Atom Probe Tomographic Imaging of PbS Quantum Dot Formation on Neodymium Clusters in Silicate Glasses.

ABSTRACT: The first 3-D direct observation of clusters of Nd oxide inside silicate glasses was achieved using atom probe tomography. Three-dimensional elemental maps of major chemical elements in glasses such as Si, Al, Zn and O showed no evidence of regions that had concentrations higher than the average values, whereas the Nd aggregated into regions of high concentration. Elemental maps of Nd and Pb recorded from the glasses containing PbS QDs showed highly-concentrated areas of both elements at the same locations; this result indicates that PbS QDs formation started in association with the Nd clusters.

SUBMITTER: Park WJ

PROVIDER: S-EPMC6624314 | biostudies-literature | 2019 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Atom Probe Tomographic Imaging of PbS Quantum Dot Formation on Neodymium Clusters in Silicate Glasses.

Park Won Ji WJ Kim Ju Eun JE Lee Ho Jeong HJ Park Chan Gyung CG Heo Jong J

Scientific reports 20190711 1

The first 3-D direct observation of clusters of Nd oxide inside silicate glasses was achieved using atom probe tomography. Three-dimensional elemental maps of major chemical elements in glasses such as Si, Al, Zn and O showed no evidence of regions that had concentrations higher than the average values, whereas the Nd aggregated into regions of high concentration. Elemental maps of Nd and Pb recorded from the glasses containing PbS QDs showed highly-concentrated areas of both elements at the sam ...[more]

PMID: 31296948

Similar Datasets

Counterion-Mediated Ligand Exchange for PbS Colloidal Quantum Dot Superlattices.

Project description:In the past years, halide capping became one of the most promising strategies to passivate the surface of colloidal quantum dots (CQDs) in thin films to be used for electronic and optoelectronic device fabrication. This is due to the convenient processing, strong n-type characteristics, and ambient stability of the devices. Here, we investigate the effect of three counterions (ammonium, methylammonium, and tetrabutylammonium) in iodide salts used for treating CQD thin films and shed light on the mechanism of the ligand exchange. We obtain two- and three-dimensional square-packed PbS CQD superlattices with epitaxial merging of nearest neighbor CQDs as a direct outcome of the ligand-exchange reaction and show that the order in the layer can be controlled by the nature of the counterion. Furthermore, we demonstrate that the acidity of the environment plays an important role in the substitution of the carboxylates by iodide ions at the surface of lead chalcogenide quantum dots. Tetrabutylammonium iodide shows lower reactivity compared to methylammonium and ammonium iodide due to the nonacidity of the cation, which eventually leads to higher order but also poorer carrier transport due to incomplete removal of the pristine ligands in the QD thin film. Finally, we show that single-step blade-coating and immersion in a ligand exchange solution such as the one containing methylammonium iodide can be used to fabricate well performing bottom-gate/bottom-contact PbS CQD field effect transistors with record subthreshold swing.

| S-EPMC4690194 | biostudies-literature

Reduced Carrier Recombination in PbS - CuInS2 Quantum Dot Solar Cells.

Project description:Energy loss due to carrier recombination is among the major factors limiting the performance of TiO2/PbS colloidal quantum dot (QD) heterojunction solar cells. In this work, enhanced photocurrent is achieved by incorporating another type of hole-transporting QDs, Zn-doped CuInS2 (Zn-CIS) QDs into the PbS QD matrix. Binary QD solar cells exhibit a reduced charge recombination associated with the spatial charge separation between these two types of QDs. A ~30% increase in short-circuit current density and a ~20% increase in power conversion efficiency are observed in binary QD solar cells compared to cells built from PbS QDs only. In agreement with the charge transfer process identified through ultrafast pump/probe spectroscopy between these two QD components, transient photovoltage characteristics of single-component and binary QDs solar cells reveal longer carrier recombination time constants associated with the incorporation of Zn-CIS QDs. This work presents a straightforward, solution-processed method based on the incorporation of another QDs in the PbS QD matrix to control the carrier dynamics in colloidal QD materials and enhance solar cell performance.

| S-EPMC4448528 | biostudies-literature

Detecting trap states in planar PbS colloidal quantum dot solar cells.

Project description:The recently developed planar architecture (ITO/ZnO/PbS-TBAI/PbS-EDT/Au) has greatly improved the power conversion efficiency of colloidal quantum dot photovoltaics (QDPVs). However, the performance is still far below the theoretical expectations and trap states in the PbS-TBAI film are believed to be the major origin, characterization and understanding of the traps are highly demanded to develop strategies for continued performance improvement. Here employing impedance spectroscopy we detect trap states in the planar PbS QDPVs. We determined a trap state of about 0.34?eV below the conduction band with a density of around 3.2?×?1016?cm-3?eV-1. Temperature dependent open-circuit voltage analysis, temperature dependent diode property analysis and temperature dependent build-in potential analysis consistently denotes an below-bandgap activation energy of about 1.17-1.20?eV.

| S-EPMC5109221 | biostudies-literature

Enhanced open-circuit voltage of PbS nanocrystal quantum dot solar cells.

Project description:Nanocrystal quantum dots (QD) show great promise toward improving solar cell efficiencies through the use of quantum confinement to tune absorbance across the solar spectrum and enable multi-exciton generation. Despite this remarkable potential for high photocurrent generation, the achievable open-circuit voltage (Voc) is fundamentally limited due to non-radiative recombination processes in QD solar cells. Here we report the highest open-circuit voltages to date for colloidal QD based solar cells under one sun illumination. This Voc of 692 ± 7?mV for 1.4?eV PbS QDs is a result of improved passivation of the defective QD surface, demonstrating Voc(mV)=553Eg/q-59 as a function of the QD bandgap (Eg). Comparing experimental Voc variation with the theoretical upper-limit obtained from one diode modeling of the cells with different Eg, these results clearly demonstrate that there is a tremendous opportunity for improvement of Voc to values greater than 1?V by using smaller QDs in QD solar cells.

| S-EPMC3715763 | biostudies-literature

Rapid Photonic Processing of High-Electron-Mobility PbS Colloidal Quantum Dot Transistors.

Project description:Recent advances in solution-processable semiconducting colloidal quantum dots (CQDs) have enabled their use in a range of (opto)electronic devices. In most of these studies, device fabrication relied almost exclusively on thermal annealing to remove organic residues and enhance inter-CQD electronic coupling. Despite its widespread use, however, thermal annealing is a lengthy process, while its effectiveness to eliminate organic residues remains limited. Here, we exploit the use of xenon flash lamp sintering to post-treat solution-deposited layers of lead sulfide (PbS) CQDs and their application in n-channel thin-film transistors (TFTs). The process is simple, fast, and highly scalable and allows for efficient removal of organic residues while preserving both quantum confinement and high channel current modulation. Bottom-gate, top-contact PbS CQD TFTs incorporating SiO2 as the gate dielectric exhibit a maximum electron mobility of 0.2 cm2 V-1 s-1, a value higher than that of control transistors (≈10-2 cm2 V-1 s-1) processed via thermal annealing for 30 min at 120 °C. Replacing SiO2 with a polymeric dielectric improves the transistor's channel interface, leading to a significant increase in electron mobility to 3.7 cm2 V-1 s-1. The present work highlights the potential of flash lamp annealing as a promising method for the rapid manufacture of PbS CQD-based (opto)electronic devices and circuits.

| S-EPMC7467567 | biostudies-literature

High Performance PbS Quantum Dot/Graphene Hybrid Solar Cell with Efficient Charge Extraction.

Project description:Hybrid colloidal quantum dot (CQD) solar cells are fabricated from multilayer stacks of lead sulfide (PbS) CQD and single layer graphene (SG). The inclusion of graphene interlayers is shown to increase power conversion efficiency by 9.18%. It is shown that the inclusion of conductive graphene enhances charge extraction in devices. Photoluminescence shows that graphene quenches emission from the quantum dot suggesting spontaneous charge transfer to graphene. CQD photodetectors exhibit increased photoresponse and improved transport properties. We propose that the CQD/SG hybrid structure is a route to make CQD thin films with improved charge extraction, therefore resulting in improved solar cell efficiency.

| S-EPMC4928821 | biostudies-literature

Stoichiometric control of the density of states in PbS colloidal quantum dot solids.

Project description:Colloidal quantum dots, and nanostructured semiconductors in general, carry the promise of overcoming the limitations of classical materials in chemical and physical properties and in processability. However, sufficient control of electronic properties, such as carrier concentration and carrier mobility, has not been achieved until now, limiting their application. In bulk semiconductors, modifications of electronic properties are obtained by alloying or doping, an approach that is not viable for structures in which the surface is dominant. The electronic properties of PbS colloidal quantum dot films are fine-tuned by adjusting their stoichiometry, using the large surface area of the nanoscale building blocks. We achieve an improvement of more than two orders of magnitude in the hole mobility, from below 10-3 to above 0.1 cm2/V⋅s, by substituting the iodide ligands with sulfide while keeping the electron mobility stable (~1 cm2/V⋅s). This approach is not possible in bulk semiconductors, and the developed method will likely contribute to the improvement of solar cell efficiencies through better carrier extraction and to the realization of complex (opto)electronic devices.

| S-EPMC5621976 | biostudies-literature

Scalable PbS Quantum Dot Solar Cell Production by Blade Coating from Stable Inks.

Project description:The recent development of phase transfer ligand exchange methods for PbS quantum dots (QD) has enhanced the performance of quantum dots solar cells and greatly simplified the complexity of film deposition. However, the dispersions of PbS QDs (inks) used for film fabrication often suffer from colloidal instability, which hinders large-scale solar cell production. In addition, the wasteful spin-coating method is still the main technique for the deposition of QD layer in solar cells. Here, we report a strategy for scalable solar cell fabrication from highly stable PbS QD inks. By dispersing PbS QDs capped with CH3NH3PbI3 in 2,6-difluoropyridine (DFP), we obtained inks that are colloidally stable for more than 3 months. Furthermore, we demonstrated that DFP yields stable dispersions even of large diameter PbS QDs, which are of great practical relevance owing to the extended coverage of the near-infrared region. The optimization of blade-coating deposition of DFP-based inks enabled the fabrication of PbS QD solar cells with power conversion efficiencies of up to 8.7%. It is important to underline that this performance is commensurate with the devices made by spin coating of inks with the same ligands. A good shelf life-time of these inks manifests itself in the comparatively high photovoltaic efficiency of 5.8% obtained with inks stored for more than 120 days.

| S-EPMC7863069 | biostudies-literature

Optimizing Quantum Dot Probe Size for Single-Receptor Imaging.

Project description:Quantum dots (QDs) are nanocrystals with bright fluorescence and long-term photostability, attributes particularly beneficial for single-molecule imaging and molecular counting in the life sciences. The size of a QD nanocrystal determines its physicochemical and photophysical properties, both of which dictate the success of imaging applications. Larger nanocrystals typically have better optical properties, with higher brightness, red-shifted emission, reduced blinking, and greater stability. However, larger nanocrystals introduce molecular-labeling biases due to steric hindrance and nonspecific binding. Here, we systematically analyze the impact of nanocrystal size on receptor labeling in live and fixed cells. We designed three (core)shell QDs with red emission (600-700 nm) and crystalline sizes of 3.2, 5.5, and 8.3 nm. After coating with the same multidentate polymer, hydrodynamic sizes were 9.2 nm (QD9.2), 13.3 nm (QD13.3), and 17.4 nm (QD17.4), respectively. The QDs were conjugated to streptavidin and applied as probes for biotinylated neurotransmitter receptors. QD9.2 exhibited the highest labeling specificity for receptors in the narrow synaptic cleft (∼20-30 nm) in living neurons. However, for dense receptor labeling for molecular counting in live and fixed HeLa cells, QD13.3 yielded the highest counts. Nonspecific binding rose sharply for hydrodynamic sizes larger than 13.3 nm, with QD17.4 exhibiting particularly diminished specificity. Our comparisons further highlight needs to continue engineering the smallest QDs to increase single-molecule intensity, suppress blinking frequency, and inhibit nonspecific labeling in fixed and permeabilized cells. These results lay a foundation for designing QD probes with further reduced sizes to achieve unbiased labeling for quantitative and single-molecule imaging.

| S-EPMC7872344 | biostudies-literature

Efficient, Stable, and Low-Cost PbS Quantum Dot Solar Cells with Cr-Ag Electrodes.

Project description:PbS quantum dots (QDs) are a promising nanostructured material for solar cells. However, limited works have been done to explore the active layer thickness, layer deposition techniques, stability improvement, and cost reduction for PbS QD solar cells. We address those issues of device fabrication herein and suggest their possible solutions. In our work, to get the maximum current density from a PbS QD solar cell, we estimated the optimized active layer thickness using Matlab simulation. After that, we fabricated a high-performance and low-cost QD photovoltaic (PV) device with the simulated optimized active layer thickness. We implemented this low-cost device using a 10 mg/mL PbS concentration. Here, spin coating and drop-cast layer deposition methods were used and compared. We found that the device prepared by the spin coating method was more efficient than that by the drop cast method. The spin-coated PbS QD solar cell provided 6.5% power conversion efficiency (PCE) for the AM1.5 light spectrum. Besides this, we observed that Cr (chromium) interfaced with the Ag (Cr-Ag) electrode can provide a highly air-stable electrode.

| S-EPMC6780186 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data