Polyaniline-Layered Rutile TiO₂ Nanorods as Alternative Photoanode in Dye-Sensitized Solar Cells.

ABSTRACT: In this paper, dye-sensitized solar cell (DSSC) performance of the less explored polymorph of TiO₂, rutile, has been explored, and its performance has been modified with polyaniline (PANI) wrapping on the surface. For this purpose, highly crystalline rutile nanorods have been synthesized without any growth-directing substrates, employing a hydrothermal treatment. Further, to understand the phase composition and morphology, the synthesized nanorods and PANI-layered nanorods have been characterized through various physicochemical methods. The synthesized rods were implemented as photoanode material for DSSCs which exhibited a photoelectric conversion efficiency (PCE) of 4.28% with a high open-circuit voltage (V _OC) of 0.84 V which is highly superior to DSSC with Degussa P25 (PCE = 3.95%) TiO₂ nanoparticles. The resultant PCE of the nanorods was further enhanced to 6.23% on in situ deposition of PANI which acts as an electron-transporting layer. Introduction of conducting PANI over the rutile rod was explored as a new concept to improve the performance of photoanode material besides conventional TiCl₄ treatment or scattering layer deposition.

SUBMITTER: Roy A

PROVIDER: S-EPMC6647995 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

A photoanode with hierarchical nanoforest TiO2 structure and silver plasmonic nanoparticles for flexible dye sensitized solar cell.

Project description:Due to unique photovoltaic properties, the nanostructured morphologies of TiO2 on flexible substrate have been studied extensively in the recent years for applications in dye sensitized solar cells (DSSCs). Microstructured electrode materials with high surface area can facilitate rapid charge transport and thus improve the light-to-current conversion efficiency. Herein we present an improved photoanode with forest like photoactive TiO2 hierarchical microstructure using a simple and facile hydrothermal route. To utilize the surface plasmon resonance (SPR) and hence increase the photon conversion efficiency, a plasmonic nanoparticle Ag has also been deposited using a very feasible photoreduction method. The branched structure of the photoanode increases the dye loading by filling the space between the nanowires, whereas Ag nanoparticles play the multiple roles of dye absorption and light scattering to increase the light-to-current conversion efficiency of the device. The branched structure provides a suitable matrix for the subsequent Ag deposition. They improve the charge collection efficiency by providing the preferential electron pathways. The high-density Ag nanoparticles deposited on the forest like structure also decrease the charge recombination and therefore improve the photovoltaic efficiency of the cells. As a result, the DSSC based on this novel photoanode shows remarkably higher photon conversion efficiency (ηmax = 4.0% and ηopt = 3.15%) compared to the device based on pristine nanowire or forest-like TiO2 structure. The flexibility of the device showed sustainable and efficient performance of the microcells.

| S-EPMC8024298 | biostudies-literature

Photovoltaic Effects of Dye-Sensitized Solar Cells Using Double-Layered TiO2 Photoelectrodes and Pyrazine-Based Photosensitizers.

Project description:In this study, to obtain high performances of the dye-sensitized solar cells using the optimal TiO2 photoelectrode for the synthesized pyrazine-based organic photosensitizers, three types of TiO2 photoelectrodes were fabricated and evaluated for comparison. The double-layered nanoporous TiO2 photoelectrode (SPD type) consisted of a dispersed TiO2 layer and a transparent TiO2 layer. The single-layered nanoporous TiO2 photoelectrodes (D type and SP type) consisted of a dispersed TiO2 layer and a transparent TiO2 layer, respectively. The surface area, pore volume, and crystalline structures of the three types of TiO2 photoelectrodes were analyzed by Brunauer-Emmett-Teller method, field-emission scanning electron microscopy, and X-ray diffractometry to confirm their crystallinity and surface morphology. The structures of the three types of TiO2 photoelectrode-adsorbed organic sensitizers were investigated using X-ray photoelectron spectroscopy. The photovoltaic performances of DSSC devices using three organic photosensitizers adsorbed onto the three types of TiO2 photoelectrodes were investigated under a light intensity of 100 mW/cm2 at AM 1.5. The DSSC device using double-layered SPD type TiO2 photoelectrodes displayed 1.31∼2.64% efficiency, compared to single-layered SP type TiO2 photoelectrodes (1.31∼2.50%) and D type TiO2 photoelectrodes (0.90∼1.54%), using organic photosensitizers. The DSSC device using the SPD type TiO2 photoelectrode and trifluoromethylbenzopyrazine (TPPF) as a photosensitizer showed the highest performances: J sc of 5.69 mA/cm2, V oc of 0.69 V, FF of 0.67, and efficiency of 2.64%. The relationship between photovoltaic effects and interfacial resistance characteristics of DSSCs using the three organic photosensitizers adsorbed onto the three types of TiO2 photoelectrodes could be interpreted from interfacial resistances according to frequency through impedance analysis.

| S-EPMC10134224 | biostudies-literature

Hierarchical TiO2 microspheres composed with nanoparticle-decorated nanorods for the enhanced photovoltaic performance in dye-sensitized solar cells.

Project description:Hierarchical TiO2 microspheres composed of nanoparticle-decorated nanorods (NP-MS) were successfully prepared with a two-step solvothermal method. There were three benefits associated with the use of NP-MS as a photoanode material. The decoration of nanoparticles improved the specific surface area and directly enhanced the dye loading ability. Rutile nanorods serving as electron transport paths resulted in fast electron transport and inhibited the charge recombination process. The three-dimensional hierarchical NP-MS structure supplied a strong light scattering capability and good connectivity. Thus, the hierarchical NP-MS combined the beneficial properties of improved scattering capability, dye loading ability, electron transport and inhibited charge recombination. Attributed to these advantages, a photoelectric conversion efficiency of up to 7.32% was obtained with the NP-MS film-based photoanode, resulting in a 43.5% enhancement compared to the efficiency of the P25 film-based photoanode (5.10%) at a similar thickness. Compared to traditional photoanodes with scattering layers or scattering centers, the fabrication process for single layered photoanodes with enhanced scattering capability was very simple. We believe the strategy would be beneficial for the easy fabrication of efficient dye-sensitized solar cells.

| S-EPMC9059954 | biostudies-literature

A diketopyrrolopyrrole dye-based dyad on a porous TiO2 photoanode for solar-driven water oxidation.

Project description:Dye-sensitised photoanodes modified with a water oxidation catalyst allow for solar-driven O2 evolution in photoelectrochemical cells. However, organic chromophores are generally considered unsuitable to drive the thermodynamically demanding water oxidation reaction, mainly due to their lack of stability upon photoexcitation. Here, the synthesis of a dyad photocatalyst (DPP-Ru) consisting of a diketopyrrolopyrrole chromophore (DPPdye) and ruthenium-based water oxidation catalyst (RuWOC) is described. The DPP-Ru dyad features a cyanoacrylic acid anchoring group for immobilisation on metal oxides, strong absorption in the visible region of the electromagnetic spectrum, and photoinduced hole transfer from the dye to the catalyst unit. Immobilisation of the dyad on a mesoporous TiO2 scaffold was optimised, including the use of a TiCl4 pretreatment method as well as employing chenodeoxycholic acid as a co-adsorbent, and the assembled dyad-sensitised photoanode achieved O2 evolution using visible light (100 mW cm-2, AM 1.5G, λ > 420 nm). An initial photocurrent of 140 μA cm-2 was generated in aqueous electrolyte solution (pH 5.6) under an applied potential of +0.2 V vs. NHE. The production of O2 has been confirmed by controlled potential electrolysis with a faradaic efficiency of 44%. This study demonstrates that metal-free dyes are suitable light absorbers in dyadic systems for the assembly of water oxidising photoanodes.

| S-EPMC8163027 | biostudies-literature

Monolithic-Structured Single-Layered Textile-Based Dye-Sensitized Solar Cells.

Project description:Textile-structured solar cells are frequently discussed in the literature due to their prospective applications in wearable devices and in building integrated solar cells that utilize their flexibility, mechanical robustness, and aesthetic appearance, but the current approaches for textile-based solar cells-including the preparation of fibre-type solar cells woven into textiles-face several difficulties from high friction and tension during the weaving process. This study proposes a new structural concept and fabrication process for monolithic-structured textile-based dye-sensitized solar cells that are fabricated by a process similar to the cloth-making process, including the preparation of wires and yarns that are woven for use in textiles, printed, dyed, and packaged. The fabricated single-layered textile-based dye-sensitized solar cells successfully act as solar cells in our study, even under bending conditions. By controlling the inter-weft spacing and the number of Ti wires for the photoelectrode conductor, we have found that the performance of this type of dye-sensitized solar cell was notably affected by the spacing between photoelectrodes and counter-electrodes, the exposed areas of Ti wires to photoelectrodes, and photoelectrodes' surface morphology. We believe that this study provides a process and concept for improved textile-based solar cells that can form the basis for further research.

| S-EPMC5052609 | biostudies-literature

Influence of Tin Doped TiO2 Nanorods on Dye Sensitized Solar Cells.

Project description:The one-step hydrothermal method was used to synthesize Sn-doped TiO2 (Sn-TiO2) thin films, in which the variation in Sn content ranged from 0 to 7-wt % and, further, its influence on the performance of a dye-sensitized solar cell (DSSC) photoanode was studied. The deposited samples were analyzed by X-ray diffraction (XRD) and Raman spectroscopy, which confirmed the existence of the rutile phase of the synthesized samples with crystallite size ranges in between 20.1 to 22.3 nm. In addition, the bare and Sn-TiO2 thin films showed nanorod morphology. A reduction in the optical band gap from 2.78 to 2.62 eV was observed with increasing Sn content. The X-ray photoelectron spectroscopy (XPS) analysis confirmed Sn4+ was successfully replaced at the Ti4+ site. The 3-wt % Sn-TiO2 based DSSC showed the optimum efficiency of 4.01%, which was superior to 0.87% of bare and other doping concentrations of Sn-TiO2 based DSSCs. The present work reflects Sn-TiO2 as an advancing material with excellent capabilities, which can be used in photovoltaic energy conversion devices.

| S-EPMC8585088 | biostudies-literature

Design of blueberry anthocyanin/TiO2 composite layer-based photoanode and N-doped porous blueberry-derived carbon-loaded Ni nanoparticle-based counter electrode for dye-sensitized solar cells.

Project description:P25/PBP (TiO2, anthocyanins) prepared by combining PBP (blueberry peels) with P25, and N-doped porous carbon-supported Ni nanoparticles (Ni@NPC-X) prepared using blueberry-derived carbon were used for the application as photoanode and the counter electrode, respectively, in dye-sensitized solar cells (DSSCs) to create a new perspective for blueberry-based photo-powered energy systems. PBP was introduced into the P25 photoanode and carbonized to form a C-like structure after annealing that improved its adsorption capacity for N719 dye, contributing a 17.3% higher power conversion efficiency (PCE) of P25/PBP-Pt (5.82%) than that of P25-Pt (4.96%). The structure of the porous carbon changes from a flat surface to a petal-like structure due to the N doping by melamine, and the specific surface area increases. N-doped three-dimensional porous carbon supported the loading and reduced the agglomeration of Ni nanoparticles, reducing the charge transfer resistance, and providing a fast electron transfer path. The doping of Ni and N on the porous carbon worked synergistically to enhance the electrocatalytic activity of the Ni@NPC-X electrode. The PCE of the DSSCs assembled by Ni@NPC-1.5 and P25/PBP was 4.86%. Also, the Ni@NPC-1.5 electrode exhibited 116.12 F g-1 and a capacitance retention rate of 98.2% (10 000 cycles), further confirming good electrocatalysis and cycle stability.

| S-EPMC9987179 | biostudies-literature

MOF-derived Co2+-doped TiO2 nanoparticles as photoanodes for dye-sensitized solar cells.

Project description:Facile synthesis and application of nano-sized semiconductor metal oxides for optoelectronic devices have always affected fabrication challenges since it involves multi-step synthesis processes. In this regard, semiconductor oxides derived directly from metal-organic frameworks (MOFs) routes have gained a great deal of scientific interest owing to their high specific surface area, regular and tunable pore structures. Exploring the application potential of these MOF-derived semiconductor oxides systems for clean energy conversion and storage devices is currently a hot topic of research. In this study, titanium-based MIL-125(Ti) MOFs were used as a precursor to synthesize cobalt-doped TiO2-based dye-sensitized solar cells (DSSCs) for the first time. The thermal decomposition of the MOF precursor under an air atmosphere at 400 °C resulted in mesoporous anatase-type TiO2 nanoparticles (NPs) of uniform morphology, large surface area with narrow pore distribution. The Co2+ doping in TiO2 leads to enhanced light absorption in the visible region. When used as photoanode in DSSCs, a good power conversion efficiency (PCE) of 6.86% with good photocurrent density (Jsc) of 13.96 mA cm-2 was obtained with the lowest recombination resistance and the longest electron lifetime, which is better than the performance of the pristine TiO2-based photoanode.

| S-EPMC8358052 | biostudies-literature

Aggregated mesoporous nanoparticles for high surface area light scattering layer TiO2 photoanodes in Dye-sensitized Solar Cells.

Project description:Hierarchically structured aggregates, consisting of TiO2 nanoparticles were produced via one-step solvothermal syntheses with a mixed solvent system containing both acetic acid and ethanol. Two of the resulting structures, one ~700?nm and the other ~300?nm in diameter, were found to be comprised of 8.5?nm and 10.5?nm anatase crystals, and possess specific surface areas of 138 and 106?m2?g-1 respectively. These particles were incorporated into Dye-sensitized Solar Cells (DSCs) as high surface area scattering layers, along with a layer of a transparent material. Solar-to-electric conversion efficiencies (PCE) of 9.1% and 8.2% were recorded using these aggregated particles as compared to those of commonly used large particles scattering layer 7.4%.

| S-EPMC5583389 | biostudies-literature

Design, synthesis, and performance evaluation of TiO2-dye sensitized solar cells using 2,2'-bithiophene-based co-sensitizers.

Project description:We report on the synthesis and characterization of six novel 2,2'-bithiophene-based organic compounds (3a-c and 5a-c) that are designed to serve as co-sensitizers for dye-sensitized solar cells (DSSCs) based on TiO2. The compounds are linked to various donor and acceptor groups, and we confirm their chemical structures through spectral analyses. Our focus is on enhancing the performance of metal based N3, and the compounds were designed to operate at the nanoscale. We performed absorption and fluorescence emission measurements in dimethylformamide (DMF), where one of our compounds 5a exhibited the longest maximum absorption and maximum emission wavelengths, indicating the significant impact of the para methoxy group as a strong electron-donating group. Our dyes 5a + N3 (η = 7.42%) and 5c + N3 (η = 6.57%) outperformed N3 (η = 6.16%) alone, where the values of short current density (JSC) and open circuit voltage (VOC) for these two systems also improved. We also investigated the charge transfer resistance at the TiO2/dye/electrolyte interface using electrochemical impedance spectroscopy (EIS), which is important in the context of nanotechnology. According to the Nyquist plot, the 5a + N3 cocktail exhibited the lowest recombination rate, resulting in the highest VOC. Our theoretical calculations based on density functional theory (DFT) are also in agreement with the experimental process. These findings suggest that our compounds have great potential as efficient DSSC co-sensitizers. This study provides valuable insights into the design and synthesis of new organic compounds for use as co-sensitizers in DSSCs based on TiO2 and highlights the potential of these compounds for use in efficient solar energy conversion.

| S-EPMC10449855 | biostudies-literature