Construction of Ultrathin Nitrogen-Doped Porous Carbon Nanospheres Coated With Polyaniline Nanorods for Asymmetric Supercapacitors.

ABSTRACT: Porous carbon materials produced by biomass have been widely studied for high performance supercapacitor due to their abundance, low price, and renewable. In this paper, the series of nitrogen-doped hierarchical porous carbon nanospheres (HPCN)/polyaniline (HPCN/PANI) nanocomposites is reported, which is prepared via in-situ polymerization. A novel approach with one-step pyrolysis of wheat flour mixed with urea and ZnCl₂ is proposed to prepare the HPCN with surface area of 930 m²/g. Ultrathin HPCN pyrolysised at 900°C (~3 nm in thickness) electrode displays a gravimetric capacitance of 168 F/g and remarkable cyclability with losing 5% of the maximum capacitance after 5,000 cycles. The interconnected porous texture permits depositing of well-ordered polyaniline nanorods and allows a fast absorption/desorption of electrolyte. HPCN/PANI with short diffusion pathway possesses high gravimetric capacitance of 783 F/g. It can qualify HPCN/PANI to be used as cathode in assembling asymmetric supercapacitor with HPCN as anode, and which displays an exceptional specific capacitance of 81.2 F/g. Moreover, HPCN/PANI//HPCN device presents excellent cyclability with 88.4% retention of initial capacity over 10,000 cycles. This work will provide a simple and economical protocol to prepare the sustainable biomass materials based electrodes for energy storage applications.

SUBMITTER: Yu P

PROVIDER: S-EPMC6606993 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Porous Fe<sub>2</sub>O<sub>3</sub> Nanorods on Hierarchical Porous Biomass Carbon as Advanced Anode for High-Energy-Density Asymmetric Supercapacitors.

Project description:In this study, a novel negative electrode material was prepared by aligning α-Fe2O3 nanorods on a hierarchical porous carbon (HPC) skeleton. The skeleton was derived from wheat flour by a facile hydrothermal route to enhance conductivity, improve surface properties, and achieve substantially good electrochemical performances. The α-Fe2O3/HPC electrode exhibits enhanced specific capacitance of 706 F g-1, which is twice higher than that of α-Fe2O3. The advanced α-Fe2O3/HPC//PANI/HPC asymmetrical supercapacitor was built with an expanded voltage of 2.0 V in 1 M Li2SO4, possessing a specific capacitance of 212 F g-1 at 1 A g-1 and a maximum energy density of 117 Wh kg-1 at 1.0 kW kg-1, along with an excellent stability of 5.8% decay in capacitance after 5,000 cycles. This study affords a simple process to develop asymmetric supercapacitors, which exhibit high electrochemical performances and are applicable in next-generation energy storage devices, based on α-Fe2O3 hybrid materials.

| S-EPMC7726331 | biostudies-literature

MnO2 nanorods intercalating graphene oxide/polyaniline ternary composites for robust high-performance supercapacitors.

Project description:New ternary composites of MnO2 nanorods, polyaniline (PANI) and graphene oxide (GO) have been prepared by a two-step process. The 100 nm-long MnO2 nanorods with a diameter ~20 nm are conformably coated with PANI layers and fastened between GO layers. The MnO2 nanorods incorporated ternary composites electrode exhibits significantly increased specific capacitance than PANI/GO binary composite in supercapacitors. The ternary composite with 70% MnO2 exhibits a highest specific capacitance reaching 512 F/g and outstanding cycling performance, with ~97% capacitance retained over 5000 cycles. The ternary composite approach offers an effective solution to enhance the device performance of metal-oxide based supercapacitors for long cycling applications.

| S-EPMC4001101 | biostudies-other

Dual-ZIF-derived "reassembling strategy" to hollow MnCoS nanospheres for aqueous asymmetric supercapacitors.

Project description:Construction of delicate nanostructures with a facile, mild-condition and economical method is a key issue for building high-performance electrode materials. We demonstrate a facile and novel "reassembling strategy" to hollow MnCoS nanospheres derived from dual-ZIF for supercapacitors. The spherical shell's surface structure, thickness and Mn distribution were controlled by regulating the solvothermal reaction time. The chemical composition, phases, specific surface areas and microstructure were studied and the electrochemical performances were systematically estimated. As the unique low-crystalline and optimized hollow nanosphere structure contributes to increasing active sites, MnCoS nanospheres exhibit excellent electrochemical performance. The test results show that the specific capacitance increases with increasing solvothermal time, and the MCS with a 5 h reaction time exhibits optimal electrochemical properties with a high specific capacity of 957 C g-1 (1 A g-1). Furthermore, an MCS-5//AC asymmetric supercapacitor device delivers a specific energy as high as 36.9 W h kg-1 at a specific power of 750 W kg-1.

| S-EPMC9430545 | biostudies-literature

Nanowires of polyaniline festooned silver coated paper electrodes for efficient solid-state symmetrical supercapacitors.

Project description:This paper demonstrates a facile strategy for the development of nanosilver decorated polyaniline coated (PAg) paper-based electrodes for the fabrication of solid-state symmetrical supercapacitors. PAg based printing paper was developed through a two-step process involving initial silver nucleation and growth on the paper followed by aniline polymerization. The developed electrically conductive paper exhibited a highly porous structure and excellent mechanical stability. Further symmetrical supercapacitors having the configuration PAg/electrolyte/PAg were fabricated and evaluated for electrochemical performance such as specific capacitance (483 F g-1 and 613 F g-1 in aqueous 1 M H2SO4 and PVA-H2SO4 gel electrolytes respectively), energy density (69.56 and 85.13 W h kg-1), and power density (243.44 and 405.375 W kg-1) and cycling stability (90% of its capacitance retention even after 2000 cycles), exhibiting excellent performance under various bending conditions. All these exciting results suggest that the developed paper-based flexible solid-state energy device can serve as an efficient, sustainable, and low-cost energy storage system for portable microelectronic devices which are expected to revolutionize the perception of energy-storage devices in the electronics industry.

| S-EPMC9088673 | biostudies-literature

Hierarchical Nanosheets/Walls Structured Carbon-Coated Porous Vanadium Nitride Anodes Enable Wide-Voltage-Window Aqueous Asymmetric Supercapacitors with High Energy Density.

Project description:The energy density of aqueous asymmetric supercapacitors (ASCs) is usually limited by low potential windows and capacitances of both anode and cathode. Herein, a facile strategy to fabricate hierarchical carbon-coated porous vanadium nitride nanosheet arrays on vertically aligned carbon walls (CC/CW/p-VN@C) as anode for aqueous ASCs is reported. The potential window of CC/CW/p-VN@C electrode can be stably extended to -1.3 to 0 V (vs Ag/AgCl) with greatly improved specific capacitance (604.8 F g-1 at 1 A g-1), excellent rate capability (368 F g-1 at 60 A g-1), and remarkable electrochemical stability. To construct ASCs, a Birnessite Na0.5MnO2 nanosheet arrays (CC/CW/Na0.5MnO2) cathode is similarly built. Benefiting from the matchable potential windows and high specific capacitances of the rationally designed anode and cathode, aqueous CC/CW/p-VN@C||CC/CW/Na0.5MnO2 ASCs with a wide voltage window of 2.6 V are fabricated. Moreover, the ASCs showcase an ultrahigh energy density up to 96.7 W h kg-1 at a high power density of 1294 W kg-1, and excellent cycling stability (92.5% retention after 10 000 cycles), outperforming most of previously reported ASCs and even comparable to that of organic electrolyte supercapacitors (SCs). This efficient strategy for fabricating 2.6 V aqueous ASCs suggests a promising research system for high energy density SCs.

| S-EPMC6702630 | biostudies-literature

Ag Nanorods Coated with Ultrathin TiO2 Shells as Stable and Recyclable SERS Substrates.

Project description:TiO2-coated Ag nanorods (Ag@TiO2 NRs) have been fabricated as multifunctional surface-enhanced Raman scattering (SERS) substrates. Uniform TiO2 shells could sufficiently protect the internal Ag NRs against oxidation and sulfuration, thus the temporal stability of SERS substrates was markedly improved. Meanwhile, due to the synergetic effect between crystalline TiO2 and Ag, the nanocomposites could clean themselves via photocatalytic degradation of the adsorbed molecules under ultraviolet irradiation and water dilution, making the SERS substrates renewable. Such Ag@TiO2 NRs were shown to serve as outstanding SERS sensors featuring high sensitivity, superior stability and recyclability.

| S-EPMC4614262 | biostudies-literature

Nitrogen and Phosphorus Co-doped Porous Carbon for High-Performance Supercapacitors.

Project description:As one of the most promising fast energy storage devices, supercapacitor has been attracting intense attention for many emerging applications. However, how to enhance the electrochemical performance of electrode materials is still the main issue among various researches. In this paper, hierarchical porous carbons derived from Eleocharis dulcis has been prepared by chemical activation process with the aid of KOH at elevated temperature. Results show that the N, P co-doped porous carbon exhibits excellent electrochemical performance, it owns a specific capacitance of 340.2 F/g at 1 A/g, and obtains outstanding cycling stability of 96.9% of capacitance retention at 10 A/g after 5,000 cycles in a three-electrode system. Moreover, in the two-electrode system, the product still maintains a high specific capacitance of 227.2 F/g at 1 A/g, and achieves good electrochemical cycle stability (94.2% of capacitance retention at 10 A/g after 10,000 cycles); besides, its power/energy density are 3694.084 and 26.289 Wh/kg, respectively. Therefore, the combination of facile synthesis strategy and excellent electrochemical performance makes Eleocharis dulcis-based porous carbon as a promising electrode material for supercapacitor.

| S-EPMC7045068 | biostudies-literature

Hierarchical N-Doped Porous Carbons for Zn-Air Batteries and Supercapacitors.

Project description:Nitrogen-doped carbon materials with a large specific surface area, high conductivity, and adjustable microstructures have many prospects for energy-related applications. This is especially true for N-doped nanocarbons used in the electrocatalytic oxygen reduction reaction (ORR) and supercapacitors. Here, we report a low-cost, environmentally friendly, large-scale mechanochemical method of preparing N-doped porous carbons (NPCs) with hierarchical micro-mesopores and a large surface area via ball-milling polymerization followed by pyrolysis. The optimized NPC prepared at 1000 °C (NPC-1000) offers excellent ORR activity with an onset potential (Eonset) and half-wave potential (E1/2) of 0.9 and 0.82 V, respectively (vs. a reversible hydrogen electrode), which are only approximately 30 mV lower than that of Pt/C. The rechargeable Zn-air battery assembled using NPC-1000 and the NiFe-layered double hydroxide as bifunctional ORR and oxygen evolution reaction electrodes offered superior cycling stability and comparable discharge performance to RuO2 and Pt/C. Moreover, the supercapacitor electrode equipped with NPC prepared at 800 °C exhibited a high specific capacity (431 F g-1 at 10 mV s-1), outstanding rate, performance, and excellent cycling stability in an aqueous 6-M KOH solution. This work demonstrates the potential of the mechanochemical preparation method of porous carbons, which are important for energy conversion and storage.

| S-EPMC7770743 | biostudies-literature

Nitrogen-Doped Multi-Scale Porous Carbon for High Voltage Aqueous Supercapacitors.

Project description:Recently, "Water-in-salt" electrolyte has been reported to extend the working voltage of aqueous supercapacitor. However, this electrolyte needs the electrode materials possess some good features such as proper pore structure, high electron and ion conductivity. Herein, we fabricated the nitrogen-doped multi-scale porous carbon (NMC) by the simple enriching melamine-resorcinol-formaldehyde xerogels method with integrating triblock copolymer for micro-pores formation. All the results confirmed that our NMC is provided with a very high specific surface area (3,170 m2 g-1) and its monoliths are composed of multi-scale porous structure. By employing the nanostructured NMC as electrode materials, we have investigated the capability for high-voltage aqueous supercapacitor applications. The superconcentrated "Water-in-salt" electrolyte expand stability operating potential window of aqueous symmetric supercapacitor up to 2.4 V with a high energy density of 33 Wh kg-1 at power density of 0.3 kW kg-1. Our studies indicate that the NMC is potential materials for high performance over wider voltage range.

| S-EPMC6199383 | biostudies-literature

Controlled growth of NiCo?O? nanorods and ultrathin nanosheets on carbon nanofibers for high-performance supercapacitors.

Project description:Two one-dimensional hierarchical hybrid nanostructures composed of NiCo2O4 nanorods and ultrathin nanosheets on carbon nanofibers (CNFs) are controllably synthesized through facile solution methods combined with a simple thermal treatment. The structure of NiCo2O4 can be easily controlled to be nanorods or nanosheets by using different additives in the synthesis. These two different nanostructures are evaluated as electrodes for high performance supercapacitors, in view of their apparent advantages, such as high electroactive surface area, ultrathin and porous features, robust mechanical strength, shorter ion and electron transport path. Their electrochemical performance is systematically studied, and both of these two hierarchical hybrid nanostructures exhibit high capacitance and excellent cycling stability. The remarkable electrochemical performance will undoubtedly make these hybrid structures attractive for high-performance supercapacitors with high power and energy densities.

| S-EPMC3600593 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data