Stereolithography 3D Printing of Lignin-Reinforced Composites with Enhanced Mechanical Properties.

ABSTRACT: Due to the availability, biodegradability, and biological effects, lignin has emerged as an interesting alternative to petroleum-based compounds for developing sustainable chemicals, materials, and composites. In this study, lignin at various concentrations was incorporated into methacrylate resin via solution blending to fabricate lignin-reinforced composites using stereolithography apparatus three-dimensional printing. Softwood kraft lignin in the amounts of 0.2, 0.4, 0.5, 0.8, and 1.0 wt % in the methacrylate resin was used as a printing ink, and the gel contents and relative contents of the residual resin in the printed samples with various lignin concentrations were measured. The effects of the lignin on the ultimate mechanical properties of the non-postcured and postcured printed composites were determined. The tensile testing results revealed that the incorporation of lignin in the composite increased the tensile strength by 46-64% and Young's modulus by 13-37% for the postcured printed composites compared with that of the control sample (no lignin added). Employing a 0.4 wt % softwood kraft lignin, the tensile strength of the postcured printed composite reached the highest value of 49.0 MPa, which was a 60% increase in comparison to that of the control sample with 30.7 MPa. Scanning electron microscopy images of the fracture samples illustrated that the lignin-incorporated composites exhibited a rougher fracture surface that can presumably dissipate the stress, which could be a contributing factor for the mechanical enhancement.

SUBMITTER: Zhang S

PROVIDER: S-EPMC6893962 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

3D Printing of Continuous Fiber Reinforced Low Melting Point Alloy Matrix Composites: Mechanical Properties and Microstructures.

Project description:A novel 3D printing route to fabricate continuous fiber reinforced metal matrix composite (CFRMMC) is proposed in this paper. It is distinguished from the 3D printing process of polymer matrix composite that utilizes the pressure inside the nozzle to combine the matrix with the fiber. This process combines the metallic matrix with the continuous fiber by utilizing the wetting and wicking performances of raw materials to form the compact internal structures and proper fiber-matrix interfaces. CF/Pb50Sn50 composites were printed with the Pb50Sn50 alloy wire and modified continuous carbon fiber. The mechanical properties of the composite specimens were studied, and the ultimate tensile strength reached 236.7 MPa, which was 7.1 times that of Pb50Sn50 alloy. The fracture and interfacial microstructure were investigated and analyzed. The relationships between mechanical properties and interfacial reactions were discussed. With the optimized process parameters, several composites parts were printed to demonstrate the advantages of low cost, short fabrication period and flexibility in fabrication of complex structures.

| S-EPMC7475899 | biostudies-literature

Two-Step Preparation of CCF/PEEK Wrapped Yarn for 3D Printing Composites with Enhanced Mechanical Properties.

Project description:Continuous fiber reinforced thermoplastic composites (CFTPCs) have shown advantages such as high strength, long life, corrosion resistance, and green recyclability. Three-dimensional printing of CFTPCs opened up a new strategy for the fabrication of composites with complicated structures, low cost, and short production cycles. However, a traditional 3D printing process usually causes poor impregnation of the fiber or surface damage of the fiber due to the short impregnation time or high viscosity of the thermoplastic resin. Here, continuous carbon fiber/poly(ether-ether-ketones) (CCF/PEEK) wrapped yarn was fabricated via powder impregnation and using double spinning technology for the 3D printing. The concentration of PEEK powder suspension and wire speed were optimized as 15% and 2.0 m/min. The twist of wrapped yarn was optimized as 1037 T/m. Mechanical testing showed that the 3D-printed composite wire had excellent tensile and bending strength, which was about 1.6~4.2 times larger than those without the powder pre-impregnation process. It is mainly attributed to the improved impregnation of the CF which took place during the powder pre-impregnation process. We believe that our research on wrapped yarn for 3D-printed composites provides an effective strategy for the 3D printing of composites with enhanced mechanical properties.

| S-EPMC9921352 | biostudies-literature

Mechanical Properties of Nonwoven Reinforced Thermoplastic Polyurethane Composites.

Project description:Reinforcement of flexible fibre reinforced plastic (FRP) composites with standard textile fibres is a potential low cost solution to less critical loading applications. The mechanical behaviour of FRPs based on mechanically bonded nonwoven preforms composed of either low or high modulus fibres in a thermoplastic polyurethane (TPU) matrix were compared following compression moulding. Nonwoven preform fibre compositions were selected from lyocell, polyethylene terephthalate (PET), polyamide (PA) as well as para-aramid fibres (polyphenylene terephthalamide; PPTA). Reinforcement with standard fibres manifold improved the tensile modulus and strength of the reinforced composites and the relationship between fibre, fabric and composite's mechanical properties was studied. The linear density of fibres and the punch density, a key process variable used to consolidate the nonwoven preform, were varied to study the influence on resulting FRP mechanical properties. In summary, increasing the strength and degree of consolidation of nonwoven preforms did not translate to an increase in the strength of resulting fibre reinforced TPU-composites. The TPU composite strength was mainly dependent upon constituent fibre stress-strain behaviour and fibre segment orientation distribution.

| S-EPMC5553526 | biostudies-literature

Mechanical, thermal, morphological, and rheological characteristics of high performance 3D-printing lignin-based composites for additive manufacturing applications.

Project description:The article presents different mechanical, thermal and rheological data corresponding to the morphological formation within various renewable lignin-based composites containing acrylonitrile butadiene styrene (ABS), acrylonitrile butadiene rubber (NBR41, 41 mol% nitrile content), and carbon fibers (CFs). The data of 3D-printing properties and morphology of 3D-printed layers of selected lignin-based composites are revealed. This data is related to our recent research article entitled "A general method to improve 3D-printability and inter-layer adhesion in lignin-based composites" (Nguyen et al., 2018 [1]).

| S-EPMC5997980 | biostudies-literature

Micrometer Copper-Zinc Alloy Particles-Reinforced Wood Plastic Composites with High Gloss and Antibacterial Properties for 3D Printing.

Project description:In this work, micrometer copper-zinc alloy particles-reinforced particleboard wood flour/poly (lactic acid) (mCu-Zn/PWF/PLA) wood plastic composites with high gloss and antibacterial properties for 3D printing were prepared by a melt blending process. The structure and properties of the composites with different contents of mCu-Zn were analyzed by means of mechanical testing, dynamic mechanical analysis, thermogravimetric analysis, differential scanning calorimetry, X-ray diffraction, scanning electron microscopy, and antibacterial testing. The results showed that the mechanical properties, thermal stability, and antibacterial performance of the composites were significantly improved, as mCu-Zn was added into the wood plastic composites. When adding 2 wt.% mCu-Zn, the flexural strength of mCu-Zn/PWF/PLA composites (with 5 wt.% of particleboard wood flour) (PWF) increased by 47.1% compared with pure poly (lactic acid) (PLA), and 18.9% compared with PWF/PLA wood plastic composites. The surface gloss was increased by 1142.6% compared with PWF/PLA wood plastic composites. Furthermore, the inhibition rates of mCu-Zn/PWF/PLA composites against Escherichia coli reached 90.43%. Therefore, this novel high gloss and antibacterial wood plastic composites for fused deposition modeling (FDM) 3D printing have potential applications in personalized and classic furniture, art, toys, etc.

| S-EPMC7182845 | biostudies-literature

Desktop-Stereolithography 3D-Printing of a Poly(dimethylsiloxane)-Based Material with Sylgard-184 Properties.

Project description:The advantageous physiochemical properties of poly(dimethylsiloxane) (PDMS) have made it an extremely useful material for prototyping in various technological, scientific, and clinical areas. However, PDMS molding is a manual procedure and requires tedious assembly steps, especially for 3D designs, thereby limiting its access and usability. On the other hand, automated digital manufacturing processes such as stereolithography (SL) enable true 3D design and fabrication. Here the formulation, characterization, and SL application of a 3D-printable PDMS resin (3DP-PDMS) based on commercially available PDMS-methacrylate macromers, a high-efficiency photoinitiator and a high-absorbance photosensitizer, is reported. Using a desktop SL-printer, optically transparent submillimeter structures and microfluidic channels are demonstrated. An optimized blend of PDMS-methacrylate macromers is also used to SL-print structures with mechanical properties similar to conventional thermally cured PDMS (Sylgard-184). Furthermore, it is shown that SL-printed 3DP-PDMS substrates can be rendered suitable for mammalian cell culture. The 3DP-PDMS resin enables assembly-free, automated, digital manufacturing of PDMS, which should facilitate the prototyping of devices for microfluidics, organ-on-chip platforms, soft robotics, flexible electronics, and sensors, among others.

| S-EPMC6286193 | biostudies-literature

Laminar Tendon Composites with Enhanced Mechanical Properties.

Project description:PURPOSE:A strong isotropic material that is both biocompatible and biodegradable is desired for many biomedical applications, including rotator cuff repair, tendon and ligament repair, vascular grafting, among others. Recently, we developed a technique, called "bioskiving" to create novel 2D and 3D constructs from decellularized tendon, using a combination of mechanical sectioning, and layered stacking and rolling. The unidirectionally aligned collagen nanofibers (derived from sections of decellularized tendon) offer good mechanical properties to the constructs compared with those fabricated from reconstituted collagen. METHODS:In this paper, we studied the effect that several variables have on the mechanical properties of structures fabricated from tendon slices, including crosslinking density and the orientation in which the fibers are stacked. RESULTS:We observed that following stacking and crosslinking, the strength of the constructs is significantly improved, with crosslinked sections having an ultimate tens ile strength over 20 times greater than non-crosslinked samples, and a modulus nearly 50 times higher. The mechanism of the mechanical failure mode of the tendon constructs with or without crosslinking was also investigated. CONCLUSIONS:The strength and fiber organization, combined with the ability to introduce transversely isotropic mechanical properties makes the laminar tendon composites a biocompatiable material that may find future use in a number of biomedical and tissue engineering applications.

| S-EPMC4327911 | biostudies-literature

Biobased Acrylate Photocurable Resin Formulation for Stereolithography 3D Printing.

Project description:To facilitate the ongoing transition toward a circular economy, the availability of renewable materials for additive manufacturing becomes increasingly important. Here, we report the successful fabrication of complex shaped prototypes from biobased acrylate photopolymer resins, employing a commercial stereolithography apparatus (SLA) 3D printer. Four distinct resins with a biobased content ranging from 34 to 67% have been developed. All formulations demonstrated adequate viscosity and were readily polymerizable by the UV-laser-based SLA process. Increasing the double-bond concentration within the resin results in stiff and thermally resilient 3D printed products. High-viscosity resins lead to high-resolution prototypes with a complex microarchitecture and excellent surface finishing, comparable to commercial nonrenewable resins. These advances can facilitate the wide application of biobased resins for construction of new sustainable products via stereolithographic 3D printing methods.

| S-EPMC6641428 | biostudies-literature

Carbon Fiber Reinforced Recycled Polypropylene/Polyolefin Elastomer Composites with High Mechanical Properties.

Project description:The treatment of waste plastics has gradually become a hot topic in the current scientific community. In response to the needs for high-impact performance R-PP-based composites, carbon fiber (CF)-reinforced polyolefin elastomer (POE)/recycled polypropylene (R-PP) composite (CF/POE/R-PP) was prepared by the mechanical blending method, and its mechanical and thermal properties were systematically studied. It was found that the CF could effectively improve the bending and notch impact strength as well as enhance the thermal stability of POE/R-PP. Furthermore, a stable and dispersed composite interface formed by the combination of maleic anhydride-grafted polypropylene (PP-g-MAH) with the surface of CF and the fusion alkyl chains in R-PP and POE further enhanced the CF's reinforcing effect. As a result, the addition of 9 wt.% CF successfully improved the heat resistance of the composite material, and the residual carbon content increased by 97.84% after sintering. The composite toughening of POE and CF effectively improved the impact strength of the composite material, with a maximum increase of over 1000%. This study ultimately resulted in a high-impact-resistant composite material.

| S-EPMC11013364 | biostudies-literature

Study on micromolecular mechanical properties of C-atom reinforced SBR polymer composites.

Project description:A three-layer microscopic model with Fe atoms as the top and bottom layer and SBR polymer composites as the middle layer and SBR polymer composite was established and studied. By adding C atoms as reinforcement, the stability and elastic modulus and frictional coefficient changes of SBR polymer composites before and after adding C atoms were studied. In this study, the molecular dynamics method was used to change of elastic modulus was observed by stretching, compression and shear of the SBR polymer composite; The simulation shows that after adding C atom the elastic modulus of SBR polymer composite increased, the friction coefficient of polymer composite upper and lower decreases and the relative atomsic concentration, temperature, velocity, overall temperature average, kinetic energy, total energy and MSD in the thickness direction are reduced after adding C atoms. The stability of SBR polymer composites is enhanced, and the deformation under shear is weakened. In addition, it is found that the binding energy between SBR polymer composites and Fe atoms is reduced after adding C atoms.The stability of SBR polymer composites is improved during use. This work provides a method for studying the properties of rubber composites by studying the enhancement of the stability of SBR polymer composites from the microscopic point of view.

| S-EPMC10762060 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data