High-performance visible light photodetectors based on inorganic CZT and InCZT single crystals.

ABSTRACT: Herein, the optoelectrical investigation of cadmium zinc telluride (CZT) and indium (In) doped CZT (InCZT) single crystals-based photodetectors have been demonstrated. The grown crystals were configured into photodetector devices and recorded the current-voltage (I-V) and current-time (I-t) characteristics under different illumination intensities. It has been observed that the photocurrent generation mechanism in both photodetector devices is dominantly driven by a photogating effect. The CZT photodetector exhibits stable and reversible device performances to 632 nm light, including a promotable responsivity of 0.38 AW^-1, a high photoswitch ratio of 152, specific detectivity of 6.30 × 10¹¹ Jones, and fast switching time (rise time of 210 ms and decay time of 150 ms). When doped with In, the responsivity of device increases to 0.50 AW^-1, photoswitch ratio decrease to 10, specific detectivity decrease to 1.80 × 10¹¹ Jones, rise time decrease to 140 ms and decay time increase to 200 ms. Moreover, these devices show a very high external quantum efficiency of 200% for CZT and 250% for InCZT. These results demonstrate that the CZT based crystals have great potential for visible light photodetector applications.

SUBMITTER: Shkir M

PROVIDER: S-EPMC6711974 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Growth and High-Performance Photodetectors of CsPbBr<sub>3</sub> Single Crystals.

Project description:Organic-inorganic hybrid perovskites have demonstrated exceptional photovoltaic properties, making them highly promising for solar cells and photodetectors (PDs). However, the organic components of these materials are vulnerable to heat and strong light illumination, limiting their application prospects. All-inorganic cesium-based perovskite PDs, on the other hand, possess enhanced thermal tolerance and stability, making them ideal for perovskite applications. The utilization of a ternary mixture solvent and additives in combination with single crystal (SC) growth has enabled the production of highly crystalline SCs with a defect density of 3.79 × 109 cm-3. The performance of the SC PDs had been evaluated using metal-semiconductor-metal devices, which demonstrated excellent results with a dark current as low as 0.198 μA at 10 V bias, on-off ratios exceeding 103, and a response time of shorter than 1 ms.

| S-EPMC10372932 | biostudies-literature

Integrated avalanche photodetectors for visible light.

Project description:Integrated photodetectors are essential components of scalable photonics platforms for quantum and classical applications. However, most efforts in the development of such devices to date have been focused on infrared telecommunications wavelengths. Here, we report the first monolithically integrated avalanche photodetector (APD) for visible light. Our devices are based on a doped silicon rib waveguide with a novel end-fire input coupling to a silicon nitride waveguide. We demonstrate a high gain-bandwidth product of 234 ± 25 GHz at 20 V reverse bias measured for 685 nm input light, with a low dark current of 0.12 μA. We also observe open eye diagrams at up to 56 Gbps. This performance is very competitive when benchmarked against other integrated APDs operating in the infrared range. With CMOS-compatible fabrication and integrability with silicon photonic platforms, our devices are attractive for sensing, imaging, communications, and quantum applications at visible wavelengths.

| S-EPMC7988121 | biostudies-literature

Near-infrared and visible light dual-mode organic photodetectors.

Project description:We report a dual-mode organic photodetector (OPD) that has a trilayer visible light absorber/optical spacer/near-infrared (NIR) light absorber configuration. In the presence of NIR light, photocurrent is produced in the NIR light-absorbing layer due to the trap-assisted charge injection at the organic/cathode interface at a reverse bias. In the presence of visible light, photocurrent is produced in the visible light-absorbing layer, enabled by the trap-assisted charge injection at the anode/organic interface at a forward bias. A high responsivity of >10 A/W is obtained in both short and long wavelengths. The dual-mode OPD exhibits an NIR light response operated at a reverse bias and a visible light response operated at a forward bias, with a high specific detectivity of ~1013 Jones in both NIR and visible light ranges. A bias-switchable spectral response OPD offers an attractive option for applications in environmental pollution detection, bioimaging process, wellness, and security monitoring in two distinct bands.

| S-EPMC6994203 | biostudies-literature

High-Performance Photodetectors Based on Semiconducting Graphene Nanoribbons.

Project description:The inherent zero-band gap nature of graphene and its fast photocarrier recombination rate result in poor optical gain and responsivity when graphene is used as the light absorption medium in photodetectors. Here, semiconducting graphene nanoribbons with a direct bandgap of 1.8 eV are synthesized and employed to construct a vertical heterojunction photodetector. At a bias voltage of -5 V, the photodetector exhibits a responsivity of 1052 A/W, outperforming previous graphene-based heterojunction photodetectors by several orders of magnitude. The achieved detectivity of 3.13 × 1013 Jones and response time of 310 μs are also among the best values for graphene-based heterojunction photodetectors reported until date. Furthermore, even under zero bias, the photodetector demonstrates a high responsivity and detectivity of 1.04 A/W and 2.45 × 1012 Jones, respectively. The work shows a great potential of graphene nanoribbon-based photodetection technology.

| S-EPMC10786164 | biostudies-literature

Flexible Optical Amplifier for Visible-Light Communications Based on Organic-Inorganic Hybrids.

Project description:Visible-light communications (VLCs) based on white light-emitting diodes (LEDs) are emerging as a low-cost and energy-efficient alternative solution to wireless communications. As white emitting LEDs use a combination of a long-lived yellow emission combined with the faster response of a blue emitting LED (∼460 nm), VLC technology requires amplification of the blue component to improve the signal-to-noise ratio. We report the fabrication and characterization of planar and channel waveguides based on a blue-emitting polyfluorene conjugated polyelectrolyte, namely, poly[9,9-bis(4-sulfonylbutoxyphenyl)fluorene-2,7-diyl-alt-1,4-phenylene] (PBS-PFP) incorporated into diureasil organic-inorganic hybrids for optical amplification in VLC. Taking advantage of the diureasil host as a UV self-patternable material, direct UV laser writing was used to pattern channel waveguides with a larger refractive index (Δn=0.09) compared to the nonexposed region, enabling confinement and guidance of the PBS-PFP emission with a maximum optical gain efficiency value of 1.62 ± 0.02 cm μJ-1. This value is among the best figures of merit known for polymeric materials with additional advantages added by the diureasil hybrid host, namely, mechanical flexibility, thermal stability, and low insertion losses due to the nearly null refractive index contrast between the optical fiber and the amplification device, establishing the proposed approach as a promising cost-effective solution for optical amplification in VLCs.

| S-EPMC6644746 | biostudies-literature

P3HT-based visible-light organic photodetectors using PEI/PAA multilayers as a p-type buffer layer.

Project description:A low leakage current is critical for achieving organic photodetectors (OPDs) with high detectivity. The insertion of buffer layers is an effective approach for reducing the reverse-biased leakage current. In this study, polyelectrolyte multilayers comprising polyethyleneimine (PEI) and polyacrylic acid (PAA) were introduced by a spin-assisted layer-by-layer technique into an OPD as a p-type buffer layer. Although PEI/PAA multilayers are insulators, when used as a buffer layer in our device, they suppressed the leakage current and also provided a high photocurrent due to the light-assisted tunneling effect. The prepared device configuration was ITO/(PEI/PAA)2/P3HT:PC60BM/Yb/Al. The performances of the OPDs were investigated by measuring the current-voltage characteristics, external quantum efficiency, and transient photocurrent. In addition, the operating mechanism of the OPDs was confirmed by impedance analysis. The device comprising (PEI/PAA)2 showed a specific detectivity of 3.11 × 1012 Jones and a bandwidth of 103.2 kHz at -1 V and 525 nm. This performance is a numerical value that can be used in devices such as a line scan camera. In addition, because this device is fabricated by a low-temperature solution process, flexible and large-area substrates can be used.

| S-EPMC9075515 | biostudies-literature

Single-Crystalline InGaAs Nanowires for Room-Temperature High-Performance Near-Infrared Photodetectors.

Project description:InGaAs is an important bandgap-variable ternary semiconductor which has wide applications in electronics and optoelectronics. In this work, single-crystal InGaAs nanowires were synthesized by a chemical vapor deposition method. Photoluminescence measurements indicate the InGaAs nanowires have strong light emission in near-infrared region. For the first time, photodetector based on as-grown InGaAs nanowires was also constructed. It shows good light response over a broad spectral range in infrared region with responsivity of 6.5 × 103 A W-1 and external quantum efficiency of 5.04 × 105 %. This photodetector may have potential applications in integrated optoelectronic devices and systems.

| S-EPMC6223916 | biostudies-literature

Monolithically integrated, broadband, high-efficiency silicon nitride-on-silicon waveguide photodetectors in a visible-light integrated photonics platform.

Project description:Visible and near-infrared spectrum photonic integrated circuits are quickly becoming a key technology to address the scaling challenges in quantum information and biosensing. Thus far, integrated photonic platforms in this spectral range have lacked integrated photodetectors. Here, we report silicon nitride-on-silicon waveguide photodetectors that are monolithically integrated in a visible light photonic platform on silicon. Owing to a leaky-wave silicon nitride-on-silicon design, the devices achieved a high external quantum efficiency of >60% across a record wavelength span from λ ~ 400 nm to ~640 nm, an opto-electronic bandwidth up to 9 GHz, and an avalanche gain-bandwidth product up to 173 ± 30 GHz. As an example, a photodetector was integrated with a wavelength-tunable microring in a single chip for on-chip power monitoring.

| S-EPMC9606291 | biostudies-literature

High-performance graphene-quantum-dot photodetectors.

Project description:Graphene quantum dots (GQDs) have received much attention due to their novel phenomena of charge transport and light absorption/emission. The optical transitions are known to be available up to ~6?eV in GQDs, especially useful for ultraviolet (UV) photodetectors (PDs). Thus, the demonstration of photodetection gain with GQDs would be the basis for a plenty of applications not only as a single-function device in detecting optical signals but also a key component in the optoelectronic integrated circuits. Here, we firstly report high-efficient photocurrent (PC) behaviors of PDs consisting of multiple-layer GQDs sandwiched between graphene sheets. High detectivity (>10(11)?cm Hz(1/2)/W) and responsivity (0.2 ~ 0.5 A/W) are achieved in the broad spectral range from UV to near infrared. The observed unique PD characteristics prove to be dominated by the tunneling of charge carriers through the energy states in GQDs, based on bias-dependent variations of the band profiles, resulting in novel dark current and PC behaviors.

| S-EPMC4083259 | biostudies-literature

High-performance nanotube-enhanced perovskite photodetectors.

Project description:Organic-inorganic perovskites have already shown a tremendous potential for low-cost light-harvesting devices. Yet, the relatively low carrier mobilities in bulk perovskites still prevent large-area devices with performances competing with state-of-the-art technologies. Here, we tackle this fundamental challenge by incorporating single-wall carbon nanotubes within a perovskite matrix by means of a simple two-step method in ambient air. Using this nano-engineered hybrid film, we demonstrate large-area photodetectors with responsivities up-to 13.8 A.W-1 and a broad spectral response from 300 to 800 nm, indicating that photocurrent generation arises from the charge transfer from the perovskite matrix to the embedded nanotube network. As the nanotubes facilitate the carrier extraction, these photodetectors also show a fast response time of 10 ms. This is significantly faster than most of previous reports on perovskite-based photodetectors, including devices with much smaller photosensitive areas. This approach is also well-suited for large-scale production of other perovskite-based light-harvesting devices.

| S-EPMC5371979 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data