Recycling Waste Polyester via Modification with a Renewable Fatty Acid for Enhanced Processability.

ABSTRACT: Polyethylene terephthalate (PET) waste often contains a large amount of thermally unstable contaminants and additives that negatively impacts processing. A reduced processing temperature is desired. In this work, we report using a renewably sourced tall oil fatty acid (TOFA) as a modifier for recycled PET. To that end, PET was compounded with TOFA at different concentrations and extruded at 240 °C. Phase transition behaviors characterized by thermal and dynamic mechanical analyses exhibit shifts in the melting and recrystallization temperatures of PET to lower temperatures and depression of glass transition temperature from 91 to 65 °C. Addition of TOFA also creates crystal-phase imperfection that slows recrystallization, an important processing parameter. Changes in the morphology of plasticized PET reduces and stabilizes the melt viscosity at 240 and 250 °C. Melt-spun, undrawn continuous filaments of diameter 36-46 ?m made from these low-melting PET exhibit 29-38 MPa tensile strength, 2.7-2.8 GPa tensile modulus, and 20-36% elongation. These results suggest a potential path for reusing waste PET as high-performance polymeric fibers.

SUBMITTER: Akato KM

PROVIDER: S-EPMC6645103 | biostudies-literature | 2018 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Recycling Waste Polyester via Modification with a Renewable Fatty Acid for Enhanced Processability.

Akato Kokouvi M KM Nguyen Ngoc A NA Bonnesen Peter V PV Harper David P DP Naskar Amit K AK

ACS omega 20180906 9

Polyethylene terephthalate (PET) waste often contains a large amount of thermally unstable contaminants and additives that negatively impacts processing. A reduced processing temperature is desired. In this work, we report using a renewably sourced tall oil fatty acid (TOFA) as a modifier for recycled PET. To that end, PET was compounded with TOFA at different concentrations and extruded at 240 °C. Phase transition behaviors characterized by thermal and dynamic mechanical analyses exhibit shifts ...[more]

PMID: 31459188

Similar Datasets

Project description:To explore the potential of long chain polyhydroxyalkanoates as non-toxic food packaging materials, the characterization of polyesters prepared from a natural occurring polyhydroxylated C16 carboxylic acid (9,10,16-trihydroxyhexadecanoic or aleuritic acid) has been addressed. Such monomer has been selected to elucidate the reactivity of primary and secondary hydroxyl groups and their contribution to the structure and properties of the polyester. Resulting polyaleuritate films have been produced using an open mold in one-step, solvent-free self-polycondensation in melt state and directly in air to evaluate the effect of oxygen in their final physical and chemical properties. These polymers are amorphous, insoluble, and thermostable, being therefore suitable for solvent, and heat resistant barrier materials. Structurally, most of primary hydroxyls are involved in ester bonds, but there is some branching arising from the partial participation of secondary O-H groups. The oxidative cleavage of the vicinal diol moiety and a subsequent secondary esterification had a noticeable effect on the amorphization and stiffening of the polyester by branching and densification of the ester bond network. A derivation of such structural modification was the surface compaction and the reduction of permeability to water molecules. The addition of Ti(OiPr)4 as a catalyst had a moderate effect, likely because of a poor diffusion within the melt, but noticeably accelerated both the secondary esterification and the oxidative processes. Primary esterification was a high conversion bulk reaction while oxidation and secondary esterification was restricted to nearby regions of the air exposed side of cast films. The reason was a progressive hindering of oxygen diffusion as the reaction progresses and a self-regulation of the altered layer growth. Despite such a reduced extent, the oxidized layer noticeably increased the UV-vis light blockage capacity. In general, characterized physical properties suggest a high potential of these polyaleuritate polyesters as food preserving materials.

Dataset Information

Recycling Waste Polyester via Modification with a Renewable Fatty Acid for Enhanced Processability.

Publications

Recycling Waste Polyester via Modification with a Renewable Fatty Acid for Enhanced Processability.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure