Nano Hard Carbon Anodes for Sodium-Ion Batteries.

ABSTRACT: A hindrance to the practical use of sodium-ion batteries is the lack of adequate anode materials. By utilizing the co-intercalation reaction, graphite, which is the most common anode material of lithium-ion batteries, was used for storing sodium ion. However, its performance, such as reversible capacity and coulombic efficiency, remains unsatisfactory for practical needs. Therefore, to overcome these drawbacks, a new carbon material was synthesized so that co-intercalation could occur efficiently. This carbon material has the same morphology as carbon black; that is, it has a wide pathway due to a turbostratic structure, and a short pathway due to small primary particles that allows the co-intercalation reaction to occur efficiently. Additionally, due to the numerous voids present in the inner amorphous structure, the sodium storage capacity was greatly increased. Furthermore, owing to the coarse co-intercalation reaction due to the surface pore structure, the formation of solid-electrolyte interphase was greatly suppressed and the first cycle coulombic efficiency reached 80%. This study shows that the carbon material alone can be used to design good electrode materials for sodium-ion batteries without the use of next-generation materials.

SUBMITTER: Kim DY

PROVIDER: S-EPMC6567009 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Micro-nano structure hard carbon as a high performance anode material for sodium-ion batteries.

Project description:Superior first-cycle Coulomb efficiency (above 80%) is displayed by filter paper-derived micro-nano structure hard carbon, and it delivers a high reversible capacity of 286?mAh g-1 after 100 cycles as the anode for Na-ion battery at 20?mA g-1. These advantageous performance characteristics are attributed to the unique micro-nano structure, which reduced the first irreversible capacity loss by limiting the contact between the electrode and electrolyte, and enhanced the capacity by accelerating electron and Na-ion transfer through inter-connected nano-particles and nano-pores, respectively. The good electrochemical performance indicates that this low-cost hard carbon could be a promising anode for Na-ion batteries.

| S-EPMC5067775 | biostudies-literature

3D Flower-like Tin Monosulfide/Carbon Nanocomposite Anodes for Sodium-Ion Batteries.

Project description:The nanostructured tin monosulfide/carbon composites were synthesized by a simple wet chemical synthesis approach. It was revealed that the 3D flower-like tin monosulfide nanoparticles are usable as an active anode material for sodium-ion batteries, exhibiting a specific capacity of 480.4 mAh/g. The 3D flower-like tin monosulfide nanoparticles were wrapped with reduced graphene oxide sheets by a solvothermal heterogeneous synthetic method. By incorporating the reduced graphene oxide sheets as a mechanically flexible and electrically conductive additive, a specific capacity of 633.2 mAh/g was obtained from tin monosulfide/carbon nanocomposite anodes, providing an excellent rate capability even at a high current density condition of 5000 mA/g.

| S-EPMC9028553 | biostudies-literature

Peat-derived hard carbon electrodes with superior capacity for sodium-ion batteries.

Project description:Herein we demonstrate how peat, abundant and cheap biomass, can be successfully used as a precursor to synthesize peat-derived hard carbons (PDCs), applicable as electrode materials for sodium-ion batteries (SIB). The PDCs were obtained by pre-pyrolysing peat at 300-800 °C, removing impurities with base-acid solution treatment and thereafter post-pyrolysing the materials at temperatures (T) from 1000 to 1500 °C. By modification of pre- and post-pyrolysis temperatures we obtained hard carbons with low surface areas, optimal carbonization degree and high electrochemical Na+ storage capacity in SIB half-cells. The best results were obtained when pre-pyrolysing peat at 450 °C, washing out the impurities with KOH and HCl solutions and then post-pyrolysing the obtained carbon-rich material at 1400 °C. All hard carbons were electrochemically characterized in half-cells (vs. Na/Na+) and capacities as high as 350 mA h g-1 at 1.5 V and 250 mA h g-1 in the plateau region (E < 0.2 V) were achieved at charging current density of 25 mA g-1 with an initial coulombic efficiency of 80%.

| S-EPMC9054124 | biostudies-literature

Low-Cost and High-Performance Hard Carbon Anode Materials for Sodium-Ion Batteries.

Project description:As an anode material for sodium-ion batteries (SIBs), hard carbon (HC) presents high specific capacity and favorable cycling performance. However, high cost and low initial Coulombic efficiency (ICE) of HC seriously limit its future commercialization for SIBs. A typical biowaste, mangosteen shell was selected as a precursor to prepare low-cost and high-performance HC via a facile one-step carbonization method, and the influence of different heat treatments on the morphologies, microstructures, and electrochemical performances was investigated systematically. The microstructure evolution studied using X-ray diffraction, Raman, Brunauer-Emmett-Teller, and high-resolution transmission electron microscopy, along with electrochemical measurements, reveals the optimal carbonization condition of the mangosteen shell: HC carbonized at 1500 °C for 2 h delivers the highest reversible capacity of ∼330 mA h g-1 at a current density of 20 mA g-1, a capacity retention of ∼98% after 100 cycles, and an ICE of ∼83%. Additionally, the sodium-ion storage behavior of HC is deeply analyzed using galvanostatic intermittent titration and cyclic voltammetry technologies.

| S-EPMC6641066 | biostudies-literature

N-doped catalytic graphitized hard carbon for high-performance lithium/sodium-ion batteries.

Project description:Hard carbon attracts wide attentions as the anode for high-energy rechargeable batteries due to its low cost and high theoretical capacities. However, the intrinsically disordered microstructure gives it poor electrical conductivity and unsatisfactory rate performance. Here we report a facile synthesis of N-doped graphitized hard carbon via a simple carbonization and activation of a urea-soaked self-crosslinked Co-alginate for the high-performance anode of lithium/sodium-ion batteries. Owing to the catalytic graphitization of Co and the introduction of nitrogen-functional groups, the hard carbon shows structural merits of ordered expanded graphitic layers, hierarchical porous channels, and large surface area. Applying in the anode of lithium/sodium-ion batteries, the large surface area and the existence of nitrogen functional groups can improve the specific capacity by surface adsorption and faradic reaction, while the hierarchical porous channels and expanded graphitic layers can provide facilitate pathways for electrolyte and improve the rate performance. In this way, our hard carbon provides its feasibility to serve as an advanced anode material for high-energy rechargeable lithium/sodium-ion batteries.

| S-EPMC6028452 | biostudies-literature

Sulfur-Doped and Bio-Resin-Derived Hard Carbon@rGO Composites as Sustainable Anodes for Lithium-Ion Batteries.

Project description:Hard carbon derived from fossil products is widely used as anode material for lithium-ion batteries. However, there are still several main shortcomings such as high cost, and poor rate performance, which restrict its wide application. Then tremendous efforts have been devoted to developing biomaterials in the battery applications. Recently, especially agricultural and industrial by-products have attracted much attention due to the electric double-layer capacitors. Herein, we report the sulfur-doped hard carbon (SHC) materials from the tannin-furanic resins (TF-Resin) of the derived agricultural by-products, followed by enveloping rGO on its surface through the hexadecyl trimethyl ammonium bromide. SHC provides sites for the storage of lithium, while the rGO layers can offer a highly conductive matrix to achieve good contact between particles and promote the diffusion and transport of ions and electrons. As a result, the SHC@rGO shows excellent lithium storage performance with initial discharge capacity around 746 mAh g-1 at a current density of 50 mA g-1, and shows superb stability keeping capacity retention of 91.9% after 200 cycles. Moreover, even at a high current density of 2,000 mAg-1, SHC@rGO still delivers a specific capacity of 188 mAg-1. These desired promising properties are active to the implement in the possible practical application.

| S-EPMC7142261 | biostudies-literature

Heteroatom Doped-Carbon Nanospheres as Anodes in Lithium Ion Batteries.

Project description:Long cycle performance is a crucial requirement in energy storage devices. New formulations and/or improvement of "conventional" materials have been investigated in order to achieve this target. Here we explore the performance of a novel type of carbon nanospheres (CNSs) with three heteroatom co-doped (nitrogen, phosphorous and sulfur) and high specific surface area as anode materials for lithium ion batteries. The CNSs were obtained from carbonization of highly-crosslinked organo (phosphazene) nanospheres (OPZs) of 300 nm diameter. The OPZs were synthesized via a single and facile step of polycondensation reaction between hexachlorocyclotriphosphazene (HCCP) and 4,4'-sulphonyldiphenol (BPS). The X-ray Photoelectron Spectroscopy (XPS) analysis showed a high heteroatom-doping content in the structure of CNSs while the textural evaluation from the N₂ sorption isotherms revealed the presence of micro- and mesopores and a high specific surface area of 875 m²/g. The CNSs anode showed remarkable stability and coulombic efficiency in a long charge-discharge cycling up to 1000 cycles at 1C rate, delivering about 130 mA·h·g-1. This study represents a step toward smart engineering of inexpensive materials with practical applications for energy devices.

| S-EPMC5456559 | biostudies-literature

Electrochemically Expandable Soft Carbon as Anodes for Na-Ion Batteries.

Project description:Na-ion batteries (NIBs) have attracted great attention for scalable electrical energy storage considering the abundance and wide availability of Na resources. However, it remains elusive whether carbon anodes can achieve the similar scale of successes in Na-ion batteries as in Li-ion batteries. Currently, much attention is focused on hard carbon while soft carbon is generally considered a poor choice. In this study, we discover that soft carbon can be a high-rate anode in NIBs if the preparation conditions are carefully chosen. Furthermore, we discover that the turbostratic lattice of soft carbon is electrochemically expandable, where d-spacing rises from 3.6 to 4.2 Å. Such a scale of lattice expansion only due to the Na-ion insertion was not known for carbon materials. It is further learned that portions of such lattice expansion are highly reversible, resulting in excellent cycling performance. Moreover, soft carbon delivers a good capacity at potentials above 0.2 V, which enables an intrinsically dendrite-free anode for NIBs.

| S-EPMC4827671 | biostudies-literature

Lanthanide doping induced electrochemical enhancement of Na2Ti3O7 anodes for sodium-ion batteries.

Project description:Na2Ti3O7 is considered as a promising anode material for sodium ion batteries (SIBs) due to its excellent high-rate performance compared with hard carbons. However, the electrochemical performance of Na2Ti3O7 is heavily limited by its low electrical conductivity. In this study, we synthesized a series of lanthanide (Ln = La, Ce, Nd, Sm, Gd, Er, and Yb) doped microsized Na2Ti3O7 anode materials and systematically studied the electrochemical performance. Compared with pristine Na2Ti3O7, all the doped samples show superior electrochemical performance. Especially, the Yb3+ doped sample not only delivers a high reversible capacity of 89.4 mA h g-1 at 30C, but also maintains 71.6 mA h g-1 at 5C after 1600 cycles, nearly twice that of pristine Na2Ti3O7. It is found for the first time that the enhancement in doped samples is attributed to the introduction of lanthanides which induces lattice distortion and oxygen vacancies.

| S-EPMC5931090 | biostudies-literature

Blackberry Seeds-Derived Carbon as Stable Anodes for Lithium-Ion Batteries

Project description: Not available

| S-EPMC11007718 | biostudies-literature