Effect of adding TiO2 nanoparticles on the SEM morphology and mechanical properties of conventional heat-cured acrylic resin.

ABSTRACT: Background. The current study evaluated the compressive, flexural and impact strengths of heat-cured acrylic resins reinforced by TiO2 nanoparticles (NPs). Methods. TiO2 NPs were provided and characterized using scanning electron microscopy (SEM) to determine their morphology and crystalline structure. For three mechanical tests, 12 acrylic resin groups (n=9), totaling 108 specimens, were prepared using a special mold for each test, with TiO2 nanoparticle contents of 0, 0.5, 1 or 2 wt% in different groups. After curing, the compressive, flexural and impact strengths of the specimens were examined according to ISO 1567. Results. In the SEM and XRD study of TiO2 NPs, anatase was identified as the major crystalline phase followed by rutile (average particle size: 20.4 nm). SEM images showed that the nanocomposite with 1 wt% NPs had a more homogenized blend. 1 wt% TiO2 nanocomposite exhibited a higher, but non-significant, impact strength compared to the controls. ANOVA showed significant differences in the impact and flexural strengths between nanocomposites with various contents of TiO2 NPs. Conclusion. The nanocomposite with 1 wt% TiO2 NPs exhibited fewer micro-pores and micro-cracks in the SEM crosssections. A non-significant increase was also observed in the impact strength with TiO2 NPs at 1 wt%. Further increase in TiO2 NPs decreased both the impact and flexural strengths. The compressive strength of the heat-cured acrylic resin was not affected by the incorporation of NPs.

SUBMITTER: Moslehifard E

PROVIDER: S-EPMC6904916 | biostudies-literature | 2019

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Effect of adding TiO2 nanoparticles on the SEM morphology and mechanical properties of conventional heat-cured acrylic resin.

Moslehifard Elnaz E Robati Anaraki Mahmood M Shirkavand Saeed S

Journal of dental research, dental clinics, dental prospects 20191007 3

Background. The current study evaluated the compressive, flexural and impact strengths of heat-cured acrylic resins reinforced by TiO2 nanoparticles (NPs). Methods. TiO2 NPs were provided and characterized using scanning electron microscopy (SEM) to determine their morphology and crystalline structure. For three mechanical tests, 12 acrylic resin groups (n=9), totaling 108 specimens, were prepared using a special mold for each test, with TiO ...[more]

PMID: 31857871

Similar Datasets

Project description:Flexural strength (FS) of denture base resins (DBRs) had been improved by reinforcing it with different glass fibers. However, a limited data are available on the effect of glass fiber reinforcement with conventional heat-cured resin after prolonged water storage.This study aimed to evaluate the reinforcing effect of novel S-glass and nylon fibers on the FS of acrylic DBRs. It also aimed to evaluate the effect of glass fiber reinforcement on the FS of acrylic DBRs after a prolonged storage in water.One hundred and sixty identical specimens were fabricated in specially designed molds according to the manufacturer's instructions. The three experimental groups were prepared consisting of conventional (unreinforced) acrylic resin, novel S-glass fiber-reinforced and nylon fiber-reinforced acrylic resin. The specimens were fabricated in a standardized fashion for each experimental group. Each group was further subdivided into two groups on the basis of storage conditions (dry and wet). FS was tested using a three-point universal testing machine at a crosshead speed of 5 mm/min. Glass fiber-reinforced group was further tested after prolonged storage in distilled water. Entered data were statistically analyzed with one-way ANOVA and least significant difference post hoc test.In this study, statistically significant differences were noted in the FS of all the groups. S-glass fiber-reinforced group had highest FS compared to the other two groups (P < 0.001). Nylon fiber-reinforced group had lowest FS. All the groups stored in distilled water revealed a decrease in strength compared to those stored in dry atmosphere. Among wet specimens, those stored for 3 weeks had a significantly higher FS than those stored at one and 2 weeks (P < 0.01).Within the limitations of this investigation, the FS of heat-cured acrylic DBR was improved after reinforcement with glass fibers. It can be recommended to strengthen distal extension partial and complete denture bases. Nylon fibers may not be desirable for strengthening acrylic denture bases.

Dataset Information

Effect of adding TiO2 nanoparticles on the SEM morphology and mechanical properties of conventional heat-cured acrylic resin.

Publications

Effect of adding TiO<sub>2</sub> nanoparticles on the SEM morphology and mechanical properties of conventional heat-cured acrylic resin.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets