

PROVIDER: S-EPMC6408552 | biostudies-literature | 2019 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Physicochemical, cytotoxicity and in vivo biocompatibility of a high-plasticity calcium-silicate based material.

Ferreira Cláudio M A CMA Sassone Luciana M LM Gonçalves Alexia S AS de Carvalho Jorge José JJ Tomás-Catalá Christopher J CJ García-Bernal David D Oñate-Sánchez Ricardo E RE Rodríguez-Lozano Francisco J FJ Silva Emmanuel João Nogueira Leal EJNL

Scientific reports 20190308 1

The purpose of this work was to evaluate the physicochemical properties, the cytotoxicity and in vivo biocompatibility of MTA Repair HP (MTA HP) and White MTA (WMTA). The setting time, flow, radiopacity and water solubility were assessed. To the cytotoxicity assay, primary human osteoblast cells were exposed to several dilutions of both materials eluates. MTT assay, apoptosis assay and cell adhesion assay were performed. The in vivo biocompatibility was evaluated through histological analysis us ...[more]

PMID: 30850648

Similar Datasets

Project description:ObjectiveThis study evaluated the bioactivity and physicochemical properties of three commercial calcium silicate-based endodontic materials (MTA, EndoSequence Root Repair Material putty, and Biodentine™). Material and Methods. Horizontal sections of 3 mm thickness from 18 root canals of human teeth were subjected to biomechanical preparation with WaveOne Gold large rotary instruments. The twelve specimens were filled with three tested materials (MM-MTA, EndoSequence Root Repair Material putty, and Biodentine™) and immersed in phosphate-buffered saline for 7 and 30 days. After this period of time, each specimen of each material was processed for morphological observation, surface precipitates, and interfacial dentin using SEM. In addition, the surface morphology of the set materials, without soaking in phosphate-buffered solution after one day and after 28 days stored in phosphate-buffered saline, was evaluated using SEM; also, the pH of the soaking water and the amount of calcium ions released from the test materials were measured by using an inductively coupled plasma-optical emission spectroscopy test. Data obtained were analyzed using one-way analysis of variance and Tukey's honest significant difference test with a significance level of 5%.ResultThe formation of precipitates was observed on the surfaces of all materials at 1 week and increased substantially over time. Interfacial layers in some areas of the dentin-cement interface were found from one week of immersion. All the analyzed materials showed alkaline pH and capacity to release calcium ions; however, the concentrations of released calcium ions were significantly more in Biodentine and ESRRM putty than MM-MTA (P < 0.05). ESRRM putty maintained a pH of around 11 after 28 days.ConclusionCompared with MM-MTA, Biodentine and ESRRM putty showed significantly more calcium ion release. However, exposure of three tested cements to phosphate-buffered solution resulted in precipitation of apatite crystalline structures over both cement and dentin that increased over time. This suggests that the tested materials are bioactive.

Project description:The purpose of this study was to compare the cytotoxic effects and mineralization activity of three calcium silicate-based root canal sealers to those of a conventional resin-based sealer. Experiments were performed using human dental pulp stem cells grown in a monolayer culture. The root canal sealers tested in this study were EndoSequence BC Sealer (Brasseler), BioRoot RCS (Septodont), Endoseal MTA (Maruchi), and AH Plus (Dentsply DeTrey). Experimental disks 6 mm in diameter and 3 mm in height were made and stored in a 100% humidity chamber at 37 °C for 72 h to achieve setting. The cytotoxicity of various root canal sealers was evaluated using a methyl-thiazoldiphenyl-tetrazolium (MTT) assay. To evaluate cell migration ability, a scratch wound healing method was used, and images of the scratch area were taken using a phase-contrast microscope. Cell morphology was evaluated by a scanning electron microscope after direct exposure for 72 h to each sealer disk. In the cell viability assay, there were no significant differences between the EndoSequence BC, BioRoot RCS, Endoseal MTA, and control groups in any experimental period (p > 0.05). In the cell migration assay, there were no significant differences between the EndoSequence BC, Endoseal MTA, and control groups in any experimental period (p > 0.05). BioRoot RCS exhibited slower cell migration relative to EndoSequence BC and Endoseal MTA for up to 72 h (p < 0.05). Conversely, it showed a similar wound healing percentage at 96 h (p > 0.05). In an evaluation of cell morphology, cells in direct contact with EndoSequence BC, BioRoot RCS, and Endoseal MTA disks showed superior spreading compared to those in contact with the AH Plus disk. In an Alizarin red staining assay, EndoSequence BC, BioRoot RCS, and Endoseal MTA showed a significant increase in mineralized nodule formation compared to the AH Plus group (p < 0.05). In conclusion, all calcium silicate-based root canal sealers tested in this study showed good biological properties and mineralization activity compared to conventional resin-based sealer.

Dataset Information

Physicochemical, cytotoxicity and in vivo biocompatibility of a high-plasticity calcium-silicate based material.

Publications

Physicochemical, cytotoxicity and in vivo biocompatibility of a high-plasticity calcium-silicate based material.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets