Biopolymer from Tragacanth Gum as a Green Corrosion Inhibitor for Carbon Steel in 1 M HCl Solution.

ABSTRACT: A biopolymer from tragacanth gum, arabinogalactan (AG), was investigated for its adsorption and corrosion inhibition traits for carbon steel corrosion in 1 M HCl. Gravimetric method, potentiodynamic polarization measurements, electrochemical impedance spectroscopy, UV-visible spectroscopy, scanning electron microscopy, and atomic force microscopy were used to judge the adsorptive nature of AG in the acid solution. The inhibition efficiency improved with an increase in AG concentration and temperature of the acid solution. Thermodynamic and activation parameters (?G _ads, E _a, ?H, and ?S) were also calculated and discussed. The adsorption of AG favored Langmuir adsorption isotherm. The results of corrosion tests confirmed that AG could serve as an efficient green corrosion inhibitor for the carbon steel in 1 M HCl, yielding high efficiency and a low risk of environmental pollution. Theoretical quantum chemical and Monte Carlo simulation studies corroborated the experimental results.

SUBMITTER: Mobin M

PROVIDER: S-EPMC6641194 | biostudies-literature | 2017 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Biopolymer from Tragacanth Gum as a Green Corrosion Inhibitor for Carbon Steel in 1 M HCl Solution.

Mobin Mohammad M Rizvi Marziya M Olasunkanmi Lukman O LO Ebenso Eno E EE

ACS omega 20170726 7

A biopolymer from tragacanth gum, arabinogalactan (AG), was investigated for its adsorption and corrosion inhibition traits for carbon steel corrosion in 1 M HCl. Gravimetric method, potentiodynamic polarization measurements, electrochemical impedance spectroscopy, UV-visible spectroscopy, scanning electron microscopy, and atomic force microscopy were used to judge the adsorptive nature of AG in the acid solution. The inhibition efficiency improved with an increase in AG concentration and temper ...[more]

PMID: 31457703

Similar Datasets

Project description:Food contamination due to metal corrosion and the consequent leakage of metals into foods is a problem. Understanding the mechanism(s) of metal corrosion in food media is vital to evaluating, mitigating, and predicting contamination levels. Fruit juices have been employed as model corrosive media to study the corrosion behaviour of metallic material in food media. Carbon steel corrosion in fresh juices of tomato, orange, pineapple, and lemon, as well as dilute hydrochloric acid solutions at varied pH, was studied using scanning electron microscopy, gravimetric and spectrophotometric techniques, and comparisons made between the corrosivity of these juices and mineral acids of comparable pH. The corrosion of carbon steel in fruit juices and HCl solutions manifests as a combination of uniform and pitting corrosion. Gravimetric data acquired after one hour of immersion at ambient temperature (22 °C) indicated corrosion rates of 0.86 mm yr-1 in tomato juice (pH ≈ 4.24), 1.81 mm yr-1 in pineapple juice (pH ≈ 3.94), 1.52 mm yr-1 in orange juice (pH ≈ 3.58), and 2.89 mm yr-1 in lemon juice (pH ≈ 2.22), compared to 2.19 mm yr-1 in 10-2 M HCl (pH ≈ 2.04), 0.38 mm yr-1 in 10-3 M HCl (pH ≈ 2.95), 0.17 mm yr-1 in 10-4 M HCl (pH ≈ 3.95), and 0.04 mm yr-1 in 10-5 M HCl (pH ≈ 4.98). The correlation of gravimetrically acquired corrosion data with post-exposure spectrophotometric analysis of fruit juices enabled de-convolution of iron contamination rates from carbon steel corrosion rates in fruit juices. Elemental iron contamination after 50 h of exposure to steel samples was much less than the values predicted from corrosion data (≈40%, 4.02%, 8.37%, and 9.55% for tomato, pineapple, orange, and lemon juices, respectively, relative to expected values from corrosion (weight loss) data). Tomato juice (pH ≈ 4.24) was the least corrosive to carbon steel compared to orange juice (pH ≈ 3.58) and pineapple juice (pH ≈ 3.94). The results confirm that though the fruit juices are acidic, they are generally much less corrosive to carbon steel compared to hydrochloric acid solutions of comparable pH. Differences in the corrosion behaviour of carbon steel in the juices and in the different mineral acid solutions are attributed to differences in the compositions and pH of the test media, the nature of the corrosion products formed, and their dissolution kinetics in the respective media. The observation of corrosion products (iron oxide/hydroxide) in some of the fruit juices (tomato, pineapple, and lemon juices) in the form of apparently hollow microspheres indicates the feasibility of using fruit juices and related wastes as "green solutions" for the room-temperature and hydrothermal synthesis of metal oxide/hydroxide particles.

Dataset Information

Biopolymer from Tragacanth Gum as a Green Corrosion Inhibitor for Carbon Steel in 1 M HCl Solution.

Publications

Biopolymer from Tragacanth Gum as a Green Corrosion Inhibitor for Carbon Steel in 1 M HCl Solution.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets