Planar Heterojunction Solar Cell Employing a Single-Source Precursor Solution-Processed Sb2S3 Thin Film as the Light Absorber.

ABSTRACT: We discuss here a solution-processed thin film of antimony trisulphide (Sb2S3; band gap ? 1.7 eV; electronic configuration: ns2np0) for applications in planar heterojunction (PHJ) solar cells. An alternative solution processing method involving a single-metal organic precursor, viz., metal-butyldithiocarbamic acid complex, is used to grow the thin films of Sb2S3. Because of excess sulphide in the metal complex, the formation of any oxide is nearly retarded. Sb2S3 additionally displays structural anisotropy with a ribbon-like structure along the [001] direction. These ribbon-like structures, if optimally oriented with respect to the electron transport layer (ETL)/glass substrate, can be beneficial for light-harvesting and charge-transport properties. A PHJ solar cell is fabricated comprising Sb2S3 as the light absorber and CdS as an ETL coated on to FTO. With varying film sintering temperature and thickness, the typical ribbon-like structures predominantly with planes hkl: l = 0 stacked horizontally along with respect to CdS/FTO are obtained. The morphology of the films is observed to be a function of the sintering temperature, with higher sintering temperatures yielding compact and smooth films with large-sized grains. Maximum photon to electricity efficiency of 2.38 is obtained for PHJ solar cells comprising 480 nm thick films of Sb2S3 sintered at 350 °C having a grain size of few micrometers (>5 ?m). The study convincingly shows that improper grain orientation, which may lead to nonoptimal alignments of the intrinsic structure with regard to the ETL/glass substrate, is not the sole parameter for determining photovoltaics performance. Other solution-processing parameters can still be suitably chosen to generate films with optimum morphology, leading to high photon to electricity efficiency.

SUBMITTER: Tamilselvan M

PROVIDER: S-EPMC6682112 | biostudies-literature | 2019 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Planar Heterojunction Solar Cell Employing a Single-Source Precursor Solution-Processed Sb2S3 Thin Film as the Light Absorber.

Tamilselvan Muthusamy M Byregowda Archana A Su Ching-Yuan CY Tseng Chung-Jen CJ Bhattacharyya Aninda J AJ

ACS omega 20190701 7

We discuss here a solution-processed thin film of antimony trisulphide (Sb2S3; band gap ≈ 1.7 eV; electronic configuration: ns2np0) for applications in planar heterojunction (PHJ) solar cells. An alternative solution processing method involving a single-metal organic precursor, viz., metal-butyldithiocarbamic acid complex, is used to grow the thin films of Sb2S3. Because of excess sulphide in the metal complex, the formation of an ...[more]

PMID: 31460242

Similar Datasets

Project description:Large-scale commercial synthesis of bulk-heterojunction (BHJ) solar cell materials is very challenging and both time and energy consuming. Synthesis of π-conjugated polymers (CPs) with uniform batch-to-batch molecular weight and low dispersity is a key requirement for better reproducibility of high-efficiency polymer solar cells. Herein, a conjugated polymer (CP) PTB7-Th, well known for its high performance, has been synthesized with high molecular weight and low dispersity in a closed microwave reactor. The microwave reaction procedure is known to be more controlled and consumes less energy. The precursors were strategically reacted for different reaction time durations to obtain the optimum molecular weight. All different CPs were well characterized using 1H NMR, gel permeation chromatography (GPC), UV-vis, photoluminescence (PL), electron spin resonance (ESR), and Raman spectroscopy, whereas the film morphology was extensively studied via atomic force microscopy (AFM) and grazing incidence X-ray diffraction (GIXRD) techniques. The effect of molecular weight on a conventional BHJ solar cell with PC71BM acceptor was investigated to derive systematic structure-property relationships. The CP obtained after 35 min of reaction time and integrated into BHJ devices under ambient conditions provided the best performance with a power conversion efficiency (PCE) of 8.09%, which was quite similar to the results of CPs synthesized via a thermal route. An enhanced PCE of 8.47% was obtained for the optimized polymer (35 min microwave reaction product) when device fabrication was carried out inside a glovebox. The organic thin-film transistor (OTFT) device with the microwave-synthesized CP displayed better hole mobility (0.137 cm2 V-1 s-1) as compared to that with the thermally synthesized CP. This study also proved that the device stability and reproducibility of the microwave-synthesized CP were much better and more consistent than those of the thermally developed CP.

Dataset Information

Planar Heterojunction Solar Cell Employing a Single-Source Precursor Solution-Processed Sb2S3 Thin Film as the Light Absorber.

Publications

Planar Heterojunction Solar Cell Employing a Single-Source Precursor Solution-Processed Sb<sub>2</sub>S<sub>3</sub> Thin Film as the Light Absorber.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets