Multifunctional Bioactive Resin for Dental Restorative Materials.

ABSTRACT: Resin-based composites are widely used as dental restorative materials due to their excellent properties. They must have high modulus, high hardness, and be chemically inert while minimizing moisture uptake. To fulfill these higher standard prerequisites and properties, continuous improvements in each of their components are required. This study develops novel composites with multiple biofunctions. Light-cured Bis-GMA/TEGDMA dental resin (RK)/layered double hydroxide intercalated with fluoride ions (LDH-F)/calcium bentonite (Bt) hybrid composites were prepared. The loading ratio of LDH-F to Bt was varied, ranging from 2.5/2.5 to 10/10 parts per hundred RK and structural, mechanical, and biological properties were studied. The incorporation of even small mass fractions (e.g., 2.5 wt % of LDH-F and 2.5 wt % of Bt) in RK dental resin significantly improved the mechanical properties of the pristine resin. The synthetized materials showed antibacterial and antibiofilm effects against three bacterial strains isolated from healthy volunteers' saliva (Streptococcus spp., Bacteroides fragilis, and Staphylococcus epidermidis) without affecting its ability to induce dental pulp stem cells differentiation into odontoblast-like cells. The capability to balance between the antibiofilm activity and dental pulp stem cells differentiation in addition with improved mechanical properties make these materials a promising strategy in preventive and restorative dentistry.

SUBMITTER: Tammaro L

PROVIDER: S-EPMC7077377 | biostudies-literature | 2020 Feb

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Multifunctional Bioactive Resin for Dental Restorative Materials.

Tammaro Loredana L Salle Anna Di AD Calarco Anna A Luca Ilenia De I Riccitiello Francesco F Peluso Gianfranco G Vittoria Vittoria V Sorrentino Andrea A

Polymers 20200205 2

Resin-based composites are widely used as dental restorative materials due to their excellent properties. They must have high modulus, high hardness, and be chemically inert while minimizing moisture uptake. To fulfill these higher standard prerequisites and properties, continuous improvements in each of their components are required. This study develops novel composites with multiple biofunctions. Light-cured Bis-GMA/TEGDMA dental resin (RK)/layered double hydroxide intercalated with fluoride i ...[more]

PMID: 32033310

Similar Datasets

Project description:Step-growth thiol-Michael photopolymerizable resins, constituting an alternative chemistry to the current methacrylate-based chain-growth polymerizations, were developed and evaluated for use as dental restorative materials. The beneficial features inherent to anion-mediated thiol-Michael polymerizations were explored, such as rapid photocuring, low stress generation, ester content tunability, and improved mechanical performance in a moist environment. An ester-free tetrafunctional thiol and a ultraviolet-sensitive photobase generator were implemented to facilitate thiol-Michael photopolymerization. Thiol-Michael resins of varied ester content were fabricated under suitable light activation. Polymerization kinetics and shrinkage stress were determined with Fourier-transform infrared spectroscopy coupled with tensometery measurements. Thermomechanical properties of new materials were evaluated by dynamic mechanical analysis and in 3-point bending stress-strain experiments. Photopolymerization kinetics, polymerization shrinkage stress, glass transition temperature, flexural modulus, flexural toughness, and water sorption/solubility were compared between different thiol-Michael systems and the BisGMA/TEGDMA control. Furthermore, the mechanical performance of 2 thiol-Michael composites and a control composite were compared before and after extensive conditioning in water. All photobase-catalyzed thiol-Michael polymerization matrices achieved >90% conversion with a dramatic reduction in shrinkage stress as compared with the unfilled dimethacrylate control. One prototype of ester-free thiol-Michael formulations had significantly better water uptake properties than the BisGMA/TEGDMA control system. Although exhibiting relatively lower Young's modulus and glass transition temperatures, highly uniform thiol-Michael materials achieved much higher toughness than the BisGMA/TEGDMA control. Moreover, low-ester thiol-Michael composite systems show stable mechanical performance even after extensive water treatment. Although further resin/curing methodology optimization is required, the photopolymerized thiol-Michael prototype resins can now be recognized as promising candidates for implementation in composite dental restorative materials.

Dataset Information

Multifunctional Bioactive Resin for Dental Restorative Materials.

Publications

Multifunctional Bioactive Resin for Dental Restorative Materials.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets