Protection of Mild Steel by Waterborne Epoxy Coatings Incorporation of Polypyrrole Nanowires/Graphene Nanocomposites.

ABSTRACT: Polypyrrole nanowires/graphene (PPyNG) nanocomposites as anticorrosive fillers were prepared by in situ polymerization in order to improve the anticorrosion performance of waterborne epoxy coatings. Field emission scanning electron microscope (FESEM) and Fourier transform infrared spectroscopy (FTIR) characterized the morphologies and structures of the synthesized PPyNG. The polypyrrole nanowires with about 50 nm in diameter were obtained. Conjugation length of PPy was increased with the addition of graphene. Open circuit potential (OCP) measurements, Tafel polarization curves, and electrochemical impedance spectroscopy (EIS) using an electrochemical workstation evaluated the anticorrosion properties of the waterborne epoxy/PPyNG coatings (EPPyNG). The studied nanocomposite coating possessed superior corrosion protection performance when the graphene content of the filler was 2 wt %. Its corrosion rate was about 100 times lower than that of neat epoxy coating. The higher barrier properties of nanocomposite coating and passivation effect of polypyrrole nanowires were beneficial in corrosion protection.

SUBMITTER: Ding Y

PROVIDER: S-EPMC6960955 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Corrosion resistance of graphene/waterborne epoxy composite coatings in CO<sub>2</sub>-satarated NaCl solution.

Project description:This study investigated the corrosion resistance of graphene/waterborne epoxy composite coatings in CO2-satarated NaCl solution. The coatings were prepared by dispersing graphene in waterborne epoxy with the addition of carboxymethylcellulose sodium. The structure and composition of the coatings were characterized by scanning electron microscopy, transmission electron microscopy, Fourier-transform infrared and Raman spectroscopies. The corrosion resistance of the composite coatings was investigated by potentiodynamic polarization measurements and electrochemical impedance spectroscopy. Composite coatings with more uniform surfaces and far fewer defects than blank waterborne epoxy coatings were obtained on 1020 steel. The 0.5 wt% graphene/waterborne epoxy composite coating exhibited a much lower corrosion rate and provided better water resistance properties and long-term protection than those of the blank epoxy coating in CO2-satarated NaCl solution.

| S-EPMC7277262 | biostudies-literature

Preparation and Characterization of Graphene Oxide/Polyaniline/Polydopamine Nanocomposites towards Long-Term Anticorrosive Performance of Epoxy Coatings.

Project description:To address the challenging issues of metal materials corrosion in industries, which has caused huge economic losses and security threats to many facilities in marine environments, functional polymer coatings have been widely used and regarded as one of the simplest and most effective methods to prevent such an undesirable event. In this study, a new type of coating filler consisting of graphene oxide/polyaniline/polydopamine (GO-PANI-PDA) nanocomposites has been successfully synthesized. The morphology, structure, composition, and corrosion resistance performance of the GO-PANI-PDA (GPP) nanocomposites were investigated via a series of characterization methods. The results from our electrochemical impedance spectroscopy, potentiodynamic polarization curve and salt spray experiment showed that the best corrosion resistance performance of the coating is from GPP 21 with the epoxy/GO-PANI:PDA ratio of 2:1, which exhibited a positive corrosion potential (-0.51 V) shift from epoxy/GO-PANI coating (-0.64 V). The corrosion current density (3.83 × 10-8 A/cm2) of GPP 21 is nearly an order of magnitude lower than that of epoxy/GO-PANI (7.05 × 10-7 A/cm2). The good anti-corrosion performance was fascinatingly observed in salt spray tests even without obvious corrosion phenomenon after 30 days of testing. Due to these remarkable properties, GPP nanocomposites can be an outstanding candidate for the rapid development of broadband shielding and anticorrosive materials.

| S-EPMC9416128 | biostudies-literature

Plasma-enabled superhydrophobic coatings on mild steel.

Project description:This work demonstrates a new pathway to the direct on-surface fabrication of a superhydrophobic surface coating on mild steel. The coating was formed using dielectric barrier discharge (DBD) plasma to convert a liquid small-molecule precursor (1,2,4-tricholorobenzene) to a solid film via plasma-assisted on-surface polymerization. Plasma treatments were performed under a nitrogen atmosphere with a variety of power levels and durations. Samples were analysed by optical and scanning electron microscopy (SEM), energy-dispersive x-ray spectroscopy (EDS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), Raman spectroscopy, optical profilometry, contact angle measurement, and potentiodynamic polarisation tests. Wettability of the films varied with the plasma parameters, and through the inclusion of graphene nanoplatelets in the precursor. High-dose plasma exposures of the nanoplatelet-containing precursor created superhydrophobic films with water contact angles above 150°. Potentiodynamic polarisation tests revealed that the superhydrophobic coating provided little or no corrosion protection.

| S-EPMC9816161 | biostudies-literature

Novel nitrogen doped carbon dots enhancing the anticorrosive performance of waterborne epoxy coatings.

Project description:There are lots of research studies reporting the excellent performances of waterborne epoxy resin coatings to reduce environmental VOC levels. However, it has also been manifested that waterborne epoxy resin coatings do not have high corrosion resistance because of being hydrophilic. Herein, we utilized a kind of N doped carbon dot (N-CD) which has high ethanol solubility and low cytotoxicity to enhance the corrosion resistance of waterborne epoxy resin coatings as a nanofiller. The N-CDs were obtained through a solvothermal method by using 4-aminosalicylic acid (ASA) as a precursor. The diameter and height of N-CDs confirmed by scanning probe microscopy and transmission electron microscopy are 3-5 nm. Corrosion resistance performance of the coatings without and with N-CDs is investigated by electrochemical impedance spectroscopy by immersing them in 3.5 wt% NaCl (aq) for 70 days. The results indicate that the composite coatings with 0.5 wt% N-CDs show superior anticorrosive performance due to bond interactions between N-CDs and polymer chains, the defect repairing effect of N-CDs and the formation of compact Fe2O3 and Fe3O4 passivation layers.

| S-EPMC9418709 | biostudies-literature

Biobased Waterborne Polyurethane-Urea/SWCNT Nanocomposites for Hydrophobic and Electrically Conductive Textile Coatings.

Project description:Waterborne polyurethane-urea dispersions (WPUD), which are based on 100% bio-based semi-crystalline polyester polyol and isophorone diisocyanate, have been successfully synthesized and doped with single-walled carbon nanotubes (SWCNT) to obtain a finishing agent that provides textiles with multifunctional properties. The chemical structure of WPUD has been characterized by Fourier-transform infrared spectroscopy (FTIR) and nuclear magnetic resonance (NMR). The thermal properties have been evaluated by differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and dynamic mechanical thermal analysis (DMTA). Mechanical properties have been studied by tensile stress-strain analysis. Moreover, the particle size, particle size distribution (PSD), and stability of developed waterborne dispersions have been assessed by dynamic light scattering (DLS), Z-potential, and accelerated aging tests (analytical centrifugation). Subsequently, selected fabrics have been face-coated by the WPUD using knife coating method and their properties have been assessed by measuring water contact angle (WCA), water column, fabric stiffness, and air permeability. The electrical conductivity of textiles coated with SWCNT-doped WPUD has been evaluated by EN 1149 standard. Finally, the surface morphologies of uncoated and coated fabrics have been studied by scanning electron microscopy (SEM). All of the synthesized polyurethane-ureas provide the coated substrates with remarkable water-repellency and water column, being therefore a more sustainable alternative to waterproof coatings based on fluoropolymers, such as PTFE. The additivation of the polymeric matrices with SWCNT has led to textile coatings with excellent electrical conductivity, maintaining water column properties, giving rise to multifunctional coatings that are highly demanded in protective workwear and technical textiles.

| S-EPMC8156085 | biostudies-literature

Structural Properties of Epoxy-Silica Barrier Coatings for Corrosion Protection of Reinforcing Steel.

Project description:Reinforcement steel extensively applied in civil construction is susceptible to corrosion due to the carbonation process in reinforced concrete and chloride ions diffusion. Epoxy-silica-based coatings are a promising option to guarantee the long-term stability of reinforced concrete structures. In this study, the influence of the proportion between the poly (bisphenol-A-co-epichlorhydrin) resin (DGEBA) and the curing agent diethylenetriamine (DETA) on the structural, morphological, and barrier properties of epoxy-silica nanocomposites were evaluated. To simulate different stages of concrete aging, electrochemical impedance spectroscopy (EIS) assays were performed for coated samples in a 3.5 wt.% NaCl solution (pH 7) and in simulated concrete pore solutions (SCPS), which represent the hydration environment in fresh concrete (SCPS2, pH 14) and after carbonation (SCPS1, pH 8). The results showed that coatings with an intermediate DETA to DGEBA ratio of 0.4, presented the best long-term corrosion protection with a low-frequency impedance modulus of up to 3.8 GΩ cm2 in NaCl and SCPS1 solutions. Small-angle X-ray scattering and atomic force microscopy analysis revealed that the best performance observed for the intermediate DETA proportion is associated with the presence of larger silica nanodomains, which act as a filler in the cross-linked epoxy matrix, thus favoring the formation of an efficient diffusion barrier.

| S-EPMC9460649 | biostudies-literature

Disulfide exchange assisted self-healing epoxy/PDMS/graphene oxide nanocomposites.

Project description:Vitrimers, a class of polymeric networks that change their topology above a threshold temperature, have been investigated in recent years. In order to further extend their properties, in this research, we demonstrate disulfide exchange assisted polydimethylsiloxane (PDMS)- and graphene oxide (GO)-involved epoxy vitrimers, which exhibit a reduction in glass transition temperature and storage modulus with increase in flexural strain and low-temperature self-healing. Stress relaxation and Arrhenius study were carried out for the analysis of vitrimeric behavior, where the prepared epoxy material displays self-healing at 80 °C for 5 min, whereas a low-temperature self-healing (60 °C) was observed for epoxy/PDMS/GO nanocomposites.

| S-EPMC9419268 | biostudies-literature

Experimental Characterization and Modeling Multifunctional Properties of Epoxy/Graphene Oxide Nanocomposites.

Project description:Thermomechanical modeling of epoxy/graphene oxide under quasi-static and dynamic loading requires thermo-mechanical properties such as Young's modulus, Poisson's ratio, thermal conductivity, and frequency-temperature dependent viscoelastic properties. In this study, the effects of different graphene oxide (GO) concentrations (0.05, 0.1, and 0.2 wt%) within an epoxy matrix on several mechanical and thermal properties were investigated. The distribution of GO fillers in the epoxy was investigated using transmission electron microscopy (TEM). The digital image correlation (DIC) technique was employed during the tensile testing to determine Young's modulus and Poisson's ratio. Analytical models were used to predict Young's modulus and thermal conductivity, with an error of less than 13% and 9%, respectively. Frequency-temperature dependent phenomenological models were proposed to predict the storage moduli and loss tangent, with a reasonable agreement with experimental data. A relatively high storage modulus, heat-resistance index (THRI), and thermal conductivity were observed in 0.2 wt% nanocomposite samples compared with pure epoxy and other lower concentration GO nanocomposites. A high THRI and derivative of thermogravimetric analysis peak temperatures (Tm1 and Tm2) were exhibited by adding nano-fillers in the epoxy, which confirms higher thermal stability of nanocomposites than that of pristine epoxy.

| S-EPMC8401890 | biostudies-literature

A direct one-step synthesis of a smart graphene/silica nanocomposite and its application for improving the acid resistance and corrosion resistance properties of waterborne epoxy coatings.

Project description:Graphene has attracted tremendous attention as a potential building block of modern high performance coating systems. Herein, we demonstrate a green method for making reduced oxide graphene (rGO) using the natural product rutin as the reducing agent. The rGO, with residual rutin on the surface to provide surface affinity, is used in the one-step fabrication of a nanocomposite of rGO and silica nanoparticles (SN) with a corrosion inhibitor, benzotriazole (BTA), loaded in situ. The ternary nanocomposite, BTA@SN-rGO, can be easily dispersed in water. It not only has a high inhibitor loading capacity (85.1 μg mg-1) but also can release the inhibitor in a controlled manner triggered by pH. Combining both the extraordinarily good barrier properties and smart nanocontainer features, BTA@SN-rGO was further incorporated into an epoxy latex to assemble an intelligent anticorrosion coating. The effective duration of the coating protection for steel was remarkably prolonged in different media, especially in acidic media. In addition to the barrier capability, smart self-healing of artificial damage to the modified coating films is also shown. Electrochemical impedance spectroscopy (EIS) was applied to monitor the failure process of different kinds of coatings. All the results confirm the synergy of the passive and active functions of the BTA@SN-rGO coating.

| S-EPMC11016887 | biostudies-literature

Mechanical property and structure of covalent functionalised graphene/epoxy nanocomposites.

Project description:Thermally reduced graphene nanoplatelets were covalently functionalised via Bingel reaction to improve their dispersion and interfacial bonding with an epoxy resin. Functionalised graphene were characterized by microscopic, thermal and spectroscopic techniques. Thermal analysis of functionalised graphene revealed a significantly higher thermal stability compared to graphene oxide. Inclusion of only 0.1 wt% of functionalised graphene in an epoxy resin showed 22% increase in flexural strength and 18% improvement in storage modulus. The improved mechanical properties of nanocomposites is due to the uniform dispersion of functionalised graphene and strong interfacial bonding between modified graphene and epoxy resin as confirmed by microscopy observations.

| S-EPMC3953726 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data