Plasticized Cellulosic Films by Partial Esterification and Welding in Low-Concentration Ionic Liquid Electrolyte.

ABSTRACT: Alternatives to petroleum-based plastics are of great significance not only from the point of view of their scientific and practical impact but to reduce the environmental footprint. Inspired by the composition and structure of wood's cell walls, we used phenolic acids to endow cellulosic fibers with new properties. The fiber dissolution and homogeneous modification were performed with a recyclable ionic liquid (IL) (tetrabutylammonium acetate ([N₄₄₄₄][OAc]):dimethyl sulfoxide) to attain different levels of reaction activity for three phenolic acids ( p-hydroxybenzoic acid, vanillic acid, and syringic acid). The successful autocatalytic Fischer esterification reaction was thoroughly investigated by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, elemental analysis, and nuclear magnetic resonance spectroscopy (¹³C CP-MAS, diffusion-edited ¹H NMR and multiplicity-edited heteronuclear single quantum coherence). Control of the properties of cellulose in the dispersed state, welding, and IL plasticization were achieved during casting and recrystallization to the cellulose II crystalline allomorph. Films of cellulose carrying grafted acids were characterized with respect to properties relevant to packaging materials. Most notably, despite the low degree of esterification (DS < 0.25), the films displayed a remarkable strength (3.5 GPa), flexibility (strains up to 35%), optical transparency (>90%), and water resistance (WCA ? 90°). Moreover, the measured water vapor barrier was found to be similar to that of poly(lactic acid) composite films. Overall, the results contribute to the development of the next-generation green, renewable, and biodegradable films for packaging applications.

SUBMITTER: Niu X

PROVIDER: S-EPMC6550441 | biostudies-literature | 2019 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Plasticized Cellulosic Films by Partial Esterification and Welding in Low-Concentration Ionic Liquid Electrolyte.

Niu Xun X Liu Yating Y King Alistair W T AWT Hietala Sami S Pan Hui H Rojas Orlando J OJ

Biomacromolecules 20190429 5

Alternatives to petroleum-based plastics are of great significance not only from the point of view of their scientific and practical impact but to reduce the environmental footprint. Inspired by the composition and structure of wood's cell walls, we used phenolic acids to endow cellulosic fibers with new properties. The fiber dissolution and homogeneous modification were performed with a recyclable ionic liquid (IL) (tetrabutylammonium acetate ([N<sub>4444</sub>][OAc]):dimethyl sulfoxide) to att ...[more]

PMID: 30983326

Similar Datasets

Project description:With the development of mobile electronic devices, there are more and more requirements for high-energy storage equipment. Traditional lithium-ion batteries, like lithium-iron phosphate batteries, are limited by their theoretical specific capacities and might not meet the requirements for high energy density in the future. Lithium-sulfur batteries (LSBs) might be ideal next-generation energy storage devices because they have nearly 10 times the theoretical specific capacities of lithium-ion batteries. However, the severe capacity decay of LSBs limits their application, especially at high currents. In this study, an ionic liquid (IL) electrolyte additive, TDA+TFSI, was reported. When 5% of the TDA+TFSI additive was added to a traditional ether-based organic electrolyte, the cycling performance of the LSBs was significantly improved compared with that of the LSBs with the pure traditional organic electrolyte. At a rate of 0.5 C, the discharge specific capacity in the first cycle of the LSBs with the 5% TDA+TFSI electrolyte additive was 1167 mAh g-1; the residual specific capacities after 100 cycles and 300 cycles were 579 mAh g-1 and 523 mAh g-1, respectively; and the average capacity decay rate per cycle was only 0.18% in 300 cycles. Moreover, the electrolyte with the TDA+TFSI additive had more obvious advantages than the pure organic ether-based electrolyte at high charge and discharge currents of 1.0 C. The residual discharge specific capacities were 428 mAh g-1 after 100 cycles and 399 mAh g-1 after 250 cycles, which were 13% higher than those of the LSBs without the TDA+TFSI additive. At the same time, the Coulombic efficiencies of the LSBs using the TDA+TFSI electrolyte additive were more stable than those of the LSBs using the traditional organic ether-based electrolyte. The results showed that the LSBs with the TDA+TFSI electrolyte additive formed a denser and more uniform solid electrolyte interface (SEI) film during cycling, which improved the stability of the electrochemical reaction.

Dataset Information

Plasticized Cellulosic Films by Partial Esterification and Welding in Low-Concentration Ionic Liquid Electrolyte.

Publications

Plasticized Cellulosic Films by Partial Esterification and Welding in Low-Concentration Ionic Liquid Electrolyte.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets