Physicochemical Properties, Cytocompatibility, and Biocompatibility of a Bioactive Glass Based Retrograde Filling Material.
Ontology highlight
ABSTRACT:
SUBMITTER: Murata K
PROVIDER: S-EPMC8308453 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:The purpose of this work was to evaluate the physicochemical properties, the cytotoxicity and in vivo biocompatibility of MTA Repair HP (MTA HP) and White MTA (WMTA). The setting time, flow, radiopacity and water solubility were assessed. To the cytotoxicity assay, primary human osteoblast cells were exposed to several dilutions of both materials eluates. MTT assay, apoptosis assay and cell adhesion assay were performed. The in vivo biocompatibility was evaluated through histological analysis using different staining techniques. No differences were observed between MTA HP and WMTA for setting time, radiopacity, solubility and water absorption (P > 0.05). However, MTA HP showed a significantly higher flow when compared to WMTA (P < 0.05). Cell viability results revealed that the extracts of WMTA and MTA HP promoted the viability of osteoblasts. After incubation of cells with the endodontic cement extracts, the percentage of apoptotic or necrotic cells was very low (<3%). Furthermore, SEM results showed a high degree of cell proliferation and adhesion on both groups. MTA HP showed similar in vivo biocompatibility to the WMTA and the control group in all time-points. The MTA HP presented adequate physicochemical and biological properties with improved flow ability when compared to WMTA. Such improved flow ability may be a result of the addition of a plasticizing agent and should be related to an improvement in the handling of MTA HP.
| S-EPMC6408552 | biostudies-literature
Project description:Radio-opacity is an essential attribute of ideal root-end filling materials because it is important for clinicians to observe root canal filling and to facilitate the follow-up instructions. The novel root-end filling material (NRFM) has good cytocompatibility and physicochemical properties but low intrinsic radio-opacity value. To improve its radio-opacity value, three novel radio-opaque root-end filling materials (NRRFMs) were developed by adding barium sulphate (NRFM-Ba), bismuth trioxide (NRFM-Bi) and zirconium dioxide (NRFM-Zr) to NRFM, respectively. The purpose of this study was to identify the suitable radio-opacifier for NRFM through evaluating their physicochemical and biological properties, in comparison with NRFM and glass ionomer cement (GIC).NRRFMs were characterized using X-ray diffraction (XRD) and Fourier transform infrared spectrophotometry (FTIR). Physicochemical properties including setting time, compressive strength, porosity, pH variation, solubility, washout resistance, contact angle and radiopacity were investigated. Cytocompatibility of both freshly mixed and set NRRFMs was investigated by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. Alkaline phosphatase (ALP) activity assay and alizarin red staining were used to investigate the osteogenic differentiation potential of NRFM-Zr. Data were analyzed using two-way ANOVA (pH variation, solubility and ALP activity) and one-way ANOVA (for the other variables).(1) NRRFMs were primarily composed of hydroxyapatite, calcium carboxylate salt and the corresponding radio-opacity agents (barium sulphate, bismuth trioxide or zirconium dioxide). (2) Besides similar physicochemical properties in terms of setting time, pH variation, solubility, washout resistance and contact angle to NRFM, NRFM-Bi and NRFM-Zr exhibited lower porosity and greater compressive strength after being set for 7 days and their radio-opacity were greater than the 3 mm aluminium thickness specified in ISO 6876 (2001). (3) MTT assay revealed that freshly mixed and set NRFM-Zr presented better cell viability than NRFM-Ba and NRFM-Bi at 24 hours and 48 hours (P<0.05). (4) NRFM-Zr significantly enhanced ALP activity and calcium formation of human osteoblast-like Saos-2 cells when compared with negative group and GIC (P<0.05).NRFM-Zr presents desirable physicochemical and biological properties, thus zirconium dioxide may be a suitable radio-opacifier for NRFM.
| S-EPMC5805173 | biostudies-literature
Project description:A lot of nanomaterials have been applied to various nano-biotechnological fields, such as contrast agents, drug or gene delivery systems, cosmetics, and so on. Despite the expanding usage of nanomaterials, concerns persist regarding their potential toxicity. To address this issue, many scientists have tried to develop biocompatible nanomaterials containing phytochemicals as a promising solution. In this study, we synthesized biocompatible nanomaterials by using gallic acid (GA), which is a phytochemical, and coating it onto the surface of iron oxide nanoparticles (IONPs). Importantly, the GA-modified iron oxide nanoparticles (GA-IONPs) were successfully prepared through environmentally friendly methods, avoiding the use of harmful reagents and extreme conditions. The presence of GA on the surface of IONPs improved their stability and bioactive properties. In addition, cell viability assays proved that GA-IONPs possessed excellent biocompatibility in human dermal papilla cells (HDPCs). Additionally, GA-IONPs showed antioxidant activity, which reduced intracellular reactive oxygen species (ROS) levels in an oxidative stress model induced by hydrogen peroxide (H2O2). To investigate the impact of GA-IONPs on exosome secretions from oxidative stress-induced cells, we analyzed the number and characteristics of exosomes in the culture media of HDPCs after H2O2 stimulation or GA-IONP treatment. Our analysis revealed that both the number and proportions of tetraspanins (CD9, CD81, and CD63) in exosomes were similar in the control group and the GA-IONP-treated groups. In contrast, exosome secretion was increased, and the proportion of tetraspanin was changed in the H2O2-treated group compared to the control group. It demonstrated that treatment with GA-IONPs effectively attenuated exosome secretion induced by H2O2-induced oxidative stress. Therefore, this GA-IONP exhibited outstanding promise for applications in the field of nanobiotechnology.
| S-EPMC10649306 | biostudies-literature
Project description:Implant-associated infections and non-absorbing materials are two important reasons for a second surgical procedure to remove internal fixation devices after an orthopedic internal fixation surgery. The objective of this study was to produce an antibacterial and absorbable fixation screw by adding gentamicin to silk-based materials. The antibacterial activity was assessed against Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) in vitro by plate cultivation and scanning electron microscopy (SEM). We also investigated the properties, such as the mechanical features, swelling properties, biocompatibility and degradation, of gentamicin-loaded silk-based screws (GSS) in vitro. The GSS showed significant bactericidal effects against S. aureus and E. coli. The antibacterial activity remained high even after 4 weeks of immersion in protease solution. In addition, the GSS maintained the remarkable mechanical properties and excellent biocompatibility of pure silk-based screws (PSS). Interestingly, after gentamicin incorporation, the degradation rate and water-absorbing capacity increased and decreased, respectively. These GSS provide both impressive material properties and antibacterial activity and have great potential for use in orthopedic implants to reduce the incidence of second surgeries.
| S-EPMC5116670 | biostudies-literature
Project description:BackgroundAlthough several materials have been used for retrograde filling following apical surgeries, there is no consensus on a single best material. Tricalcium silicate-based types of cement have been developed as root-end filling materials mainly due to tricalcium silicate's hydraulic properties. However, its unfavorable setting characteristics and minimal antimicrobial properties have necessitated the introduction of new additives into the existing commercially available materials. To design an affordable product based on a dicalcium silicate with a shorter set time, minimal cytotoxic complications, and enhanced antibacterial activity, we developed a new endodontic cement from pure raw materials, intending to satisfy the prerequisites of ideal retrograde material.MethodsThe composition of the experimental calcium silicate-based cement included the addition of calcium chloride and silver nanoparticles in varying concentrations. Structural characterization was carried out using energy dispersive analysis by X-rays using scanning electron microscope (EDAX SEM) and hydration characteristics were performed using an X-ray diffractometer (XRD). The experimental material was further evaluated for biocompatibility using MTT ([3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyl-2H-tetrazolium bromide)assay and antibacterial activity was evaluated using an agar diffusion test against Enterococcus faecalis.ResultsThe structural characterization and hydration characteristics revealed that the experimental cement was dicalcium silicate based with favorable biocompatibility and enhanced antibacterial activity. Tricalcium silicate based mineral trioxide aggregate (MTA) also had favourable biocompatibility, however, its antibacterial activity was significantly decreased when compared to the novel cement.ConclusionAll hydraulic cements that are available in the dental market are predominantly tricalcium silicate-based materials. There has been no evidence in the literature to date wherein it has been explored whether a dicalcium silicate-based hydraulic cement can solely be used in root-end cavities. The findings of the study revealed a dicalcium silicate based retrograde filling material with favourable biocompatibility exhibited immediately as well as in the set samples. Incorporation of silver nanoparticles boosted the antibacterial activity when compared to that of ProRoot MTA. This material could potentially reinstate the usual hype created with tricalcium silicate types of cement since dicalcium silicate cements also exhibit similar properties.
| S-EPMC9899052 | biostudies-literature
Project description:The development of innovative materials for bone tissue engineering to promote bone regeneration while avoiding fibrous tissue infiltration is of paramount importance. Here, we combined the known osteopromotive properties of bioactive glasses (BaGs) with the biodegradability, biocompatibility, and ease to shape/handle of poly-l-co-d,l-lactic acid (PLDLA) into a single biphasic material. The aim of this work was to unravel the role of the surface chemistry and topography of BaG surfaces on the stability of a PLDLA honeycomb membrane, in dry and wet conditions. The PLDLA honeycomb membrane was deposited using the breath figure method (BFM) on the surface of untreated BaG discs (S53P4 and 13-93B20), silanized with 3-aminopropyltriethoxysilane (APTES) or conditioned (immersed for 24 h in TRIS buffer solution). The PLDLA membranes deposited onto the BaG discs, regardless of their composition or surface treatments, exhibited a honeycomb-like structure with pore diameter ranging from 1 to 5 μm. The presence of positively charged amine groups (APTES grafting) or the precipitation of a CaP layer (conditioned) significantly improved the membrane resistance to shear as well as its stability upon immersion in the TRIS buffer solution. The obtained results demonstrated that the careful control of the substrate surface chemistry enabled the deposition of a stable honeycomb membrane at their surface. This constitutes a first step toward the development of new biphasic materials enabling osteostimulation (BaG) while preventing migration of fibrous tissue inside the bone defect (honeycomb polymer membrane).
| S-EPMC8289249 | biostudies-literature
Project description:Graphene, an allotrope of carbon, consists of a single layer of carbon atoms with uniquely tuneable properties. As such, graphene-based materials (GBMs) have gained interest for tissue engineering applications. GBMs are often discussed in the context of how different physicochemical properties affect cell physiology, without explicitly considering the impact of adsorbed proteins. Establishing a relationship between graphene properties, adsorbed proteins, and cell response is necessary as these proteins provide the surface upon which cells attach and grow. This review highlights the molecular adsorption of proteins on different GBMs, protein structural changes, and the connection to cellular function.
| S-EPMC9814659 | biostudies-literature
Project description:To prepare nanocomposite cements based on the incorporation of bioactive glass nanoparticles (nBGs) into BiodentineTM (BD, Septodent, Saint-Maur-des-Fosses Cedex, France) and to assess their bioactive properties.nBGs were synthesised by the sol-gel method. BD nanocomposites (nBG/BD) were prepared with 1 and 2% nBGs by weight; unmodified BD and GC Fuji IX (GIC, GC Corporation, Tokyo, Japan) were used as references. The in vitro ability of the materials to induce apatite formation was assessed in SBF by X-ray diffraction (XRD), attenuated total reflectance with Fourier transform infrared spectroscopy (ATR-FTIR), and scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analysis. BD and nBG/BD were also applied to dentine discs for seven days; the morphology and elemental composition of the dentine-cement interface were analysed using SEM-EDX.One and two percent nBG/BD composites accelerated apatite formation on the disc surface after short-term immersion in SBF. Apatite was detected on the nBG/BD nanocomposites after three days, compared with seven days for unmodified BD. No apatite formation was detected on the GIC surface. nBG/BD formed a wider interfacial area with dentine than BD, showing blockage of dentine tubules and Si incorporation, suggesting intratubular precipitation.The incorporation of nBGs into BD improves its in vitro bioactivity, accelerating the formation of a crystalline apatite layer on its surface after immersion in SBF. Compared with unmodified BD, nBG/BD showed a wider interfacial area with greater Si incorporation and intratubular precipitation of deposits when immersed in SBF.
| S-EPMC5393538 | biostudies-other
Project description:Objective:To compare the elastic modulus, flexural strength, and hardness of an experimental resin based composite (RBC) with and without containing silver nanoparticles (AgNPs) and bioactive glass (BAG) with a commercially available RBC. Methods:This study was conducted, during the period August 2016-May 2018, at the Department of Dental Materials, Peshawar Dental College, Peshawar (Pakistan) and Department of Chemistry, University of Montreal, Canada. Test specimens made in the commercial RBC acted as Group-1 (G1). An experimental RBC containing 70 wt % filler content was synthesized. It was first used as such to prepare test specimens to act as the experimental control group (G2). This RBC was then modified by adding various amounts of BAG (5%, 10% and 15%) and a fixed amount of 0.009% AgNPs to use the so modified RBCs for preparing the test specimens to belong to three groups (G3, G4 & G5). The AgNPs had been synthesized in situ by reduction of salt during photo-polymerization. Flexural strength (FS), elastic modulus (EM) and Vickers hardness were determined using universal testing machine and hardness tester respectively. Data were analyzed using one-way ANOVA and Tukey post-hoc test. Results:Except for G3 restorations showing significantly lower mean FS value, the FS for those in the other groups were not significantly different (p>0.05). Elastic modulus of the experimental RBC restorations was though higher than those of the others but the difference was statistically insignificant (p>0.05). Reduced Vickers hardness values were documented for the restorations in the G4 and G5 compared to those in the G3 but again the difference was insignificant (p>0.05). Flexural strength and hardness values of the test specimens in the experimental RBCs were significantly lower than those made in the commercial hybrid RBC (p<0.05). Conclusion:BAG and AgNPs addition to the experimental RBC in the mentioned concentration adversely affected the tested mechanical properties.
| S-EPMC7260929 | biostudies-literature
Project description:Compared to other materials such as 45S5 bioactive glass (BG), ?-tricalcium phosphate (?-TCP)-based bone substitutes such as Vitoss show limited material-driven stimulation of osteogenesis and/or angiogenesis. The unfavorable degradation kinetics of ?-TCP-based bone substitutes may result in an imbalance between resorption and osseous regeneration. Composite materials like Vitoss BA (Vitoss supplemented with 20 wt % 45S5-BG particles) might help to overcome these limitations. However, the influence of BG particles in Vitoss BA compared to unsupplemented Vitoss on osteogenesis, resorption behavior, and angiogenesis is not yet described. In this study, Vitoss and Vitoss BA scaffolds were seeded with human mesenchymal stromal cells before subcutaneous implantation in immunodeficient mice for 10 weeks. Scaffold resorption was monitored by micro-computed tomography, while osteoid formation and vascularization were assessed by histomorphometry and gene expression analysis. Whilst slightly more osteoid and improved angiogenesis were found in Vitoss BA, maturation of the osteoid was more advanced in Vitoss scaffolds. The volume of Vitoss implants decreased significantly, combined with a significantly increased presence of resorbing cells, whilst the volume remained stable in Vitoss BA scaffolds. Future studies should evaluate the interaction of 45S5-BG with resorbing cells and bone precursor cells in greater detail to improve the understanding and application of ?-TCP/45S5-BG composite bone substitute materials.
| S-EPMC6747147 | biostudies-literature