Analysis of Cement Deterioration in Outdoor High-Voltage Insulator.

ABSTRACT: Suspension type porcelain insulators used in overhead transmission lines comprise metal, ceramic, and cement. The deterioration of cement can lead to mechanical separation. For the degradation analysis, varied sizes of pores ranging from a few µm (capillary pores) to tens to hundreds of mm (detectable by naked eyes) were considered. Cracks that were hard to view with naked eyes were identified by staining with a fuchsine solution. The hydrogen ion concentration and pH value indicate the extent to which the cement is deteriorated. The longer the cement is used, the lower its pH value. High mechanical strength is considered an important advantage of porcelain insulators, and it may decline, if the cement is used for a longer period of time. Water ingress may also occur, resulting in expansion, due to the rehydration of the cement. The process and mechanism of expansion of cement, due to infiltration of water were described. As a method of analysis, a universal indicator was employed to evaluate the pH changes in cement. It was observed that the pH value was 12-13 for new products. However, for products that were used for 52 years, the pH value was under 7, which indicated an acidic tendency, due to deterioration.

SUBMITTER: Kim T

PROVIDER: S-EPMC6947335 | biostudies-literature | 2019 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Analysis of Cement Deterioration in Outdoor High-Voltage Insulator.

Kim Taeyong T Sanyal Simpy S Koo Ja-Bin JB Son Ju-Am JA Choi In-Hyuk IH Yi Junsin J

Materials (Basel, Switzerland) 20191213 24

Suspension type porcelain insulators used in overhead transmission lines comprise metal, ceramic, and cement. The deterioration of cement can lead to mechanical separation. For the degradation analysis, varied sizes of pores ranging from a few µm (capillary pores) to tens to hundreds of mm (detectable by naked eyes) were considered. Cracks that were hard to view with naked eyes were identified by staining with a fuchsine solution. The hydrogen ion concentration and pH value indicate the extent t ...[more]

PMID: 31847266

Similar Datasets

Project description:Bamboo's mechanical and aesthetic properties are significantly influenced by fungi. However, few studies have been conducted to investigate the structure and dynamics of fungal communities in bamboo during its natural deterioration. In this study, fungal community succession and characteristic variations of round bamboo in roofed and unroofed environments over a period of 13 weeks of deterioration were deciphered using high-throughput sequencing and multiple characterization methods. A total of 459 fungal Operational Taxonomic Units (OTUs) from eight phyla were identified. The fungal community's richness of roofed bamboo samples showed an increasing trend, whereas that of unroofed bamboo samples presented a declining trend during deterioration. Ascomycota and Basidiomycota were the dominant phyla throughout the deterioration process in two different environments: Basidiomycota was found to be an early colonizer of unroofed bamboo samples. Principal Coordinates Analysis (PCoA) analysis suggested that the deterioration time had a greater impact on fungal community variation compared to the exposure conditions. Redundancy analysis (RDA) further revealed that temperature was a major environmental factor that contributed to the variation in fungal communities. Additionally, the bamboo epidermis presented a descending total amount of cell wall components in both roofed and unroofed conditions. The correlation analysis between the fungal community and relative abundance of three major cell wall components elucidated that Cladosporium was negatively correlated with hemicellulose in roofed samples, whereas they presented a positive correlation with hemicellulose and a negative correlation with lignin in unroofed samples. Furthermore, the contact angle decreased during the deterioration process in the roofed as well as unroofed samples, which could arise from the degradation of lignin. Our findings provide novel insights into the fungal community succession on round bamboo during its natural deterioration and give useful information for round bamboo protection.

Project description:In amphibian skeletal muscle calcium (Ca2+) sparks occur both as voltage-dependent and voltage-independent ligand-activated release events. However, whether their properties and their origin show similarities are still in debate. Elevated K+, constant Cl- content solutions were used to initiate small depolarizations of the resting membrane potential to activate dihydropyridine receptors (DHPR) and caffeine to open ryanodine receptors (RyR) on intact fibers. The properties of Ca2+ sparks observed under control conditions were compared to those measured on depolarized cells and those after caffeine treatment. Calcium sparks were recorded on intact frog skeletal muscle fibers using high time resolution confocal microscopy (x-y scan: 30 Hz). Sparks were elicited by 1 mmol/l caffeine or subthreshold depolarization to different membrane potentials. Both treatments increased the frequency of sparks and altered their morphology. Images were analyzed by custom-made computer programs. Both the amplitude (in ΔF/F0; 0.259 ± 0.001 vs. 0.164 ± 0.001; n = 24942 and 43326, respectively; mean ± SE, p < 0.001) and the full width at half maximum (FWHM, in μm; parallel with fiber axis: 2.34 ± 0.01 vs. 1.92 ± 0.01, p < 0.001; perpendicular to fiber axis: 2.08 ± 0.01 vs. 1.68 ± 0.01, p < 0.001) of sparks was significantly greater after caffeine treatment than on depolarized cells. 9.8% of the sparks detected on depolarized fibers and about one third of the caffeine activated sparks (29.7%) overlapped with another one on the previous frame on x-y scans. Centre of overlapping sparks travelled significantly longer distances between consecutive frames after caffeine treatment then after depolarization (in μm; 1.66 ± 0.01 vs. 0.95 ± 0.01, p < 0.001). Our results suggest that the two types of ryanodine receptors, the junctional RyRs controlled by DHPRs and the parajunctional RyRs are activated independently, using alternate ways, with the possibility of cooperation between neighboring release channels.

Dataset Information

Analysis of Cement Deterioration in Outdoor High-Voltage Insulator.

Publications

Analysis of Cement Deterioration in Outdoor High-Voltage Insulator.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets