Influence of Different Post-Plasma Treatment Storage Conditions on the Shear Bond Strength of Veneering Porcelain to Zirconia.
Ontology highlight
ABSTRACT:
SUBMITTER: Lee MH
PROVIDER: S-EPMC5456530 | biostudies-other | 2016 Jan
REPOSITORIES: biostudies-other
Similar Datasets
Project description:The aim of this in vitro study was to assess the influence of surface pretreatment on shear bond strength (SBS) of an adhesive resin cement (G-CEM Link Force TM, GC Corporation, Tokyo, Japan) to three different yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP) ceramics: (1) Copran Zirconia Monolith HT, COP; (2) Katana ML Zirconia, KAT; and (3) Metoxit Z-CAD HTL Zirconia, MET. In total, 45 cylinders (5 mm in diameter, 1 mm height) for each type of zirconia ceramic were prepared used a computer-aided design and computer-aided manufacturing (CAD/CAM) machine (software CEREC 4.2). Each type of zirconia was subdivided into three groups and each group received a different surface pretreatment; 15 samples were not conditioned as control (groups COP 1, KAT 1, MET 1), 15 samples were air-borne particle abraded with aluminum dioxide particles of 50-?m size at 0.3 MPa for 20 s (groups COP 2, KAT 2, MET 2), and 15 samples were hot-etched with a solution of hydrochloric acid and ferric chloride (groups COP 3, KAT 3, MET 3). After specimen fabrication, the adhesive cement-ceramic interface was analyzed using an SBS test. Subsequently, the adhesive remnant index (ARI) was measured. Data were submitted to statistical analysis. Air-borne particle abraded specimens showed the highest SBS values for COP and KAT groups. For MET, no significant difference was reported between air-borne particle abraded specimens and untreated controls. The lowest values were detected for acid-etched groups. A higher frequency of ARI = "1" and ARI = "2" was reported in control and air-borne particle abraded groups, whereas ARI = "3" was detected in hot-etched groups. No correlation was found between ARI score and shear bond strength. Air-borne particle abrasion is considered the best treatment for Zirconia Copran and Zirconia Katana ML, if it is followed by using dual-curing resin cement.
| S-EPMC7040603 | biostudies-literature
Project description:This study was designed to evaluate the effect of hot-etching surface treatment on the shear bond strength between zirconia ceramics and two commercial resin cements. Ceramic cylinders (120 units; length: 2.5 mm; diameter: 4.7 mm) were randomly divided into 12 groups (n = 10) according to different surface treatments (blank control; airborne-particle-abrasion; hot-etching) and different resin cements (Panavia F2.0; Superbond C and B) and whether or not a thermal cycling fatigue test (5°-55° for 5000 cycles) was performed. Flat enamel surfaces, mounted in acrylic resin, were bonded to the zirconia discs (diameter: 4.7 mm). All specimens were subjected to shear bond strength testing using a universal testing machine with a crosshead speed of 1 mm/min. All data were statistically analyzed using one-way analysis of variance and multiple-comparison least significant difference tests (α = 0.05). Hot-etching treatment produced higher bond strengths than the other treatment with both resin cements. The shear bond strength of all groups significantly decreased after the thermal cycling test; except for the hot-etching group that was cemented with Panavia F2.0 (p < 0.05). Surface treatment of zirconia with hot-etching solution enhanced the surface roughness and bond strength between the zirconia and the resin cement.
| S-EPMC5458836 | biostudies-other
Project description:This study analyzed the shear bond strength (SBS) of resin composite on zirconia surface to which a specific conditioner was applied before sintering. After sintering of either conditioner-coated or uncoated specimens, both groups were divided into three subgroups by their respective surface modifications (n = 10 per group): no further treatment; etched with hydrofluoric acid; and sandblasted with 50 µm Al₂O₃ particles. Surfaces were characterized by measuring different surface roughness parameters (e.g., Ra and Rmax) and water contact angles. Half of the specimens underwent thermocycling (10,000 cycles, 5-55 °C) after self-adhesive resin cement build-up. The SBSs were measured using a universal testing machine, and the failure modes were analyzed by microscopy. Data were analyzed by nonparametric and parametric tests followed by post-hoc comparisons (α = 0.05). Conditioner-coated specimens increased both surface roughness and hydrophilicity (p < 0.01). In the non-thermocycled condition, sandblasted surfaces showed higher SBSs than other modifications, irrespective of conditioner application (p < 0.05). Adhesive fractures were commonly observed in the specimens. Thermocycling favored debonding and decreased SBSs. However, conditioner-coated specimens upon sandblasting showed the highest SBS (p < 0.05) and mixed fractures were partially observed. The combination of conditioner application before sintering and sandblasting after sintering showed the highest shear bond strength and indicated improvements concerning the failure mode.
| S-EPMC5456913 | biostudies-other
Project description:This study evaluated the bond strength of veneering porcelain with an experimental conditioner-coated zirconia. Pre-sintered Y-TZP specimens (n = 44) were divided in two groups based on conditioning type. After sintering, all sample surfaces were sandblasted and layered with veneering porcelain. Additionally, half of the specimens in each group underwent thermal cycling (10,000 cycles, 5-55 °C), and all shear bond strengths were measured. After testing, the failure mode of each fractured specimen was determined. Differences were tested by parametric and Fisher's exact tests (α = 0.05). The differences in bond strength were not statistically significant. Adhesive fractures were dominantly observed for the non-thermal cycled specimens. After thermal cycling, the conditioner-coated group showed cohesive and mixed fractures (p = 0.0021), whereas the uncoated group showed more adhesive fractures (p = 0.0021). Conditioning of the pre-sintered Y-TZP did not change the shear bond strength of the veneering porcelain, but did improve the failure mode after thermal cycling.
| S-EPMC5457043 | biostudies-other
Project description:IntroductionThis study aimed to compare the micro-shear bond strength (µSBS) performances of two resin-based calcium silicate-based cement (CSC) (TheraCal PT and TheraCal LC), Biodentine, and two modified-MTA CSC materials (NeoMTA 2 and BioMTA+) to bulk-fill restorative material.Materials and methodsFifty 3D printed cylindrical resin blocks with a central hole were used (2 mm in depth and 4 mm in diameter). CSCs were placed in the holes (per each group n = 10) and incubated for 24 h. Cylindrical polyethylene molds (2 mm in height and diameter) were used to place the bulk-fill restorative materials on the CSCs and polymerize for 20 s. Then, all specimens were incubated for 24 h at 37 °C at a humidity of 100%. Specimen's µSBSs were determined with a universal testing machine. Data were analyzed with one-way ANOVA (Welch) and Tamhane test.ResultsStatistically higher µSBS was found for TheraCal PT (29.91 ± 6.13 MPa) (p < 0.05) respect to all the other materials tested. TheraCal LC (20.23 ± 6.32 MPa) (p > 0.05) reported higher µSBS than NeoMTA 2 (11.49 ± 5.78 MPa) and BioMTA+ (6.45 ± 1.89 MPa) (p < 0.05). There was no statistical difference among TheraCal LC, NeoMTA 2 and Biodentine (15.23 ± 7.37 MPa) and between NeoMTA 2 and BioMTA+ (p > 0.05).ConclusionChoosing TheraCal PT as the pulp capping material may increase the adhesion and µSBS to the bulk-fill composite superstructure and sealing ability.
| S-EPMC10066686 | biostudies-literature
Project description:Background: Polymer infiltrated ceramic networks, or hybrid ceramics, are a combination of infiltrating polymerizable organic monomers into a pre-sintered porous ceramic matrix. In addition to having good mechanical properties, the polymer infiltrated ceramic network must comply with the possibility of adequate bonding to the resinous cement. The surface conditioning of this hybrid material must be carefully considered due to its organic composition and ceramic network. The purpose of this research is to evaluate the effect of hydrofluoric acid and a self-etching ceramic primer, under two different application times, on the bond strength of a polymer infiltrated ceramic network. Methods: Blocks of a polymer infiltrated ceramic network were cut to obtain sheets, and these were randomized into five groups. For the group termed AAS, airborne-particle abrasion with Al 2O 3 (aluminum oxide) of 50µm was used. For groups HF2 and HF6, hydrofluoric acid was used for 20 and 60 seconds respectively, and for the groups MB2 and MB6, a self-etch ceramic primer was applied for 20 and 60 seconds respectively. A silane was applied to the groups AAS, HF2, and HF6 after the treatment. After 24-hour storage in distilled water, a micro-shear bond strength test was performed using a universal mechanical testing machine. All samples were evaluated in a stereomicroscope at 40x and 50x to determine the type of failure. Results: The highest and lowest values of bond strength were reported by groups MB6 and AAS, respectively. Groups HF2, HF6, MB6, and MB2 did not report statistically significant differences. The predominant failure pattern was a mixed failure. Conclusions: With the limitations of the present investigation, the treatments of self-etching ceramic primer and hydrofluoric acid followed by silane were reported to be statistically equal at 20 and 60 seconds.
| S-EPMC10665602 | biostudies-literature
Project description:This study aimed to evaluate the bonding strength and thermal properties of demineralized dentin with and without EDC treatment. Sound human molars were randomly divided into seven treatment groups (n = 20): control, 80% ethanol, and five EDC ethanol solutions (0.01-1.0 M). In each group, 16 samples were used for bond strength assessment and 4 samples were used for scanning electron microscopy (SEM) analysis. A further 70 intact molars were used to obtain a fine demineralized dentin powder, treated with the same solutions and were evaluated the crosslink degree by ninhydrin test and denaturation temperature (Td) by differential scanning calorimetry. EDC-treated specimens (<1.0 M) had a higher bond strength, especially 0.3 and 0.5 M group, than the control counterpart. There was a significant drop in bond strength of 1.0 M EDC group. SEM revealed a homogeneous and regular interface under all treatments. EDC treatment significantly increased the demineralized dentin cross-link degree and Td compared with the control and ethanol treatments. The 0.3 and 0.5 M treatments showed the highest cross-link degree and Td. In terms of mechnical and theramal properties consideration, 0.3 and 0.5 M EDC solutions may be favorable for when applied with etch-and-rinse adhesives, but it is still needed further long-term study.
| S-EPMC5457252 | biostudies-other
Project description:Background. Repairing aged composite resin is a challenging process. Many surface treatment options have been proposed to this end. This study evaluated the effect of different surface treatments on the shear bond strength (SBS) of nano-filled composite resin repairs. Methods. Seventy-five cylindrical specimens of a Filtek Z350XT composite resin were fabricated and stored in 37°C distilled water for 24 hours. After thermocycling, the specimens were divided into 5 groups according to the following surface treatments: no treatment (group 1); air abrasion with 50-μm aluminum oxide particles (group 2); irradiation with Er:YAG laser beams (group 3); roughening with coarse-grit diamond bur + 35% phosphoric acid (group 4); and etching with 9% hydrofluoric acid for 120 s (group 5). Another group of Filtek Z350XT composite resin samples (4×6 mm) was fabricated for the measurement of cohesive strength (group 6). A silane coupling agent and an adhesive system were applied after each surface treatment. The specimens were restored with the same composite resin and thermocycled again. A shearing force was applied to the interface in a universal testing machine. Data were analyzed using one-way ANOVA and post hoc Tukey tests (P < 0.05). Results. One-way ANOVA indicated significant differences between the groups (P < 0.05). SBS of controls was significantly lower than the other groups; differences between groups 2, 3, 4, 5 and 6 were not significant. Surface treatment with diamond bur + 35% phosphoric acid resulted in the highest bond strength. Conclusion. All the surface treatments used in this study improved the shear bond strength of nanofilled composite resin used.
| S-EPMC4831615 | biostudies-other
Project description:The purpose of the present study was to assess the proper time to perform a restoration (immediately or delayed) after placement of two calcium silicate-based cements (CSCs) and to test the performance of two different restorative protocols regarding shear bond strength (SBS). Seventy-five acrylic blocks were randomly divided into five groups (n = 15). Specimens were filled with either ProRoot MTA (Dentsply Tulsa Dental) or Biodentine (Septodont). The restoration was performed at an immediate (12 min) or delayed (seven days) timeframe, using a resin-based flowable composite (SDR) (bonded to the CSC using a universal bonding system) or glass ionomer cement (GIC) as restorative materials. SBS was measured using a universal testing machine. Fractured surfaces were evaluated, and the pattern was registered. Statistical analysis was performed using the Dunn⁻Sidak post hoc test (P < 0.05). Biodentine/immediate SDR showed the highest mean SBS value (4.44 MPa), with statistically significant differences when compared to mineral trioxide aggregate (MTA)/GIC (1.14 MPa) and MTA/immediate SDR (1.33 MPa). MTA/GIC and MTA/immediate SDR did not present significant differences regarding SBS. No statistical differences were verified concerning mean SBS between both CSCs within the 7 day groups. MTA/delayed SDR (3.86 MPa) presented statistical differences compared to MTA/immediate SDR, whereas no differences were observed regarding Biodentine performance (Biodentine/immediate SDR and Biodentine/delayed SDR (3.09 MPa)). Bonding procedures directly on top of MTA might be preferably performed at a delayed timeframe, whereas Biodentine might allow for immediate restoration.
| S-EPMC6265959 | biostudies-literature
Project description:This study aimed to evaluate the shear bond strength of self-adhesive flowable resin composite on both enamel and dentin and investigate whether surface pretreatment with a phosphoric acid etch affects the bond strength. In this in vitro study, 80 sound human premolars were flattened to create (40) uniform enamel (E) and (40) dentin (D) surfaces. Groups were divided according to surface pretreatment: E1 : Scotchbond™ Universal Etchant + Single Bond Universal Adhesive + Filtek™ Z350 XT flowable composite; E2: Single Bond Universal self-etch adhesive + Filtek Z350 XT flowable composite; E3 : Scotchbond Universal Etchant + Fusio Liquid Dentin self-adhesive flowable composite; E4: Fusio Liquid Dentin self-adhesive flowable composite; D1 : Scotchbond Universal Etchant + Single Bond Universal Adhesive + Filtek Z350 XT flowable composite; D2: Single Bond Universal self-etch adhesive + Filtek Z350 XT flowable composite; D3: Scotchbond Universal Etchant + Fusio Liquid Dentin self-adhesive flowable composite; D4: Fusio Liquid Dentin self-adhesive flowable composite. After 2500 thermal cycles, the SBS was measured with a universal testing machine. One-way analysis of variance and Tukey's test for multiple comparisons were used to compare results. Two-way ANOVA was done to observe the significance of interaction between the type of surface and treatment. The maximum (49.38 ± 1.23 MPa) and minimum (21.41 ± 5.27 MPa) SBS values were noted in groups D1 and E2, respectively. Shear bond test results showed that self-adhesive flowable composite exhibited similar shear bond strengths on enamel and dentin and the bond strength improved with selective acid etching.
| S-EPMC9106484 | biostudies-literature