Multifunctional flexible membranes from sponge-like porous carbon nanofibers with high conductivity.

ABSTRACT: Conductive porous carbon nanofibers are promising for environmental, energy, and catalysis applications. However, increasing their porosity and conductivity simultaneously remains challenging. Here we report chemical crosslinking electrospinning, a macro-micro dual-phase separation method, to synthesize continuous porous carbon nanofibers with ultrahigh porosity of >80% and outstanding conductivity of 980 S cm^-1. With boric acid as the crosslinking agent, poly(tetrafluoroethylene) and poly(vinyl alcohol) are crosslinked together to form water-sol webs, which are then electrospun into fibrous films. After oxidation and pyrolysis, the as-spun fibers are converted into B-F-N triply doped porous carbon nanofibers with well-controlled macro-meso-micro pores and large surface areas of ~750 m² g^-1. The sponge-like porous carbon nanofibers with substantially reduced mass transfer resistances exhibit multifunction in terms of gas adsorption, sewage disposal, liquid storage, supercapacitors, and batteries. The reported approach allows green synthesis of high-performance porous carbon nanofibers as a new platform material for numerous applications.

SUBMITTER: Yan J

PROVIDER: S-EPMC6897989 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Membranes of MnO Beading in Carbon Nanofibers as Flexible Anodes for High-Performance Lithium-Ion Batteries.

Project description:Freestanding yet flexible membranes of MnO/carbon nanofibers are successfully fabricated through incorporating MnO2 nanowires into polymer solution by a facile electrospinning technique. During the stabilization and carbonization processes of the as-spun membranes, MnO2 nanowires are transformed to MnO nanoparticles coincided with a conversion of the polymer from an amorphous state to a graphitic structure of carbon nanofibers. The hybrids consist of isolated MnO nanoparticles beading in the porous carbon and demonstrate superior performance when being used as a binder-free anode for lithium-ion batteries. With an optimized amount of MnO (34.6 wt%), the anode exhibits a reversible capacity of as high as 987.3 mAh g(-1) after 150 discharge/charge cycles at 0.1 A g(-1), a good rate capability (406.1 mAh g(-1) at 3 A g(-1)) and an excellent cycling performance (655 mAh g(-1) over 280 cycles at 0.5 A g(-1)). Furthermore, the hybrid anode maintains a good electrochemical performance at bending state as a flexible electrode.

| S-EPMC4570985 | biostudies-literature

Flexible, Porous, and Metal-Heteroatom-Doped Carbon Nanofibers as Efficient ORR Electrocatalysts for Zn-Air Battery.

Project description:Developing an efficient and durable oxygen reduction electrocatalyst is critical for clean-energy technology, such as fuel cells and metal-air batteries. In this study, we developed a facile strategy for the preparation of flexible, porous, and well-dispersed metal-heteroatom-doped carbon nanofibers by direct carbonization of electrospun Zn/Co-ZIFs/PAN nanofibers (Zn/Co-ZIFs/PAN). The obtained Zn/Co and N co-doped porous carbon nanofibers carbonized at 800 °C (Zn/Co-N@PCNFs-800) presented a good flexibility, a continuous porous structure, and a superior oxygen reduction reaction (ORR) catalytic activity to that of commercial 20 wt% Pt/C, in terms of its onset potential (0.98 V vs. RHE), half-wave potential (0.89 V vs. RHE), and limiting current density (- 5.26 mA cm-2). In addition, we tested the suitability and durability of Zn/Co-N@PCNFs-800 as the oxygen cathode for a rechargeable Zn-air battery. The prepared Zn-air batteries exhibited a higher power density (83.5 mW cm-2), a higher specific capacity (640.3 mAh g-1), an excellent reversibility, and a better cycling life than the commercial 20 wt% Pt/C + RuO2 catalysts. This design strategy of flexible porous non-precious metal-doped ORR electrocatalysts obtained from electrospun ZIFs/polymer nanofibers could be extended to fabricate other novel, stable, and easy-to-use multi-functional electrocatalysts for clean-energy technology.

| S-EPMC7770869 | biostudies-literature

Self-Assembled Porous-Silica within N-Doped Carbon Nanofibers as Ultra-flexible Anodes for Soft Lithium Batteries.

Project description:Silica is an attractive anode material for soft lithium batteries owing to its high specific capacity, but it suffers severe problems of large volume change and unstable solid-electrolyte interface. Moreover, it is a challenge to fabricate flexible silica anodes. Here, we report a low-cost and scalable strategy to create flexible anodes of N-doped carbon nanofiber-confined porous silica (p-SiO2@N-CNF) by developing a sol-gel electrospinning process followed by carbonization. This approach causes the p-SiO2 nanoparticles (NPs) to be self-assembled within the N-CNFs, which act like elastomer and electrolyte barrier to accommodate volume changes and to enhance the stability of SiO2, whereas the NPs act as soft plasticizer providing strength to the CNF skeletons. Benefiting from the hierarchical structures, the anodes with high p-SiO2 loadings (>1.6 mg/cm2) exhibit exceptional cycling performance (>1,000 cycles) in terms of bending, current rate, and capacity. Moreover, the batteries remain stable when discharging at 0.5 C and charging at 2 C.

| S-EPMC6545390 | biostudies-literature

Stepwise Fabrication of Co-Embedded Porous Multichannel Carbon Nanofibers for High-Efficiency Oxygen Reduction.

Project description:A novel nonprecious metal material consisting of Co-embedded porous interconnected multichannel carbon nanofibers (Co/IMCCNFs) was rationally designed for oxygen reduction reaction (ORR) electrocatalysis. In the synthesis, ZnCo2O4 was employed to form interconnected mesoporous channels and provide highly active Co3O4/Co core-shell nanoparticle-based sites for the ORR. The IMC structure with a large synergistic effect of the N and Co active sites provided fast ORR electrocatalysis kinetics. The Co/IMCCNFs exhibited a high half-wave potential of 0.82 V (vs. reversible hydrogen electrode) and excellent stability with a current retention up to 88% after 12,000 cycles in a current-time test, which is only 55% for 30 wt% Pt/C.

| S-EPMC7770944 | biostudies-literature

Multifunctional Polymer Nanofibers: UV Emission, Optical Gain, Anisotropic Wetting, and High Hydrophobicity for Next Flexible Excitation Sources.

Project description:The use of UV light sources is highly relevant in many fields of science, being directly related to all those detection and diagnosis procedures that are based on fluorescence spectroscopy. Depending on the specific application, UV light-emitting materials are desired to feature a number of opto-mechanical properties, including brightness, optical gain for being used in laser devices, flexibility to conform with different lab-on-chip architectures, and tailorable wettability to control and minimize their interaction with ambient humidity and fluids. In this work, we introduce multifunctional, UV-emitting electrospun fibers with both optical gain and greatly enhanced anisotropic hydrophobicity compared to films. Fibers are described by the onset of a composite wetting state, and their arrangement in uniaxial arrays further favors liquid directional control. The low gain threshold, optical losses, plastic nature, flexibility, and stability of these UV-emitting fibers make them interesting for building light-emitting devices and microlasers. Furthermore, the anisotropic hydrophobicity found is strongly synergic with optical properties, reducing interfacial interactions with liquids and enabling smart functional surfaces for droplet microfluidic and wearable applications.

| S-EPMC4598823 | biostudies-literature

Encapsulating MoO2 Nanocrystals into Flexible Carbon Nanofibers via Electrospinning for High-Performance Lithium Storage.

Project description:Design and synthesis of flexible and self-supporting electrode materials in high-performance lithium storage is significant for applications in the field of smart wearable devices. Herein, flexible carbon nanofiber membranes with uniformly distributed molybdenum dioxide (MoO2) nanocrystals are fabricated by a needlefree electrospinning method combined with the subsequent carbonization process, which exhibits outstanding structural stability under abrasion and deformation. The as-fabricated lithium-ion batteries (LIBs) exhibit a high discharge of 450 mAh g-1 after 500 cycles at 2000 mA g-1 by using the MoO2/C nanofiber membrane as the self-supporting anode. Further, the nanofibers structure remains intact after 500 cycles, which reflects the excellent stability of the materials. This study provides a simple and effective method for the preparation of MoO2/C nanofiber materials, which can not only maintain its excellent electrochemical and physical properties, but also easily realize large-scale production. It is undoubtedly beneficial for the development of flexible LIBs and smart wearable devices.

| S-EPMC7793480 | biostudies-literature

A green approach to prepare hierarchical porous carbon nanofibers from coal for high-performance supercapacitors.

