Sideways and stable crack propagation in a silicone elastomer.

ABSTRACT: We have discovered a peculiar form of fracture that occurs in a highly stretchable silicone elastomer (Smooth-On Ecoflex 00-30). Under certain conditions, cracks propagate in a direction perpendicular to the initial precut and in the direction of the applied load. In other words, the crack deviates from the standard trajectory and instead propagates perpendicular to that trajectory. The crack arrests stably, and thus the material ahead of the crack front continues to sustain load, thereby enabling enormous stretchabilities. We call this phenomenon "sideways" and stable cracking. To explain this behavior, we first perform finite-element simulations that demonstrate a propensity for sideways cracking, even in an isotropic material. The simulations also highlight the importance of crack-tip blunting on the formation of sideways cracks. Next, we provide a hypothesis on the origin of sideways cracking that relates to microstructural anisotropy (in a nominally isotropic elastomer). To substantiate this hypothesis, we transversely prestretch samples to various extents before fracture testing, as to determine the influence of microstructural arrangement (chain alignment and strain-induced crystallization) on fracture energy. We also perform microstructural characterization that indicates that significant chain alignment and strain-induced crystallization indeed occur in this material upon stretching. We conclude by characterizing how a number of loading conditions, such as sample geometry and strain rate, affect this phenomenon. Overall, this paper provides fundamental mechanical insight into basic phenomena associated with fracture of elastomers.

SUBMITTER: Lee S

PROVIDER: S-EPMC6511042 | biostudies-literature | 2019 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Crack propagation in bamboo's hierarchical cellular structure.

Project description:Bamboo, as a natural hierarchical cellular material, exhibits remarkable mechanical properties including excellent flexibility and fracture toughness. As far as bamboo as a functionally graded bio-composite is concerned, the interactions of different constituents (bamboo fibers; parenchyma cells; and vessels.) alongside their corresponding interfacial areas with a developed crack should be of high significance. Here, by using multi-scale mechanical characterizations coupled with advanced environmental electron microscopy (ESEM), we unambiguously show that fibers' interfacial areas along with parenchyma cells' boundaries were preferred routes for crack growth in both radial and longitudinal directions. Irrespective of the honeycomb structure of fibers along with cellular configuration of parenchyma ground, the hollow vessels within bamboo culm affected the crack propagation too, by crack deflection or crack-tip energy dissipation. It is expected that the tortuous crack propagation mode exhibited in the present study could be applicable to other cellular natural materials as well.

| S-EPMC4083283 | biostudies-literature

A thermo-reversible silicone elastomer with remotely controlled self-healing.

Project description:Soft thermoplastic elastomers with increased durability and reliability are in high demand for a broad spectrum of applications. Silicone elastomers are soft and durable, but they are not thermoplastic in nature, and under extreme conditions such as high voltage or large deformations, reliability may also suffer. Thus, as a solution to these shortcomings, which are typical of silicone elastomers, it is natural to propose a thermo-reversible, self-healing, and recyclable silicone-based elastomer. Stimuli-responsivity is imparted to the silicone polymer by incorporating supramolecular 2-ureido-4[1H]-pyrimidone (UPy) self-assembling motifs via free radical polymerisation. Self-healing of the novel elastomer may be triggered by both direct and indirect heating, the latter by means of incorporating Fe3O4 particles into the elastomer and subsequent exposure to an alternating magnetic field. As a consequence of temperature responsiveness and high thermal stability, the elastomer is proven recyclable, by withstanding multiple reprocessing procedures with no substantial effects on the resulting properties. The synergy of these valuable characteristics makes this novel material a smart candidate for innumerable applications where soft and reliable elastomers are sought.

| S-EPMC9078532 | biostudies-literature

Highly Sensitive Flexible Pressure Sensors Enabled by Mixing of Silicone Elastomer With Ionic Liquid-Grafted Silicone Oil.

Project description:Developing highly sensitive flexible pressure sensors has become crucially urgent due to the increased societal demand for wearable electronic devices capable of monitoring various human motions. The sensitivity of such sensors has been shown to be significantly enhanced by increasing the relative dielectric permittivity of the dielectric layers used in device construction via compositing with immiscible ionic conductors. Unfortunately, however, the elastomers employed for this purpose possess inhomogeneous morphologies, and thus suffer from poor long-term durability and unstable electrical response. In this study, we developed a novel, flexible, and highly sensitive pressure sensor using an elastomeric dielectric layer with particularly high permittivity and homogeneity due to the addition of synthesized ionic liquid-grafted silicone oil (denoted LMS-EIL). LMS-EIL possesses both a very high relative dielectric permittivity (9.6 × 105 at 10-1 Hz) and excellent compatibility with silicone elastomers due to the covalently connected structure of conductive ionic liquid (IL) and chloropropyl silicone oil. A silicone elastomer with a relative permittivity of 22 at 10-1 Hz, Young's modulus of 0.78 MPa, and excellent homogeneity was prepared by incorporating 10 phr (parts per hundreds rubber) of LMS-EIL into an elastomer matrix. The sensitivity of the pressure sensor produced using this optimized silicone elastomer was 0.51 kPa-1, which is 100 times higher than that of the pristine elastomer. In addition, a high durability illustrated by 100 loading-unloading cycles and a rapid response and recovery time of approximately 60 ms were achieved. The excellent performance of this novel pressure sensor suggests significant potential for use in human interfaces, soft robotics, and electronic skin applications.

| S-EPMC8488264 | biostudies-literature

Controlled mud-crack patterning and self-organized cracking of polydimethylsiloxane elastomer surfaces.

Project description:Exploiting pattern formation - such as that observed in nature - in the context of micro/nanotechnology could have great benefits if coupled with the traditional top-down lithographic approach. Here, we demonstrate an original and simple method to produce unique, localized and controllable self-organised patterns on elastomeric films. A thin, brittle silica-like crust is formed on the surface of polydimethylsiloxane (PDMS) using oxygen plasma. This crust is subsequently cracked via the deposition of a thin metal film - having residual tensile stress. The density of the mud-crack patterns depends on the plasma dose and on the metal thickness. The mud-crack patterning can be controlled depending on the thickness and shape of the metallization - ultimately leading to regularly spaced cracks and/or metal mesa structures. Such patterning of the cracks indicates a level of self-organization in the structuring and layout of the features - arrived at simply by imposing metallization boundaries in proximity to each other, separated by a distance of the order of the critical dimension of the pattern size apparent in the large surface mud-crack patterns.

| S-EPMC4594096 | biostudies-literature

Numerical simulation study on the crack propagation of conglomerate.

Project description:The conglomerate reservoir is rich in oil and gas reserves; however, the gravel's mechanical properties and laws are difficult to gain through laboratory experiments, which furthermore constrain the hydraulic fracturing design. To analyse the failure law of conglomerate, we simulated the uniaxial compression test based on discrete element software PFC2D and analysed the effect of different cementation strength, gravel content and gravel geometry on the rock deformation and failure characteristics. Results show that (i) as the cementation strength decreases, the compressive strength and elasticity modulus both reduce clearly, while the crack shapes get more complex and the critical value is 0.3; (ii) as the gravel content increases, the conglomerate strength first decreases then increases under the influences of cracks bypassing gravels; cementation strength and gravel content of the conglomerate both contribute to the increase in local additional stress, which leads to a series of changes in crack shapes and mechanical properties of the conglomerate. Based on the above research, the conglomerate strength and crack shapes after failure are relatively complex due to the common influence of cementation strength and gravel content. The gravel edge crack caused by stress concentration is the micro-mechanism that affects the conglomerate mechanical properties.

| S-EPMC8292759 | biostudies-literature

Protein unfolding under force: crack propagation in a network.

Project description:The mechanical unfolding of a set of 12 proteins with diverse topologies is investigated using an all-atom constraint-based model. Proteins are represented as polypeptides cross-linked by hydrogen bonds, salt bridges, and hydrophobic contacts, each modeled as a harmonic inequality constraint capable of supporting a finite load before breaking. Stereochemically acceptable unfolding pathways are generated by minimally overloading the network in an iterative fashion, analogous to crack propagation in solids. By comparing the pathways to those from molecular dynamics simulations and intermediates identified from experiment, it is demonstrated that the dominant unfolding pathways for 9 of the 12 proteins studied are well described by crack propagation in a network.

| S-EPMC3145275 | biostudies-literature

Faster and Greener Chemical Reaction Workup Using Silicone Elastomer-Coated Glass Powders.

Project description:We have developed a substantially faster and greener technique for routine chemical reaction workups. We use silicone elastomer-coated glass powder ("FastWoRX") as an absorbent to extract organic products from a quenched aqueous reaction mixture. After filtration, FastWoRX powder loaded with organic products can serve as a convenient input for flash chromatographic separations. With this technique, tedious and solvent-consuming liquid-liquid extractions are replaced by a simple filtration. Use of FastWoRX reduces solvent use and the E-factor by up to an order of magnitude compared to traditional liquid-liquid extraction-based workup.

| S-EPMC6644892 | biostudies-literature

Crack initiation and propagation in sweet cherry skin: A simple chain reaction causes the crack to 'run'.

Project description:Rain cracking severely affects the commercial production of many fleshy-fruit species, including of sweet cherries. The objectives were to investigate how the gaping macroscopic cracks (macrocracks) of a rain-cracked fruit can develop from microscopic cracks in the cuticle (microcracks). Incubating fruit in deionized water is well known to cause significant macrocracking. We found that after a lag phase of 2 h, the numbers and lengths of macrocracks increased. Macrocrack number approached an asymptote at 12 h, whereas macrocrack length continued to increase. The rate of macrocrack propagation (extension at the crack tip) was initially 10.8 mm h-1 but then decreased to a near-constant 0.5 mm h-1. Light microscopy revealed three characteristic zones along a developing macrocrack. In zone I (ahead of the crack), the cuticle was intact, the epidermal cells were unbroken and their cell walls were thin. In zone II, the cuticle was fractured, the first epidermal cells died and their cell walls began to thicken (swell). In zone III, most epidermal cells had died, their cell walls were swollen and cell:cell separation began along the middle lamellae. The thickness of the anticlinal epidermal cell walls and the percentage of intact living cells along a crack were closely and negatively related. Cracks were stained by calcofluor white, but there was no binding of monoclonal antibodies (mAbs) specific for hemicelluloses (LM11, LM21, LM25). Strong binding was obtained with the anti-homogalacturonan mAb (LM19), indicating the presence of unesterified homogalacturonans on the crack surface. We conclude that macrocrack propagation is related to cell death and to cell wall swelling. Cell wall swelling weakens the cell:cell adhesion between neighbouring epidermal cells, which separate along their middle lamellae. The skin macrocrack propagates like a 'run' in a fine, knitted fabric.

| S-EPMC6668808 | biostudies-literature

Crack propagation and fracture in silicon wafers under thermal stress.

Project description:The behaviour of microcracks in silicon during thermal annealing has been studied using in situ X-ray diffraction imaging. Initial cracks are produced with an indenter at the edge of a conventional Si wafer, which was heated under temperature gradients to produce thermal stress. At temperatures where Si is still in the brittle regime, the strain may accumulate if a microcrack is pinned. If a critical value is exceeded either a new or a longer crack will be formed, which results with high probability in wafer breakage. The strain reduces most efficiently by forming (hhl) or (hkl) crack planes of high energy instead of the expected low-energy cleavage planes like {111}. Dangerous cracks, which become active during heat treatment and may shatter the whole wafer, can be identified from diffraction images simply by measuring the geometrical dimensions of the strain-related contrast around the crack tip. Once the plastic regime at higher temperature is reached, strain is reduced by generating dislocation loops and slip bands and no wafer breakage occurs. There is only a small temperature window within which crack propagation is possible during rapid annealing.

| S-EPMC3769070 | biostudies-literature

Highly durable crack sensor integrated with silicone rubber cantilever for measuring cardiac contractility.

Project description:To date, numerous biosensing platforms have been developed for assessing drug-induced cardiac toxicity by measuring the change in contractile force of cardiomyocytes. However, these low sensitivity, low-throughput, and time-consuming processes are severely limited in their real-time applications. Here, we propose a cantilever device integrated with a polydimethylsiloxane (PDMS)-encapsulated crack sensor to measure cardiac contractility. The crack sensor is chemically bonded to a PDMS thin layer that allows it to be operated very stably in culture media. The reliability of the proposed crack sensor has been improved dramatically compared to no encapsulation layer. The highly sensitive crack sensor continuously measures the cardiac contractility without changing its gauge factor for up to 26 days (>5 million heartbeats), while changes in contractile force induced by drugs are monitored using the crack sensor-integrated cantilever. Finally, experimental results are compared with those obtained via conventional optical methods to verify the feasibility of building a contraction-based drug-toxicity testing system.

| S-EPMC6985253 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data