Stiffening of graphene oxide films by soft porous sheets.

ABSTRACT: Graphene oxide (GO) sheets have been used as a model system to study how the mechanical properties of two-dimensional building blocks scale to their bulk form, such as paper-like, lamellar-structured thin films. Here, we report that the modulus of multilayer GO films can be significantly enhanced if some of the sheets are drastically weakened by introducing in-plane porosity. Nanometer-sized pores are introduced in GO sheets by chemical etching. Membrane-deflection measurements at the single-layer level show that the sheets are drastically weakened as the in-plane porosity increases. However, the mechanical properties of the corresponding multilayer films are much less sensitive to porosity. Surprisingly, the co-assembly of pristine and etched GO sheets yields even stiffer films than those made from pristine sheets alone. This is attributed to the more compliant nature of the soft porous sheets, which act as a binder to improve interlayer packing and load transfer in the multilayer films.

SUBMITTER: Mao L

PROVIDER: S-EPMC6695419 | biostudies-literature | 2019 Aug

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Stiffening of graphene oxide films by soft porous sheets.

Mao Lily L Park Hun H Soler-Crespo Rafael A RA Espinosa Horacio D HD Han Tae Hee TH Nguyen SonBinh T ST Huang Jiaxing J

Nature communications 20190815 1

Graphene oxide (GO) sheets have been used as a model system to study how the mechanical properties of two-dimensional building blocks scale to their bulk form, such as paper-like, lamellar-structured thin films. Here, we report that the modulus of multilayer GO films can be significantly enhanced if some of the sheets are drastically weakened by introducing in-plane porosity. Nanometer-sized pores are introduced in GO sheets by chemical etching. Membrane-deflection measurements at the single-lay ...[more]

PMID: 31417093

Similar Datasets

Laser-induced porous graphene films from commercial polymers.

Project description:The cost effective synthesis and patterning of carbon nanomaterials is a challenge in electronic and energy storage devices. Here we report a one-step, scalable approach for producing and patterning porous graphene films with three-dimensional networks from commercial polymer films using a CO2 infrared laser. The sp3-carbon atoms are photothermally converted to sp2-carbon atoms by pulsed laser irradiation. The resulting laser-induced graphene (LIG) exhibits high electrical conductivity. The LIG can be readily patterned to interdigitated electrodes for in-plane microsupercapacitors with specific capacitances of >4 mF cm-2 and power densities of ~9 mW cm-2. Theoretical calculations partially suggest that enhanced capacitance may result from LIG's unusual ultra-polycrystalline lattice of pentagon-heptagon structures. Combined with the advantage of one-step processing of LIG in air from commercial polymer sheets, which would allow the employment of a roll-to-roll manufacturing process, this technique provides a rapid route to polymer-written electronic and energy storage devices.

| S-EPMC4264682 | biostudies-literature

Hierarchical Porous Reduced Graphene Oxide/Poly(l-lactic acid) Fiber Films: The Influence of Recrystallization on Strength

Project description: Not available

| S-EPMC11209683 | biostudies-literature

Pressurized carbonization of mixed plastics into porous carbon sheets on magnesium oxide.

Project description:Conversion of waste thermoplastics into porous carbons has attracted wide attention due to the requirement of recycling of large quantities of municipal solid waste. This work reports the preparation of porous carbon sheets on magnesium oxide from mixed thermoplastics including polyethylene, polypropylene, polystyrene, polyvinyl chloride, and polyethylene terephthalate in a closed autoclave at 500 °C. The influence of the weight ratio of magnesium oxide to mixed plastics on the yield and textural properties of the carbon was examined. The morphology and structure of the porous carbon were also characterized. The maximum BET surface area was 713 m2 g-1 at a weight ratio of MgO/polymer of 4 and the maximum pore volume was 5.27 cm3 g-1 at a weight ratio of MgO/polymer of 6. The reaction mechanism was explored by analyzing the product distribution and composition of gas and liquid at different reaction times. Aromatics were the main source for the growth of carbon. Model experiments of carbonization of different aromatics were conducted to evaluate the carbonization reactivity of aromatics. Polycyclic aromatic hydrocarbons, especially acenes, produced more carbon.

| S-EPMC9077333 | biostudies-literature

Electron-Induced Perpendicular Graphene Sheets Embedded Porous Carbon Film for Flexible Touch Sensors.

Project description:Graphene-based materials on wearable electronics and bendable displays have received considerable attention for the mechanical flexibility, superior electrical conductivity, and high surface area, which are proved to be one of the most promising candidates of stretching and wearable sensors. However, polarized electric charges need to overcome the barrier of graphene sheets to cross over flakes to penetrate into the electrode, as the graphene planes are usually parallel to the electrode surface. By introducing electron-induced perpendicular graphene (EIPG) electrodes incorporated with a stretchable dielectric layer, a flexible and stretchable touch sensor with "in-sheet-charges-transportation" is developed to lower the resistance of carrier movement. The electrode was fabricated with porous nanostructured architecture design to enable wider variety of dielectric constants of only 50-μm-thick Ecoflex layer, leading to fast response time of only 66 ms, as well as high sensitivities of 0.13 kPa-1 below 0.1 kPa and 4.41 MPa-1 above 10 kPa, respectively. Moreover, the capacitance-decrease phenomenon of capacitive sensor is explored to exhibit an object recognition function in one pixel without any other integrated sensor. This not only suggests promising applications of the EIPG electrode in flexible touch sensors but also provides a strategy for internet of things security functions.

| S-EPMC7770710 | biostudies-literature

Graphene Oxide Sheets Combine into Conductive Coatings by Direct Oxidative Electropolymerization.

Project description:New coatings are obtained when graphene oxide is further oxidized at moderate anodic potentials (≤~1.3 V vs. Ag/AgCl). Based on a variety of spectroscopic and electrochemical observations, the coatings are attributed to the direct electropolymerization of graphene oxide sheets via oxidation of the phenol edge groups on graphene. Depending on the applied potential, ether or carboxylic groups are formed. The coatings obtained via further oxidation are characterized by a lower O/C ratio due to decarboxylation and a higher content of C=C bonds. These bonds extend aromatic conjugation into the combined graphene oxide sheets and are responsible for the highly conductive nature of these coatings.

| S-EPMC5504004 | biostudies-literature

Large and pristine films of reduced graphene oxide.

Project description:A new self-assembly concept is introduced to form large and pristine films (15 cm in diameter) of reduced graphene oxide (RGO). The resulting film has different degrees of polarity on its two different sides due to the characteristic nature of the self-assembly process. The RGO film can be easily transferred from a glass substrate onto water and a polymer substrate after injection of water molecules between the RGO film and glass substrate using an electric steamer. The RGO film can also be easily patterned into various shapes with a resolution of around ± 10 μm by a simple taping method, which is suitable for mass production of printed electronics at low cost.

| S-EPMC4686933 | biostudies-literature

Graphene oxide microstructure control of electrosprayed thin films.

Project description:The graphene oxide (GO) microstructure, in terms of flake distribution, folding, and crumpling, in thin films affects properties such as electrical conductivity and optical transparency after GO reduction. A thin film can be tailored to the user's application if the microstructure resulting from different deposition methods can be controlled. In this work, we compare the microstructures of GO coatings created through electrospray deposition (ESD) with random deposition processes. The comparisons include both MATLAB simulations and a dip coating process. The microstructure of ESD GO thin films can be altered by changing the distance between the nozzle and the substrate. We developed a semi-automatic image analysis script that analyzes scanning electron microscopy images to find effects of GO stacking or agglomeration, without the risk of human bias. A low nozzle to substrate distance creates structures of flat GO flakes, but solvent flooding the samples causes drying patterns. A high nozzle to substrate distance causes folding and crumpling of the GO flakes due to solvent evaporation, resulting in agglomerated GO on the substrate. For our ESD setup, a nozzle to substrate distance of 2-4 mm produced GO coatings with the lowest combined influence of drying effects and GO flake folding or crumpling.

| S-EPMC9809207 | biostudies-literature

Growth of Epitaxial Oxide Thin Films on Graphene.

Project description:The transfer process of graphene onto the surface of oxide substrates is well known. However, for many devices, we require high quality oxide thin films on the surface of graphene. This step is not understood. It is not clear why the oxide should adopt the epitaxy of the underlying oxide layer when it is deposited on graphene where there is no lattice match. To date there has been no explanation or suggestion of mechanisms which clarify this step. Here we show a mechanism, supported by first principles simulation and structural characterisation results, for the growth of oxide thin films on graphene. We describe the growth of epitaxial SrTiO3 (STO) thin films on a graphene and show that local defects in the graphene layer (e.g. grain boundaries) act as bridge-pillar spots that enable the epitaxial growth of STO thin films on the surface of the graphene layer. This study, and in particular the suggestion of a mechanism for epitaxial growth of oxides on graphene, offers new directions to exploit the development of oxide/graphene multilayer structures and devices.

| S-EPMC4981861 | biostudies-literature

Porous Aluminum Oxide and Magnesium Oxide Films Using Organic Hydrogels as Structure Matrices.

Project description:We describe the synthesis of mesoporous Al₂O₃ and MgO layers on silicon wafer substrates by using poly(dimethylacrylamide) hydrogels as porogenic matrices. Hydrogel films are prepared by spreading the polymer through spin-coating, followed by photo-cross-linking and anchoring to the substrate surface. The metal oxides are obtained by swelling the hydrogels in the respective metal nitrate solutions and subsequent thermal conversion. Combustion of the hydrogel results in mesoporous metal oxide layers with thicknesses in the μm range and high specific surface areas up to 558 m²∙g-1. Materials are characterized by SEM, FIB ablation, EDX, and Kr physisorption porosimetry.

| S-EPMC5923516 | biostudies-literature

Next-generation sequencing reveals size-dependent pulmonary impact of thin graphene oxide sheets in mice: towards safe-by-design

Project description:Safety assessment of graphene-based materials (GBMs) including graphene oxide (GO) is essential for their safe use across many sectors of society. In particular, the link between specific material properties and biological effects needs to be further elucidated. Here we compared the effects of lateral dimensions of GO sheets in acute and chronic pulmonary responses after single intranasal instillation in mice. Micrometre-sized GO (1–30 μm) induced stronger pulmonary inflammation than nanometre-sized GO, despite a reduced translocation to the lungs. Genome-wide RNA sequencing also revealed distinct size dependent effects of GO, in agreement with the histopathological results. Although large GO, but not the smallest GO (10–300 nm), triggered the formation of granulomas that persisted up to 90 days, no pulmonary fibrosis was observed. These results could be partly explained by the pattern of size-independent in situ biotransformation of GO, as evidenced by Raman spectroscopy imaging. Our findings demonstrate that lateral dimensions play a fundamental role in the pulmonary response to GO, and suggest that airborne exposure to micrometer sized GO should be avoided in production plant or applications, such as spray coating or painting, where aerosolised dispersions are likely to occur. These results are important for the development of evidence-based risk assessment, and provide information towards the implementation of a safer-by-design approach for GBM enhanced products and applications, for the benefit of workers and end-users.

2020-09-30 | GSE146796 | GEO

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data