Repair bond strength of composite to Er,Cr:YSGG laser irradiated zirconia and porcelain surfaces.

ABSTRACT:

Background

Fracture or chipping are major concerning failures of an all-ceramic restoration. Repairing of the failure restoration using intra-oral technique is time saving and cost effective treatment modality. The present study was proposed to evaluate effect of Er,Cr:YSGG laser irradiation on shear bond strength between zirconia/porcelain and composite resin.

Methods

Thirty zirconia and thirty zirconia based porcelain disc shape specimens were prepared. Three different surface treatment procedure were applied the specimens. For control groups (Group ZC and PC), instruction manual of an intra-oral porcelain repair system was followed. Different pulse rates of Er,Cr:YSGG laser irradiation (short and long pulses) were applied to zirconia and porcelain surfaces for other groups (Group ZS, ZL, PS, and PL). Porcelain repair kit was used to repair specimens using standard cylindrical teflon mold (2 × 2 mm). Repair bond strength of the repaired specimens was tested using a universal testing machine.

Results

Highest mean bond strength value was observed at Group PC that was significantly higher than laser applied porcelain groups. Long pulse laser irradiation illustrated that increased mean bond strength compared to short pulse application on to the porcelain surface. Laser applied zirconia groups showed better mean bond strength than Group ZC, but differences between the groups were not statistically significant.

Conclusion

Different modes of Er,Cr:YSGG laser irradiation enhanced repair bond strength of the composite resin to zirconia, but these were not significant. Following the instruction manual for surface treatment on the porcelain surface was better method than Er,Cr:YSGG laser surface conditioning.

SUBMITTER: Tokar E

PROVIDER: S-EPMC6717752 | biostudies-literature | 2019 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Repair bond strength of composite to Er,Cr:YSGG laser irradiated zirconia and porcelain surfaces.

Tokar Emre E Polat Serdar S Ozturk Caner C

Biomedical journal 20190601 3

<h4>Background</h4>Fracture or chipping are major concerning failures of an all-ceramic restoration. Repairing of the failure restoration using intra-oral technique is time saving and cost effective treatment modality. The present study was proposed to evaluate effect of Er,Cr:YSGG laser irradiation on shear bond strength between zirconia/porcelain and composite resin.<h4>Methods</h4>Thirty zirconia and thirty zirconia based porcelain disc shape specimens were prepared. Three different surface t ...[more]

PMID: 31466713

Similar Datasets

Project description:BackgroundThe objective of this study was to investigate the influence of Er,Cr:YSGG laser irradiated at different powers on the micromorphology and the bonding property of non-carious sclerotic dentin to resin composites.MethodsTwo hundred bovine incisors characterized by non-carious sclerotic dentin were selected, and the seventy-two teeth of which for surface morphological analysis were divided into nine groups according to various treatments (A: the control group, B: only treated with the adhesive Adper Easy One, C: diamond bur polishing followed by Adper Easy One, D-I: Er,Cr:YSGG laser irradiating at 1W, 2W, 3W, 4W, 5W, 6W output power, respectively, followed by Adper Easy One). The surface roughness values were measured by the non-contact three-dimensional morphology scanner, then the surface micromorphologies of surfaces in all groups were assessed by scanning electron microscopy (SEM); meanwhile, Image Pro-Plus 6.0 software was used to measure the relative percentage of open tubules on SEM images. The rest, one hundred twenty-eight teeth for bond strength test, were divided into eight groups according to the different treatments (A: only treated with the adhesive Adper Easy One, B: diamond bur polishing followed by the above adhesive, C-H: Er,Cr:YSGG laser irradiating at 1 W, 2 W, 3 W, 4 W, 5 W, 6 W output power, respectively, followed by the above adhesive), and each group was subsequently divided into two subgroups according to whether aging is performed (immediately tested and after thermocycling). Micro-shear bond strength test was used to evaluate the bond strength.ResultsThe 4W laser group showed the highest roughness value (30.84±1.93?m), which was statistically higher than the control group and the diamond bur groups (p<0.05). The mean percentages ((27.8±1.8)%, (28.0±2.2)%, (30.0±1.9)%) of open tubules area in the 4W, 5W, 6W group were higher than other groups (p<0.05). The 4W laser group showed the highest micro-shear bond strength not only in immediately tested (17.60±2.55 PMa) but after thermocycling (14.35±2.08MPa).ConclusionThe Er,Cr:YSGG laser at 4W power can effectively improve the bonding property between non-carious sclerotic dentin and resin composites by increasing the roughness and mean percentage area of open tubules.

Dataset Information

Repair bond strength of composite to Er,Cr:YSGG laser irradiated zirconia and porcelain surfaces.

Background

Methods

Results

Conclusion

Publications

Repair bond strength of composite to Er,Cr:YSGG laser irradiated zirconia and porcelain surfaces.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets