Thermal Analysis of Crystallization and Phase Transition in Novel Polyethylene Glycol Grafted Butene-1 Copolymers.

ABSTRACT: Copolymerization is an effective strategy to regulate the molecular structure and tune crystalline structures. In this work, novel butene-1 copolymers with different polyethylene glycol (PEG) grafts (number-average molecular weight M_n = 750, 2000, and 4000 g/mol) were synthesized, for the first time introducing long-chain grafts to the polybutene-1 main chain. For these PEG-grafted copolymers, crystallization, melting, and phase transition behaviors were explored using differential scanning calorimetry. With respect to the linear homopolymer, the incorporation of a trimethylsilyl group decreases the cooling crystallization temperature (T_c), whereas the presence of the long PEG grafts unexpectedly elevates T_c. For isothermal crystallization, a critical temperature was found at 70 °C, below which all polyethylene glycol-grafted butene-1 (PB-PEG) copolymers have faster crystallization kinetics than polybutene-1 (PB). The subsequent melting process shows that for the identical crystallization temperature, generated PB-PEG crystallites always have lower melting temperatures than that of PB. Moreover, the II-I phase transition behavior of copolymers is also dependent on the length of PEG grafts. When form II, obtained from isothermal crystallization at 60 °C, was annealed at 25 °C, PB-PEG-750, with the shortest PEG grafts of M_n = 750 g/mol, could have the faster transition rate than PB. However, PB-PEG-750 exhibits a negative correlation between transition rate and crystallization temperature. Differently, in PB-PEG copolymers with PEG grafts M_n = 2000 and 4000 g/mol, transition rates rise with elevating crystallization temperature, which is similar with homopolymer PB. Therefore, the grafting of the PEG side chain provides the available method to tune phase transition without sacrificing crystallization capability in butene-1 copolymers.

SUBMITTER: An C

PROVIDER: S-EPMC6572506 | biostudies-literature | 2019 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Green energy-storage materials enable the sustainable use of renewable energy and waste heat. As such, a form-stable phase-change nanohybrid (PCN) is demonstrated to solve the fluidity and leakage issues typical of phase-change materials (PCMs). Here, we introduce the advantage of solid-to-gel transition to overcome the drawbacks of typical solid-to-liquid counterparts in applications related to thermal energy storage and regulation. Polyethylene glycol (PEG) is form-stabilized with cellulose nanofibrils (CNFs) through surface interactions. The cellulosic nanofibrillar matrix is shown to act as an organogelator of highly loaded PEG melt (85 wt %) while ensuring the absence of leakage. CNFs also preserve the physical structure of the PCM and facilitate handling above its fusion temperature. The porous CNF scaffold, its crystalline structure, and the ability to hold PEG in the PCN are characterized by optical and scanning electron imaging, infrared spectroscopy, and X-ray diffraction. By the selection of the PEG molecular mass, the lightweight PCN provides a tailorable fusion temperature in the range between 18 and 65 °C for a latent heat storage of up to 146 J/g. The proposed PCN shows remarkable repeatability in latent heat storage after 100 heating/cooling cycles as assessed by differential scanning calorimetry. The thermal regulation and light-to-heat conversion of the PCN are confirmed via infrared thermal imaging under simulated sunlight and in a thermal chamber, outperforming those of a reference, commercial insulation material. Our PCN is easily processed as a structurally stable design, including three-dimensional, two-dimensional (films), and one-dimensional (filaments) materials; they are, respectively, synthesized by direct ink writing, casting/molding, and wet spinning. We demonstrate the prospects of the lightweight, green nanohybrid for smart-energy buildings and waste heat-generating electronics for thermal energy storage and management.

Project description:In this research, novel, organic, solid-liquid phase-change materials (PCMs) derived from methoxy polyethylene glycol (MPEG) and aromatic acyl chlorides (ACs) were prepared through a condensation reaction. The MPEGs were used as phase-change functional chains with different molecular weights (350, 550, 750, 2000, and 5000 g/mol). The aromatic ACs, terephthaloyl chloride (TPC) and isophthaloyl chloride (IPC), were employed as bulky linker cores. Solubility tests demonstrated that this family of PCMs is soluble in protic polar solvents such as H2O and MeOH, and insoluble in nonpolar solvents such as n-hexane. Fourier-ransform infrared spectroscopy (FT-IR UATR) and nuclear magnetic resonance (1H, 13C, DEPT 135°, COSY, HMQC, and HMBC NMR) were used to confirm the bonding of MPEG chains to ACs. The crystalline morphology of the synthesized materials was examined using polarized optical microscopy (POM), revealing the formation of spherulites with Maltese-cross-extinction patterns. Furthermore, it was confirmed that PCMs with higher molecular weights were crystalline at room temperature and exhibited an increased average spherulite size compared to their precursors. Thermal stability tests conducted through thermogravimetric analysis (TGA) indicated decomposition temperatures close to 400 °C for all PCMs. The phase-change properties were characterized by differential scanning calorimetry (DSC), revealing that the novel PCMs melted and crystallized between -23.7 and 60.2 °C and -39.9 and 45.9 °C, respectively. Moreover, the heat absorbed and released by the PCMs ranged from 57.9 to 198.8 J/g and 48.6 to 195.6 J/g, respectively. Additionally, the PCMs exhibited thermal stability after undergoing thermal cycles of melting-crystallization, indicating that energy absorption and release occurred at nearly constant temperatures. This study presents a new family of high-performance organic PCMs and demonstrates that the orientation of substituent groups in the phenylene ring influences supercooling, transition temperatures, and thermal energy storage capacity depending on the MPEG molecular weight.

Dataset Information

Thermal Analysis of Crystallization and Phase Transition in Novel Polyethylene Glycol Grafted Butene-1 Copolymers.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets