Fabrication of Silica Nanoparticle Monolayer Arrays Using an Anodic Aluminum Oxide Template.

ABSTRACT: Non-close-packed (NCP) silica nanoparticle monolayer arrays (SNMA) on ordered porous anodic aluminum oxide (AAO) templates were fabricated for the first time by a novel two-step spin-coating technique. The obtained NCP-SNMA-AAO was composed of silica nanoparticles (average primary particle size of 440 nm) and well-organized nanopores on the AAO substrates. NCP-SNMA-AAO with a supporting ratio of 87% silica nanoparticles showed a hydrophilic surface (water contact angle of 51.0°), while the original AAO substrate shows a hydrophobic surface (water contact angle of 107.9°). The maximum coefficient of static friction was decreased by 29% (0.327 ? 0.233). The coefficient of dynamic friction was also decreased by 20% (0.281 ? 0.226). We found that controlling the silica supporting ratio using the two-step spin-coating technique is an effective approach for surface modification of an AAO substrate.

SUBMITTER: Sekiguchi K

PROVIDER: S-EPMC6733172 | biostudies-literature | 2019 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Fabrication of Silica Nanoparticle Monolayer Arrays Using an Anodic Aluminum Oxide Template.

Sekiguchi Kazutoshi K Nakanishi Takayuki T Segawa Hiroyo H Yasumori Atsuo A

ACS omega 20190822 10

Non-close-packed (NCP) silica nanoparticle monolayer arrays (SNMA) on ordered porous anodic aluminum oxide (AAO) templates were fabricated for the first time by a novel two-step spin-coating technique. The obtained NCP-SNMA-AAO was composed of silica nanoparticles (average primary particle size of 440 nm) and well-organized nanopores on the AAO substrates. NCP-SNMA-AAO with a supporting ratio of 87% silica nanoparticles showed a hydrophilic surface (water contact angle of 51.0°), while the origi ...[more]

PMID: 31508559

Similar Datasets

Dual effects of ultrasound on fabrication of anodic aluminum oxide.

Project description:Ultrasound has been proven to enhance the mass transfer process and impact the fabrication of anodic aluminum oxide (AAO). However, the different effects of ultrasound propagating in different media make the specific target and process of ultrasound in AAO remain unclear, and the effects of ultrasound on AAO reported in previous studies are contradictory. These uncertainties have greatly limited the application of ultrasonic-assisted anodization (UAA) in practice. In this study, the bubble desorption and mass transfer enhancement effects were decoupled based on an anodizing system with focused ultrasound, such that the dual effects of ultrasound on different targets were distinguished. The results showed that ultrasound has the dual effects on AAO fabrication. Specifically, ultrasound focused on the anode has a nanopore-expansion effect on AAO, leading to a 12.24 % improvement in fabrication efficiency. This was attributed to the promotion of interfacial ion migration through ultrasonic-induced high-frequency vibrational bubble desorption. However, AAO nanopores were observed to shrink when ultrasound was focused on the electrolyte, accompanied by a 25.85 % reduction in fabrication efficiency. The effects of ultrasound on mass transfer through jet cavitation appeared to be the reason for this phenomenon. This study resolved the paradoxical phenomena of UAA in previous studies and is expected to guide AAO application in electrochemistry and surface treatments.

| S-EPMC10352598 | biostudies-literature

Fabrication of Polymeric Antireflection Film Manufactured by Anodic Aluminum Oxide Template on Dye-Sensitized Solar Cells.

Project description:In this study, high energy conversion efficient dye-sensitized solar cells (DSSCs) were successfully fabricated by attaching a double anti-reflection (AR) layer, which is composed of a subwavelength moth-eye structured polymethyl methacrylate (PMMA) film and a polydimethylsiloxane (PDMS) film. An efficiency of up to 6.79% was achieved. The moth-eye structured PMMA film was fabricated by using an anodic aluminum oxide (AAO) template which is simple, low-cost and scalable. The nano-pattern of the AAO template was precisely reproduced onto the PMMA film. The photoanode was composed of Titanium dioxide (TiO₂) nanoparticles (NPs) with a diameter of 25 nm deposited on the fluorine-doped tin oxide (FTO) glass substrate and the sensitizer N3. The double AR layer was proved to effectively improve the short-circuit current density (JSC) and conversion efficiency from 14.77 to 15.79 mA/cm² and from 6.26% to 6.79%, respectively.

| S-EPMC5503351 | biostudies-other

Preparation of Aluminum Nanomesh Thin Films from an Anodic Aluminum Oxide Template as Transparent Conductive Electrodes.

Project description:We have employed anodic aluminum oxide as a template to prepare ultrathin, transparent, and conducting Al films with a unique nanomesh structure for transparent conductive electrodes. The anodic aluminum oxide template is obtained through direct anodization of a sputtered Al layer on a glass substrate, and subsequent wet etching creates the nanomesh metallic film. The optical and conductive properties are greatly influenced by experimental conditions. By tuning the anodizing time, transparent electrodes with appropriate optical transmittance and sheet resistance have been obtained. The results demonstrate that our proposed strategy can serve as a potential method to fabricate low-cost TCEs to replace conventional indium tin oxide materials.

| S-EPMC4735723 | biostudies-other

Structural defects in a nanomesh of bulk MoS<sub>2</sub> using an anodic aluminum oxide template for photoluminescence efficiency enhancement.

Project description:Two-dimensional (2D) materials beyond graphene have attracted considerable interest because of the zero bandgap drawbacks of graphene. Transition metal dichalcogenides (TMDs), such as MoS2 and WSe2, are the potential candidates for next 2D materials because atomically thin layers of TMDs exhibit unique and versatile electrical and optical properties. Although bulk TMDs materials have an indirect bandgap, an indirect-to-direct bandgap transition is observed in monolayers of TMDs (MoS2, WSe2, and MoSe2). Optical properties of TMD films can be improved by the introduction of structural defects. For example, large-area spatial tuning of the optical transition of bulk MoS2 films is achieved by using an anodic aluminum oxide (AAO) template to induce structural defects such as edge- and terrace-terminated defects in a nanomesh structure. Strong photoluminescence emission peaks with a band gap of 1.81?eV are observed, possibly because of radiative transition at the defect sites. This work shows that the AAO template lithography method has potential for the production of homogenous large-scale nanomesh structures for practical semiconductor processing applications in future MoS2-based electronic and optical devices.

| S-EPMC5923261 | biostudies-literature

Templated Synthesis of Diamond Nanopillar Arrays Using Porous Anodic Aluminium Oxide (AAO) Membranes.

Project description:Diamond nanostructures are mostly produced from bulk diamond (single- or polycrystalline) by using time-consuming and/or costly subtractive manufacturing methods. In this study, we report the bottom-up synthesis of ordered diamond nanopillar arrays by using porous anodic aluminium oxide (AAO). Commercial ultrathin AAO membranes were adopted as the growth template in a straightforward, three-step fabrication process involving chemical vapor deposition (CVD) and the transfer and removal of the alumina foils. Two types of AAO membranes with distinct nominal pore size were employed and transferred onto the nucleation side of CVD diamond sheets. Subsequently, diamond nanopillars were grown directly on these sheets. After removal of the AAO template by chemical etching, ordered arrays of submicron and nanoscale diamond pillars with ~325 nm and ~85 nm diameters were successfully released.

| S-EPMC10004781 | biostudies-literature

Functionalized anodic aluminum oxide membrane-electrode system for enzyme immobilization.

Project description:A nanoporous membrane system with directed flow carrying reagents to sequentially attached enzymes to mimic nature’s enzyme complex system was demonstrated. Genetically modified glycosylation enzyme, OleD Loki variant, was immobilized onto nanometer-scale electrodes at the pore entrances/exits of anodic aluminum oxide membranes through His6-tag affinity binding. The enzyme activity was assessed in two reactions—a one-step “reverse” sugar nucleotide formation reaction (UDP-Glc) and a two-step sequential sugar nucleotide formation and sugar nucleotide-based glycosylation reaction. For the one-step reaction, enzyme specific activity of 6–20 min(–1) on membrane supports was seen to be comparable to solution enzyme specific activity of 10 min(–1). UDP-Glc production efficiencies as high as 98% were observed at a flow rate of 0.5 mL/min, at which the substrate residence time over the electrode length down pore entrances was matched to the enzyme activity rate. This flow geometry also prevented an unwanted secondary product hydrolysis reaction, as observed in the test homogeneous solution. Enzyme utilization increased by a factor of 280 compared to test homogeneous conditions due to the continuous flow of fresh substrate over the enzyme. To mimic enzyme complex systems, a two-step sequential reaction using OleD Loki enzyme was performed at membrane pore entrances then exits. After UDP-Glc formation at the entrance electrode, aglycon 4-methylumbelliferone was supplied at the exit face of the reactor, affording overall 80% glycosylation efficiency. The membrane platform showed the ability to be regenerated with purified enzyme as well as directly from expression crude, thus demonstrating a single-step immobilization and purification process.

| S-EPMC4148145 | biostudies-literature

Synthesis of Co-Fe 1D Nanocone Array Electrodes Using Aluminum Oxide Template.

Project description:Porous anodic alumina oxide (AAO) obtained via two-step anodization is a material commonly used as a template for fabricating 1D nanostructures. In this work, copper and cobalt-iron 1D nanocones were obtained by an electrodeposition method using AAO templates. The templates were produced using two-step anodization in H2C2O4. The Co-Fe nanostructures are characterized by homogeneous pore distribution. The electrocatalytic activity of the produced nanomaterials was determined in 1 M NaOH using the linear sweep voltammetry (LSV) and chronopotentiometry (CP) methods. These materials can be used as catalysts in the water-splitting reaction. The sample's active surface area was calculated and compared with bulk materials.

| S-EPMC8036432 | biostudies-literature

Grapefruit Extract-Mediated Fabrication of Photosensitive Aluminum Oxide Nanoparticle and Their Antioxidant and Anti-Inflammatory Potential.

Project description:Aluminum oxide nanoparticles (Al2O3 NPs) were synthesized using a simple, eco-friendly green synthesis approach in an alkaline medium from the extract of grapefruit peel waste. The pre-synthesized, nano-crystalline Al2O3 NPs were characterized by using spectroscopic (UV-vis, FTIR, XRD, and EDX) and microscopic (SEM and TEM) techniques. The formed Al2O3 NPs exhibited a pronounced absorption peak at 278 nm in the UV-vis spectrum. The average particle size of the as-prepared Al2O3 NPs was evaluated to be 57.34 nm, and the atomic percentages of O and Al were found to be 54.58 and 45.54, respectively. The fabricated Al2O3 NPs were evaluated for antioxidant, anti-inflammatory, and immunomodulatory properties. The Al2O3 NPs showed strong antioxidant potential towards all the four tested assays. The anti-inflammatory and immunomodulatory potential of Al2O3 NPs was investigated by measuring the production of nitric oxide and superoxide anion (O2•-), as well as proinflammatory cytokines tumour necrosis factor (TNF-α, IL-6) and inhibition of nuclear factor kappa B (NF- κB). The results revealed that Al2O3 NPs inhibited the production of O2•- (99.4%) at 100 μg mL-1 concentrations and intracellular NO•- (55%), proinflammatory cytokines IL-6 (83.3%), and TNF-α (87.9%) at 50 μg mL-1 concentrations, respectively. Additionally, the Al2O3 NPs inhibited 41.8% of nuclear factor kappa B at 20 μg mL-1 concentrations. Overall, the outcomes of current research studies indicated that Al2O3 NPs possess anti-inflammatory and immunomodulatory properties and could be used to treat chronic and acute anti-inflammatory conditions.

| S-EPMC9182307 | biostudies-literature

Fabrication of Inorganic Oxide Fiber Using a Cigarette Filter as a Template.

Project description:Inorganic oxides with unique physical and chemical properties have attracted much attention because they can be applied in a wide range of fields. Herein, recycled cigarette filters are deacetylated to cellulose filters (CFs), which are then applied as templates to prepare fiber-like inorganic oxides (titanium dioxide, TiO2, and silicon dioxide, SiO2). Inorganic oxides are prepared using CF as a template by a typical sol-gel reaction of metal alkoxides. Owing to the fibrous structure of the CF template, the prepared inorganic oxides (TiO2 and SiO2) show similar fibrous structures, which was confirmed by scanning electron microscopy and nitrogen adsorption-desorption analysis. Moreover, the prepared inorganic oxides (TiO2 and SiO2) show high surface areas and pore volumes. Furthermore, the TiO2 fiber-like materials are evaluated for their photocatalytic properties by analyzing the methylene blue (MB) and methyl orange (MO) degradation. In this study, we provide a clean method, which can convert cellulose acetate-based waste into useful templates to prepare inorganic oxides with relatively simple steps, and the prepared inorganic oxides can be applied in water treatment.

| S-EPMC8210397 | biostudies-literature

Correlation of Fabrication Methods and Enhanced Wear Performance in Nanoporous Anodic Aluminum Oxide with Incorporated Molybdenum Disulfide (MoS<sub>2</sub>) Nanomaterials.

Project description:Wear performance is integral to component longevity, minimizing industrial waste and excess energy costs in a wide variety of applications. Anodized aluminum oxide (AAO) has many beneficial properties leading to its wide use across industries as a surface treatment for many aluminum components, but the wear properties of the coating could be improved significantly. Here, we used an electrochemical method to incorporate molybdenum disulfide (MoS2), a nanomaterial used as a dry lubricant, to modify alloys of aluminum during AAO preparation. Using Raman spectroscopy and tribological scratch measurements, we thoroughly characterized the structure and wear behavior of the films. The MoS2 deposition procedure was optimal on aluminum 5052 anodized in higher acid concentrations, with friction coefficients at around 0.05 (~10× better than unmodified AAO). Changing anodization conditions to produce harder films with smaller pores led to worsened wear properties, likely because of lower MoS2 content. Studying a commercial MoS2/AAO film of a different Al alloy (7075) showed that a heat treatment step intended to fully convert all deposited MoSx species to MoS2 can adversely affect wear in some alloys. While Al 6061 and 1100 produced films with worse wear performance compared to Al 5052 or 7075, our results show evidence that acid cleaning after initial anodization likely removes residual alloying elements, affecting MoS2 incorporation. This study demonstrates a nanomaterial modified AAO film with superior wear characteristics to unmodified AAO and relates fabrication procedure, film structure, and practical performance.

| S-EPMC10934346 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data