A diketopyrrolopyrrole dye-based dyad on a porous TiO₂ photoanode for solar-driven water oxidation.

ABSTRACT: Dye-sensitised photoanodes modified with a water oxidation catalyst allow for solar-driven O₂ evolution in photoelectrochemical cells. However, organic chromophores are generally considered unsuitable to drive the thermodynamically demanding water oxidation reaction, mainly due to their lack of stability upon photoexcitation. Here, the synthesis of a dyad photocatalyst (DPP-Ru) consisting of a diketopyrrolopyrrole chromophore (DPPdye) and ruthenium-based water oxidation catalyst (RuWOC) is described. The DPP-Ru dyad features a cyanoacrylic acid anchoring group for immobilisation on metal oxides, strong absorption in the visible region of the electromagnetic spectrum, and photoinduced hole transfer from the dye to the catalyst unit. Immobilisation of the dyad on a mesoporous TiO₂ scaffold was optimised, including the use of a TiCl₄ pretreatment method as well as employing chenodeoxycholic acid as a co-adsorbent, and the assembled dyad-sensitised photoanode achieved O₂ evolution using visible light (100 mW cm^-2, AM 1.5G, λ > 420 nm). An initial photocurrent of 140 μA cm^-2 was generated in aqueous electrolyte solution (pH 5.6) under an applied potential of +0.2 V vs. NHE. The production of O₂ has been confirmed by controlled potential electrolysis with a faradaic efficiency of 44%. This study demonstrates that metal-free dyes are suitable light absorbers in dyadic systems for the assembly of water oxidising photoanodes.

SUBMITTER: Anton-Garcia D

PROVIDER: S-EPMC8163027 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Polyaniline-Layered Rutile TiO2 Nanorods as Alternative Photoanode in Dye-Sensitized Solar Cells.

Project description:In this paper, dye-sensitized solar cell (DSSC) performance of the less explored polymorph of TiO2, rutile, has been explored, and its performance has been modified with polyaniline (PANI) wrapping on the surface. For this purpose, highly crystalline rutile nanorods have been synthesized without any growth-directing substrates, employing a hydrothermal treatment. Further, to understand the phase composition and morphology, the synthesized nanorods and PANI-layered nanorods have been characterized through various physicochemical methods. The synthesized rods were implemented as photoanode material for DSSCs which exhibited a photoelectric conversion efficiency (PCE) of 4.28% with a high open-circuit voltage (V OC) of 0.84 V which is highly superior to DSSC with Degussa P25 (PCE = 3.95%) TiO2 nanoparticles. The resultant PCE of the nanorods was further enhanced to 6.23% on in situ deposition of PANI which acts as an electron-transporting layer. Introduction of conducting PANI over the rutile rod was explored as a new concept to improve the performance of photoanode material besides conventional TiCl4 treatment or scattering layer deposition.

| S-EPMC6647995 | biostudies-literature

A photoanode with hierarchical nanoforest TiO2 structure and silver plasmonic nanoparticles for flexible dye sensitized solar cell.

Project description:Due to unique photovoltaic properties, the nanostructured morphologies of TiO2 on flexible substrate have been studied extensively in the recent years for applications in dye sensitized solar cells (DSSCs). Microstructured electrode materials with high surface area can facilitate rapid charge transport and thus improve the light-to-current conversion efficiency. Herein we present an improved photoanode with forest like photoactive TiO2 hierarchical microstructure using a simple and facile hydrothermal route. To utilize the surface plasmon resonance (SPR) and hence increase the photon conversion efficiency, a plasmonic nanoparticle Ag has also been deposited using a very feasible photoreduction method. The branched structure of the photoanode increases the dye loading by filling the space between the nanowires, whereas Ag nanoparticles play the multiple roles of dye absorption and light scattering to increase the light-to-current conversion efficiency of the device. The branched structure provides a suitable matrix for the subsequent Ag deposition. They improve the charge collection efficiency by providing the preferential electron pathways. The high-density Ag nanoparticles deposited on the forest like structure also decrease the charge recombination and therefore improve the photovoltaic efficiency of the cells. As a result, the DSSC based on this novel photoanode shows remarkably higher photon conversion efficiency (ηmax = 4.0% and ηopt = 3.15%) compared to the device based on pristine nanowire or forest-like TiO2 structure. The flexibility of the device showed sustainable and efficient performance of the microcells.

| S-EPMC8024298 | biostudies-literature

Design of blueberry anthocyanin/TiO2 composite layer-based photoanode and N-doped porous blueberry-derived carbon-loaded Ni nanoparticle-based counter electrode for dye-sensitized solar cells.

Project description:P25/PBP (TiO2, anthocyanins) prepared by combining PBP (blueberry peels) with P25, and N-doped porous carbon-supported Ni nanoparticles (Ni@NPC-X) prepared using blueberry-derived carbon were used for the application as photoanode and the counter electrode, respectively, in dye-sensitized solar cells (DSSCs) to create a new perspective for blueberry-based photo-powered energy systems. PBP was introduced into the P25 photoanode and carbonized to form a C-like structure after annealing that improved its adsorption capacity for N719 dye, contributing a 17.3% higher power conversion efficiency (PCE) of P25/PBP-Pt (5.82%) than that of P25-Pt (4.96%). The structure of the porous carbon changes from a flat surface to a petal-like structure due to the N doping by melamine, and the specific surface area increases. N-doped three-dimensional porous carbon supported the loading and reduced the agglomeration of Ni nanoparticles, reducing the charge transfer resistance, and providing a fast electron transfer path. The doping of Ni and N on the porous carbon worked synergistically to enhance the electrocatalytic activity of the Ni@NPC-X electrode. The PCE of the DSSCs assembled by Ni@NPC-1.5 and P25/PBP was 4.86%. Also, the Ni@NPC-1.5 electrode exhibited 116.12 F g-1 and a capacitance retention rate of 98.2% (10 000 cycles), further confirming good electrocatalysis and cycle stability.

| S-EPMC9987179 | biostudies-literature

Visible light-driven water oxidation using a covalently-linked molecular catalyst-sensitizer dyad assembled on a TiO2 electrode.

Project description:The combination of porphyrin as a sensitizer and a ruthenium complex as a water oxidation catalyst (WOC) is promising to exploit highly efficient molecular artificial photosynthetic systems. A covalently-linked ruthenium-based WOC-zinc porphyrin (ZnP) sensitizer dyad was assembled on a TiO2 electrode for visible-light driven water oxidation. The water oxidation activity was found to be improved in comparison to the reference systems with the simple combination of the individual WOC and ZnP as well as with ZnP solely, demonstrating the advantage of the covalent linking approach over the non-covalent one. More importantly, via vectorial multi-step electron transfer triggered by visible light, the dye-sensitized photoelectrochemical cell (DSPEC) achieved a broader PEC response in the visible region than DSPECs with conventional ruthenium-based sensitizers. Initial incident photon-to-current efficiencies of 18% at 424 nm and 6.4% at 564 nm were attained under monochromatic illumination and an external bias of -0.2 V vs. NHE. Fast electron transfer from the WOC to the photogenerated radical cation of the sensitizer through the covalent linkage may suppress undesirable charge recombination, realizing the moderate performance of water oxidation. X-ray photoelectron spectroscopic analysis of the photoanodes before and after the DSPEC operation suggested that most of the ruthenium species exist at higher oxidation states, implying that the insufficient oxidation potential of the ZnP moiety for further oxidizing the intermediate ruthenium species at the photoanode is at least the bottleneck of the system.

| S-EPMC5975926 | biostudies-literature

Charge Transport Enhancement in BiVO4 Photoanode for Efficient Solar Water Oxidation.

Project description:Photoelectrochemical (PEC) water splitting in a pH-neutral electrolyte has attracted more and more attention in the field of sustainable energy. Bismuth vanadate (BiVO4) is a highly promising photoanode material for PEC water splitting. Additionally, cobaltous phosphate (CoPi) is a material that can be synthesized from Earth's rich materials and operates stably in pH-neutral conditions. Herein, we propose a strategy to enhance the charge transport ability and improve PEC performance by electrodepositing the in situ synthesis of a CoPi layer on the BiVO4. With the CoPi co-catalyst, the water oxidation reaction can be accelerated and charge recombination centers are effectively passivated on BiVO4. The BiVO4/CoPi photoanode shows a significantly enhanced photocurrent density (Jph) and applied bias photon-to-current efficiency (ABPE), which are 1.8 and 3.2 times higher than those of a single BiVO4 layer, respectively. Finally, the FTO/BiVO4/CoPi photoanode displays a photocurrent density of 1.39 mA cm-2 at 1.23 VRHE, an onset potential (Von) of 0.30 VRHE, and an ABPE of 0.45%, paving a potential path for future hydrogen evolution by solar-driven water splitting.

| S-EPMC10180425 | biostudies-literature

Efficient photoelectrochemical water oxidation using a TiO2 nanosphere-decorated BiVO4 heterojunction photoanode.

Project description:Constructing heterojunctions by coupling dissimilar semiconductors is a promising approach to boost charge separation and charge transfer in photoelectrochemical (PEC) water splitting. In this work, we fabricated a highly efficient TiO2/BiVO4 heterojunction photoanode for PEC water oxidation via a simple hydrothermal method. The resulting heterojunction photoanodes show enhanced PEC performance compared to the bare BiVO4 due to the simultaneous improvements in charge separation and charge transfer. Under simulated sunlight illumination (AM 1.5G, 100 mW cm-2), a high photocurrent of 3.3 mA cm-2 was obtained at 1.23 V (vs. the reversible hydrogen electrode (RHE)) in a neutral solution, which exceeds those attained by the previously reported TiO2/BiVO4 heterojunctions. When a molecular Co-cubane catalyst was immobilized onto the electrode, the performance of the TiO2/BiVO4 heterojunction photoanode can be further improved, achieving a higher photocurrent density of 4.6 mA cm-2 at 1.23 V, an almost three-fold enhancement over that of the bare BiVO4. These results engender a promising route to designing an efficient photoelectrode for PEC water splitting.

| S-EPMC9091981 | biostudies-literature

A silicon photoanode protected with TiO2/stainless steel bilayer stack for solar seawater splitting.

Project description:Photoelectrochemical seawater splitting is a promising route for direct utilization of solar energy and abundant seawater resources for H2 production. However, the complex salinity composition in seawater results in intractable challenges for photoelectrodes. This paper describes the fabrication of a bilayer stack consisting of stainless steel and TiO2 as a cocatalyst and protective layer for Si photoanode. The chromium-incorporated NiFe (oxy)hydroxide converted from stainless steel film serves as a protective cocatalyst for efficient oxygen evolution and retarding the adsorption of corrosive ions from seawater, while the TiO2 is capable of avoiding the plasma damage of the surface layer of Si photoanode during the sputtering of stainless steel catalysts. By implementing this approach, the TiO2 layer effectively shields the vulnerable semiconductor photoelectrode from the harsh plasma sputtering conditions in stainless steel coating, preventing surface damages. Finally, the Si photoanode with the bilayer stack inhibits the adsorption of chloride and realizes 167 h stability in chloride-containing alkaline electrolytes. Furthermore, this photoanode also demonstrates stable performance under alkaline natural seawater for over 50 h with an applied bias photon-to-current efficiency of 2.62%.

| S-EPMC10998903 | biostudies-literature

Fabrication of TiO2 on porous g-C3N4 by ALD for improved solar-driven hydrogen evolution.

Project description:Porous graphitic carbon nitride (P-g-C3N4) thin sheets were fabricated by a one-step calcination of a mixture of urea, melamine, and ammonia chloride at 550 °C. P-g-C3N4 showed 48% higher photocatalytic H2 production from methanol aqueous solution than conventional urea-derived graphitic carbon nitride (g-C3N4) because the existence of numerous pores reduces the recombination rate of charge carriers. In order to further enhance the photocatalytic activity, TiO2 was uniformly deposited on P-g-C3N4 by 60-300 cycles of atomic layer deposition (ALD) to form the TiO2@P-g-C3N4 composite. They exhibited much higher photocatalytic hydrogen production rates than both TiO2 and P-g-C3N4. Among all composites, the sample deposited with 180 ALD cycles of TiO2 showed the highest H2 production because of optimal diffusion length for electrons and holes. It also performed better than the sample of g-C3N4 deposited with 180 cycles of TiO2.

| S-EPMC9085477 | biostudies-literature

Hydrogen-doped Brookite TiO2 Nanobullets Array as a Novel Photoanode for Efficient Solar Water Splitting.

Project description:As a representative photocatalyst for photoelectrochemical solar water splitting, TiO2 has been intensively studied but most researches have focused on the rutile and anatsase phases because brookite, another important crystalline polymorph of TiO2, rarely exists in nature and is difficult to synthesize. In this work, hydrogen doped brookite (H:brookite) nanobullet arrays were synthesized via a well-designed solution reaction for the first time. H:brookite shows highly improved PEC properties with excellent stability, enhanced photocurrent, and significantly high Faradaic efficiency for overall solar water splitting. To support the experimental data, ab initio density functional theory calculations were also conducted. At the interstitial doping site that has minimum formation energy, the hydrogen atoms act as shallow donors and exist as H+. which has the minimum formation energy among three states of hydrogen (H+. H0, and H-). The calculated density of states of H:brookite shows a narrowed bandgap and an increased electron density compared to the pristine brookite. The combined experimental and theoretical results provide frameworks for the exploration of the PEC properties of doped brookite and extend our knowledge regarding the undiscovered properties of brookite of TiO2.

| S-EPMC5080591 | biostudies-literature

Hierarchically Porous, Biphasic, and C-Doped TiO2 for Solar Photocatalytic Degradation of Dyes and Selective Oxidation of Benzyl Alcohol.

Project description:Macroporous TiO2 monoliths were synthesized by self-sustained combustion reactions of molded pellets made up of a mixture of TiCl4 as a precursor, urea as a fuel, ammonium nitrate as an oxidizer, and starch as a binder. The porous TiO2 monoliths were found to be a heterostructure of anatase and rutile phases, in addition to being doped with carbon. Variation in the amount of starch yielded porous monoliths of different anatase-rutile ratios (increasing rutile component from 0 to 40%) but comparable Brunauer-Emmett-Teller (BET) surface area (∼30 m2 g-1). The porous monoliths obtained, where the TiCl4/starch mass ratio was 2.17, exhibit exceptional photocatalytic activity in the degradation of dyes (methylene blue and methyl orange) and selective oxidation of benzyl alcohol to benzaldehyde under natural sunlight. The synergistic combination of high surface area, porous network, lowered band gap due to heterostructured anatase-rutile polymorphs, and the presence of doped carbon renders the macroporous TiO2 an efficient photocatalyst.

| S-EPMC8154131 | biostudies-literature