Upcycling of polyurethane waste by mechanochemistry: synthesis of N-doped porous carbon materials for supercapacitor applications.

ABSTRACT: We developed an upcycling process of polyurethane obtaining porous nitrogen-doped carbon materials that were applied in supercapacitor electrodes. In detail, a mechanochemical solvent-free one-pot synthesis is used and combined with a thermal treatment. Polyurethane is an ideal precursor already containing nitrogen in its backbone, yielding nitrogen-doped porous carbon materials with N content values of 1-8 wt %, high specific surface area values of up to 2150 m2·g-1 (at a N content of 1.6 wt %) and large pore volume values of up to 0.9 cm3·g-1. The materials were tested as electrodes for supercapacitors in aqueous 1 M Li2SO4 electrolyte (100 F·g-1), organic 1 M TEA-BF4 (ACN, 83 F·g-1) and EMIM-BF4 (70 F·g-1).

SUBMITTER: Schneidermann C

PROVIDER: S-EPMC6693373 | biostudies-literature | 2019

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Upcycling of polyurethane waste by mechanochemistry: synthesis of N-doped porous carbon materials for supercapacitor applications.

Schneidermann Christina C Otto Pascal P Leistenschneider Desirée D Grätz Sven S Eßbach Claudia C Borchardt Lars L

Beilstein journal of nanotechnology 20190806

We developed an upcycling process of polyurethane obtaining porous nitrogen-doped carbon materials that were applied in supercapacitor electrodes. In detail, a mechanochemical solvent-free one-pot synthesis is used and combined with a thermal treatment. Polyurethane is an ideal precursor already containing nitrogen in its backbone, yielding nitrogen-doped porous carbon materials with N content values of 1-8 wt %, high specific surface area values of up to 2150 m<sup>2</sup>·g<sup>-1</sup> (at a ...[more]

PMID: 31479505

Similar Datasets

Project description:Each year about 7.6 million tons of waste glasses are landfilled without recycling, reclaiming or upcycling. Herein we have developed a solvent free upcycling method for recycled glass waste (RG) by remanufacturing it into porous recycled glass microspheres (PRGMs) with a view to explore removal of organic pollutants such as organic dyes. PRGMs were prepared via flame spheroidisation process and characterised using Scanning Electron Microscopy (SEM), X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET) and Mercury Intrusion Porosimetry (MIP) analysis. PRGMs exhibited 69% porosity with overall pore volume and pore area of 0.84 cm3/g and 8.6 cm2/g, respectively (from MIP) and a surface area of 8 m2/g. Acid red 88 (AR88) and Methylene blue (MB) were explored as a model source of pollutants. Results showed that removal of AR88 and MB by PRGMs was influenced by pH of the dye solution, PRGMs doses, and dye concentrations. From the batch process experiments, adsorption and coagulation processes were observed for AR88 dye whilst MB dye removal was attributed only to adsorption process. The maximum monolayer adsorption capacity (qe) recorded for AR88, and MB were 78 mg/g and 20 mg/g, respectively. XPS and FTIR studies further confirmed that the adsorption process was due to electrostatic interaction and hydrogen bond formation. Furthermore, dye removal capacity of the PRGMs was also investigated for column adsorption process experiments. Based on the Thomas model, the calculated adsorption capacities at flow rates of 2.2 mL/min and 0.5 mL/min were 250 mg/g and 231 mg/g, respectively which were much higher than the batch scale Langmuir monolayer adsorption capacity (qe) values. It is suggested that a synergistic effect of adsorption/coagulation followed by filtration processes was responsible for the higher adsorption capacities observed from the column adsorption studies. This study also demonstrated that PRGMs produced from recycled glass waste could directly be applied to the next cyclic experiment with similar dye removal capability. Thus, highlighting the circular economy scope of using waste inorganic materials for alternate applications such as pre-screening materials in wastewater treatment applications.

Dataset Information

Upcycling of polyurethane waste by mechanochemistry: synthesis of N-doped porous carbon materials for supercapacitor applications.

Publications

Upcycling of polyurethane waste by mechanochemistry: synthesis of N-doped porous carbon materials for supercapacitor applications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets