Microwave-assisted synthesis of high thermal stability and colourless polyimides containing pyridine.

ABSTRACT: A novel aromatic diamine containing pyridyl side group, 4-pyridine-4,4-bis(3,5-dimethyl-5-aminophenyl)methane (PyDPM), was successfully synthesized via electrophilic substitution reaction. The polyimides (PIs) containing pyridine were obtained via the microwave-assisted one-step polycondensation of the PyDPM with pyromellitic dianhydride (PMDA), 3,3',4,4'-biphenyltetracarboxylic dianhydride (BPDA), 3,3',4,4'-diphenylether tetracarboxylic dianhydride (ODPA) and 4,4'-(hexafluoroisopropylidene)diphthalic anhydride (6FDA). Contrarily to the reported similar PIs, these PIs exhibit much higher thermal stability or heat resistance, i.e. high glass transition temperatures (T gs) in the range of 358-473°C, and the decomposition temperatures at 5% weight loss over 476°C under nitrogen. They can afford flexible and strong films with tensile strength of 82.1-93.3 MPa, elongation at break of 3.7%-15.2%, and Young's modulus of 3.3-3.8 GPa. Furthermore, The PI films exhibit good optical transparency with the cut-off wavelength at 313-366 nm and transmittance higher than 73% at 450 nm. The excellent thermal and optical transmittance can be attributed to synthesis method and the introduction of pyridine rings and ortho-methyl groups. The inherent viscosities of PIs via one-step method were found to be 0.58-1.12 dl g-1 in DMAc, much higher than those via two-step method. These results indicate these PIs could be potential candidates for optical substrates of organic light emitting diodes (OLEDs).

SUBMITTER: Cheng K 

PROVIDER: S-EPMC6599801 | biostudies-literature | 2019 Jun

REPOSITORIES: biostudies-literature