Effects of non-solvents and electrolytes on the formation and properties of cellulose I filaments.

ABSTRACT: Coagulation is a critical process in the assembly of cellulose nanofibrils into filaments by wet spinning; however, so far, the role of the coagulation solvent has not been systematically elucidated in this context. This work considers organic non-solvents (ethanol, acetone) and aqueous electrolyte solutions (NaCl(aq), HCl(aq), CaCl₂(aq)) for the coagulation of negatively charged cellulose nanofibrils via wet spinning. The associated mechanisms of coagulation with such non-solvents resulted in different spinnability, coagulation and drying time. The properties of the achieved filaments varied depending strongly on the coagulant used: filaments obtained from electrolytes (using Ca²⁺ and H⁺ as counterions) demonstrated better water/moisture stability and thermomechanical properties. In contrast, the filaments formed from organic non-solvents (with Na⁺ as counterions) showed high moisture sorption and low hornification when subjected to cycles of high and low humidity (dynamic vapor sorption experiments) and swelled extensively upon immersion in water. Our observations highlight the critical role of counter-ions and non-solvents in filament formation and performance. Some of the fundamental aspects are further revealed by using quartz crystal microgravimetry with model films of nanocelluloses subjected to the respective solvent exchange.

SUBMITTER: Wang L

PROVIDER: S-EPMC6854096 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Recent Advances in Solvents for the Dissolution, Shaping and Derivatization of Cellulose: Quaternary Ammonium Electrolytes and their Solutions in Water and Molecular Solvents.

Project description:There is a sustained interest in developing solvents for physically dissolving cellulose, i.e., without covalent bond formation. The use of ionic liquids, ILs, has generated much interest because of their structural versatility that results in efficiency as cellulose solvents. Despite some limitations, imidazole-based ILs have received most of the scientific community's attention. The objective of the present review is to show the advantages of using quaternary ammonium electrolytes, QAEs, including salts of super bases, as solvents for cellulose dissolution, shaping, and derivatization, and as a result, increase the interest in further investigation of these important solvents. QAEs share with ILs structural versatility; many are liquids at room temperature or are soluble in water and molecular solvents (MSs), in particular dimethyl sulfoxide. In this review we first give a historical background on the use of QAEs in cellulose chemistry, and then discuss the common, relatively simple strategies for their synthesis. We discuss the mechanism of cellulose dissolution by QAEs, neat or as solutions in MSs and water, with emphasis on the relevance to cellulose dissolution efficiency of the charge and structure of the cation and. We then discuss the use of cellulose solutions in these solvents for its derivatization under homogeneous and heterogeneous conditions. The products of interest are cellulose esters and ethers; our emphasis is on the role of solvent and possible side reactions. The final part is concerned with the use of cellulose dopes in these solvents for its shaping as fibers, a field with potential commercial application.

| S-EPMC6017797 | biostudies-other

Comparison of Cellulose Dissolution Behavior by Alkaline and Sulfuric Acid Solvents and Their Films' Physical Properties.

Project description:Three alkaline mixtures (NaOH/thiourea, NaOH/urea/thiourea, NaOH/urea/ZnO) and sulfuric acid were used at low temperatures as cellulose solvents, and their cellulose solubility and films' physical properties for bleached chemical wood pulps and cotton linter were compared. Their degree of polymerization (DP) was controlled to 600-800 before dissolution. Among the alkaline solvents, NaOH/urea/ZnO gave the film the highest tensile strength and stretch. When compared to sulfuric acid, NaOH/urea/ZnO gave lower strength properties but higher crystallinity indices in the films. While alkaline solvents could not dissolve the high DP cellulose (DP ~ 2000), sulfuric acid could dissolve the high DP cellulose at below zero Celsius temperature, and the strength properties of the films were not much different from that of the low DP one. It appeared that the low-temperature sulfuric acid treatment did away with the cellulose's DP controlling stage; it decreased cellulose DP very quickly for the high-DP cellulose at the initial stage, and as soon as the cellulose DP reached a DP low enough for dissolution, it began to dissolve the cellulose to result in stable cellulose solution.

| S-EPMC8465038 | biostudies-literature

Effects of Cellulose Nanocrystals and Cellulose Nanofibers on the Structure and Properties of Polyhydroxybutyrate Nanocomposites.

Project description:One of the major obstacles for polyhydroxybutyrate (PHB), a biodegradable and biocompatible polymer, in commercial applications is its poor elongation at break (~3%). In this study, the effects of nanocellulose contents and their types, including cellulose nanocrystals (CNCs) and cellulose nanofibers (CNFs) on the crystallization, thermal, and mechanical properties of PHB composites were systematically compared. We explored the toughening mechanisms of PHB by adding CNCs and cellulose CNFs. The results showed that when the morphology of bagasse nanocellulose was rod-like and its content was 1 wt %, the toughening modification of PHB was the best. Compared with pure PHB, the elongation at break and Young's modulus increased by 91.2% and 18.4%, respectively. Cellulose nanocrystals worked as heterogeneous nucleating agents in PHB and hence reduced its crystallinity and consequently improved the toughness of PHB. This simple approach could potentially be explored as a strategy to extend the possible applications of this biopolymer in packaging fields.

| S-EPMC6960622 | biostudies-literature

Strength and Water Interactions of Cellulose I Filaments Wet-Spun from Cellulose Nanofibril Hydrogels.

Project description:Hydrogels comprising cellulose nanofibrils (CNF) were used in the synthesis of continuous filaments via wet-spinning. Hydrogel viscosity and spinnability, as well as orientation and strength of the spun filaments, were found to be strongly affected by the osmotic pressure as determined by CNF surface charge and solid fraction in the spinning dope. The tensile strength, Young's modulus and degree of orientation (wide-angle X-ray scattering, WAXS) of filaments produced without drawing were 297 MPa, 21 GPa and 83%, respectively, which are remarkable values. A thorough investigation of the interactions with water using dynamic vapour sorption (DVS) experiments revealed the role of sorption sites in the stability of the filaments in wet conditions. DVS analysis during cycles of relative humidity (RH) between 0 and 95% revealed major differences in water uptake by the filaments spun from hydrogels of different charge density (CNF and TEMPO-oxidised CNF). It is concluded that the mechanical performance of filaments in the presence of water deteriorates drastically by the same factors that facilitate fibril alignment and, consequently, enhance dry strength. For the most oriented filaments, the maximum water vapour sorption at 95% RH was 39% based on dry weight.

| S-EPMC4964603 | biostudies-literature

Room-Temperature Self-Standing Cellulose-Based Hydrogel Electrolytes for Electrochemical Devices.

Project description:The trend of research towards more sustainable materials is pushing the application of biopolymers in a variety of unexplored fields. In this regard, hydrogels are attracting significant attention as electrolytes for flexible electrochemical devices thanks to their combination of ionic conductivity and mechanical properties. In this context, we present the use of cellulose-based hydrogels as aqueous electrolytes for electrochemical devices. These materials were obtained by crosslinking of hydroxyethyl cellulose (HEC) with divinyl sulfone (DVS) in the presence of carboxymethyl cellulose (CMC), creating a semi-IPN structure. The reaction was confirmed by NMR and FTIR. The small-amplitude oscillatory shear (SAOS) technique revealed that the rheological properties could be conveniently varied by simply changing the gel composition. Additionally, the hydrogels presented high ionic conductivity in the range of mS cm-1. The ease of synthesis and processing of the hydrogels allowed the assembly of an all-in-one electrochromic device (ECD) with high transmittance variation, improved switching time and good color efficiency. On the other hand, the swelling ability of the hydrogels permits the tuning of the electrolyte to improve the performance of a printed Zinc/MnO2 primary battery. The results prove the potential of cellulose-based hydrogels as electrolytes for more sustainable electrochemical devices.

| S-EPMC7696359 | biostudies-literature

Structure and solvents effects on the optical properties of sugar-derived carbon nanodots.

Project description:Carbon nanodots are a new and intriguing class of fluorescent carbon nanomaterials and are considered a promising low cost, nontoxic alternative to traditional inorganic quantum dots in applications such as bioimaging, solar cells, photocatalysis, sensors and others. Despite the abundant available literature, a clear formation mechanism for carbon nanodots prepared hydrothermally from biomass precursors along with the origins of the light emission are still under debate. In this paper, we investigate the relationships between the chemical structure and optical properties of carbon nanodots prepared by the hydrothermal treatment of glucose. Our major finding is that the widely reported excitation-dependent emission originates from solvents used to suspend the as-prepared carbon nanodots, while emission from dry samples shows no excitation-dependence. Another important highlight is that the hydrothermal conversion of biomass-derivatives under subcritical conditions leads to a heterogeneous mixture of amorphous-like nanoparticles, carbon onion-type and crystalline carbons composed of at least three different phases. The potential chemical reaction pathways involved in the formation of these hydrothermal carbon products along with a comprehensive structural and optical characterization of these systems is also provided.

| S-EPMC5920085 | biostudies-literature

Investigation of cellulose dissolution in morpholinium-based solvents: impact of solvent structural features on cellulose dissolution.

Project description:A series of N-methylmorpholinium salts with varying N-alkyl chains and Cl-, OAc- and OH- as counter ions have been synthesized and investigated for their ability to dissolve cellulose, aiming at elucidating solvent structural features affecting cellulose dissolution. Synthesis procedures have been developed to, to a high extent, rely on conversions in water and microwave-assisted reactions employing a reduced number of work-up steps and ion-exchange resins that can be regenerated. Water solutions of morpholinium hydroxides proved capable of dissolving cellulose, with those of them possessing alkyl chains longer than ethyl showing surprising dissolution ability at room-temperature. Morpholinium acetates behaved as ionic liquids, and were also capable of dissolving cellulose when combined with DMSO. The obtained cellulose solutions were characterized according to their chemical and colloidal stability using 13C NMR spectroscopy, size exclusion chromatography and flow sweep measurements, while the ethanol coagulates were investigated in terms of crystallinity using solid state NMR. In contrast, the morpholinium chlorides obtained were hygroscopic with high melting points and low solubility in common organic solvents e.g., acetone, DMSO and DMAc, thus lacking the ability to swell or dissolve cellulose.

| S-EPMC10280132 | biostudies-literature

Emulsion Stabilization with Functionalized Cellulose Nanoparticles Fabricated Using Deep Eutectic Solvents.

Project description:In this experiment, the influence of the morphology and surface characteristics of cellulosic nanoparticles (i.e., cellulose nanocrystals [CNCs] and cellulose nanofibers [CNFs]) on oil-in-water (o/w) emulsion stabilization was studied using non-modified or functionalized nanoparticles obtained following deep eutectic solvent (DES) pre-treatments. The effect of the oil-to-water ratio (5, 10, and 20 wt.-% (weight percent) of oil), the type of nanoparticle, and the concentration of the particles (0.05?0.2 wt.-%) on the oil-droplet size (using laser diffractometry), o/w emulsion stability (via analytical centrifugation), and stabilization mechanisms (using field emission scanning electron microscopy with the model compound-i.e., polymerized styrene in water emulsions) were examined. All the cellulosic nanoparticles studied decreased the oil droplet size in emulsion (sizes varied from 22.5 µm to 8.9 µm, depending on the nanoparticle used). Efficient o/w emulsion stabilization against coalescence and an oil droplet-stabilizing web-like structure were obtained only, however, with surface-functionalized CNFs, which had a moderate hydrophilicity level. CNFs without surface functionalization did not prevent either the coalescence or the creaming of emulsions, probably due to the natural hydrophobicity of the nanoparticles and their instability in water. Moderately hydrophilic CNCs, on the other hand, distributed evenly and displayed good interaction with both dispersion phases. The rigid structure of CNCs meant, however, that voluminous web structures were not formed on the surface of oil droplets; they formed in flat, uniform layers instead. Consequently, emulsion stability was lower with CNCs, when compared with surface-functionalized CNFs. Tunable cellulose nanoparticles can be used in several applications such as in enhanced marine oil response.

| S-EPMC6278293 | biostudies-literature

Effects of asymmetric nanostructures on the extinction difference properties of actin biomolecules and filaments.

Project description:In this paper, symmetric and asymmetric tapering on the arms of the gammadion nanostructure is proposed to enhance both local field distribution and extinction difference (ED). The asymmetric tapered gammadion with tapering fraction (TF) of 0.67 is seen to have the largest ED and spatial local field distribution, producing a large wavelength shift of more than 50 percent as compared to the untapered gammadion nanostructures when immersed in a solution of actin molecules and filaments. The optical chirality, ? shows that the larger local field amplitudes produced by the asymmetric designs increases the rate of chiral molecules excitation. This enhanced field is strongly rotating and highly sensitive to single molecules and larger filaments. Here, we show that the ED, optical chirality, sensitivity and rate of chiral molecules excitation can be improved by incorporating asymmetric designs into chiral gammadion nanostructures through tapering.

| S-EPMC4726270 | biostudies-literature

Absorbent Filaments from Cellulose Nanofibril Hydrogels through Continuous Coaxial Wet Spinning.

Project description:A continuous and scalable method for the wet spinning of cellulose nanofibrils (CNFs) is introduced in a core/shell configuration. Control on the interfacial interactions was possible by the choice of the shell material and coagulant, as demonstrated here with guar gum (GG) and cellulose acetate (CA). Upon coagulation in acetone, ethanol, or water, GG and CA formed supporting polymer shells that interacted to different degrees with the CNF core. Coagulation rate was shown to markedly influence the CNF orientation in the filament and, as a result, its mechanical strength. The fastest coagulation noted for the CNF/GG core/shell system in acetone led to an orientation index of ?0.55 (Herman's orientation parameter of 0.40), Young's modulus of ?2.1 GPa, a tensile strength of ?70 MPa, and a tenacity of ?8 cN/tex. The system that underwent the slowest coagulation rate (CNF/GG in ethanol) displayed a limited CNF orientation but achieved an intermediate level of mechanical resistance, owing to the strong core/shell interfacial affinity. By using CA as the supporting shell, it was possible to spin CNF into filaments with high water absorption capacity (43 g water/g dry filament). This was explained by the fact that water (used as the coagulant for CA) limited the densification of the CNF core structure, yielding filaments with high accessible area and pore density.

| S-EPMC6150648 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data