Project description:A green method is designed to obtain hierarchical porous carbon nanofibers from coal. In the work, deionized water, coal, polyvinyl alcohol and Pluronic F127 are used as the aqueous solution, carbon source, spinning assistant and soft template for spinning, respectively. As electrode materials for supercapacitors, the obtained hierarchical porous carbon nanofibers exhibit a high specific capacitance of 265.2 F g-1 at 1.0 A g-1 in 6 M KOH, a good rate performance with a capacitance of 220.3 F g-1 at 20.0 A g-1 with the retention of 83.1% and a superior cycle stability without capacitance loss after 20 000 charge/discharge cycles at 10.0 A g-1. Compared with the carbon nanofibers constructed without Pluronic F127, the enhanced electrochemical performance of the sample benefits from a larger contact surface area and the mesoporous structure formed by decomposition of Pluronic F127 and good structural stability. This work not only provides a green route for high-value utilization of coal in energy storage, but also paves a new way to make hierarchical porous carbon nanofibers from coal for supercapacitor electrodes with high specific capacitance and long cycle life.

| S-EPMC9060944 | biostudies-literature

Microstructure and Electrical Conductivity of Electrospun Titanium Oxynitride Carbon Composite Nanofibers.

Project description:Titanium oxynitride carbon composite nanofibers (TiON/C-CNFs) were synthesised with electrospinning and subsequent heat treatment in ammonia gas. In situ four-probe electrical conductivity measurements of individual TiON/C-CNFs were performed. Additionally, the TiON/C-CNFs were thoroughly analysed with various techniques, such as X-ray and electron diffractions, electron microscopies and spectroscopies, thermogravimetric analysis and chemical analysis to determine the crystal structure, morphology, chemical composition, and N/O at. ratio. It was found that nanofibers were composed of 2-5 nm sized titanium oxynitride (TiON) nanoparticles embedded in an amorphous carbon matrix with a small degree of porosity. The average electrical conductivity of a single TiON/C-CNF was 1.2 kS/m and the bulk electrical conductivity of the TiON/C-CNF fabric was 0.053 kS/m. From the available data, the mesh density of the TiON/C-CNF fabric was estimated to have a characteristic length of 1.0 µm and electrical conductivity of a single TiON/C-CNF was estimated to be from 0.45 kS/m to 19 kS/m. The electrical conductivity of the measured TiON/C-CNFs is better than that of amorphous carbon nanofibers and has ohmic behaviour, which indicates that it can effectively serve as a new type of support material for electrocatalysts, batteries, sensors or supercapacitors.

| S-EPMC9268360 | biostudies-literature

Porous Ionic Membrane Based Flexible Humidity Sensor and its Multifunctional Applications.

Project description:A highly flexible porous ionic membrane (PIM) is fabricated from a polyvinyl alcohol/KOH polymer gel electrolyte, showing well-defined 3D porous structure. The conductance of the PIM changes more than 70 times as the relative humidity (RH) increases from 10.89% to 81.75% with fast and reversible response at room temperature. In addition, the PIM-based sensor is insensitive to temperature (0-95 °C) and pressure (0-6.8 kPa) change, which indicates that it can be used as highly selective flexible humidity sensor. A noncontact switch system containing PIM-based sensor is assembled, and results show that the switch responds favorably to RH change caused by an approaching finger. Moreover, an attachable smart label using PIM-based sensor is explored to measure the water contents of human skin, which shows a great linear relationship between the sensitivity of the sensor and the facial water contents measured by a commercial reference device.

| S-EPMC5441428 | biostudies-literature

Flexible membranes of MoS2/C nanofibers by electrospinning as binder-free anodes for high-performance sodium-ion batteries.

Project description:A flexible membrane consisting of MoS2/carbon nanofibers has been fabricated by a simple electrospinning method. MoS2 nanosheets are uniformly encapsulated in the inter-connected carbon nanofibers with diameters of ~150 nm. When evaluated as a binder-free electrode for sodium-ion batteries, the as-obtained electrode demonstrates high performances, including high reversible capacity of 381.7 mA h g(-1) at 100 mA g(-1) and superior rate capability (283.3, 246.5 and 186.3 mA h g(-1) at 0.5, 1 and 2 A g(-1), respectively). Most importantly, the binder-free electrode made of MoS2 and carbon nanofibers can still deliver a charge capacity of 283.9 mA h g(-1) after 600 cycles at a current density of 100 m A g(-1), indicating a very promising anode for long-life SIBs.

| S-EPMC5380159 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data