Data of resistance to the compression of restorative dental materials.
Ontology highlight
ABSTRACT:
SUBMITTER: Diaz-Caballero A
PROVIDER: S-EPMC6660634 | biostudies-literature | 2019 Apr
REPOSITORIES: biostudies-literature
Publications
Data of resistance to the compression of restorative dental materials.
Díaz-Caballero Antonio A Tarón-Dunoyer Arnulfo A Martínez-Martínez Adel A
Data in brief 20190306
This article contains data related to the research article titled "Compressive strength of glass ionomer and composite resin. In vitro study" (Blanco et al., 2017). The presented data gives information about the compressive strength of two restorative materials (Tetric N-Ceram<sup>®</sup> resin and Vitremer TM<sup>®</sup> resin) in class I cavities in birradicular premolars. The dental organs were subjected to a compressive vertical force at different deeps of cavities preparation until obtain f ...[more]
Similar Datasets
Project description:Resin-based composites are widely used as dental restorative materials due to their excellent properties. They must have high modulus, high hardness, and be chemically inert while minimizing moisture uptake. To fulfill these higher standard prerequisites and properties, continuous improvements in each of their components are required. This study develops novel composites with multiple biofunctions. Light-cured Bis-GMA/TEGDMA dental resin (RK)/layered double hydroxide intercalated with fluoride ions (LDH-F)/calcium bentonite (Bt) hybrid composites were prepared. The loading ratio of LDH-F to Bt was varied, ranging from 2.5/2.5 to 10/10 parts per hundred RK and structural, mechanical, and biological properties were studied. The incorporation of even small mass fractions (e.g., 2.5 wt % of LDH-F and 2.5 wt % of Bt) in RK dental resin significantly improved the mechanical properties of the pristine resin. The synthetized materials showed antibacterial and antibiofilm effects against three bacterial strains isolated from healthy volunteers' saliva (Streptococcus spp., Bacteroides fragilis, and Staphylococcus epidermidis) without affecting its ability to induce dental pulp stem cells differentiation into odontoblast-like cells. The capability to balance between the antibiofilm activity and dental pulp stem cells differentiation in addition with improved mechanical properties make these materials a promising strategy in preventive and restorative dentistry.
| S-EPMC7077377 | biostudies-literature
Project description:A great number of different types of materials have been used in dentistry as intermediate restoratives. Among them, new resin-based bases have been released in the dental market. The present study focuses on the identification of the organic eluates released from such materials and the study of their surface microstructure in combination with their corresponding elemental composition. For this purpose, the following materials were used:ACTIVA™BioACTIVE-BASE/LINER™, Ketac™Bond Glass Ionomer, SDR™ and Vitrebond™Light Cure Glass Ionomer Liner/Base. Methanolic leachates derived from polymerized materials were analyzed by means of gas chromatography-mass spectrometry (GC-MS). Scanning electron microscopy(SEM) was used for the surface monitoring of suitably prepared specimens. The GC-MS analysis revealed the elution of twenty different substances from the three resin-based materials, while none was eluted from the glass ionomer base. The SEM analysis for Vitrebond™ presented small pits, the one for Ketac™Bond presented elongated cracks, while no voids were present for ACTIVA™BioACTIVE-BASE/LINER™ and SDR™. Moreover, the resin matrix of some dental materials may inhibit elements' accumulation on the surface layers. Particularly, the detected organic eluents may be related to potential toxic effects.
| S-EPMC7180687 | biostudies-literature
Project description:Step-growth thiol-Michael photopolymerizable resins, constituting an alternative chemistry to the current methacrylate-based chain-growth polymerizations, were developed and evaluated for use as dental restorative materials. The beneficial features inherent to anion-mediated thiol-Michael polymerizations were explored, such as rapid photocuring, low stress generation, ester content tunability, and improved mechanical performance in a moist environment. An ester-free tetrafunctional thiol and a ultraviolet-sensitive photobase generator were implemented to facilitate thiol-Michael photopolymerization. Thiol-Michael resins of varied ester content were fabricated under suitable light activation. Polymerization kinetics and shrinkage stress were determined with Fourier-transform infrared spectroscopy coupled with tensometery measurements. Thermomechanical properties of new materials were evaluated by dynamic mechanical analysis and in 3-point bending stress-strain experiments. Photopolymerization kinetics, polymerization shrinkage stress, glass transition temperature, flexural modulus, flexural toughness, and water sorption/solubility were compared between different thiol-Michael systems and the BisGMA/TEGDMA control. Furthermore, the mechanical performance of 2 thiol-Michael composites and a control composite were compared before and after extensive conditioning in water. All photobase-catalyzed thiol-Michael polymerization matrices achieved >90% conversion with a dramatic reduction in shrinkage stress as compared with the unfilled dimethacrylate control. One prototype of ester-free thiol-Michael formulations had significantly better water uptake properties than the BisGMA/TEGDMA control system. Although exhibiting relatively lower Young's modulus and glass transition temperatures, highly uniform thiol-Michael materials achieved much higher toughness than the BisGMA/TEGDMA control. Moreover, low-ester thiol-Michael composite systems show stable mechanical performance even after extensive water treatment. Although further resin/curing methodology optimization is required, the photopolymerized thiol-Michael prototype resins can now be recognized as promising candidates for implementation in composite dental restorative materials.
| S-EPMC5958372 | biostudies-literature
Project description:OBJECTIVE:The edge chipping test was used to measure the fracture resistance of CAD/CAM dental restoration ceramics and resin composites. METHODS:An edge chipping machine was used to evaluate six materials including one feldspathic porcelain, two glass ceramics, a filled resin-composite, a yttria-stabilized zirconia, and a new ceramic-resin composite material. Force versus edge distance data were collected over a broad range of forces and distances. Data were analyzed by several approaches and several chipping resistance parameters were evaluated. The effects of using different indenter types were explored. RESULTS:The force versus distance trends were usually nonlinear with good fits to a power law equation with exponents usually ranging from 1.2 to 1.9. The order of chipping resistance (from least to greatest) was: feldspathic porcelain and a leucite glass ceramic (which were similar), followed by the lithium disilicate glass ceramic and the two resin composites (which were similar), and finally the zirconia which had the greatest resistance to chipping. Chipping with a Vickers indenter required 28-45% more force than with the sharp conical 120° indenter. The two indenters rank materials approximately the same way. The power law exponents were very similar for the two indenters for a particular material, but the exponents varied with material. The Rockwell C indenter gives different power law trends and rankings. SIGNIFICANCE:Despite the variations in the trends and indenters, simple comparisons between materials can be made by chipping with sharp conical 120° or Vickers indenters at 0.50mm. Broad distance ranges are recommended for trend evaluation.
| S-EPMC4100685 | biostudies-literature
Project description:A methyl methacrylate (MMA) -based resin cement is one of the popular luting agents to bond a dental restorative material in dental treatments. Bond strength of the MMA-based resin cement with adhesive primer to each restorative material is important for clinical success in prosthodontic treatments without debonding or fracture failures of the restoration such as a dental crown and post. However, open data on the bonding properties of combined use of the MMA-based resin cement and appropriate primers is limited. This article provides data on the bond strength and fracture mode of the 4-META/MMA-TBB resin cement (MMA-based resin cement) to the restorative materials (silver alloy, gold alloy, feldspathic porcelain, and zirconia) with four types of primer. Each restorative material was applied with the adhesive primer and bonded with the MMA-based resin cement. The cement-bonded samples were subjected to a thermocycling in which the materials were immersed alternately in water baths at 5 °C and 55 °C for 10,000 cycles. The bond strength between the resin cement and each restorative material was measured by means of a conventional tensile bond strength test. The fracture modes of the examined samples were observed and determined. The measured tensile bond strengths were statistically analysed using one-way analysis of variance (ANOVA), followed by Tukey's multiple comparison test.
| S-EPMC7586068 | biostudies-literature
Project description:ObjectivesTo test the hypotheses that (a) the chairside/handheld dental scanner combined with a metrology software will measure clinical wear in vivo in agreement with measurements from X-ray computed microtomography and; (b) polished monolithic zirconia does not cause accelerated wear of opposing enamel.Materials and methodsThirty single crowns were randomized to receive a monolithic zirconia or metal-ceramic crown. Two non-restored opposing teeth in the same quadrants were identified to serve as enamel controls. After cementation, quadrants were scanned using an intraoral dental scanner. Patients were recalled at 6-months and 1-year for re-scanning. Scanned images were compared using a metrology software to determine maximum vertical wear of teeth. The accuracy of the scanning measurements from this new method was compared with X-ray computed microtomography (micro-CT) measurements. Statistical analysis was performed using Mann-Whitney U test to determine significant differences between wear of enamel against zirconia, metal-ceramic or enamel. Linear regression analysis determined agreement between measurements obtained using intraoral scanning and micro-CT.ResultsRegression analysis demonstrated that there is a quantitative agreement between depth and volume measurements produced using intraoral scanning and the micro-CT methodologies. There was no significant difference between the wear of enamel against polished monolithic zirconia crowns and enamel against enamel.ConclusionsIntraoral scanning combined with a matching software can accurately quantify clinical wear to verify that monolithic zirconia exhibited comparable wear of enamel compared with metal-ceramic crowns and control enamel. Agreement between the intraoral scanner and the micro-CT was 99.8%. Clinical Trials.gov NCT02289781.
| S-EPMC7745065 | biostudies-literature
Project description:UnlabelledThe edge chipping resistances of six CAD/CAM dental restoration materials are analyzed and correlated to other mechanical properties. A new quadratic relationship that is based on a phenomenological model is presented.ObjectiveThe purpose of this study was to further analyze the edge chipping resistance of the brittle materials evaluated in Part 1. One objective was to determine why some force-distance trends were linear and others were nonlinear. A second objective was to account for differences in chipping resistance with indenter type.MethodsEdge chipping experiments were conducted with different indenters, including some custom-made sharp conical indenters. A new force - distance quadratic expression was correlated to the data and compared to the linear and power law trends.ResultsThe new quadratic function was an excellent fit in every instance. It can account for why some materials can be fit by a linear trend, while others can be fit by the power law trend. The effects of indenter type are accounted for variations in crack initiation and by the wedging stresses once an indentation hole is created.SignificanceThe new quadratic force - edge distance function can be used with edge chipping data for all brittle materials, not just those evaluated in this study. The data trends vary from linear to nonlinear depending upon the material's hardness, fracture toughness, and elastic modulus.
| S-EPMC4154344 | biostudies-literature
Project description:Oral biofilms attach onto both teeth surfaces and dental material surfaces in oral cavities. In the meantime, oral biofilms are not only the pathogenesis of dental caries and periodontitis, but also secondary caries and peri-implantitis, which would lead to the failure of clinical treatments. The material surfaces exposed to oral conditions can influence pellicle coating, initial bacterial adhesion, and biofilm formation, due to their specific physical and chemical characteristics. To define the effect of physical and chemical characteristics of dental prosthesis and restorative material on oral biofilms, we discuss resin-based composites, glass ionomer cements, amalgams, dental alloys, ceramic, and dental implant material surface properties. In conclusion, each particular chemical composition (organic matrix, inorganic filler, fluoride, and various metallic ions) can enhance or inhibit biofilm formation. Irregular topography and rough surfaces provide favorable interface for bacterial colonization, protecting bacteria against shear forces during their initial reversible binding and biofilm formation. Moreover, the surface free energy, hydrophobicity, and surface-coating techniques, also have a significant influence on oral biofilms. However, controversies still exist in the current research for the different methods and models applied. In addition, more in situ studies are needed to clarify the role and mechanism of each surface parameter on oral biofilm development.
| S-EPMC6213966 | biostudies-other
Project description:Polymeric materials are the first choice for restoring tooth cavities, bonding tooth-colored fillings, sealing root canal systems, and many other dental restorative applications. However, polymeric materials are highly susceptible to bacterial attachment and colonization, leading to dental diseases. Many approaches have been investigated to minimize the formation of biofilms over polymeric restorative materials and at the tooth/material interfaces. Among them, contact-killing compounds have shown promising results to inhibit dental biofilms. Contact-killing compounds can be immobilized within the polymer structure, delivering a long-lasting effect with no leaching or release, thus providing advantages compared to release-based materials. This review discusses cutting-edge research on the development of contact-killing compounds in dental restorative materials to target oral pathogens. Contact-killing compounds in resin composite restorations, dental adhesives, root canal sealers, denture-based materials, and crown cements have all demonstrated promising antibacterial properties. Contact-killing restorative materials have been found to effectively inhibit the growth and activities of several oral pathogens related to dental caries, periodontal diseases, endodontic, and fungal infections. Further laboratory optimization and clinical trials using translational models are needed to confirm the clinical applicability of this new generation of contact-killing dental restorative materials.
| S-EPMC7552663 | biostudies-literature
Project description:Tooth decay is prevalent, and secondary caries causes restoration failures, both of which are related to demineralization. There is an urgent need to develop new therapeutic materials with remineralization functions. This article represents the first review on the cutting edge research of poly(amido amine) (PAMAM) in combination with nanoparticles of amorphous calcium phosphate (NACP). PAMAM was excellent nucleation template, and could absorb calcium (Ca) and phosphate (P) ions via its functional groups to activate remineralization. NACP composite and adhesive showed acid-neutralization and Ca and P ion release capabilities. PAMAM+NACP together showed synergistic effects and produced triple benefits: excellent nucleation templates, superior acid-neutralization, and ions release. Therefore, the PAMAM+NACP strategy possessed much greater remineralization capacity than using PAMAM or NACP alone. PAMAM+NACP achieved dentin remineralization even in an acidic solution without any initial Ca and P ions. Besides, the long-term remineralization capability of PAMAM+NACP was established. After prolonged fluid challenge, the immersed PAMAM with the recharged NACP still induced effective dentin mineral regeneration. Furthermore, the hardness of pre-demineralized dentin was increased back to that of healthy dentin, indicating a complete remineralization. Therefore, the novel PAMAM+NACP approach is promising to provide long-term therapeutic effects including tooth remineralization, hardness increase, and caries-inhibition capabilities.
| S-EPMC6506538 | biostudies-literature