Deterioration characteristics of cement-improved loess under dry-wet and freeze-thaw cycles.

ABSTRACT: The effects of cement dosage, compaction coefficient, molding method (vertical vibration method and static pressure method), and dry-wet and freeze-thaw cycles on the mechanical strength of cement-improved loess (CIL) were studied to reveal its strength degradation law under dry-wet and freeze-thaw cycles. Results show that when using the vertical vibration molding method, the strength degradation effect of CIL can be improved by increasing the cement dosage and compaction coefficient; however, it is not obvious. Under the action of dry-wet cycle, damages, such as voids and cracks of CIL, develop continuously. Further, the strength deteriorates continuously and does not decrease after more than 15 dry-wet cycles. Therefore, the dry-wet cycle degradation system is selected by considering the most unfavorable conditions. In the process of freeze-thaw alternation, the pores and fissures of CIL develop and evolve continuously and the strength deteriorates continuously under the joint influence of water and low temperature. The strength tends to become stable after more than 12 freeze-thaw cycles. According to the safety principle, the deterioration coefficient of the freeze-thaw cycles is 0.3.

SUBMITTER: Jiang YJ

PROVIDER: S-EPMC8248616 | biostudies-literature | 2021

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Deterioration characteristics of cement-improved loess under dry-wet and freeze-thaw cycles.

Jiang Ying-Jun YJ Ni Chen-Yang CY Sha Hong-Wei HW Li Zong-Hua ZH Cai Lu-Yao LY

PloS one 20210701 7

The effects of cement dosage, compaction coefficient, molding method (vertical vibration method and static pressure method), and dry-wet and freeze-thaw cycles on the mechanical strength of cement-improved loess (CIL) were studied to reveal its strength degradation law under dry-wet and freeze-thaw cycles. Results show that when using the vertical vibration molding method, the strength degradation effect of CIL can be improved by increasing the cement dosage and compaction coefficient; however, ...[more]

PMID: 34197469

Similar Datasets

Project description:Permeability characteristics of compacted loess is always an important topic in soil mechanics and geotechnical engineering. This study explored the permeability characteristics of compacted loess under different dry densities and wetting-drying cycles, and found that as the dry density increases, the compacted loess surface became denser, the saturation permeability coefficient and saturation infiltration rate decreased. However, the wetting-drying cycle presented the opposite result. Meanwhile, the evolution of the microstructure was investigated by Scanning Electron Microscope (SEM) and Nuclear Magnetic Resonance (NMR) to explain the change of its permeability characteristics. The size of compacted loess aggregates was quantitatively analyzed by Image-Pro Plus (IPP) software. It showed that the size of compacted loess aggregates for different dry densities were concentrated from 10-100 μm, occupying 65.0%, 58.19%, and 51.64% of the total aggregates area respectively. And the interesting finding was that the area occupied by 10-50 μm aggregates remained basically unchanged with the number of wetting-drying cycles increasing. Therefore, the size of 10-50 μm aggregates represented the transition zone of compacted loess. NMR analyses revealed that with increasing dry density, the volume of macropores in the compacted loess rapidly decreased, the volume of mesopores and small pores increased. Meanwhile, the change in micropores was relatively small. The pore volume of the compacted loess after three wetting-drying cycles increased by 8.56%, 8.61%, and 6.15%, respectively. The proportion of macropores in the total pore volume shows the most drastic change. Variations in aggregate size and connection relationships made it easier to form overhead structures between aggregates, and the increased of macropore volume will form more water channels. Therefore, the change in permeability characteristics of compacted loess is determined by aggregate size, loess surface morphology, and the total pore volume occupied by macropores.

Project description:Tissue material properties are crucial to understanding their mechanical function, both in healthy and diseased states. However, in certain circumstances logistical limitations can prevent testing on fresh samples necessitating one or more freeze-thaw cycles. To date, the nature and extent to which the material properties of articular cartilage are altered by repetitive freezing have not been explored. Therefore, the aim of this study is to quantify how articular cartilage mechanical properties, measured by nanoindentation, are affected by multiple freeze-thaw cycles. Canine cartilage plugs (n = 11) from medial and lateral femoral condyles were submerged in phosphate buffered saline, stored at 3-5°C and tested using nanoindentation within 12h. Samples were then frozen at -20°C and later thawed at 3-5°C for 3h before material properties were re-tested and samples re-frozen under the same conditions. This process was repeated for all 11 samples over three freeze-thaw cycles. Overall mean and standard deviation of shear storage modulus decreased from 1.76 ± 0.78 to 1.21 ± 0.77MPa (p = 0.91), shear loss modulus from 0.42 ± 0.19 to 0.39 ± 0.17MPa (p=0.70) and elastic modulus from 5.13 ± 2.28 to 3.52 ± 2.24MPa (p = 0.20) between fresh and three freeze-thaw cycles respectively. The loss factor increased from 0.31 ± 0.38 to 0.71 ± 1.40 (p = 0.18) between fresh and three freeze-thaw cycles. Inter-sample variability spanned as much as 10.47MPa across freezing cycles and this high-level of biological variability across samples likely explains why overall mean "whole-joint" trends do not reach statistical significance across the storage conditions tested. As a result multiple freeze-thaw cycles cannot be explicitly or statistically linked to mechanical changes within the cartilage. However, the changes in material properties observed herein may be sufficient in magnitude to impact on a variety of clinical and scientific studies of cartilage, and should be considered when planning experimental protocols.

Project description:This study investigates the thermal conductivity (λ) and volumetric heat capacity (C) of sandy soil samples under a variety of conditions, including freeze-thaw cycles at temperatures both above and below zero and differing moisture levels. To estimate these thermal properties, a novel predictive model, EFAttNet, was developed, which utilizes custom-designed embedding and attention-based fusion networks. When compared to traditional de Vries empirical models and other baseline algorithms, EFAttNet demonstrated superior accuracy. Preliminary measurements showed that λ values increased linearly with moisture content but decreased with temperature, whereas C values exhibited a rising trend with both moisture content and freezing temperature. Following freeze-thaw cycles, both λ and C were positively influenced by moisture content and freezing temperature. The EFAttNet-based model proved highly accurate in predicting thermal properties, particularly effective at capturing nonlinear relationships among the influencing factors. Among these factors, the degree of saturation had the most significant impact, followed by the number of freeze-thaw cycles, subzero temperatures, porosity, and moisture content. Notably, dry density exerted minimal influence on thermal properties, likely due to the overriding effects of other factors or specific soil characteristics, such as particle size distribution or mineralogical composition. These findings have significant implications for construction and engineering projects, especially in terms of sustainability and energy efficiency. The demonstrated accuracy of the EFAttNet-based model in estimating thermal properties under various conditions holds promise for practical applications. Although focused on specific soil types and conditions, the insights gained can guide further research and development in managing soil thermal properties across diverse environments, thereby enhancing our understanding and application in this field.

Dataset Information

Deterioration characteristics of cement-improved loess under dry-wet and freeze-thaw cycles.

Publications

Deterioration characteristics of cement-improved loess under dry-wet and freeze-thaw cycles.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets