Crystal Chemistry, Band-Gap Red Shift, and Electrocatalytic Activity of Iron-Doped Gallium Oxide Ceramics.

ABSTRACT: This work for the first time unfurls the fundamental mechanisms and sets the stage for an approach to derive electrocatalytic activity, which is otherwise not possible, in a traditionally known wide band-gap oxide material. Specifically, we report on the tunable optical properties, in terms of wide spectral selectivity and red-shifted band gap, and electrocatalytic behavior of iron (Fe)-doped gallium oxide (?-Ga2O3) model system. X-ray diffraction (XRD) studies of sintered Ga2-x Fe x O3 (GFO) (0.0 ? x ? 0.3) compounds provide evidence for the Fe3+ substitution at Ga3+ site without any secondary phase formation. Rietveld refinement of XRD patterns reveals that the GFO compounds crystallize in monoclinic crystal symmetry with a C2/m space group. The electronic structure of the GFO compounds probed using X-ray photoelectron spectroscopy data reveals that at lower concentrations, Fe exhibits mixed chemical valence states (Fe3+, Fe2+), whereas single chemical valence state (Fe3+) is evident for higher Fe content (x = 0.20-0.30). The optical absorption spectra reveal a significant red shift in the optical band gap with Fe doping. The origin of the significant red shift even at low concentrations of Fe (x = 0.05) is attributed to the strong sp-d exchange interaction originated from the 3d5 electrons of Fe3+. The optical absorption edge observed at ?450 nm with lower intensity is the characteristic of Fe-doped compounds associated with Fe3+-Fe3+ double-excitation process. Coupled with an optical band-gap red shift, electrocatalytic studies of GFO compounds reveal that, interestingly, Fe-doped Ga2O3 compound exhibits electrocatalytic activity in contrast to intrinsic Ga2O3. Fe-doped samples (GFO) demonstrated appreciable electrocatalytic activity toward the generation of H2 through electrocatalytic water splitting. An onset potential and Tafel slope of GFO compounds include ?900 mV, ?210 mV dec-1 (x = 0.15) and ?1036 mV, ?290 mV dec-1 (x = 0.30), respectively. The electrocatalytic activity of Fe-doped Ga-oxide compounds is attributed to the cumulative effect of different mechanisms such as doping resulting in new catalytic centers, enhanced conductivity, and electron mobility. Hence, in this report, for the first time, we explored a new pathway; the electrocatalytic behavior of Fe-doped Ga2O3 resulted due to Fe chemical states and red shift in the optical band gap. The implications derived from this work may be applicable to a large class of compounds, and further options may be available to design functional materials for electrocatalytic energy production.

SUBMITTER: Mallesham B

PROVIDER: S-EPMC6963903 | biostudies-literature | 2020 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Crystal Chemistry, Band-Gap Red Shift, and Electrocatalytic Activity of Iron-Doped Gallium Oxide Ceramics.

Mallesham Bandi B Roy Swadipta S Bose Saptasree S Nair Aruna N AN Sreenivasan Sreeprasad S Shutthanandan Vaithiyalingam V Ramana Chintalapalle V CV

ACS omega 20191227 1

This work for the first time unfurls the fundamental mechanisms and sets the stage for an approach to derive electrocatalytic activity, which is otherwise not possible, in a traditionally known wide band-gap oxide material. Specifically, we report on the tunable optical properties, in terms of wide spectral selectivity and red-shifted band gap, and electrocatalytic behavior of iron (Fe)-doped gallium oxide (β-Ga<sub>2</sub>O<sub>3</sub>) model system. X-ray diffraction (XRD) studies of sintered ...[more]

PMID: 31956757

Similar Datasets

Project description:In this work, we study the influence of reduced graphene oxide (rGO) on the morphology and chemistry of highly porous N,S-doped carbon cryogels. Simultaneously, we propose an easily upscalable route to prepare such carbons by adding graphene oxide (GO) in as-received suspended form to the aqueous solution of the ι-carrageenan and urea precursors. First, 1.25-5 wt% GO was incorporated into the dual-doped polymer matrix. The CO2, CO, and H2O emitted during the thermal treatments resulted in the multifaceted modification of the textural and chemical properties of the porous carbon. This facilitated the formation of micropores through self-activation and resulted in a substantial increase in the apparent surface area (up to 1780 m2/g) and pore volume (up to 1.72 cm3/g). However, adding 5 wt% GO led to overactivation. The incorporated rGO has an ordering effect on the carbon matrix. The evolving oxidative species influence the surface chemistry in a complex way, but sufficient N and S atoms (ca. 4 and >1 at%, respectively) were preserved in addition to the large number of developing defects. Despite the complexity of the textural and chemical changes, rGO increased the electrical conductivity monotonically. In alkaline oxygen reduction reaction (ORR) tests, the sample with 1.25 wt% GO exhibited a 4e- mechanism and reasonable stability, but a higher rGO content gradually compromised the performance of the electrodes. The sample containing 5 wt% GO was the most sensitive under oxidative conditions, but after stabilization it exhibited the highest gravimetric capacitance. In Li-ion battery tests, the coulombic efficiency of all the samples was consistently above 98%, indicating the high potential of these carbons for efficient Li-ion insertion and reinsertion during the charge-discharge process, thereby providing a promising alternative for graphite-based anodes. The cell from the 1.25 wt% GO sample showed an initial discharge capacity of 313 mAh/g, 95.1% capacity retention, and 99.3% coulombic efficiency after 50 charge-discharge cycles.

Dataset Information

Crystal Chemistry, Band-Gap Red Shift, and Electrocatalytic Activity of Iron-Doped Gallium Oxide Ceramics.

Publications

Crystal Chemistry, Band-Gap Red Shift, and Electrocatalytic Activity of Iron-Doped Gallium Oxide Ceramics.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets